Synthetic nanowire/nanotube-based solid substrates for controlled cell growth
- 3.2k Downloads
The behaviour of cells can be controlled by various microenvironments such as nanostructured cell-culture substrates with controlled nanotopography and chemical properties. One of promising substrates for controlled cell growth is a solid substrate comprised of synthetic one-dimensional nanostructures such as polymer nanofibers, carbon-based nanotubes/nanofibers, and inorganic nanowires. Such nanotube/nanowire structures have a similar dimension as extracellular matrix fibers, and their nanotopography and chemical properties can be easily controlled, which expands their possible applications in controlling the growth and differentiation of cells. This paper provides a concise review on the recent applications of solid substrates based on synthetic nanowires/nanotubes for controlled cell growth and differentiation.
KeywordsNanowire Nanotube Cell adhesion Cell growth Cell proliferation Cell differentiation
Cell behaviors, such as adhesion, proliferation and differentiation, are affected by various microenvironmental factors. Such microenvironments consist of extracellular matrices (ECM) with soluble components such as growth factors and cytokines. In order to create artificial microenvironments, biologically-derived materials have been intensively explored, since they have the advantages of being biocompatible and of having similar mechanical properties as native tissues –.
Recent advances in nanotechnology present new possibilities and strategies in cell therapy and tissue engineering. Synthetic bio-inspired materials have been developed to create new controllable microenvironments rather than just to mimic in-vivo environments ,. Among the synthetic nanomaterials, nanowires and nanotubes have a similar dimension with natural ECM components such as collagen and elastic fibers. The diameter of these nanostructures can be precisely controlled, and they can be aligned, patterned or constructed 3-dimensionally . These properties facilitate mimicking microenvironments of various tissues. For example, the parallel-alignment of nanowires mimics that of ECMs in tendon and muscle, and concentric whorls in bone and mesh-like lattices of skin.
Overview of properties of synthetic nanowires/nanotubes
Poly (e-caprolactone) (PCL)
0.01 ~ 100 μm
Structure (aligned, random)
Poly (L-lactic acid) (PLLA)
Poly (D,L-lactide-co-glycolide) (PLGA)
Signle wall carbon nanotube (swCNT) multi wall carbon nanotube (mwCNT)
1 ~ 2/2 ~ 100 nm
Structure (aligned, random, vertical)
Carbon nanofiber (CNF)
3.5 ~ 500 nm
10 ~ 100 nm
10 ~ 300 nm
Structure (aligned, random, vertical)
20 ~ 100 nm
Controlled cell growth (adhesion, proliferation) 
10 ~ 200 nm
Structure (aligned, random)
3 ~ 100 nm
Controlled cell growth (adhesion, differentiation) 
3 ~ 500 nm
Structure (aligned, random, vertical)
Intracellular delivery 
In this review, we discuss the cell engineering with solid substrates based on synthetic nanowires/nanotubes, especially polymer nanofibers, carbon based nanostructures and inorganic nanowires. The cellular adhesion, proliferation and differentiation on these substrates and various other applications will be discussed.
2.1 Polymer nanofiber-based substrates
A polymer nanofiber is a one-dimensional nanostructure which is comprised of synthetic small molecules typically connected by covalent chemical bonds. The most important and distinguished property of polymer nanofibers compared to other synthetic nanowires is biodegradability. Taking an advantage of this property, polymer nanofibers can be utilized as an implantable substrate for various applications such as tissue regeneration, local treatment of disease, and drug delivery. Furthermore, polymer nanofibers can be functionalized with various biomaterials such as ECM molecules, ECM analogs and growth factors to enhance cellular functionality, and, thus, it has a great potential in biological and biomedical applications.
2.1.1 Effect on cell adhesion
Patel et al. investigated the combined effects of aligned polymer nanofibers and bioactive factors on cells . Polymer nanofibers were functionalized with laminin and basic fibroblast growth factor (bFGF) to imitate native ECM fibrils. In this research, aligned polymer nanofibers induced longer neurite outgrowth and faster skin cell migration compared with randomly-oriented polymer nanofibers. The cells were elongated, and they migrated along the direction of polymer nanofibers. In addition, growth factors attached to aligned nanofibers were found to be more effective than those in solution on neurite outgrowth.
Yang et al. also examined the effect of nanofiber alignment on the neurite outgrowth of neural stem cells (NSCs) . The aligned nanofibers supported the NSC culture, and they improved the neurite outgrowth (Figure 2 (E, F)). They also found that microscale polymer fibers have no significant effect on the neurite length. Baker et al. showed that the mechanical properties such as stiffness and elastic modulus of polymer nanofibers based cell-laden constructs depend on the alignment of polymers but not on cell type . Meniscal fibrochondrocytes (MFCs) and mesenchymal stem cells (MSCs) were tested on poly (ε-caprolactone) (PCL) polymer nanofibers. The tensile properties of aligned polymer nanofiber based cell-laden constructs were higher than those of randomly distributed one, whereas both cell-laden constructs were comparable in amount of total DNA and produced ECMs.
The diameter of polymer nanofibers is also an important factor affecting cell adhesion. Li et al. used polyaniline (PANi) and gelatin mixed polymer with different volume ratio. They found that the diameter of PANi-gelatine polymer nanofibers decreased from 803 ± 121 nm to 61 ± 13 nm with the decrease of the volume ratio of gelatin (Figure 2 (C, D)). The H9c2 rat cardiac myoblasts cultured on randomly distributed polymer fibers showed no significant difference in proliferation, but their morphology varied with the diameter of polymer nanofibers. Cells on thicker nanofibers showed a large number of pseudo-filopodia attachment to nanofibers (Figure 2 (G)), while cells on thinner nanofibers spread randomly just as those on glass surface (Figure 2 (H)).
2.1.2 Effect on cell differentiation
Cell differentiation is the process in which a progenitor cell or a stem cell becomes a more specified cell such as a bone cell, a neural cell, a liver cell, etc. There are soluble (e.g. growth factors, cytokines) and insoluble (e.g. ECM matrix, physical environments) factors which can affect the cell differentiation. Polymer nanofibers have shown the capability of supporting various stem cell differentiations, and they can even enhance the differentiation of the stem cells compared with a conventional scaffold.
Li et al. investigated the in vitro chondrogenic differentiation of MSCs on a PCL nanofiber-based scaffold in the presence of the transforming growth factor, TGF-ß1 . Cell proliferation on polymer nanofibers was similar to that in a cell pellet culture which is a widely used cell culture system. However, the contents of sulfated glycosaminoglycan (sGAG) as a chondrogenic differentiation marker on polymer nanofibers was higher than that in a cell pellet culture. It indicates that the PCL nanofiber substrate supports a chondrogenic differentiation. MSCs were differentiated into osteoblasts on PCL nanofiber based scaffold in osteogenic differentiation medium as shown by Yoshimoto et al. Cells migrated inside the polymer nanofiber-based scaffolds and produced an ECM of collagen after 1 week. MSCs on PCL nanofibers were also induced to differentiate along adipogenic, chondrogenic and osteogenic lineages in specific differentiation media . Not only PCL but also poly (D,L-lactide-co-glycolide) (PLGA) and poly (L-lactic acid) (PLLA) support cell differentiation. Xin et al. reported hMSC on PLGA retained their phenotype and differentiated into chondrogenic and osteogenic cells in differentiation media .
Smith et al. examined the effect of nanofibrous scaffolds on osteogenic differentiation . They prepared polymer nanofiber-based substrates in 2-D and 3-D formation. The nanofibrous structures in 2-D and 3-D enhanced the osteogenic differentiation of human embryonic stem cell (hESC)-derived osteogenic progenitor cells compared to the scaffolds without nanofibers.
The diameter of polymer nanofibers affects not only cell adhesion but also cell differentiation. Polyethersulfone (PES) nanofiber meshes with different diameter regulate proliferation and differentiation of rat neural stem cells (rNSCs) . They used laminin-coated PES with diameters of 238 ± 45 nm, 749 ± 153 nm and 1452 ± 312 nm. As the diameter of polymer nanofibers decreases, cells were spread more on the nanofibers. rNSCs on 238 nm nanofiber mesh were spread on the nanofiber matrix, and they were assumed cell morphology of glial lineage. On the contrary, rNSCs on 749 nm nanofiber mesh adhered onto a single fiber, and they were elongated along a fiber axis. Those cells preferentially differentiated into neuronal lineage. However, both of cells on polymer nanofiber-based substrates showed the higher-level expression of the differentiation markers than those on a flat substrate.
Researchers also investigated the synergistic effect of polymer blends. Ku et al. invesgated the synergic effects of PCL and PANi blended nanofiber alignment on myoblast differentiations . The differentiation of myoblasts on blended nanofibers was affacted by the PANi concentration. Kim et al. used commercial polymers to fabricate suitable biomaterial scaffold for the cell growth . The modified PCL nanofibers incoporated within poly (ethylene oxide) (PEO) showed a good biocompatibility.
These results show that the polymer nanofiber can support multi-lineage differentiation capability of stem cells, and it is a good candidate for a scaffold in tissue regeneration or stem cell theraphy.
2.2 Carbon-based nanotubes/nanofibers
Carbon nanomaterials including carbon nanotubes (CNTs) and carbon nanofibers (CNFs) exhibit excellent mechanical and electrical properties. They have been explored in many biological applications such as bioelectronics, tissue engineering, cellular imaging and therapeutics ,. The carbon nanomaterials can be advantageous for cell control because they do not emit ions and have a chemically-stable surface.
2.2.1 Carbon nanotubes
A CNT is a rolled-up graphene which is carbon atoms arranged in a planar honeycomb lattice. CNTs can be classified into single-walled CNT (swCNT) and multi-walled CNT (mwCNT) depending on the number of rolled-up graphene layers. Generally, the diameter of swCNT is about 1 ~ 2 nm, and that of mwCNT varies from 2 nm to over 100 nm (Table 1). A CNT is mechanically strong and easy to be functionalized. The electrical and optical properties of CNTs can be used for various applicaions such as ultrasensitive biosensors. We review the recent applications of CNT-based substrates in controlling cell behaviors.
Patterned CNTs on substrates can control the shapes or orientiations of cells. Park et al. succeeded in aligning hMSCs along the patterned CNTs . In this work, CNTs were selectively assembled on the substrate using the pre-patterned hydrophobic SAM molecules. The selective binding of ECM proteins (e.g. fibronectin) onto CNT regions could lead the hMSCs to grow along the CNT pattern. In a similar way, Jang et al. showed highly directional growth of neurites along the line-shape CNT patterns after 14 days of rat hippocampal neuron culture, which was attributed to the higher density adsorption of poly-L-lysine on the CNT patterns .
Previously, proteins have been known nonspecifically adsorbed well on sidewall of CNTs. Shim et al. demonstrated that the high affinity of proteins on CNTs could be attributed to the hydrophobic nature of CNTs or the pi-pi bonding between CNTs and proteins . The adsorbed proteins mediated the interaction between cells and CNTs for a improved adhesion.
Aligned CNTs on substrates are useful in accelerating cell migration which is important in regeneration medicine. Galvan-garcia et al. assembled highly oriented mwCNT sheets and yarns, and they observed the directed cell growth along the CNTs . In this work, the migration of fibroblasts on CNT sheets was enhanced, and the cell proliferation speed on the CNT sheets was comparable to that on glass. They also observed the directed neuronal growth along the CNT yarns, closely following the surface topography of the substrate.
A 3-D structure of CNT-film networks was explored for tissue engineering. Correa-Duarte et al. transformed a vertically-aligned structure of mwCNTs to a regular 3-D sieve structure by using chemically induced capillary forces (Figure 3 (C)) . They successfully demonstrated that the controlled growth of a mouse fibroblast cell line (L929) in this 3-D CNT structure.
Surface functionalized CNTs provide great opportunities in controlling cell growth. Hu et al. reported that chemically modified CNTs affected the outgrowth and branching patterns of neurons . The results showed that the positive charges induced more numerous growth cones, longer average neurite length and more neurite branching than the groups with neutral and negative charges (Figure 3 (D)). Zanello et al. cultured osteoblast (ROS 17/2.8) cells on the CNTs with various functional groups . They found the highest cell growth on electrically-neutral swCNTs (as-produced-swCNT and swCNT-PEG). On the other hand, the lowest cell growth was observed on CNTs with charged groups (swCNT-COOH and swCNT-poly (m-aminobenzene sulfonic acid)).
CNTs can be used to transmit electrical stimulation to neural cells. Wang et al. developed a prototype of neural interface using vertically aligned mwCNT pillars . The neurons were grown and differentiated on the hydrophilic functionalized CNT microelectrodes, and they were repeatedly excited with charge-unbalanced stimulation protocols. In this study, the CNT electrodes operated predominantly with capacitive currents without faradic reactions, which were considered ideal for neural stimulations.
CNTs were also explored to control cell differentiation. Tay et al. cultured hMSCs on a thin layer of carboxylic functionalized swCNTs with a vertical height of less than 100 nm . In this report, they showed that the neurogenic genes were increased while osteogenic genes remained at a nominal level. This result suggests that CNT nano-roughness alone was sufficient to modulate the early stage of stem cell lineage commitment without the aid of induction media.
Some researchers performed experimental studies to reveal the mechanisms for the different differentiation behaviors of cells on CNTs. Namgung et al. investigated the enhanced differentiation of hMSCs on the aligned CNT networks . They found that up-regulaed gene expressions of hMSCs related to the mechanotransduction pathways. These results supported that the high cytoskeletal tension of hMSCs could promote the differentiation of cells. Chen et al. suggested that the concentrated human bone marrow mesenchymal stem cells (hBMMSCs) following the carboxylated mwCNTs can up-regulate the secretion of growth factors .
2.2.2 Carbon nanofibers
Carbon nanofibers (CNFs) are graphene layers arranged as stacked cones, cups or plates, and their diameter ranges from 3.5 nm to 500 nm (Table 1) . CNFs have been also explored widely in tissue engineering with the combination of polymers.
The topographical effects of CNFs were investigated in cells. McKenzie et al. prepared a CNF and polycarbonate urethane (PCU) composite substrate with different diameters of CNFs ranging from 60 nm to 200 nm . They found that astrocytes preferentially adhered and proliferated on CNFs with the largest diameter. Price et al. demonstrated that this CNF-PCU substrates promoted the adhesion of osteoblasts, but the adhesions of smooth muscle cells, fibroblasts, and chondrocytes were not influenced .
Khang et al. examined osteoblast adhesion on microscale CNF patterns (30-μm-width line) on polymer substrates . The patterns of CNFs on PCU substrate were prepared using an imprinting method. Osteoblasts selectively adhered and aligned on CNF patterns on PCU. The greater attractive forces between fibronectin and CNF (compared with PCU) measured by an atomic force microscope gave a plausible explanation for the selective cell adhesion.
2.3 Inorganic nanowires/nanotubes
Inorganic nanowires/nanotubes have been commonly exploited as effective tools for controlling cell behaviors by delivering biomolecules into the cells  and sensing intra/extracellular signals ,. In addition, inorganic nanowires/nanotubes based substrates are utilized as platforms to investigate the effect of nanoscale substrate topography and size-dependent cellular responses –. Furthermore, inorganic nanowires/nanotubes have been also utilized for various other cellular applications such as controlling cell position, measuring cellular forces or sensing cellular activities. Inorganic nanowires/nanotubes could be synthesized with a variety of materials including titanium oxide (TiO2), zinc oxide (ZnO), silicon (Si), etc. The synthesis methods include CVD ,, anodization , electrochemical deposition  and solvothermal growth . Inorganic nanowires/nanotubes are rather easy to adjust their nanoscale surface topology and chemical properties for the control of cell behaviors.
2.3.1 Titanium oxide nanotubes
The interaction between cells and titanium oxide substrates has been extensively investigated for clinical implant applications. Recent studies showed that the nanoscale modulation of TiO2 surface topography enhanced the efficiency in implantation. In this study, vertically-grown TiO2 nanotubes have been used as an effective scaffold to provide various nanoscale geometries, because the diameter of TiO2 nanotubes is easily controlled in the synthesis process.
They continued experiments with various types of cells to address the dominant factors determining cell fates on TiO2 nanotubular enviroment . Three different types of cells (endothelial cell line mlEND, hMSCs and human cord blood endothelial progenitor cells) related to blood vessel formation were studied with respect to the diameter, the crystalline structure and the chemical composition of TiO2 nanotubes. As the diameter of TiO2 nanotubes decreased, the cell adhesion and proliferation were enhanced regardless of the cell type. The crystalline structure and the chemical composition of TiO2 nanotubes did not affect significantly on cell behaviors, which strongly suggests that the nanotopography should be a dominant factor for cell growth.
However, the results from Oh et al. were in conflict with previous experiments . They observed that the differentiation of hMSCs into osteoblast-like cells was enhanced on TiO2 nanotubes with larger diameters (70 nm to 100 nm) rather than smaller diameters (30 nm to 50 nm) in the absence of osteogenic inducing factors. These findings suggest that finely-tuned nanotopography of TiO2 nanotubes could determine the cell fate, even though there are still controversies regarding the optimal diameter of TiO2 nanotubes for the enhanced cell adhesion, proliferation and differentiation.
2.3.2 Zinc oxide nanowires
On the contrary, it was reported that the enhanced cell adhesion, proliferation and differentiation on ZnO nanoflowers (Figure 5 (B)) . In this work, the ZnO nanoflowers were also grown by the hydrothermal methods on the micro-patterned ZnO surface. The nanoflowers were comprised of ZnO NWs with 200 ~ 300 nm in diameter and 3 ~ 4 μm in length. In this platform, osteoblasts on ZnO nanoflowers showed stronger adhesion, more DNA content and higher ALP activity than those on the flat ZnO surface. Furthermore, ZnO nanoflowers were tightly osseointegrated with the regenerated bones in the calvarial bone defects of Sprague Dawley rats. The results were attributed to the enhanced formation of lamellipodia, filopodia, and F-actin filaments on the surface of ZnO nanoflowers.
2.3.3 Other inorganic nanowires
The control of cell adhesion and viability has been also demonstrated on various other nanowires. The effects depend on the physical and chemical properties of nanowires. Of interest, the unique properties of each nanowire allow additional cellular applications. For example, dissociated sensory neurons cultured on vertically-grown epitaxial gallium phosphide nanowires (GaP NWs) showed a higher viability than planar gallium phosphide substrates (Figure 5 (C)) . Interestingly, in other work, GaP NWs were utilized to measure cellular forces by analyzing the bending of GaP NWs (Figure 5 (D)) . The rigidity, the high aspect ratio, and the nanoascale dimension of GaP NWs allow spatially-resolved and sensitive measurements of cellular forces.
Johansson et al. investigated the effect of nickel nanowires (Ni NWs) on L929 mouse fibroblasts and dissociated dorsal root ganglia (DRG) neurons . They synthesized Ni NWs by the alumina template based electro-deposition method, which were 200 nm in diameter and 40 μm in length. They aligned Ni NWs using their magnetic property, and the cells were grown over the aligned Ni NWs. They showed that the cells displayed the contact guidance along the aligned Ni NWs. In other works, the magnetic properties of Ni NWs were utilized for the cell separation  or the cell positioning (Figure 5 (E)) .
The adhesion and the differentiation of MSCs on gold nanowires (Au NWs) were also demonstrated by Luo et al.. The well-known chemistry on Au surface allowed functionalization of Au NWs with self-assembled monolayers containing diverse functional groups. In this work, Au NWs were functionalized with a cell adhesive peptide (RGD- ONH2). As a result, MSCs on the functionalized Au NWs showed more fillopodia extensions compared to those on flat gold surfaces functionalized with the same RGD peptides. Moreover, in the process of adipogenic differentiation, the enhanced differentiation was observed on Au NWs (Figure 5 (F)).
Al/Al2O3 core/shell nanowires and patterned Si nanopillars were also studied to control the cellular responses such as cell adhesion, growth and proliferation. Lee et al. patterned periodic structures of Al/Al2O3 core/shell nanowires, and showed that the periodic patterns lead to the alignment of glial cells and dorsal root ganglia axons . Similar to the Al/Al2O3 nanowires experiment, Bucaro et al. showed that Si nanopillars could control the cell polarization and alignment by controlling the radius, height and interpillar spacing of Si nanopillars .
In summary, we discussed various synthetic nanowires/nanotubes utilized in cell engineering. Since it is easy to control the diameter, mechanical property and surface chemistry of synthetic nanowires/nanotubes, they can be utilized to create active microenvironments to control cell behaviors. Moreover, the nanowire/nanotube-based functional devices can be used as intercellular drug delivery system and ultrasensitive biosensors for real-time detection of cell activities. Although their cytotoxicity is still under debate and requires more systematic studies, synthetic nanowires/nanotubes have great potentials not only in fundamental research but also in clinical applications such as drug screening devices, organ-on-a chips and medical tissue grafts. With the advances in nanomaterials and manipulating technique, the synthetic nanowire/nanotube based system should provide enormous opportunities in biomedical applications.
SH acknowledges the support from the BioNano Health Guard Research Center (H-GUARD_2013M3A6B2078961) and the NRF grant (No. 2013–007874).
- 49.Park WI, Yoo J, GC Yi J: Korean Phys. Soc. 2005, 46: L1067-L1070.Google Scholar
- 50.Oh S, Brammer KS, Li YSJ, Teng DY, Engler AJ, Chien S, Jin SH: Proc. Natl. Acad. Sci. U. S. A.. 2009, 106: 2030–2135.Google Scholar
This article is published under license to BioMed Central Ltd. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly credited.