Liquid Phase adsorption kinetics and equilibrium of toluene by novel modified-diatomite

Journal of Environmental Health Science and Engineering volume 12, Article number: 148 (2014) Cite this article

Abstract

The adsorption equilibria of toluene from aqueous solutions on natural and modified diatomite were examined at different operation parameters such as pH, contact time, initial toluene concentration was evaluated and optimum experimental conditions were identified. The surface area and morphology of the nanoparticles were characterized by SEM, BET, XRD, FTIR and EDX analysis. It was found that in order to obtain the highest possible removal of toluene, the experiments can be carried out at pH 6, temperature 25°C, an agitation speed of 200 rpm, an initial toluene concentration of 150 mg/L, a centrifugal rate of 4000 rpm, adsorbent dosage = 0.1 g and a process time of 90 min. The results of this work show that the maximum percentage removal of toluene from aqueous solution in the optimum conditions for NONMD was 96.91% (145.36 mg/g). Furthermore, under same conditions, the maximum adsorption of natural diatomite was 71.45% (107.18 mg/g). Both adsorption kinetic and isotherm experiments were carried out. The experimental data showed that the adsorption follows the Langmuir model and Freundlich model on natural and modified diatomite respectively. The kinetics results were found to conform well to pseudo-second order kinetics model with good correlation. Thus, this study demonstrated that the modified diatomite could be used as potential adsorbent for removal of toluene from aqueous solution.

Introduction

Wastewater pollutants discharged from pharmaceutical and chemical industries contain various types of aromatic compounds, such as toluene, pyridine, and nitrobenzene, which are very harmful to human health and the ecosystem [1]. In the past decades, extensive attention has been paid to develop efficient and cost-effective methods for removal of these pollutants. Various technologies were used for the treatment of organic pollutants, including adsorption, biodegradation, chemical oxidation, photo-degradation, solvent extraction, membrane separation, etc. [2],[3]. Among these approaches, adsorption is still the most versatile and widely used method because of its high efficiency and simple operation conditions. Various adsorbents, such as active carbon, coal, fly ash, modified clays, polymeric resins, metal oxides, silicas, and zeolites, were applied to adsorb aromatic compounds in aqueous solutions [4]-[7]. For example, Roostaei and Tezel investigated toluene or benzene adsorption on silica gel, activated alumina, activated carbon, and zeolites, and found that the latter two materials provide a higher adsorption capacity for phenol [8]-[10]. Rodriguez and co-workers described activated carbons as good adsorbents for toluene and benzene [11]-[13]. Magnetic porous carbon microspheres have been reported with good adsorption properties for toluene and benzene [14]-[16]. Toluene and benzene and often coexist in wastewater because they are widely used in many industrial products and processes. Due to their biological toxicity to microorganisms, traditional biotreatment cannot be applied for an economical and effective degradation. Additionally, their coexistence will lead to the loss of degradation ability of bacteria to other pollutants [17]-[19]. Therefore, it is necessary to separate benzene and toluene from wastewater prior to their discharge into water bodies. Toluene is a typical indoor pollutant and its discharge may produce irritation of the eyes and the respiratory tract, nausea, headache, fatigue, dullness and thirst, even at very low concentrations [4]-[8]. Toluene is well known for its neurotoxicity and exposure to it may decrease neuronal activities in vitro and cause mental depression and cognitive impairment in humans [1],[6]. Toluene inhalation also results in various symptoms such as fatigue, headache, vertigo and ataxia. It is rapidly absorbed through respiratory and gastrointestinal tracts and, to a lesser extent, through the skin. American Conference of Governmental Industrial Hygienists (ACGIH) has recommended an 8-h time-weighted average (TWA) of 50 ppm (189 mg/m3) for toluene to protect against effects on the central nervous system. These studies also confirmed that porosity and surface oxygen group content have major influences on low-concentration-VOC adsorption [18]-[20]. Natural diatomite (SiO 2. nH 2 O) is made up from the skeletons of aquatic plants called diatom that usually is a pale-coloured, soft, lightweight siliceous sedimentary rock [21]. Diatomite contains a wide variety of shape and sized diatoms, typically 10-200 μm, in a structure including up to 80-90% pore spaces [19]-[21]. Diatomite’s extremely porous structure, low density and high surface area make it suitable as an adsorbent for organic and inorganic chemicals [22],[23]. In general, the literature includes few experimental data for modified natural adsorbent for removal of VOCs pollutants. In the present investigation, for the first time, the usage of Nickel Oxide Nanoparticles-Modified Diatomite (NONMD) for the adsorption of toluene has been studied, as a less expensive adsorbent for removal of toluene from an aqueous medium. The equilibrium and kinetic study are investigated to observe the effects of various process parameters such as pH, contact time, initial toluene concentration, calcinations and sorbent dosage on the adsorption process. Equilibrium data are attempted by various adsorption isotherms including Langmuir, Freundlich and Brunauer-Emmett-Teller (BET) isotherms in order to select an appropriate isotherm model. Moreover, a kinetics study of the adsorption process is also considered to describe the rate of sorption. Comparing natural and modified diatomite (NONMD) well shows that this process was successful and the removal percentage increased [24],[25].

Experimental procedure

Preparation of adsorbent

Diatomite sample was obtained from Tabriz, Iran. The sample was washed several times with distilled water and HCl (1 M) to remove fines and other adhered impurities and to achieve neutralization. The sample was finally filtered, dried at 60°C for 24 h, and stored in closed containers for further use.

The nanoparticles of NiO were synthesized by using following reaction (Equation 1):

N i 2 S O 4 +2NaOH→Ni O H 2 +N a 2 S O 4
(1)

The nanoparticles of NiO were synthesized by adding NiSO 4 and NaOH (1 M) to the solution. It means that 2.0 g of previously dried diatomite was added to 25 ml of Nickel hydroxide (1 M), Stirrer speed of 200 rpm, for 1 h. The new material, Ni-diatomite was sequentially separated by filtration. The calcination process was carried out by placing Modified diatomite sample in the furnace at 250°C for 4.5 h. The sample was then allowed to cool in a desiccator. The modified sample was used to examine the effect of nickel oxide nanoparticles, silanol groups and the role of pore size distribution on the adsorption process. FT-IR spectra and EDX analysis illustrate that the raise of metal oxide content at the modified diatomite can be the main reason for increasing the adsorption capacity. In industries, there are many heavy metals contaminated materials. Recovery of materials and clean up these contaminations is very difficult and expensive [26]-[34]. This investigation can be a useful method to change a poisonous industrial waste to a valuable by product.

Materials and solutions

Toluene (AR grade min. 99.6% Merck) was supplied by Quick Lab Sdn. Bhd., Ipoh, Perak. Distilled water was throughout employed as solvent. For adsorption experiments, various concentrations of toluene solutions (100, 150, 200, 250 and 300 mg/L) were prepared. The pH measurements were made using Hach pH meter. These chemicals were purchased from Merck, Germany.

Adsorption procedure

The adsorption experiments were performed by mixing various amounts of diatomite (0.03 – 0.12 g) in 100 mL of toluene solutions with varying concentrations (ranging from 100-300 mg/L) at natural pH (pH = 6). The natural pH to determine the maximum toluene removal could be achieved with diatomite, because this pH was more suitable for industrial purposes. Adsorption experiments were conducted at optimum amount of diatomite (0.1 g) at pH 6, an agitation speed of 200 rpm and temperature 25 ± 1°C for 1 h to attain equilibrium conditions. The changes of absorbance were determined at certain time intervals (5, 10, 30, 60 and 90 min) during the adsorption process. After adsorption experiments, the toluene solutions were centrifuged for 10 min in a Hettich EBA20 centrifuge at 4000 rpm in order to separate the sorbent from the solution and toluene concentration was then determined. The amount of toluene adsorbed by the adsorbent at equilibrium, q e (mg/g), was calculated by using the following equation:

q e = V C 0 − C e W
(2)

Where C 0 and C e (mg/L) are the initial and equilibrium concentrations of toluene, respectively, V (L) is the volume of the toluene solution and W (g) is the adsorbent mass.

Analysis

The residual toluene concentrations in aqueous medium were determined using a Perkin-Elmer spectrophotometer corresponding to maximum wavelength (λ max ) of toluene. The XRD analysis was performed on natural and modified diatomite samples using a Philips Xpert x-ray diffractometer. Scanning electron microscopic (SEM) of both natural and modified diatomite were carried out using LEO 1455VP scanning electron microscope before and after modification process. The samples were coated with gold (Au) prior to the scanning in the electron microscope. By using nitrogen adsorption method the BET specific surface area adsorbents was measured, using Autosorb-1MP apparatus from Qantachrome at 77 K. The analysis on compositions was determined by energy dispersive X-ray technique using EDX-System (Tescan Vega /2/ Instrument) which is fitted to the SEM instrument.

Results and discussion

Surface characterization

As the calcination process decreases the diatomite capacity for the removal of dye from aqueous solutions, therefore in this investigation, we decide to compare adsorption properties of modified diatomite with natural diatomite instead of modified diatomite. In order to explore the surface characteristics of diatomite, a Fourier Transformed Infra-Red (FTIR) analysis was performed in the range of 450 to 4000 cm−1. Figure 1a and b show the FTIR spectra of natural and modified diatomite samples before the adsorption process, respectively. On the other hand, the FTIR spectra of both samples after the adsorption process are shown in Figure 2a and b. The FTIR spectral values and specific type of bonds are given in Table 1.

Figure 1
figure 1

FT-IR spectra of adsorbents before adsorption (a) natural and (b) NONMD.

Full size image
Figure 2
figure 2

FT-IR spectra of adsorbents after adsorption (a) natural and (b) NONMD.

Full size image
Table 1 FTIR spectroscopy of spectra of natural and modified diatomite before and after the adsorption process
Full size table

As can be seen in Figure 1b, the nickel content of NONMD is too low and there is a recognisable difference in this region regarding to nickel oxide nanoparticles on diatomite [35]. In addition, Figure 1a and b illustrate that the amount of silanol group has decreased slightly, and the metal oxide content has risen at the modified diatomite; however, the adsorption capacity has increased at NONMD. Comparison of Figures 1 and 2 show that there is a new peak at 1871 cm−1 for the adsorption of dye (combi group of aromatic rings) on both samples after the adsorption process and peaks’ transmittance of silanol, siloxane, and metal oxide groups is slightly decreased in Figure 2.

Scanning electron micrographs (SEM) of natural and modified diatomite, before and after the adsorption process, are shown in Figure 3. These figures present that natural diatomite particles are amorphous, their pore spaces are lower than modified adsorbent, and particles of NONMD are more uniform and geometrical significantly. After modification and calcination process at 250°C, the structure of the adsorbent changed from amorphous sheets to semi-sphere shapes. Therefore, the volume of the pore spaces has increased, and the surface functional groups of modified diatomite have improved. Hence, the diffusion resistance of adsorption process has decreased, and the kinetics and capacity of dye adsorption process have risen. Moreover, adsorption of dye has caused a sticky phenomenon on structure of both adsorbents.

Figure 3
figure 3

Scanning electron micrographs before adsorption (a) natural and (b) NONMD, after adsorption (c) natural and (d) NONMD.

Full size image

XRD analysis results of the natural and modified diatomite are shown in Figure 4. It can be seen from Figure 4 that the x-ray pattern of the natural diatomite is different from the pattern of the modified diatomite, suggesting that a phase transformation probably occurred during the modification and calcinations processes. The main composition of natural diatomite is quartz, anorthite and muscovite. It is evident that sanidine was appeared; while anorthite and muscovite were completely removed as the diatomite was calcined at 250°C.

Figure 4
figure 4

XRD patterns of (a) natural and (b) modified diatomite.

Full size image

In fact, some peaks in the diatomite disappeared and some peaks were created by modification process. It can be a trace of nickel oxide particles particles from modification process and ammonia ions because of calcination at high temperature and existence of nitrogen in air. Similar behaviour was previously investigated by other researchers [19],[35].

As evident from EDX analyses (Figure 5), the natural diatomite did not have any Nickel but after modification process Ni was appeared (3.96%W). The surface area of the diatomite was determined by BET method (Figure 6). By using nitrogen adsorption method the BET specific surface area adsorbents was measured, using Autosorb-1MP apparatus from Qantachrome at 77 K. In this investigation the values 7.5 (m2/g) and 28.45 (m2/g) for natural and modified diatomite were calculated respectively.

Figure 5
figure 5

EDX patterns of (a) natural and (b) modified diatomite.

Full size image
Figure 6
figure 6

Effect of adsorbent dosage on the removal percentage of toluene by natural and modified diatomite, Temperature = 25 ± 1°C , initial toluene concentration = 150 mg/L , pH = 6 , agitation speed = 200 rpm .

Full size image

Effect of adsorbent dosage

The effect of natural and modified diatomite dosage on the adsorption of toluene was investigated at 25 ± 1°C by varying the adsorbent amount from 0.03 to 0.12 g while keeping the volume of toluene solution constant equal to 100 mL, with an initial toluene concentration of 150 mg/L. Figure 6 shows the percentage removal of toluene versus adsorbent amount. It is clear from the Figure 6, the removal percentage of toluene increased with an increase in the adsorbent amount. The main reason for this fact is due to the greater availability of the adsorption sites at higher concentrations of the adsorbent [19],[35]-[37]. Based on the results shown in Figure 6, 0.1 g of the natural and modified diatomite was used for further experiments.

Effect of initial toluene concentration

A change in the initial toluene concentration can considerably affect the adsorption process. Figure 7 depicts the effect of toluene concentration on the percentage removal of toluene by adsorbents. Evident from the Figure 7, when the toluene concentration increased from 100 to 300 mg/L the percentage removal of toluene decreased from 97.68 to 88.09% for modified and from 74.3 to 65.21 for natural diatomite.

Figure 7
figure 7

Effect of initial toluene concentration on adsorption of toluene by natural and modified diatomite, Contact time = 90 min , Temperature = 25 ± 1°C , pH = 6 , agitation speed = 200 rpm .

Full size image

As expected, when the concentration of toluene is increased, the limited capacity of the adsorbent checks any further adsorption of toluene and hence the overall removal percentage decreased.

Effect of contact time

The adsorption of toluene onto diatomite was evaluated as a function of contact time. Figure 8 shows the effect of contact time on the percentage removal of toluene in the aqueous phase by natural (Figure 8a) and modified diatomite (Figure 8b). The initial toluene concentration was varied from 100 to 300 mg/L. At all initial toluene concentrations investigated, the adsorption occurs very fast initially. After 5 min of adsorption process, the amount of adsorption by natural diatomite reaches to 66.99 and 64.09% of the ultimate adsorption of toluene for initial toluene concentrations of 100 and 150 mg/L respectively. As illustrated in Figure 8b, the adsorption is also fast at early stage of the adsorption process for modified diatomite. Typically about 87.87% of the ultimate adsorption of toluene with an initial concentration of 150 mg/L takes place within the first 5 min of contact and it almost remains constant thereafter. It means that the most of mass transfer resistance is in bulk of fluid and high rate agitation would decrease this resistant. In addition, these results show that the most of the toluene molecules are adsorbed on the external surface of the adsorbent, and transferred to the pores and internal surfaces layer. More experiments are necessary to be carried out to prove this investigation. As expected, when the concentration of toluene is increased, the limited capacity of the adsorbent checks any further adsorption of toluene and hence the overall removal percentage decreases.

Figure 8
figure 8

Effect of contact time on adsorption of toluene on (a) natural and (b) modified diatomite, Equilibrium time = 90 min , pH = 6 , agitation speed = 200 rpm , adsorbent dosage = 0.1 g .

Full size image

Adsorption isotherms

The distribution of toluene between the adsorbent and the toluene solution at equilibrium is important in establishing the capacity of the adsorbent for toluene removal from aqueous systems. The adsorption isotherms of toluene on both natural and modified diatomite are shown in Figure 9. It is clearly seen from Figure 9 showed that the amount of adsorbed toluene on natural diatomite was much lower than that of modified diatomite.

Figure 9
figure 9

Adsorption isotherms of toluene onto natural and modified diatomite.

Full size image

The experimental data obtained were evaluated by various isotherm models incorporating Langmuir, Freundlich [37]-[39] and Brunauer-Emmett-Teller (BET) [39]-[41] isotherms.

Langmuir isotherm is applicable for monolayer adsorption on a surface containing a finite number of identical adsorption sites [42],[43]. A linear expression for the Langmuir isotherm is as follows:

1/ q e = 1 K L Q 0 1 / C e +1/ Q 0
(3)

Where C e is the concentration of toluene under equilibrium condition (mg/L), q e denotes the amount of toluene adsorbed at equilibrium (mg/g), Q 0 indicates the maximum adsorption capacity and K L is the Langmuir isotherm constant (L/mg). The values of K L and Q 0 were calculated from the slope and intercept of the linear plot of 1/q e versus 1/C e .

Freundlich equation was also applied for the adsorption of toluene on diatomite as given below:

q e = K F C e 1 n
(4)

Where C e is the equilibrium toluene concentration in aqueous system (mg/L), q e is the amount of toluene adsorbed per weight of the adsorbent used (mg/g), K F and n are Freundlich isotherm constants incorporating all factors affecting the adsorption process. Taking log10 from both sides of the Eq. ([4]) yields the following equation:

log 10 q e = log 10 K F + 1 n log 10 C e
(5)

Linear plot of log10 q e versus log10 C e gives the values of K F and n.

Brunauer-Emmett-Teller (BET) model was also used to fit the adsorption data according to the linear form of its rearranged adsorption isotherm model, which may be expressed as:

C e C s − C e q e = 1 K b q m + K b − 1 K b q m C e C s
(6)

where C e is the concentration of toluene in solution (mg/L), C s denotes the saturation concentration of toluene (mg/L), q e is the amount of toluene adsorbed per weight of the diatomite used (mg/g), q m is the amount of toluene adsorbed in forming a complete monolayer (mg/g), K b indicates a constant explaining the energy of interaction with the surface. The values of K b and q m were calculated from the slope and intercept of the linear plot of C e C S − C e 1 q e versus C e C S .

The Q 0 , K L , r 1 2 (correlation coefficient for Langmuir isotherm), K F , 1/n, r 2 2 (correlation coefficient for Freundlich isotherm), K b , q m and r 3 2 (correlation coefficient for BET isotherm) are given in Table 2. The negative values of K b related to the BET isotherm model describe that the adsorption process for natural diatomite did not follow the BET isotherm model, since this constant is indicative of the surface binding energy. In addition, standard statistics of root mean squared error (RMSE) was carried out to support the best fit adsorption model. RMSE can be expressed as:

RMSE= 1 n ∑ q p − q O 2 1 2
(7)
Table 2 Parameters of various isotherms for adsorption of toluene onto natural diatomite and NONMD
Full size table

Where q p is the predicted sorption capacity (mg/g), q o is the observed sorption capacity (mg/g) and n is the number of samples. Thus, based on the high r2 and low RMSE values, the results present that the adsorption of BR 46 on the natural diatomite and the NONMD follow the Langmuir model and the BET model, respectively [27]. It is evident from Table 2 that the isotherm data for the adsorption of toluene by natural diatomite were best-fitted using Langmuir model with a correlation coefficient of 0.997. Furthermore, the Freundlich model is most appropriate for the adsorption of toluene on modified diatomite with a correlation coefficient of 0.998.

Adsorption kinetics

The prediction of the adsorption kinetics of toluene from aqueous system is important in order to design a suitable treatment system. The kinetics of adsorption of toluene on diatomite may be described by the pseudo-first-order Lagergren rate equation [43]-[45] and the pseudo-second-order rate expression developed by Ho and McKay [46]-[49]. The Lagergren equation is:

log q e − q t =log q e − K 1 , ad 2.303 t
(8)

Where q e and q t are the amounts of toluene (mg/g) adsorbed at equilibrium and at time t (min) and K 1,ad is the pseudo-first-order rate constant (1/min) [49].

The Ho and McKay equation is given below:

t q t = 1 K 2 , ad q e 2 + t q e
(9)

Where q e and q t are the amounts of toluene (mg/g) adsorbed at equilibrium and at time t (min) and K 2,ad is the rate constant of the pseudo-second -order model (g/mg.min) [49].

Linear plot of log10 (q e  − q t ) against t gives the rate constant of K 1,ad Moreover, the value of K 2,ad is obtained from the intercept of the linear plot of t/q t versus t. Adsorption kinetics constants of the pseudo-first-order and pseudo-second-order models at pH 6, temperature 25 ± 1°C, an agitation speed of 200 rpm, an initial concentration of 150 mg/L and for a time period of 90 min are given in Table 3. From Table 3, the high values of correlation coefficients of the pseudo-second-order model for both natural and modified diatomite showed that the adsorption data conformed well to the Ho and McKay kinetics model [Eq. ([8])].

Table 3 Kinetics constants for toluene adsorption by natural diatomite and NONMD
Full size table

Conclusions

Diatomite has been studied for the removal of toluene from aqueous solution. Modification treatment of the adsorbent with nickel oxide nanoparticles was useful and its adsorption capacity increased. The adsorption process was not influenced by solution pH and used natural pH of the solutions. It was found that in order to obtain the highest possible removal of toluene, the experiments can be carried out at pH 6, temperature 25°C, an agitation speed of 200 rpm, an initial toluene concentration of 150 mg/L, a centrifugal rate of 4000 rpm, adsorbent dosage = 0.1 g and a process time of 90 min. The results of this work show that the maximum percentage removal of toluene from aqueous solution in the optimum conditions for NONMD was 96.91% (145.36 mg/g). Furthermore, under same conditions, the maximum adsorption of natural diatomite was 71.45% (107.18 mg/g).

The most important thing to design and run an industrial adsorption plant is the knowledge of adsorption kinetics and isotherms. Hence, the experimental results were analyzed by using the Langmuir, Freundlich and BET equations. Equilibrium data for the adsorption of toluene by natural diatomite fit well to the Langmuir isotherm model. Furthermore, the Freundlich model is most appropriate for the adsorption of toluene on NONMD. In addition, the rate of adsorption process for both of them obeys the pseudo-second-order kinetics model.

Symbols used

C 0 [mg L−1] initial concentration of toluene

C e [mg L−1] residual concentration at equilibrium

C s [mg L−1] saturation concentration of toluene

K 1,ad [min−1] rate constant of Pseudo-first-order

K 2,ad [min−1] rate constant of Pseudo-second-order

k F [(mg g−1)( mg L−1)-1/n] Freundlich constant

k L [L mg−1] Langmuir constant

k b [–] BET constant

m [g] mass of adsorbent used

n [–] parameter indicating the intensity of adsorption

q e [mg g−1] residual amount adsorbed at equilibrium

q p [mg g−1] predicted sorption capacity

q o [mg g−1] observed sorption capacity

Q o [mg g−1] maximum sorption capacity

r2 [–] correlative coefficient for all models

V [L] volume of toluene solution

References

  1. Bouhamra WS, Baker CGJ, Elkilani AS, Alkandari AA, Al-Mansour AAA: Adsorption of toluene and 1,1,1-trichloroethane on selected adsorbents under a range of ambient conditions. Adsorption 2009, 15: 461–475. 10.1007/s10450-009-9195-4

    CAS  Article  Google Scholar 

  2. Toh YC, Yen JJL, Jeffrey PO, Ting YP: Decolourisation of azo dyes by whiterot fungi (WRF) isolated in Singapore. Enzyme Microb Technol 2003, 35: 569–575. 10.1016/S0141-0229(03)00177-7

    Article  Google Scholar 

  3. Sivaraj R, Namasivayam C, Kadirvelu K: Orange peel as an adsorbent in theremoval of acid violet 17 (acid dye) from aqueous solutions. Waste Manage 2001, 21: 105–110. 10.1016/S0956-053X(00)00076-3

    CAS  Article  Google Scholar 

  4. Nacera Y, Aicha B: Equilibrium and kinetic modelling of methylene blue sorption by pretreated dead Streptomyces rimosus: effect of temperature. Chem Eng J 2006, 119: 121–125. 10.1016/j.cej.2006.01.018

    CAS  Article  Google Scholar 

  5. Zhang Y, Chen X, Bi HT S: Application of wave propagation theory to adsorption breakthrough studies of toluene on activated carbon fiber beds. Carbon 2010, 48: 2317–2326. 10.1016/j.carbon.2010.03.008

    CAS  Article  Google Scholar 

  6. Khraisheh MAM, Al-Ghouti MA, Allen SJ, Ahmad MN: Effect of OH and Silanol groups in the removal of dyes from aqueous solution using diatomite. Water Res 2005, 39: 922–932. 10.1016/j.watres.2004.12.008

    CAS  Article  Google Scholar 

  7. Khalighi Sheshdeh R, Khosravi Nikou MR, Badii KH, Mohammadzadeh S: Evaluation of Adsorption Kinetics and Equilibrium for the Removal of Benzene by Modified Diatomite. Chem Eng Technol 2013, 36: 1713–1720. 10.1002/ceat.201300041

    CAS  Article  Google Scholar 

  8. Hachem C, Bocquillon F, Zahraa O, Bouchy M: Decolourization of textile industry wastewater by the photocatalytic degradation process. Dyes Pigments 2001, 49: 117–125. 10.1016/S0143-7208(01)00014-6

    CAS  Article  Google Scholar 

  9. Mahmoodi NM, Arami M, Yousefi Limaee N, Salman Tabrizi N: Decolorization and aromatic ring degradation kinetics of Direct Red 80 by UV oxidation in the presence of hydrogen peroxide utilizing TiO 2 as a photocatalyst. Chem Eng J 2005, 112: 191–196. 10.1016/j.cej.2005.07.008

    CAS  Article  Google Scholar 

  10. Pearce CL, Lloyd JR, Guthrie JT: The removal of colour from textile wastewater using whole bacterial cells: a review. Dyes Pigments 2003, 58: 179–196. 10.1016/S0143-7208(03)00064-0

    CAS  Article  Google Scholar 

  11. Vlyssides AG, Loizidou M, Karlis PK, Zorpas AA, Papaioannou D: Electrochemical oxidation of a textile dye wastewater using a Pt/Ti electrode. J Hazard Mater 1999, 70: 41–52. 10.1016/S0304-3894(99)00130-2

    CAS  Article  Google Scholar 

  12. Khattri SD, Singh MK: Colour removal from synthetic dye wastewater using a bioadsorbent. Water Air Soil Pollut 2000, 120: 283–294. 10.1023/A:1005207803041

    CAS  Article  Google Scholar 

  13. Benkli YE, Can MF, Turan M, Çelik MS: Modification of organo-zeolite surface for the removal of reactive azo dyes in fixed-bed reactors. Water Res 2005, 39: 487–493. 10.1016/j.watres.2004.10.008

    CAS  Article  Google Scholar 

  14. Shawabkeh RA, Tutunji MF: Experimental study and modelling of basic dye sorption by diatomaceous clay. Applied Clay Sci 2003, 24: 111–120. 10.1016/S0169-1317(03)00154-6

    CAS  Article  Google Scholar 

  15. Gong R, Ding Y, Li M, Yang C, Liu H, Sun Y: Utilization of powdered peanut hull as biosorbent for removal of anionic dyes from aqueous solution. Dyes Pigments 2005, 64: 187–192. 10.1016/j.dyepig.2004.05.005

    CAS  Article  Google Scholar 

  16. Fu Y, Viraraghavan T: Removal of Congo Red from an aqueous solution by fungus Aspergillus niger. Adv Environ Res 2002, 7: 239–247. 10.1016/S1093-0191(01)00123-X

    CAS  Article  Google Scholar 

  17. Gucek A, Sener S, Bilgen S, Mazmanci ML: Adsorption and kinetic studies of cationic and anionic dyes on pyrophyllite from aqueous solutions. J Colloid Interf Sci 2005, 286: 53–60. 10.1016/j.jcis.2005.01.012

    Article  Google Scholar 

  18. Wang S, Boyjoo Y, Choueib A, Zhu ZH: Removal of dyes from aqueous solution using fly ash and red mud. Water Res 2005, 39: 129–138. 10.1016/j.watres.2004.09.011

    CAS  Article  Google Scholar 

  19. Netpradit S, Thiravetyan P, Towprayoon S: Adsorption of three azo reactive dyes by metal hydroxide sludge: effect of temperature, pH, and electrolytes. J Colloid Interf Sci 2004, 270: 255–261. 10.1016/j.jcis.2003.08.073

    CAS  Article  Google Scholar 

  20. Pala A, Tokat E: Color removal from cotton textile industry wastewater in an activated sludge system with various additives. Water Res 2002, 36: 2920–2925. 10.1016/S0043-1354(01)00529-2

    CAS  Article  Google Scholar 

  21. Aksu Z: Application of biosorption for the removal of organic pollutants: a review. Process Biochem 2005, 40: 997–1026. 10.1016/j.procbio.2004.04.008

    CAS  Article  Google Scholar 

  22. Shawabkeh R, Al-Harahsheh A, Al-Otoom A: Copper and zinc sorption by treated oil shale ash. Sep Purif Technol 2004, 40: 251–257. 10.1016/j.seppur.2004.03.006

    CAS  Article  Google Scholar 

  23. Lin YH, Leu JY: Kinetics of reactive azo-dye decolorization by Pseudomonas luteola in a biological activated carbon process. Biochem Eng J 2008, 39: 457–467. 10.1016/j.bej.2007.10.015

    CAS  Article  Google Scholar 

  24. Annadurai G, Juang RS, Lee DJ: Factorial design analysis for adsorption of dye on activated carbon beads incorporated with calcium alginate. Adv Environ Res 2002, 6: 191–198. 10.1016/S1093-0191(01)00050-8

    Article  Google Scholar 

  25. Chakraborty S, De S, Das Gupta S, Basu JK: Adsorption study for the removal of a basic dye: experimental and modeling. Chemosphere 2005, 58: 1079–1086. 10.1016/j.chemosphere.2004.09.066

    CAS  Article  Google Scholar 

  26. Deniz F, Karaman S: Removal of Basic Red 46 dye from aqueous solution by pine tree leaves. Chem Eng J 2011, 170: 67–74. 10.1016/j.cej.2011.03.029

    CAS  Article  Google Scholar 

  27. Deniz F, Saygideger SD: Removal of a hazardous azo dye (Basic Red 46) from aqueous solution by princess tree leaf. Desalin 2011, 268: 6–11. 10.1016/j.desal.2010.09.043

    CAS  Article  Google Scholar 

  28. Bennani Karim A, Mounir B, Hachkar M, Bakasse M, Yaacoubi A: Removal of Basic Red 46 dye from aqueous solution by adsorption onto Moroccan clay. J Hazard Mater 2009, 168: 304–309. 10.1016/j.jhazmat.2009.02.028

    Article  Google Scholar 

  29. Olgun A, Atar N: Equilibrium and kinetic adsorption study of Basic Yellow 28 and Basic Red 46 by a boron industry waste. J Hazard Mater 2009, 161: 148–156. 10.1016/j.jhazmat.2008.03.064

    CAS  Article  Google Scholar 

  30. Zaitana H, Korrir A, Chafik T, Bianchi D: Evaluation of the potential of volatile organic compound (di-methylbenzene) removal using adsorption on natural minerals compared to commercial oxides. J Hazard Mater 2013, 262: 365–376. 10.1016/j.jhazmat.2013.08.071

    Article  Google Scholar 

  31. Aivalioti M, Vamvasakis I, Gidarakos E: BTEX and MTBE adsorption onto natural and thermally modified diatomite. J Hazard Mater 2010, 178: 136–143. 10.1016/j.jhazmat.2010.01.053

    CAS  Article  Google Scholar 

  32. Aivalioti M, Papoulias P, Kousaiti A, Gidarakos E: Adsorption of BTEX, MTBE and TAME on natural and modified diatomite. J Hazard Mater 2012, 207–208: 117–127. 10.1016/j.jhazmat.2011.03.040

    Article  Google Scholar 

  33. Senturk HB, Ozdes D, Duran C: Biosorption of Rhodamine 6G from aqueous solutions onto almond shell (Prunus dulcis) as a low cost biosorbent. Desalin 2010, 252: 81–87. 10.1016/j.desal.2009.10.021

    CAS  Article  Google Scholar 

  34. Senthil Kumar P, Ramalingam S, Senthamarai C, Niranjanaa M, Vijayalakshmi P, Sivanesan S: Adsorption of dye from aqueous solution by cashew nut shell: studies on equilibrium isotherm kinetics and thermodynamics of interactions. Desalin 2010, 261: 52–60. 10.1016/j.desal.2010.05.032

    CAS  Article  Google Scholar 

  35. Khraisheh MAM, Al-degs YS, Mcminn WAM: A remediation of wastewater containing heavy metals using natural and modified diatomite. Chem Eng J 2004, 99: 177–184. 10.1016/j.cej.2003.11.029

    CAS  Article  Google Scholar 

  36. Allen SJ, Gan Q, Matthews R, Johnson PA: Comparison of optimised isotherm models for basic dye adsorption by kuzdu. Bioresour Technol 2003, 88: 143–152. 10.1016/S0960-8524(02)00281-X

    CAS  Article  Google Scholar 

  37. Bhattacharyya KG, Sarma A: Adsorption characteristics of the dye, Brilliant green, on Neem leaf powder. Dyes Pigments 2003, 57: 211–222. 10.1016/S0143-7208(03)00009-3

    CAS  Article  Google Scholar 

  38. Demir H, Top A, Balkose D, Ulku S: Dye adsorption behaviour of Luffa cylindrical fibers. J Hazard Mater 2008, 153: 389–394. 10.1016/j.jhazmat.2007.08.070

    CAS  Article  Google Scholar 

  39. Hameed BH: Equilibrium and kinetic studies of methyl violet sorption by agricultural waste. J Hazard Mater 2008, 154: 204–212. 10.1016/j.jhazmat.2007.10.010

    CAS  Article  Google Scholar 

  40. Arami M, Limaee NY, Mahmoodi NM, Tabrizi NS: Equilibrium and kinetics studies for the adsorption of direct and acid dyes from aqueous solution by soymeal hull. J Hazard Mater 2006, B135: 171–179. 10.1016/j.jhazmat.2005.11.044

    Article  Google Scholar 

  41. Ferrero F: Dye removal by low cost adsorbents: hazelnut shells in comparison with wood sawdust. J Hazard Mater 2007, 142: 144–152. 10.1016/j.jhazmat.2006.07.072

    CAS  Article  Google Scholar 

  42. Khalighi Sheshdeh R, Khosravi Nikou MR, Badii KH, Yousefi Limaee N: Adsorption of Acid Blue 92 Dye on Modified Diatomite by Nickel Oxide Nanoparticles in Aqueous Solutions. Prog Color Colorants Coat 2012, 5: 101–116.

    Google Scholar 

  43. Al-Degs Y, Khraisheh MAM, Tutunji MF: Sorption of lead ions on diatomite and manganese oxides modified diatomite. Water Res 2001, 35: 3724–3733. 10.1016/S0043-1354(01)00071-9

    CAS  Article  Google Scholar 

  44. Al-Ghouti M, Khraisheh MAM, Ahmad MNM, Allen S: Thermodynamic behaviour and the effect of temperature on the removal of dyes from aqueous solution using modified diatomite. A kinetic study. J Colloid Interf Sci 2005, 287: 6–13. 10.1016/j.jcis.2005.02.002

    CAS  Article  Google Scholar 

  45. Colgecen G, Erdem E, Donat R: The removal of Textile Dyes by Diatomite Earth. J Colloid interf Sci 2005, 282: 314–319. 10.1016/j.jcis.2004.08.166

    Article  Google Scholar 

  46. Hayat K, Gondal MA, Khaled MM, Ahmed S: Effect of Operational Key Parameters on Photocatalytic Degradation of Phenol using Nano Nickel Oxide Synthesized by Sol Gel Method J. Mol Catal A- Chem 2011, 336: 64–71. 10.1016/j.molcata.2010.12.011

    CAS  Article  Google Scholar 

  47. Badii K, Doulati Ardejani F, Aziz Saberi M, Yousefi Limaee N, Shafaei SZ: Adsorption of Acid blue 25 dye on diatomite in aqueous solutions. Indian J Chem Technol 2010, 17: 7–11.

    CAS  Google Scholar 

  48. Mahmoodi NM: Photocatalytic ozonation of dyes using copper ferrite nanoparticle prepared by co-precipitation method. Desalin 2011, 279: 332–337. 10.1016/j.desal.2011.06.027

    CAS  Article  Google Scholar 

  49. Khalighi Sheshdeh R, Khosravi Nikou MR, Badii KH, Yousefi Limaee N, Golkarnarenji G: Equilibrium and kinetics studies for the adsorption of Basic Red 46 on nickel oxide nanoparticles-modified diatomite in aqueous solutions. J Taiwan Ins Chem Eng 2014, 45: 1792–1802. 10.1016/j.jtice.2014.02.020

    Article  Google Scholar 

Download references

Acknowledgments

The authors are thankful to Petroleum University of Technology for providing the financial help and to Institute for Color Science and Technology (ICST), for supporting this research.

Author information

Affiliations

  1. School of Chemical Engineering, College of Engineering, University of Tehran, Tehran, Iran

    Reza Khalighi Sheshdeh

  2. Department of Chemical Engineering, Tarbiat Modares University, Tehran, Iran

    Saeed Abbasizadeh

  3. Ahwaz Faculty of Petroleum, Petroleum University of Technology (PUT), Ahwaz, Iran

    Mohammad Reza Khosravi Nikou & Mohammad Sadegh Sharafi

  4. Department of Environmental Researches, Institute for Color Science and Technology (ICST), Tehran, Iran

    Khashayar Badii

Authors
  1. Reza Khalighi Sheshdeh
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Saeed Abbasizadeh
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Mohammad Reza Khosravi Nikou
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Khashayar Badii
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Mohammad Sadegh Sharafi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Reza Khalighi Sheshdeh.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

The overall implementation of this study including design, experiments and data analysis, and manuscript preparation were the results of efforts by all of the authors. All authors have made extensive contribution into the review and finalization of this manuscript. All authors read and approved the final manuscript.

Authors’ original submitted files for images

Rights and permissions

This article is published under an open access license. Please check the 'Copyright Information' section either on this page or in the PDF for details of this license and what re-use is permitted. If your intended use exceeds what is permitted by the license or if you are unable to locate the licence and re-use information, please contact the Rights and Permissions team.

About this article

Verify currency and authenticity via CrossMark

Cite this article

Sheshdeh, R.K., Abbasizadeh, S., Nikou, M.R.K. et al. Liquid Phase adsorption kinetics and equilibrium of toluene by novel modified-diatomite. J Environ Health Sci Engineer 12, 148 (2014). https://doi.org/10.1186/s40201-014-0148-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s40201-014-0148-9

Keywords

  • Diatomite
  • Adsorption
  • Toluene
  • Isotherm
  • Kinetics