Efficient broadband absorption of solar radiation is desired for sea water desalination, icephobicity and other renewable energy applications. We propose an idea of superimposing two high-loss resonances to broaden bandwidths of a few-layer absorber, which is made of dielectric/ metal/dielectric/ metal layers. Both the simulation and experiment show that the structure has an averaged absorption efficiency higher than 97% at wavelengths ranging from 350 to 1200 nm. The bandwidth of the absorption larger than 90% is up to 1000 nm (410–1410 nm), which is greater than that (≤ 750 nm) of previous MIM planar absorbers. Especially, the average absorption from 350 to 1000 nm is kept above 90% at an incidence angle as high as 65°, meanwhile still maintained above 80% even at an incident angle of 75°. The performance of angular insensitivity is much better than that of previous few-layer solar absorbers. The flexible 1D nonoble metasurface absorbers are fabricated in a single evaporation step. Under the illumination of a halogen lamp of P = 1.2 kW/m2, the flexible metasurface increases its surface temperature by 25.1 K from room temperature. Further experiments demonstrate that the heat localization rapidly melts the accumulated ice. Our illumination intensity (P = 1.2 kW/m2) is only half of that (P = 2.4 kW/m2) in previous solar anti-ice studies based on gold/TiO2 particle metasurfaces, indicating that our metasurface is more advantageous topractical applications. Our results illustrate an effective pathway toward the broadband metasurface absorbers with the attractive properties of mechanical flexibility, low cost of the no-noble metals, and large-area fabrications, which have promising prospects in the applications of solar heat utilization.
An optical absorber with a high and broad absorption has long been a major scientific and technological goals [1,2,3,4,5,6,7,8,9] for many applications, including thermal photovoltaic [10,11,12,13,14,15], steam generation [16, 17], and photodetection . In recent years, the optical metamaterial/metasurface absorbers, artificially structured materials made from 2D arrays of subwavelength unit-cells, have been widely investigated and developed [1, 2], such as densely packed nanowires , nanotubes , tapered grooves [20,21,22], and pyramidal designs [23, 24]. Although enormous efforts are made in performance enhancements of these absorbers based on 2D arrays [25,26,27,28,29,30,31,32,33,34,35,36,37], the fabrication complexity of most these nanostructures, requiring electron beam lithography (EBL) , focused ion beam (FIB) milling , Nanoimprint lithography , or Lithography technology , hinders their further upscaling.
For solving these problems, 1D metasurfaces based on the concept of lithography-free planar designs become a topic of intensive investigations in recent years [1, 5, 8, 25,26,27]. Recently, scientists proved the absorption capability of some few-layer configurations (such as single noble metal layer, insulator–metal (IM), and metal–insulator-metal (MIM) structure) [1, 8, 25,26,27, 38,39,40,41,42,43,44,45,46,47,48], which are favorable to local accumulation of absorbed heat. Firstly, for the simple planar configurations based on noble metals (such as Au and Ag), the absorption bandwidths (A > 90%) are smaller than 500 nm because the absorption is caused by only a surface plasmon polaritons (SPP) effect mechanism [1,2,3,4,5,6,7,8]. These absorbers based on the SPP effect also show innately angle-dependent property due to the momentum matching conditions [1,2,3,4,5,6,7,8]. Besides, some absorbers using noble metals based on IM or MIM planar configuration were also proposed and demonstrated by using Fabry–Perot (FP) resonance. However, for these planar absorbers (such as Ge/Au  and Ag/Si/Ag ), the absorption bandwidths (A > 80%) are generally less than 300 nm owing to the utilization of only one FP resonance. Meanwhile, the material cost of noble metal in most of the above-mentioned absorbers is expensive [1,2,3,4,5,6,7,8, 48, 50]. Recently, several groups used non-noble metals (such as Mo or Gr) based on MIM planar nanostructures to demonstrate optical absorbers [50, 51]. The Mo/Al2O3/Mo absorber based on a single Febry–Perot (FP) resonance showed absorption above 90% from 400 to 900 nm . The Cr/Al2O3/Cr absorber based on one FP resonance showed absorption above 90% from 400 to 1150 nm . For most of the reported few-layer planar absorbers, the bandwidth ∆λBW (A > 90%) in the visible-near infrared wavelengths is smaller than 750 nm. Meanwhile, for these MIM planar nanostructures based on one FP resonance, the average absorption efficiency at wavelengths of 400–1000 nm would drop below 90% for an incident angle greater than 40° under a TE–polarization incidence. Such angle dependent spectral characteristic is a significant drawback, which makes the absorbers difficult to be applicable in practical usages. Thus, designing and realizing few-layer non-noble 1D metasurfaces to achieve omnidirectional, broadband, and efficient absorption are challenging but necessary for practical applications.
Here, we propose and experimentally demonstrate a few-layer non-noble 1D metasurface, which superimposes two high-loss resonators to broaden bandwidths (∆λBW) of absorbers. The few-layer non-noble 1D metasurface is dielectric/metal/dielectric thin layers on a thick metal film, and it comprises of two high-loss resonators. Due to the superimposing of the two high-loss resonators, the average absorption efficiency of our proposed metasurface is above 97% at wavelengths from 400 to 1200 nm. The absorption bandwidths (A > 90%) is up to 1000 nm (410–1410 nm), which is greater than that (∆λBW = 750 nm) of previous MIM planar absorbers [1,2,3,4,5,6,7,8, 48, 50]. Moreover, the average absorption for a wide range of incident angles up to 0–65° all surpasses 90% at wavelengths ranging from 350 to 1000 nm. This makes our absorbers more beneficial for practical applications compared to previous MIM planar absorbers [1,2,3,4,5,6,7,8, 48, 50], of which the average absorption efficiency at wavelengths of 400–1000 nm would drop below 90% for an incident angle larger than 40° under TE-polarization incidence. The metasurface is fabricated by a single step of electron beam vapor deposition on a glass substrate as well as a flexible PET substrate. The measured absorption spectra of the non-noble metasurface match well with the simulation results. Due to the efficient optical absorption and photothermal energy conversion in the ultra-thin absorption layer (thickness = 10 nm), the non-noble metasurface exhibits a temperature increase (ΔTe = 25.1 K) when it is illuminated by a halogen light source (P = 1.2 kW/m2). The increased temperature (ΔTe = 25.1 K) is higher than that of the recently reported solar absorbers based on a gold-particle metasurface (ΔTe = 12 °C under P = 2.4 kW/m2)  and gold/nickel plasmonic metasurface (ΔTe = 8 °C under P = 1.2 kW/m2) . For practical applications, we demonstrate that the metasurface is capable of removing ice under a halogen light source (P = 1.2 kW/m2). This is more efficient compared to the previous solar anti-ice work based on a gold/TiO2 particle metasurface using a halogen light source with P = 2.4 kW/m2 . The lithography-free fabrication of our 1D few-layer metasurface is easy to scale, facilitating its extensive use in practical photo-thermal applications.
Design and Methods
The designed 1D few-layer metasurface is consisting of insulator/metal (high-loss)/insulator thin layers on a thick metal film, as shown in Fig. 1a. The thicknesses of the top three thin layers are h1, hm, and, h2, respectively. The illuminating light can be reflected back and forth off the dielectric-air interface and the dielectric-metal interface in the IM planar nanostructure, constructing a resonator , as shown in Fig. 1b (Resonator 1). The length of Resonator 1 is h1. Similarly, the metal (high-loss)/insulator/metal (high-loss) planar nanostructure is also a resonator [49,50,51] (denoted by Resonator 2 in Fig. 1c), and the length of Resonator 2 is h2. The resonant condition of the two resonators is
Herein, λres is the resonance wavelength. ni and ti are the refractive index and thickness of the insulator layer, respectively. m is an integer number that determines the order of the resonant mode. Φb and Φt are the phase shift acquired from two reflections. Based on Eq. (1), by increasing ti, the resonant wavelength λres will red-shift. Besides, with the increase of the thickness (ti) of the insulator layer, the number of resonant modes will increase. To increase the absorption and broaden the operation bandwidth (∆λBW) of resonators, high-loss metal materials are employed for both the top and bottom metal layers. As we all know, there are many high-loss materials in nature, such as Ti, W, and Ni. These materials are inexpensive. Herein, Ti is chosen as the high-loss metal (the second layer and fourth layer). An MgF2 layer is chosen as the first and third layer. Other similar dielectrics such as SiO2, TiO2, and polymers can also be used as the dielectric layers.
To prove that the structure in Fig. 1a has two resonators, the absorption spectra of the IM and MIM planar structures in Fig. 1b, c are simulated and depicted, respectively. The absorption of the metasurface can be calculated using a formula of A = 1 − R − T. The two-dimensional finite-difference time-domain (FDTD) method is performed to simulate the proposed structure. A normally incident light is incident along the negative z-direction with the polarization along the x-direction. The mesh size is set to be 1 nm. Periodic boundary conditions are applied in the x and y directions. Perfectly matched layers (PML) are implemented at the upper and bottom boundary of the model. For the permittivity values of dielectric and metal materials, the experimental data in are employed. In the experiment, the designed metasurface is fabricated by using an E-beam evaporator. The optical transmission (T) and reflection (R) spectra of the metasurface are measured by a Shimadzu UV3600 spectrophotometer.
Simulation Results and Discussion
For the IM structure in Fig. 1b, the MgF2/Ti planar structure is placed on the MgF2 substrate, and the thickness (hm) of the Ti layer is 10 nm. As shown in Fig. 2a, with the increase of the thickness of the dielectric layer, it can be observed the number of resonance modes in the MgF2/Ti layers structure gradually increases, agreeing well with Eq. (1). This indicates that the MgF2/Ti layers structure in Fig. 1b is a resonator . Meanwhile, we also can find that the lower resonance mode (corresponding to the smaller thickness of the dielectric layer) has larger bandwidth (∆λBW). For the MIM structure in Fig. 1c, the thickness (h2) of the top Ti layer is designed to be 10 nm, whereas the bottom Ag is infinite to block the transmitted light. Similarly, we can see the obvious resonance behavior, and the lower-order resonance mode has larger bandwidth (∆λBW), as shown in Fig. 2b.
In order to obtain a broadband absorption spectrum, both of the Resonator 1 and the Resonator 2 operate in the lowest-order resonant mode by reasonable selecting the thickness (h1 = 105 nm, h2 = 95 nm) of the two dielectric (phase matching) layers. Since the reflectivity of the dielectric-air interface and dielectric-metal interface is relatively low, the fundamental resonant mode has a high optical loss. Figure 2c plots the simulation results of the absorption (red solid line) of the metasurface over the visible and near-infrared wavelengths ranging from 350 to 1500 nm. Due to the existence of two resonators, there are two absorption peaks at a shorter wavelength (around 470 nm) and a longer wavelength (around 790 nm), as shown in Fig. 2c. These two resonant peaks deviate slightly from the resonant peaks of the isolated resonators, because of the interaction of the two resonators. Due to the superimposition of the resonators, the 1D few-layer metasurface has an averaged absorption efficiency higher than 97% at wavelengths of 350–1200 nm. The operating bandwidth (A > 90%) of ∆λBW = 1000 nm is greater than those (∆λBW ≤ 750 nm)of the previous solar absorbers based on IM and MIM structures [1,2,3,4,5,6,7,8].
To further verify the physical mechanism of the 1D metasurface absorbers, the maps of power dissipation density distributions at the two absorption peaks are calculated, and the results are depicted in Fig. 2d. As expected, the incident light is mainly absorbed in the thin absorbing (high-loss metal) layer. Moreover, to prove the effectiveness and universality of the proposed structural design, we also simulate the performance of the metasurfaces by other high-loss metals. For example, the simulation results of the absorption, transmission, and reflection of the non-noble metasurfaces by using other metals (such as W, Ni and Cr) are depicted in Additional file 1: Fig. S1. In the simulation, the materials of the first and third layers are MgF2. The metasurface by using W also has an average absorption above 97% at wavelengths ranging from 350 to 1000 nm.
The absorption spectra of metasurfaces with different thicknesses of the absorbing layer are calculated and discussed in Fig. 3a. The metasurface absorber maintains its average absorption above 90% at wavelengths of 400-1200 nm within a wide range of the thickness of the thin absorbing layer (6 nm < dm < 16 nm). The result indicates a high absorption performance can be achieved in a wide range of the thickness of a thin absorbing layer, which is propitious for convenient fabrication. However, the previous work only using a single resonator requires a high-precision thickness of the thin absorbing layer for a critical coupling condition to achieve an efficient absorption.
The angle and polarization dependences are also an important criterion to evaluate an optical absorber, so we further calculate its absorption spectra under different incident angles for both transverse electric (TE) and transverse magnetic (TM) modes, as shown in Fig. 3b, c. The average absorption at wavelengths ranging from 350 to 1000 nm is also calculated and depicted in Fig. 3d. We can clearly see that the average absorption at wavelengths ranging from 350 to 1000 nm is kept above 90% at an incidence angle as high as 65°. Their average absorption is decreased slightly with the increase of incident angles and is still up to 80% for incident angles up to 75° under TE-polarized and TM-polarized light. For these previous few-layer planar nanostructures based on one resonator, the average absorption efficiency at wavelengths ranging from 400 to 1000 nm would drop below 90% for an incident angle larger than 40° under TE-polarization incidence.[1,2,3,4,5,6,7,8, 48, 50].These results show that this metasurface possessses the best performance of angular independence compared with previous few-layer planar absorbers [1,2,3,4,5,6,7,8]. The reason is that, most previously reported few-layer planar absorbers are based on only one kind of absorption mechanisms. However, the absorption in our absorber is based on the superimposing of two high-loss resonators. Based on the simulated absorption spectra, we calculate the solar-to-thermal conversion efficiency ƞ, as follows
where Eα is the total solar absorbance; ER is the thermal radiation loss; Esolar is the spectral solar irradiation; EB (λ,TA) is the blackbody radiation at temperature TA; and C is the concentration factor that is usually on the order of 1 to 1000. The calculated results are displayed by the solid lines in Fig. 3e. The absorber performs high ƞsolar thermal of > 0.9 under a TE-polarized light with an incident angle of θ < = 60°, as shown in Fig. 3e. Meanwhile, the absorber remains ƞ > = 0.9 under a TM-polarized light with an incident angle of θ < = 55°, as shown in Fig. 3e. This performance is better than that of previous solar absorbers . ƞ with various incident angles in Ref.  is depicted by the dotted line in Fig. 3e. For TM polarization, the ƞ of our absorber is about 20% higher than that of the absorber in . These results reveal that the optical absorption of our metasurface is not only broadband but also wide-angle.
Experimental Results and Discussion
To validate the proposed 1D metasurface absorber, we fabricate the designed metasurface by only using an E-beam evaporator. The bottom layer of Ti (150 nm), a spacer of MgF2 (95 nm), a thin absorption Ti layer (10 nm), and a MgF2 layer (105 nm) are deposited on a glass substrate. The image of the fabricated absorber is depicted in Fig. 4a, and we can observe that the sample is all black. Next, the optical transmission (T) and reflection (R) spectra of the metasurface are measured at wavelengths of 350–1500 nm with a Shimadzu UV3600 spectrophotometer attached to the integrating sphere (ISR-3100). The absorption (A) is then calculated by A = 1–R –T. Clearly, we see a broadband absorption spectrum with two absorption peaks, exhibiting a good agreement between simulation results in Fig. 2c and experiment results in Fig. 4b. The average absorption of the experiment results is above 97% at wavelengths from 350 to 1200 nm. The BW (∆λBW) of the absorption larger than 90% is up to 1030 nm (350 nm-1380 nm), which is greater than that (∆λBW = 750 nm ) of previously reported IM and MIM planar absorber [2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17].
Moreover, we also deposit the metasurface structure on a flexible (PE, polyethylene) substrate, and Fig. 4c represents the image of the fabricated flexible sample, which is also black. The optical properties of the flexible sample are also measured and depicted in Fig. 4d, and an average absorption above 95% at wavelengths of 350–1100 nm is obtained. The reason of the small absorption difference at shorter wavelengths between Fig. 4b, d is that it is a little difficult to ensure its high-precision thickness of metal/dielectric in deposition processes. As shown in Fig. 4e, we also measure the absorption spectra under different incident angles with unpolarized light. The experiment results show that our absorber is insensitive to the incident angle, which is consistent with the simulation results. The measured average absorption ranging from 350 to 1000 nm at various incident angles from 0° to 70° is also depicted in Fig. 4f.The measured average absorption at wavelengths ranging from 350 nm-1000 nm is kept above 90% at incidence angle as high as 65°, which is in good agreement with the simulation result in Fig. 3d. Note that, for these reported few-layer planar nanostructures based on one resonator, the average absorption efficiency at wavelengths ranging from 400 to 1000 nm would drop below 90% for incident angles larger than 40° under TE-polarization incidence.[1,2,3,4,5,6,7,8, 48, 50]
For further evaluating the potential of our metasurface in photo-thermal applications, we also characterize its light-heating property. We use a broadband halogen light source, and then record the increased temperature of a metasurface sample by a XINTEST-HT18 infrared thermometer. The power of the halogen light source is measured by a XINBAO-SM206 photometer in the following experiment. From Fig. 5a, it can be clearly seen that the generated heats are highly confined around the metasurface sample. The flexible metasurface increases its surface temperature by 25.1 K from room temperature under the halogen light of P = 1.2 kW/m2. The increase of surface temperature is higher than that of the recently reported solar absorbers based on a gold-particle metasurface (A = 83%, ∆Te = 12 °C, P = 2.4 kW/m2) and gold/nickel plasmonic metasurface (∆Te = 8 °C, P = 1kw/m2)  Furthermore, Fig. 5b, c shows representative image sequences of a frozen water droplet on a metasurface and glass samples. Firstly, a single water droplet is deposited and frozen on the surface of a metasurface and glass. Then, a halogen lamp light (P ≈ 1.2 kW/m2) illuminates the surface with the frozen droplet adhered to the metasurface or glass. For the metasurface sample, the droplet starts sliding after 40 s, and it is fully removed within approximately 75 s. In contrast, no changes of the frozen droplet are seen for the glass under the same illumination. Note that, the illumination intensity (P = 1.2 kW/m2) of the incident light in our work is only half of that (P = 2.4 kW/m2) in previous solar anti-ice studies based on gold/TiO2 particle metasurfaces, indicating that our metasurface is more advantageous to practical applications.
In summary, an efficient design strategy was proposed to achieve broadband absorbers based on 1D non-noble metasurface, consisting of dielectric/metal/dielectric/ metal layers. Owing to the superimposing of two high-loss resonators, an average absorption above 97% at wavelengths of 350–1200 nm was achieved. The bandwidth of the absorption larger than 90% was up to 1000 nm (410–1410 nm), which was greater than that (≤ 750 nm) of previous MIM planar absorbers [1, 5, 8, 25,26,27]. The metasurface was fabricated by a simple E-beam deposition method, providing the possibility of large-area applications. The simulation and experiment results showed that the broadband absorption of our absorbers was kept above 90% at an incidence angle as high as 65° ranging from 350 to 1000 nm. For previous few-layer planar absorbers, the average absorption efficiency at wavelengths ranging from 400 to 1000 nm would drop below 90% for an incident angle larger than 40° under a TE-polarization incidence.[1,2,3,4,5,6,7,8, 48, 50].Additionally, the flexibility was also demonstrated by deposit the metasurface on a flexible substrate. The flexible metasurface increased its surface temperature by 25.1 K from room temperature under a halogen lamp of P = 1.2 kW/m2. For practical applications, we investigated the capability of the flexible metasurface for removing ice under a halogen lamp of P = 1.2 kW/m2. This 1D metasurface with broadband and efficient absorption might have potential applications in solar-energy-driven icephobicity.
Availability of Data and Materials
The datasets generated during and/or analyzed during the current study are available from the corresponding authors on reasonable request.
finite-difference time domain
Landy NI, Sajuyigbe S, Mock JJ et al (2008) Perfect metamaterial absorber. Phys Rev Lett 100(20):207402
Hedayati MK, Javaherirahim M, Mozooni B et al (2011) Design of a perfect black absorber at visible frequencies using plasmonic metamaterials. Adv Mater 23(45):5410–5414
Liu N, Mesch M, Weiss T et al (2010) Infrared perfect absorber and its application as plasmonic sensor. Nano Lett 10(7):2342–2348
Yong Z, Zhang S, Gong C et al (2016) Narrow band perfect absorber for maximum localized magnetic and electric field enhancement and sensing applications. Sci Rep 6:24063
Yang C, Ji C, Shen W et al (2016) Compact multilayer film structures for ultrabroadband, omnidirectional, and efficient absorption. ACS Photon 5b00689
Wu D, Liu Y, Li R et al (2016) Infrared perfect ultra-narrow band absorber as plasmonic sensor. Nanoscale Res Lett 11
Lu X, Zhang L, Zhang T (2015) Nanoslit-microcavity-based narrow band absorber for sensing applications. Opt Express 23(16):20715–20720
Chang WS, Ha JW, Slaughter LS et al (2010) Plasmonic nanorod absorbers as orientation sensors. Proc Natl Acad Sci 107(7):2781–2786
Lu X, Wan R, Zhang T (2015) Metal-dielectric-metal based narrow band absorber for sensing applications. Opt Express 23(23):29842
Rinnerbauer V, Lenert A, Bierman DM et al (2015) Metallic photonic crystal absorber-emitter for efficient spectral control in high-temperature solar thermophotovoltaics. Adv Energy Mater 4(12):3412–3420
Wang H, Chen Q, Wen L et al (2015) Titanium-nitride-based integrated plasmonic absorber/emitter for solar thermophotovoltaic application. Photon Res 3(6):329
Wang H, Wang L (2013) Perfect selective metamaterial solar absorbers. Opt Express 21(S6):A1078–A1093
Rephaeli E, Fan S (2009) Absorber and emitter for solar thermo-photovoltaic systems to achieve efficiency exceeding the Shockley-Queisser limit. Opt Express 17(17):15145–15159
Wu C, Burton N III, John J et al (2011) Metamaterial-based integrated plasmonic absorber/emitter for solar thermo-photovoltaic systems. J Opt 14(2):24005–24011(7)
Farhat M, Cheng TC, Le KQ et al (2016) Mirror-backed dark alumina: a nearly perfect absorber for thermoelectronics and thermophotovotaics. Sci Rep 6:19984
Zhou L, Tan Y, Ji D et al (2016) Self-assembly of highly efficient, broadband plasmonic absorbers for solar steam generation. Ref Adv 2(4):e1501227–e1501227
Bae K, Kang G, Cho SK et al (2015) Flexible thin-film black gold membranes with ultrabroadband plasmonic nanofocusing for efficient solar vapour generation. Nature Commun 6:10103
Li W, Valentine J (2012) Metamaterial perfect absorber based hot electron photodetection. Nano Lett 14(6):3510–3514
Ghobadi A, Dereshgi SA, Hajian H et al (2017) 97 percent light absorption in an ultrabroadband frequency range utilizing an ultrathin metal layer: randomly oriented, densely packed dielectric nanowires as an excellent light trapping scaffold. Nanoscale
SNdergaard T, Novikov SM, Holmgaard T et al (2012) Plasmonic black gold by adiabatic nanofocusing and absorption of light in ultra-sharp convex grooves. Nature Commun 3(1):969
Ji D, Song H, Zeng X et al (2014) Broadband absorption engineering of hyperbolic metafilm patterns. Sci Rep 4:4498
Cui Y, Fung KH, Xu J et al (2011) Ultra-broadband light absorption by a sawtooth anisotropic metamaterial slab. Nano Lett 12(3):1443–1447
Michal LM et al (2014) Plasmon hybridization in pyramidal metamaterials: a route towards ultra-broadband absorption. Opt Express 22:12678–12690
Lin Y, Cui Y, Ding F et al (2017) Tungsten based anisotropic metamaterial as an ultra-broadband absorber. Opt Mater Express 7:606–617
Avitzour Y, Urzhumov YA, Shvets G (2009) Wide-angle infrared absorber based on a negative-index plasmonic metamaterial. Phys Rev 79(4):298–302
Tao H, Bingham CM, Pilon D et al (2010) A dual band terahertz metamaterial absorber. J Phys D Appl Phys 43(22):225102
Wen QiYe, Xie YunSong, Zhang HuaiWu et al (2009) Transmission line model and fields analysis of metamaterial absorber in the terahertz band. Opt Express 17(22):20256
Yang J, Sauvan C, Jouanin A et al (2012) Ultrasmall metal-insulator-metal nanoresonators: impact of slow-wave effects on the quality factor. Opt Express 20(15):16880–16891
Lin L, Zheng Y (2015) Optimizing plasmonic nanoantennas via coordinated multiple coupling. Sci Rep 5:14788
Luo SW, Zhao J et al (2016) Perfect narrow band absorber for sensing applications. Opt Express 24:9288–9294
Chen Y, Dai J, Yan M et al (2014) Metal-insulator-metal plasmonic absorbers: influence of lattice. Opt Express 22(25):30807–30814
Wang W, Zhao D, Chen Y et al (2014) Grating-assisted enhanced optical transmission through a seamless gold film. Opt Express 22(5):5416
Kim W, Simpkins BS, Long JP et al (2015) Localized and nonlocalized plasmon resonance enhanced light absorption in metal-insulator-metal nanostructures. J Opt Soc Am B 32(8):1686–1692
Le KQ, Bai J (2015) Enhanced absorption efficiency of ultrathin metamaterial solar absorbers by plasmonic Fano resonance. J Opt Soc Am B: Opt Phys 32(4):595–600
Koechlin C, Bouchon P et al (2013) Analytical description of subwavelength plasmonic MIM resonators and of their combination Abstract. Opt Express 21:7025–7032
Chen X, Shi Y, Lou F et al (2014) Photothermally tunable silicon-microring-based optical add-drop filter through integrated light absorber. Opt Express 22(21)
Yan M (2013) Metal-insulator-metal light absorber: a continuous structure. J Opt 15(2):5006
Hao J, Wang J, Liu X et al (2010) High performance optical absorber based on a plasmonic metamaterial. Appl Phys Lett 96(25):4184
Aydin K, Ferry VE, Briggs RM et al (2011) Broadband polarization-independent resonant light absorption using ultrathin plasmonic super absorbers. Nature Commun 2:517
Wu D, Liu C, Liu Y et al (2017) Numerical study of an ultra-broadband near-perfect solar absorber in the visible and near-infrared region. Opt Lett 42:450–453
Ding F, Dai J, Chen Y et al (2016) Broadband near-infrared metamaterial absorbers utilizing highly lossy metals. Sci Rep 6:39445
Michael G, Nielsen A et al (2012) Efficient absorption of visible radiation by gap plasmon resonators. Opt Express
Lu Y, Dong W, Chen Z et al (2016) Gap-plasmon based broadband absorbers for enhanced hot-electron and photocurrent generation. Reports 6:30650
Guo W, Liu Y, Han T (2016) Ultra-broadband infrared metasurface absorber. Opt Express 24:20586–20592
Tagliabue G, Eghlidi H, Poulikakos D (2013) Facile multifunctional plasmonic sunlight harvesting with tapered triangle nanopatterning of thin films. Nanoscale 5(20):9957–9962
Hu D, Wang HY, Zhu QF (2016) Design of an ultra-broadband and polarization-insensitive solar absorber using a circular-shaped ring resonator. J Nanophoton 10(2):026021
Ghobadi A, Hajian H, Gokbayrak M et al (2017) Visible light nearly perfect absorber: an optimum unit cell arrangement for near absolute polarization insensitivity. Opt Express 25(22):27624–27634
Kats MA, Blanchard R, Genevet P et al (2013) Nanometre optical coatings based on strong interference effects in highly absorbing media. Nat Mater 12(1):20–24
Lee KT, Seo S et al (2014) Strong resonance effect in a lossy medium-based optical cavity for angle robust spectrum filters. Adv Mater 26(36):6324–6328
Majid A, Amin K, Bayram B et al (2018) Large-area, cost-effective, ultra-broadband perfect absorber utilizing manganese in metal-insulator-metal structure. Sci Rep 8(1):9162
Tuning the metal filling fraction in metal-insulator-metal ultra-broadband perfect absorbers to maximize the absorption bandwidth. Photon Res 6(03):168 (2018)
Lin KT, Lin H, Yang T et al (2020) Structured graphene metamaterial selective absorbers for high efficiency and omnidirectional solar thermal energy conversion. Nature Commun 11(1)
Palik ED (1998) Handbook of Optical Constants of Solids. Academic, London
Efstratios M, Schutzius TM, Alba S et al (2018) Metasurfaces leveraging solar energy for icephobicity. ACS Nano 8b02719
Jnsson GE, Tordera D, Pakizeh T et al (2017) Solar transparent radiators by optical nanoantennas. Nano Lett 7b02962
This work was supported by the National Key Research and Development Program of China (2018YFA0704401, 2017YFF0206103, and 2016YFA0203500), the National Natural Science Foundation of China (61922002, 11904012, 91850103, 11674014, 61475005, 11527901, 11525414, and 91850111), the Beijing Natural Science Foundation (Z180015), the National Postdoctoral Program for Innovative Talents (BX20180014), and the China Postdoctoral Science Foundation (2019M660284).
The authors declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file 1: Fig. S1
. Simulated absorption for the metasurface absorbers consisting of MgF2/W/MgF2/W, MgF2/Ni/MgF2/Ni, and MgF2/Cr/MgF2/Cr layers, respectively.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, D., Chen, J. Broadening Bandwidths of Few-Layer Absorbers by Superimposing Two High-Loss Resonators. Nanoscale Res Lett 16, 26 (2021). https://doi.org/10.1186/s11671-020-03471-1
- Solar energy
- Non-noble metal