Abstract
In this work, an ultrafast and facile method is developed to synthesize Au(I)-dodecanethiolate nanotubes (Au(I)NTs) with the assistance of glycyl-glycyl-glycine (G-G-G). Transmission electron microscopy (TEM) images reveal that the as-prepared Au(I)NTs can be obtained in a 2-h reaction instead of a previous 24-h reaction and are uniform with a hollow structure and smooth surface by virtue of the G-G-G peptide tubular template. According to structural analysis, a possible preparative mechanism is proposed that the G-G-G peptide could help to curl into tube-like morphology in alkaline situation spontaneously to accelerate the formation of Au(I)NTs. Meanwhile, PVDF-stabilized Au(I)NT-modified glassy carbon electrodes present their promising potential for Hg2+ detection.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
Nanotubes have become an area of increasing interest because of their wide application in nanotechnology [1–5]. Gold nanotubes (AuNTs) are paid attention due to their unique optical and electrical properties in surface-enhanced Raman spectra (SERS)-active substrate [6] and as a refractive index reporter [7]. Up to now, one of the popular methods is hard template approach, using Ag nanowires [8], Ni nanorods [9], polymer nanowires [10], and Co nanoparticles (CoNPs) [11] as sacrificial templates. These templates are usually synthesized in the anodizing aluminum oxide (AAO) template first, since the pore diameter and pore arrangement of AAO can be tuned and controlled. However, these templating materials have to be removed via accurate control so that the conditions would be complex, and the environment would be polluted by using some strong acid, alkali, or oxidant. Recently, Zhang et al. reported a unique and green strategy to fabricate Au(0) nanotubes using Au(I)NTs as seed precursor [12]. They found that when HAuCl4 met 1-dodecanethiol in the strong alkali and stirring condition, the hybrids had a tendency to curl into tubes, followed by reduction into Au(0)NTs under electron beam irradiation. However, the self-assembly of Au(I)-alkanethiolate nanotubes would cost at least 20 h, limiting its wide application in biosensors and chemical sensors. With regard to accelerating the formation process of this special nanotube, some efforts have been put through.
As we know, cyclic peptide favored the self-assembly synthesis of organic nanotubes [13, 14]. This kind of organic nanotubes can serve as the building block to assemble to nanometer-scale devices [15–19] due to their unique advantages such as the mild synthesizing condition, low cost, and environment friendly. Herein, we combine the self-assembly of Au(I)-organic with the peptide nanotube to successfully synthesize Au(I) nanotube in a very short time. According to our recent work [20], this kind of novel Au(I) nanotubes also present potential selectivity for Hg2+ detection, as well as other Au nanostructures [21–24].
Methods
All the chemicals including aqueous hydrogen tetrachloroaurate trihydrate (HAuCl4 · 3H2O, 99.99%, Alfa Aesar, Ward Hill, MA, USA), 1-dodecanethiol (DDT, C12H25SH, 98%, Alfa Aesar), glycyl-glycyl-glycine (G-G-G, C6H11N3O4, 99%, Alfa Aesar), sodium hydroxide (NaOH, 98%, Chuandong Chemical, Chongqing, China), and Hg(NO3)2 (98%, Chuandong Chemical) were used without further purification.
The Au(I)-dodecanethiolate nanotubes were synthesized by a modified method [12]. In a typical synthesis, the reaction mixture containing 1 mL of DDT ethanol solution (0.1 M) was added to 1 mL of aqueous HAuCl4 (0.01 M) under static condition. Then, 1 mL of NaOH solution (1 M) was added dropwise to the above solution under vigorous stirring. Subsequently, 1 mL of G-G-G aqueous solution (0.1 M) was injected into the solution. The resulting mixture was maintained at room temperature under vigorous stirring condition for 2 h. The products were collected by centrifugation, followed by washing with ethanol for three times. Finally, the gold samples obtained were re-dispersed in ethanol.
The structural and morphological investigations of the samples were carried out by high-resolution transmission electron microscopy (HRTEM; ZEISS LIBRA 200, 200 kV, Carl Zeiss AG, Oberkochen, Germany). The crystallographic information and chemical composition of the as-prepared products were established by powder X-ray diffraction (XRD; D/max2500, Cu Kα). The presence of 1-dodecanthiolate in Au(I)-SC12H25 nanotubes was confirmed with Fourier transform infrared spectroscopy using the KBr pellet method (FTIR; Nicolet 5DXC FT-IR). The percentage of the organic phase in the hybrid nanotubes was analyzed by the thermogravimetric analysis (TGA; NETZSCH STA 449 F3, NETZSCH, Shanghai, China) under Ar atmosphere.
As for the Hg2+ sensor application, a bare glass carbon electrode (GCE) was first polished to a mirror-like surface with 0.3 and 0.5 μm alumina powder followed by rinsing thoroughly with deionized water, then sonicated in 1:1 nitric acid (v/v for HNO3/H2O) and deionized water, and then dried at room temperature. The cleaned electrode was modified with PVDF-stabilized Au(I)NTs by a simple casting method. Typically, 0.5 wt% nafion solution (5 μL) and prepared Au(I)NT solution (10 μL) were mixed first, then cast on the electrode surface, and dried at room temperature to obtain a PVDF-Au(I)NT-modified electrode. Hg2+ work solution was prepared in 0.1 M HCl solution and then accumulated at -0.60 V for 500 s while stirring the solution. The solution was then left for 30 s, and the square wave anodic stripping voltammetry (SWASV) measurements were performed in the potential range from -1.0 to +0.60 V with a frequency of 30 Hz, amplitude of the square wave of 25 mV, and a potential step of 4 mV. The peak heights were measured at -0.20 V.
Results and discussion
Figure 1 presents the representative TEM images of the as-prepared Au(I)-dodecanethiolate nanotubes with or without gly-gly-gly. Detailedly, Figure 1a displays a macroscopical view of uniform nanotube formation without any nanosheet, indicative of an enhancive yield [12]. Figure 1b reveals that the nanotubes have smooth surface and narrow diameter distribution with 100 nm in diameter. Since Au(I) compounds rest with beam sensitive matter, Au(I)NTs could be reduced into Au(0) nanotubes, with obvious gold nanoparticle morphology and uniform distribution (approximately 2 nm; Au+ can be deoxidated to Au0 by the electron beam) [12]. The thickness of the walls is in the range of ca. 35 nm, and the ends of the nanotubes are always open). Figure 1c shows the HRTEM image of the as-prepared Au(I)-dodecanethiolate nanotubes and the well-resolved lattice fringe which is consistent with the XRD patterns. In comparison, there are only mesoporous Au(I) nanosheet without the assistance of G-G-G in initial 2 h (see Figure 1d). This porous network has sparse curling nanosheet, presenting the important role of surfactant ligands such as gly-gly-gly.
To further reveal the chemical constitution and structure of the hybrid nanotubes, XRD patterns were obtained in Figure 2a, presenting that there is no Au(0) existence in the nanotube as there is no XRD signal of the Au(0). The periodic diffraction indicates the bilayer structure of the nanotubes, and the nearest distance between two adjacent walls is in the range of 3.384 ± 0.010 nm, in accord with our previous work [12]. This finding also verifies that gly-gly-gly does not tune the distance of Au(I)-thiol bilayer structures.
The FTIR spectrum of the nanotubes (see Figure 2b) shows the general fingerprint features of linear dodecanethiolate, confirmed by the absence of the absorption band of ν(S-H) at 2,526 cm-1. The TGA analysis of the nanotubes (see Figure 2c) indicates that the organic phase in the nanotubes has a population of about 40.66%.
On the basis of the above observation, the possible ultrafast formation mechanism of the Au(I)-alkanethiolate nanotubes is shown in Figure 3. We conclude that 1) the hybrid of HAuCl4 and DDT can form nanotubes through self-assembly method; the reaction equation is Au3+ +3RH → Au(I)-SR + RS-SR +3H+[19], but this process requires a longer time (stirring for at least 20 h). 2) The G-G-G peptides behave like a surfactant, which can easily build into tubular structures via hydrogen bonding (‘suspended’ ligands). The ligands connect each other and serve as the soft tubular-like template to synthesize the gold-organic nanotubes. The G-G-G peptides can accelerate the formation of Au(I) nanotubes, instead of doping or intercalation in the bilayer structure.
In order to elucidate the practical application of Hg2+ sensor, SWASV response is examined, as shown in Figure 4, indicating that the adsorbed Hg2+ was reduced to Hg0 at a certain potential. The SWASV analytical characteristics of bare GCE and PVDF-Au(I)NT-modified GCE present different responses in 5 μM Hg2+ in 0.1 M HCl solution. The sharper and higher peak current for Hg2+ is obtained at the PVDF-Au(I)NT-modified GCE, compared with the bare GCE, and this phenomena is consistent with the previous work [20].
Conclusions
In this work, we have developed a very quick self-assembly method to synthesize Au(I) nanotubes from 24 to 2 h via introducing G-G-G. The as-prepared Au(I) nanotubes have a uniform morphology of bilayer structure of Au-SC12H25 and well-distributed diameters with the help of G-G-G tubular template. Intriguingly, G-G-G peptide-assisted Au(I) nanotubes also demonstrate their selective sensor response of Hg2+ detection.
Abbreviations
- AAO:
-
anodic aluminum oxide
- Au(I)NTs:
-
Au(I)-dodecanethiolate nanotubes
- AuNTs:
-
gold nanotubes
- CoNPs:
-
Co nanoparticles
- DDT:
-
1-dodecanethiol
- G-G-G:
-
glycyl-glycyl-glycine
- HAuCl4 · 3H2O:
-
aqueous hydrogen tetrachloroaurate trihydrate
- NaOH:
-
sodium hydroxide
- SERS:
-
surface-enhanced Raman spectra
- SI:
-
supporting information
- TEM:
-
transmission electron microscopy.
References
Iijima S: Helical microtubules of graphitic carbon. Nature 1991, 354: 56–58. 10.1038/354056a0
Cao Q, Rogers JA: Ultrathin films of single-walled carbon nanotubes for electronics and sensors: a review of fundamental and applied aspects. Adv Mater 2009, 21: 29–53. 10.1002/adma.200801995
Kogiso M, Aoyagi M, Asakawa M, Shimizu T: Highly efficient production of various organic nanotubes with different surfaces and their application to an adsorbent. Soft Matter 2010, 6: 4528–4535. 10.1039/c0sm00077a
Roy P, Berger S, Schmuki P: TiO2 nanotubes: synthesis and applications. Angew Chem Int Ed 2011, 50: 2904–2939. 10.1002/anie.201001374
Liu Z, Tabakman S, Welsher K, Dai H: Carbon nanotubes in biology and medicine: in vitro and in vivo detection, imaging and drug delivery. Nano Res 2009, 2: 85–120. 10.1007/s12274-009-9009-8
Daniel Cardoso R, Andrade GFS, Temperini MLA: SERS performance of gold nanotubes obtained by sputtering onto polycarbonate track-etched membranes. Phys Chem Chem Phys 2013, 15: 1169–1176. 10.1039/c2cp43229c
Bridges CR, DiCarmine PM, Seferos DS: Gold nanotubes as sensitive, solution-suspendable refractive index reporters. Chem Mater 2012, 24: 963–965. 10.1021/cm203184d
Costa JC, Corio P, Camargo PH: Silver-gold nanotubes containing hot spots on their surface: facile synthesis and surface-enhanced Raman scattering investigations. RSC Advances 2012, 2: 9801–9804. 10.1039/c2ra21562d
Sander MS, Gao H: Aligned arrays of nanotubes and segmented nanotubes on substrates fabricated by electrodeposition onto nanorods. J Am Chem Soc 2005, 127: 12158–12159. 10.1021/ja0522231
Bridges CR, DiCarmine PM, Fokina A, Huesmann D, Seferos DS: Synthesis of gold nanotubes with variable wall thicknesses. J Mater Chem A 2013, 1: 1127–1133. 10.1039/c2ta00729k
Schwartzberg AM, Olson TY, Talley CE, Zhang JZ: Gold nanotubes synthesized via magnetic alignment of cobalt nanoparticles as templates. J Phys Chem C 2007, 111: 16080–16082. 10.1021/jp076034b
Zhang YX, Zeng HC: Gold(I)-alkanethiolate nanotubes. Adv Mater 2009, 21: 4962–4965. 10.1002/adma.200901677
Ghadiri MR, Granja JR, Milligan RA, McRee DE, Khazanovich N: Self-assembling organic nanotubes based on a cyclic peptide architecture. Nature 1993, 366: 324–327. 10.1038/366324a0
Gao X, Matsui H: Peptide-based nanotubes and their applications in bionanotechnology. Adv Mater 2005, 17: 2037–2050. 10.1002/adma.200401849
Vauthey S, Santoso S, Gong H, Watson N, Zhang S: Molecular self-assembly of surfactant-like peptides to form nanotubes and nanovesicles. Proc Natl Acad Sci 2002, 99: 5355–5360. 10.1073/pnas.072089599
Song Y, Challa SR, Medforth CJ, Qiu Y, Watt RK, Peña D: Synthesis of peptide-nanoparticle composites. Chem Commun 2004, 9: 1044–1045.
Reches M, Gazit E: Casting metal nanowires within discrete self-assembled peptide nanotubes. Science 2003, 300: 625–627. 10.1126/science.1082387
George J, Thomas KG: Surface plasmon coupled circular dichroism of Au nanoparticles on peptide nanotubes. J Am Chem Soc 2010, 132: 2502–2503. 10.1021/ja908574j
Kim JU, Cha SH, Shin K, Jho JY, Lee JC: Synthesis of gold nanoparticles from gold(I)-alkanethiolate complexes with supramolecular structures through electron beam irradiation in TEM. J Am Chem Soc 2005, 127: 9962–9963. 10.1021/ja042423x
Xie W, Zhang H, He SX, Tang DY, Fang SX, Huang Y, Du CL, Zhang YX, Zhang W: A novel electrochemical sensor based on nafion-stabilized Au(I)-alkanethiolate nanotubes modified glassy carbon electrode for the detection of Hg2+. Analytical Method 2014, 6: 4988–4990. 10.1039/c4ay00640b
Xu XX, Duan GT, Li Y, Liu GQ, Wang JJ, Zhang HW, Dai ZF, Cai WP: Fabrication of gold nanoparticles by laser ablation in liquid and their application for simultaneous electrochemical detection of Cd2+, Pb2+, Cu2+, Hg2+. ACS Appl Mater Interfaces 2014, 6: 65–71. 10.1021/am404816e
Hofmann CM, Essner JB, Baker GA, Baker SN: Protein-templated gold nanoclusters sequestered within sol–gel thin films for the selective and ratiometric luminescence recognition of Hg2+. Nanoscale 2014, 6: 5425–5431. 10.1039/c4nr00610k
Annadhasan M, Muthukumarasamyvel T, Sankar BVR, Rajendiran N: Green synthesized silver and gold nanoparticles for colorimetric detection of Hg2+, Pb2+, and Mn2+ in aqueous medium. ACS Sustain Chem Eng 2014, 2: 887–896. 10.1021/sc400500z
Wu XF, Li RY, Li ZJ, Liu JK, Wang GL, Gu ZG: Synthesis of double gold nanoclusters/graphene oxide and its application as a new fluorescence probe for Hg2+ detection with greatly enhanced sensitivity and rapidity. RSC Advances 2014, 4: 24978–24985. 10.1039/c4ra03217a
Acknowledgements
The authors gratefully acknowledge the financial support provided by the National Natural Science Foundation of China (Grant no. 51104194 and 21207165) and the National Key Laboratory of Fundamental Science of Micro/Nanodevice and System Technology (No. 2013MS06, Chongqing University).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
ZZ and YZ synthesized and characterized the Au(I)-dodecanethiolate nanotubes and wrote the manuscript. CM and LH prepared the advanced Hg2+ sensor electrodes. SZ and XH conceived and designed the experiments. WX and WZ coordinated the study. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (https://creativecommons.org/licenses/by/4.0), which permits use, duplication, adaptation, distribution, and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Zhang, Z., Ma, C., He, L. et al. Ultrafast synthesis of Au(I)-dodecanethiolate nanotubes for advanced Hg2+ sensor electrodes. Nanoscale Res Lett 9, 601 (2014). https://doi.org/10.1186/1556-276X-9-601
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-601