Morphological transformation of gold nanoparticles on graphene oxide: effects of capping ligands and surface interactions
- 85 Downloads
This article presents the influence of capping ligand and surface interaction types on the coarsening or reshaping behavior of surface-immobilized gold nanoparticles with different core size and shape. The morphological transformation of gold nanoparticles and nanorods on graphene oxide upon heating at temperatures ranging from 50 to 200 °C was investigated. The aggregation and coarsening behaviors of spherical nanoparticles on graphene oxide were slightly affected by the core size of nanoparticles (~ 1, 3, and 10 nm). The comparison of two different surface ligands revealed that glutathione ligands provide much better protection than cetyltrimethylammonium bromide ligands against the morphological transformation of nanoparticles. In addition, the evaluation of surface binding interactions indicated that the attachment of nanoparticles and nanorods onto graphene oxide with additional thiol functional groups could improve the immobilization of particles and therefore decelerate coarsening and reshaping of nanoparticle and nanorods.
KeywordsNanoparticles Nanorods Graphene oxide Stability Morphology Gold
thiol-functionalized graphene oxide
glutathione-capped gold nanoparticles
cetyltrimethylammonium bromide-capped gold nanoparticles
cetyltrimethylammonium bromide-capped gold nanorods
transmission electron microscopy
Metal nanoparticles are a class of functional materials with unique physical and chemical properties, which are closely related to their size, shape, composition, and structure [1, 2]. Especially, gold nanoparticles (AuNP) and gold nanorods (AuNR) have gained a lot of attention because of their applications in catalysis, electronics, and sensors [2, 3, 4, 5, 6, 7, 8, 9, 10, 11]. They have also exhibited many attractive features such as strong plasmonic activity, facile ligand functionalization, water solubility, and excellent biocompatibility, which have made them good candidates for biomedical applications [6, 7, 9, 10, 11, 12, 13, 14, 15, 16, 17]. Deposition of AuNPs on solid supports has often been necessary for various reasons including enhanced stability and synergistic activity [2, 5, 10, 11, 14]. Therefore, the preparation of nanoparticle hybrids with the appropriate support materials and understanding the influence of supports to nanoparticles are critical to the expansion of practical applications of AuNPs [18, 19].
Since AuNPs anchored on graphene families could exhibit interesting catalytic, electrical and optical activities [2, 5, 8, 10, 11, 20], understanding the nature and extent of morphological transformation of gold nanoparticle-graphene oxide (AuNP-GO) hybrids could maximize their potentials for many practical applications [18, 19, 20, 21, 22, 23]. Previous studies from our research group have shown that the presence of GO supports negatively affects the stability of AuNPs and AuNRs causing their core to undergo size and/or shape evolutions more easily . The disruption and stripping of the protecting organic ligands by GO through strong electrostatic interactions were proposed as a main mechanism of nanoparticle destabilization on GO.
The gradual changes in size and shape of nanoparticles, when they are exposed to heat or light irradiation [21, 22, 25, 26, 27], could seriously impede their long-term technological advancements for device and catalysis applications. Therefore, further understanding of various factors determining morphological transformations of nanoparticles is required for developing new strategies for improving their overall stability and performance. In this study, AuNPs with different core sizes are assembled on the surface of GO to study their heat-induced coarsening behavior. AuNPs with different surface capping ligands (glutathione and cetyltrimethylammonium bromide (CTAB)) on GO was also prepared to understand the relationship between the stability of AuNPs and the type of surface ligand-nanoparticle interactions. The chemical interaction or bond formation between GO supports and ligand-capped AuNPs was also controlled by using thiol-functionalized GO (tGO) to see the influence of additional metal-sulfur bond against the morphological transformation of AuNP and AuNR. Various AuNP-GO and AuNR-GO hybrid materials are annealed from 50 to 200 °C to examine the influence of various structural components.
Detailed information regarding materials, synthetic procedures, and characterizations (1H NMR, FT-IR, and TGA) for glutathione-capped gold nanoparticles (gAuNP) [28, 29, 30, 31], cetyltrimethylammonium bromide (CTAB)-capped gold nanoparticles (cAuNP) , and CTAB-capped gold nanorods (cAuNR) , and instrumental methods used to conduct the research presented in this article are provided in the previous publications and Additional file 1 [15, 24, 29].
2.1 Preparation of thiol-functionalized graphene oxide (tGO)
Thiol-functionalized graphene oxide was made by following the published procedure [22, 30, 32]. First, 5 mL of 0.4 M EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide), 5 mL of 0.1 M NHS (N-hydroxysuccinimide), and 5 mL 0.1 M l-cysteine were prepared. A 0.5 mL solution of concentrated hydrochloric acid was added to the l-cysteine solution to dissolve the l-cysteine crystals. Solutions of EDC, NHS, and l-cysteine were added to 8 mL of 4 mg/mL graphene oxide suspension in the order mentioned. As soon as the EDC/NHS/l-cysteine solutions were added, graphene oxide begins to separate from solution due to the decrease in polarity of GO with the incorporation of thiol functional groups from l-cysteine. The mixture is left sitting for 10 min, then centrifuged. The supernatant is discarded, and the precipitate was washed with nanopure water and centrifuged to precipitate the tGO. This process was repeated twice. The final product was left to dry in a vacuum overnight. IR spectra of isolated tGO showed the presence of S–H stretching bands at ~ 2565 cm−1.
2.2 Preparation of gold nanoparticle-graphene oxide (AuNP-GO) and nanorod-graphene oxide (AuNR-GO) hybrids
Graphene oxide solution was made by dispersing GO flakes in nanopure water. GO flakes were not readily dispersed in water, hence the mixture was sonicated for 30 min until the GO formed a homogeneous dispersion. The concentration of GO solution was 1 mg/mL. The GO dispersion in water exhibited long-term stability. The gAuNP of size ~ 1, 3, and 10 nm, cAuNP, and cAuNR were bonded to GO as follows: Gold nanorods/nanoparticles were dissolved in water (~ 1 mg/mL) forming homogeneous solutions. The solutions of GO and gold nanorods/nanoparticles were mixed at a 1:1 ratio (v/v: 1 mL GO solution to 1 mL gold nanorod/nanoparticle solution) for 24 h.
To prepare the hybrids of tGO with AuNP and AuNR, the dried tGO was re-dispersed in nanopure water and the aqueous solutions of AuNP and AuNR were added to this solution. The mixture was then stirred at room temperature for 24 h to allow the formation of metal-sulfur bonds, so that the nanoparticles and nanorods can be covalently anchored to graphene oxide. The final hybrid product is then centrifuged, and the supernatant was discarded. The resulting precipitate was stored in a vacuum desiccator for at least 72 h to remove all solvents.
2.3 Heat-treatment of AuNP-GO and AuNR-GO hybrids
The hybrids were heated from 50 to 200 °C, at 50 °C increments using a Barnstead Thermolyne 1300 Furnace. Each sample was heated for 1 h in a glass vial in air. Solvents were removed to dryness before the particle samples were heated in powder form.
3 Results and discussion
3.1 Gold nanoparticles with different sizes and stabilizing ligands
Core size evolution of gold nanoparticles and nanorods (nanometers)
Supported on GO (or tGO)
Heated at 50 °C
Heated at 100 °C
Heated at 150 °C
Heated at 200 °C
11.1 ± 1.2
10.1 ± 6.9
10.9 ± 4.8
11.5 ± 6.6
20.2 ± 8.6
22.1 ± 6.2
3.0 ± 1.4
3.0 ± 0.9a
2.9 ± 1.1
3.1 ± 1.8a
3.1 ± 1.1
3.3 ± 1.6a
3.3 ± 1.6
7.0 ± 3.6a
5.1 ± 2.0
10.1 ± 5.4a
7.6 ± 3.8
1.2 ± 0.3
1.3 ± 0.4
1.4 ± 0.5
1.4 ± 0.7
4.7 ± 0.8
5.3 ± 1.6
2.7 ± 1.1
3.6 ± 1.6
10.0 ± 6.0
13.7 ± 10.5
68.5 ± 20.1
53.6 ± 8.2
15.1 ± 3.6
53.8 ± 13.2a
17.3 ± 6.3a
54.4 ± 7.1
14.8 ± 2.3
89.4 ± 52.3a
52.4 ± 6.7
12.9 ± 2.2
3.2 Gold nanoparticles and nanorods on graphene oxide
When cAuNP3nm and cAuNR are deposited on GO, the SP bands at ~ 520 nm almost completely disappear and the longitudinal plasmon band of cAuNR decreases in intensity (Fig. 4b), which is another piece of evidence for electronic and optical interference of GO for plasmonic nanostructures. Such changes in the plasmon response of cAuNR adsorbed on GO have also been observed by others [37, 38]. The absence of any shift for the longitudinal plasmon band of cAuNR indicated, however, that the aspect ratio of cAuNR mostly remained the same.
Additional file 1: Figure S1 shows TEM images of various gAuNP-GO hybrid materials and their respective histograms showing size distribution. GO sheets are apparent in all the TEM images as darker regions. The actual particle core size of gAuNP10nm-GO is estimated to be ~ 10 nm, which is similar to the size of free standing gAuNP10nm (Table 1). However, the images showed many particles to be positioned closely together making an accurate histogram analysis a bit more difficult. These apparent formations of nanoparticle aggregates must be the main reason for the large red shift of the SP bands of gAuNP10nm after GO adsorption. TEM image and histogram results agreed that the gAuNP3nm-GO have relatively well dispersed nanoparticles with the average core size near ~ 3 nm. The histogram results indicated gAuNP3nm are relatively stable after GO immobilization showing no evidence of core size evolution. For gAuNP1nm-GO hybrids, TEM images and histogram results indicated there is a slight increase in average core size of gAuNP1nm after adsorption onto GO. This size change corresponded well with the UV–vis results of gAuNP1nm-GO and support the previous discovery reported by Ghosh et al.  regarding the size evolution of Au25 clusters when in contact with graphene substrate.
TEM results shown in Additional file 1: Figure S2 indicated that cAuNP3nm and cAuNR are immobilized on GO without any aggregation or reshaping maintaining a similar core size and an aspect ratio of over 3 (~ 54 nm in length and ~ 17 nm in width), respectively. The TEM results agreed relatively well with their corresponding UV–vis spectra of their original sizes and shapes shown in Fig. 4b. The dampening of the plasmon bands of cAuNP3nm and cAuNR at ~ 520 nm was clearly not a result of any significant morphological size or shape changes.
When comparing the core sizes of the nanoparticles before and after their assembly onto GO, it is clear that the use of pre-formed nanoparticles mostly affords the retention of core size and dispersity of assembled nanoparticles without any significant change. However, very small clusters (~ 1 nm) and large colloidal nanoparticles (> 10 nm) that usually exhibit low stability alone in solution phase are also susceptible to a slight change in their morphologies after immobilization on GO. This result is confirmed by TEM analysis and the changes in their optical activity. Gold nanorods immobilized on GO avoided extensive aggregations suggesting the presence of CTAB bilayer ligands on their surfaces.
3.3 Effects of core size on coarsening of gAuNP on GO
Our previous work has shown that the presence of GO facilitates the coarsening of gAuNP3nm . As shown in Table 1, large increases in the average core size of gAuNP3nm on GO took place at heating temperatures between 100 and 150 °C. The transition, however, took place between 150 and 200 °C for free standing gAuNP3nm . The hypothesis was that the GO, being a flexible material, can bend and wrap around the nanoparticles and chemically interact with the ligands due to the presence of many oxygen-containing functional groups. The ligands on AuNP are then pulled away from the nanoparticle and spilled over to GO during heat treatment facilitating the coarsening of the nanoparticles.
Heat treatments of gAuNP10nm-GO and gAuNP1nm-GO were performed from 50 to 200 °C at 50 °C increments to see the effects of particle size on the heat-induced coarsening behavior of gAuNP. UV–vis spectra of gAuNP10nm-GO showed the decreased intensity and significant broadening of SP bands after the heat treatments of the hybrids at 100 °C, which is lower than the temperature required for gAuNP3nm-GO (Additional file 1: Figure S3). The transitions continued with heating at increased temperatures and quickly reached the status of film-like insoluble materials showing only small scattering effects [39, 40, 41]. This fast transition would likely be caused by the formation of particle aggregations upon the adsorption of gAuNP10nm on GO.
UV–vis spectra of gAuNP1nm-GO (Additional file 1: Figure S4) show that the transition is gradually taking place throughout the heating temperature between 50 and 200 °C with decreasing intensity of spectra. The film-like spectral feature has appeared after heat treatments at 200 °C. This overall transition after heat treatment resembles quite similarly to that of gAuNP10nm-GO as shown above. The presence of small SP bands of gold is apparent for gAuNP1nm-GO after heating at 50 °C, which indicates some aggregation and coarsening of nanoparticles to slightly larger nanoparticles (~ 1.5–2.5 nm). The absence of any strong SP bands after heating at high temperature, however, indicates that the significant coarsening of gAuNP1nm on GO to larger (> 3 nm) particles did not take place.
TEM images of the heated gAuNP1nm-GO are shown in Additional file 1: Figure S5 and the changes in the average core size and distribution are summarized in Table 1. The results suggested that the more rapid transition is observed at temperature below 150 °C for the gAuNP1nm-GO compared to other gAuNP on GO. The gAuNP1nm-GO began to reach the extensive coarsening stage and became mostly insoluble during the heat treatment at 200 °C. These results also corresponded well with the data obtained from UV–vis spectra.
3.4 Effects of capping ligands for coarsening of gold nanoparticles on graphene oxide (gAuNP3nm-GO vs cAuNP3nm-GO)
3.5 Effects of additional thiol functional groups on graphene oxide for coarsening of gold nanoparticles and nanorods (GO vs tGO)
The gAuNP3nm and cAuNR were also adsorbed on thiol-functionalized GO (tGO) to study the effect of additional thiol-gold interaction between nanoparticles and GO during coarsening or reshaping. The tGO was prepared by the well-established method using the coupling of l-cysteine to graphene oxide in the presence of EDC and NHS [22, 30, 32]. The tGO was then mixed with a solution containing gAuNP3nm or cAuNR which resulted in the self-assembly of nanoparticles onto the surface of tGO with the formation of gold-sulfur bonds in addition to all electrostatic interactions unmodified GO provide. TEM and histogram results showed that the gAuNP3nm-tGO still have the surface immobilized particles with the average core size near ~ 3 nm (Additional file 1: Figure S6). Any immediate aggregation after the adsorption of gAuNP3nm on tGO was not observed from TEM results.
Additional file 1: Figure S7 shows the UV–vis spectra of gAuNP3nm-tGO after heat treatments at temperature ranging from 50 to 200 °C. The intensity of SP bands along with the overall absorbance spectra, which show an exponential decay from lower wavelength to higher wavelength, continuously decreased after heat treatments at the range between 50 and 150 °C. The results were almost identical with the ones observed for gAuNP3nm-GO indicating the particles have begun to aggregate and become partially insoluble . The UV–vis spectra of gAuNP3nm-tGO heated at 200 °C showed completely different spectral features for the particles heated at high temperature, which resemble the characteristic of localized metallic film-like structures [24, 39, 40, 41, 42].
Additional file 1: Figure S8 shows TEM images of heated gAuNP3nm-tGO at temperature from 50 to 150 °C. These results showed that the average core size increase occurred the most between 100 and 150 °C as we have seen from the heat treatments of gAuNP3nm-GO. However, after heating at 150 °C, TEM image and histogram results showed that the gAuNP3nm-tGO had a smaller average core size (5.09 ± 1.97 nm) than gAuNP3nm-GO (7.04 ± 3.61 nm). Although the difference is still within the standard deviation of each sample, the result suggests that there might be some stabilizing influence of tGO with the formation of Au–S bonds between tGO and gAuNP (Table 1). The presence of stronger Au–S bonds in addition to other electrostatic interactions would provide more robust interactions between nanoparticles and GO. Thus, with the use of tGO, the immobilized AuNP would be more kinetically trapped and become slightly less susceptible to aggregation and coarsening.
In this study, the coarsening behavior of gold nanoparticles on graphene oxide was investigated with the focus on the influence of particle core size, stabilizing ligands, and thiol linkers. For gold nanoparticles, the core size evolution was slightly affected by the size of nanoparticles. Gold nanoparticles smaller than 1.5 nm and large colloidal gold nanoparticles of ~ 10 nm were less stable than gold nanoparticles with ~ 3 nm core, undergoing immediate coarsening and/or aggregation upon adsorption on the surface of graphene oxide. The core size evolution during heat treatments at the temperature ranging from 50 to 200 °C, however, was similar for all three gold nanoparticles with different core sizes. Glutathione was observed to be a more stabilizing ligand than CTAB by having a stronger bond with the gold surface and a greater resistance to being removed from the nanoparticles by graphene oxide. Much greater core size evolution was observed from CTAB-capped gold nanoparticles on graphene oxide. The presence of thiol linkers on graphene oxide allowed for the formation of strong Au–S bonds that immobilized the nanoparticles strongly onto graphene oxide. The improvement in the stability of nanoparticles by Au–S bond formation was even more profound for the gold nanorods. The heat treatments of gold nanorods on graphene oxide at 50 °C resulted in the complete reshaping of nanorods to spherical particles. Under the same condition, the reshaping of gold nanorods on thiol-functionalized graphene oxide was not observed indicating that the formation of Au–S bonds allows the gold nanorod to withstand the thermal energy even after the disruption of CTAB ligands around nanorods. The overall results proved that small modification in the nanoparticle and/or graphene oxide functional groups would have a large influence on intrinsic stability of nanomaterials.
HP and SL contributed equally on conducting both experimental work related to the synthesis and characterization of nanoparticles, nanoparticle hybrids, and heat-treated hybrids. NW and BW contributed partially for TEM imaging and analysis of nanoparticles and hybrids. YS supervised the project. The manuscript was initially written through contributions of HP and SL and revised by BW and YS. All authors read and approved the final manuscript.
The authors declare that they have no competing interests.
This study was funded by the National Institute of General Medical Science (#SC3GM089562) of the National Institutes of Health.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
- 6.X. Zhang, J. Zhang, H. Wang, Y. Hao, X. Zhang, T. Wang, Y. Wang, R. Zhao, H. Zhang, B. Yang, Thermal-induced surface plasmon band shift of gold nanoparticle monolayer: morphology and refractive index sensitivity. Nanotechnology 21, 1–11 (2010)Google Scholar
- 39.Y.-S. Shon, M. Aquino, T.V. Pham, D. Rave, M. Ramirez, K. Lin, P. Vaccarello, G. Lopez, T. Gredig, C. Kwon, Stability and morphology of gold nanoisland arrays generated from layer-by-layer assembled nanoparticle multilayer films: effects of heating temperature and particle size. J. Phys. Chem. C 115, 10597–10605 (2011)CrossRefGoogle Scholar
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.