BMC Chemistry

, 13:17 | Cite as

Synthesis of lignin based composites of TiO2 for potential application as radical scavengers in sunscreen formulation

  • Mohamad Nasir Mohamad IbrahimEmail author
  • Anwar Iqbal
  • Chai Chuan Shen
  • Showkat Ahmad Bhawani
  • Farook Adam
Open Access
Research article
Part of the following topical collections:
  1. Environmental and Energy Chemistry


Titanium dioxide (TiO2) is added in sunscreens due to its ability to absorb ultraviolet (UV) light. However, upon irradiation of UV light, reactive oxygen species particularly hydroxyl radical which can damage human skin will be generated. In this study, lignin/TiO2 composites were employed to quench the hydroxyl radicals generated by the TiO2. The lignin was extracted from oil palm empty fruit bunch (OPEFB) via kraft and soda pulping processes. The kraft lignin composite was labelled as KL/TiO2 whereas the soda lignin composite was labelled as SL/TiO2. The lignins and the composites were characterized by FTIR, UV spectroscopy, 13C NMR, SEM, EDX, and XRD. The relative hydroxyl radical production of composites and TiO2 were compared through photo-oxidation of coumarin to 7-hydroxycoumarin as a test medium. The effect of types and amounts of lignin used were studied. The KL/TiO2 composite showed the least radical production due to higher phenolic hydroxyl content of kraft lignin. The activity of the hydroxyl radicals will be quenched when it abstract hydrogen atoms from the phenolic hydroxyl groups.


TiO2 Hydroxyl radical Lignin Oil palm empty fruit bunch Lignin/TiO2 composite 



titanium II dioxide


oil palm empty fruit bunch


kraft lignin


soda lignin


Titanium dioxide (TiO2) is used as an inorganic agent in sunscreens due to its ability to reflect, scatter and absorb a wide range of ultraviolet radiation in sunlight [1]. The maximum loading of TiO2 in sunscreens is 25%, and the crystalline form of TiO2 that mostly used for this application is anatase [2]. The TiO2 is also employed as opacifiers and pigments in paints and paper coatings due to the whiteness and opaque characteristics [3]. Moreover, TiO2 possesses excellent photocatalytic capability which makes it suitable for removal of organic compounds in contaminated water [4]. However, this capability of TiO2 is a double-edged sword. The photocatalytic activity of TiO2 can generate superoxide and hydroxyl radicals by the irradiation of sunlight. This is unfavorable for the application in sunscreens. These reactive oxygen species with cytotoxic and genotoxic characteristics can react with biomolecules such as protein and DNA upon formation on the surface of TiO2 [5]. This may result in carcinogenesis, enzyme inactivation and potential damage of biomolecules [5]. The reactive oxygen species will cause the degradation of other organic agents in sunscreen [6].

A variety of methods have adopted by many researchers to reduce the photocatalytic activity of TiO2. The alumina was used to coat TiO2 by Picatonotto et al. [7]. The inorganic surface coating minimizes the photocatalytic activity by reducing holes and electrons generation and enhancing electron–hole recombination which leads to quenching of photocatalytic activity. The encapsulation of TiO2 in zeolites reduced its photocatalytic efficiency by increasing the band gap so that excitation can only take place under ultraviolet radiation with the wavelength below 265 nm (ultraviolet C (UVC) region) [8]. The UVC can be absorbed by the ozone layer and will not reach the surface of the earth. Moreover, instead of inhibiting the photocatalytic activity of TiO2, Chen et al. [9] utilized the antioxidant properties of chitosan to capture the free radicals generated by the photocatalytic activity of TiO2.

Chemically, lignin is a natural, amorphous and cross-linked phenolic biopolymer with very complex structure [10]. Lignin provides structural rigidity for plants and supports transport of nutrients and water in plants. It can be extracted from the black liquor which is always considered as waste in pulping and paper industries [11]. Lignin is made up of three major phenylpropanoid units that differ in the amount of methoxyl groups namely p-hydroxyphenyl (H), guaiacyl (G) and syringyl (S) as shown in Fig. 1 [10]. It can be extracted from different biomass materials such as oil palm ligocellulosic waste, and kenaf through soda, kraft, ethanol or other pulping processes [10, 12]. The composition and properties of lignin vary for different pulping processes, types, and parts of plants.
Fig. 1

The structure of three major phenylpropanoid units of lignin

The oil palm empty fruit bunch (OPEFB) is one of the agriculture wastes generated by the oil palm industry. The oil palm agriculture wastes are normally burned in incinerators and thus lead to environmental pollutions such as haze which affect human health [13]. In the previous studies, OPEFB lignin has been employed in several applications such as food emulsifying agent, heavy metal adsorption for waste water treatment, wood adhesive, corrosion inhibitor and additives in mud drilling [14]. The special advantage of OPEFB lignin is that it can be obtained from agriculture wastes instead of other plants such as pine tree and acacia tree which may involve deforestation.

The previous study showed that oil palm empty fruit bunch lignin exhibited antioxidant properties and acted as free radical scavenger due to the presence of phenolic hydroxyl group [15]. The phenolic hydroxyl groups act as a proton donor and can stabilize the resulting radicals by substituents and delocalization. Besides the antioxidant properties, the cytotoxic effects of lignin from different sources have been studied and lignin from all sources are proved safe to the human cell [16]. This previous research has removed the doubts about the safety concerns of lignin. Lignin can be a natural sun blocker for broad spectrum since it contains a large amount of ultraviolet absorbing functional groups such as phenolic, ketone and other chromophores as reported by Qian et al. [17].

The antioxidant properties and UV absorption capability of lignin had motivated us to employ lignin to scavenge the hydroxyl radicals generated from the photocatalytic activity of TiO2 by forming a lignin/TiO2 composite. The effects of types and amounts of lignin were investigated. Although lignin has been used for reducing phototoxicity of TiO2 by some researches [2, 18], the lignin extracted from oil palm empty fruit bunch for scavenging free radical generated by TiO2 has not been explored yet. Therefore, this study also intends to recycle the oil palm lignocellulosic waste into a useful product for potential cosmetic application. Thus, a disposal alternative of agriculture wastes in the oil palm industry is suggested.



The oil palm empty fruit bunch (OPEFB) fiber used in this study was supplied by Sabutek (M) Sdn. Bhd., Malaysia, a local company specializing in recycling oil palm lignocellulosic waste. All the chemicals used are analytical reagent grade. Most of them are from Qrec (Asia) Sdn. Bhd., Malaysia and Sigma-Aldrich Chemie GmbH, Germany.

Kraft and soda pulping processes

Both kraft and soda pulping processes were carried out in a 10 L stainless steel rotary digester. The OPEFB (500 g) fiber was used for both pulping processes. For kraft pulping, 19% of active alkali and 25% of sulfidity with water to fiber ratio of 8 were added to the digester. The digester was heated from room temperature to 170 °C for 1 h and maintained at 170 °C for another 3 h. For soda pulping, 25% of active alkali with no percentage of sulfidity was added into the digester and similar conditions as kraft pulping were used [15]. The black liquor produced from the pulping processes was separated from the pulp by filtering with screening through a filtering sieve twice and collected. The black liquor was filtered again via vacuum filtration for further removing the pulp from black liquor.

Preparation of OPEFB Kraft and Soda Lignin

The pH of kraft and soda black liquors measured were 13.75 and 13.49, respectively. The kraft and soda lignins were precipitated from concentrated black liquors by acidifying them until pH 2.0 using 20% (v/v) sulfuric acid. The suspensions were centrifuged at 3500 rpm for 10 min. The liquid layer was discarded while the precipitate was washed with acidified distilled water (pH 2.0). The kraft and soda lignins were dried in an oven at 55 °C for 3 days [15].

Synthesis of lignin/TiO2 composites

The lignin/TiO2 composites were synthesized by using the previously reported method [18]. The kraft lignin (1.0 g) was mixed with 70 mL of ultrapure water under stirring. The solubilization of kraft lignin was carried out by adding 30 mL of 1 M NaOH dropwise followed by the addition of 0.1 g of anatase TiO2. The mixture was homogenized at 900 rpm for 40 min and sonicated at 40 kHz for 150 min. The mixture was cooled down to 0 °C in an ice bath and diluted with 200 mL of ultrapure water. The kraft lignin/TiO2 composite was precipitate by adding 300 mL of 0.25 M. The kraft lignin/TiO2 suspension was centrifuged at 3500 rpm for 10 min. The liquid layer was discarded. The precipitate was washed with ultrapure water twice and dried in an oven at 80 °C for 6 h. The dried kraft lignin/TiO2 composite was ground into powder and labeled as KL/TiO2-1.0. The procedures were repeated by using soda lignin to produce soda lignin/TiO2 composite. The composite was labelled as SL/TiO2-1.0. The other three composites were prepared by varying the weight of kraft lignin added (0.5 g, 1.5 g, and 2.0 g). The kraft lignin/TiO2 composites formed were labeled as KL/TiO2-0.5, KL/TiO2-1.5 and KL/TiO2-2.0, respectively.

Characterization of Lignin and Lignin/TiO2 Composite

FTIR analysis

The FTIR analysis was performed for lignins, lignin/TiO2 composites and anatase TiO2 by using Perkin Elmer model System 2000 instrument. The FTIR spectra were recorded in a direct transmittance mode and a frequency range of 4000 to 400 cm−1 with a resolution of 4 cm−1 and 16 scans. The KBr pellet for FTIR analysis was prepared by mixing the solid sample with KBr in a ratio of 1:100 (w/w).

UV spectroscopy

The UV spectrometric analysis of kraft and soda lignins in dioxane solution and alkaline solution were conducted. In brief, 7 mg of lignin was dissolved in 5 mL of dioxane-water solution (9:1, v/v). Similarly, 7 mg of lignin was dissolved in 5 mL of pH 12 NaOH solution. Subsequently, 50-fold dilution was carried out for both solutions [10]. The UV spectra were recorded by using UV Perkin Elmer Lambda 35.

13C NMR analysis

Since lignin is difficult to dissolve in most deuterated solvents [12], acetylation was done to enhance the results of the analysis. 1.0 g of lignin, 7.5 mL pyridine and 7.5 mL acetic anhydride were mixed in 250 mL conical flask and stirred for 24 h at room temperature. The mixture was cooled down to 0 °C in an ice bath. Into the solution, 150 mL of 1% HCl (w/v) was then added dropwise. The formed precipitate was filtered using vacuum filtration. The resulting precipitate was washed with distilled water and dried in an oven at 50 °C for 48 h. The acetylated lignin (150 mg) was dissolved in 0.4 mL d6-DMSO and injected into the NMR tube. The analysis was conducted at 50 °C with 22,000 scans by using Bruker Avance 500 MHz.

XRD analysis

The XRD analysis was performed for KL/TiO2-1.0 and SL/TiO2-1.0 using Bruker D8 Advance equipped with Cu Kα radiation, λ of 0.154 nm, the voltage of 40 kV and current of 40 mA. The XRD diffractogram were recorded with 2 theta degree ranged from 10°to 90° at a continuous scanning rate of 3° min−1.

SEM and EDX analysis

The SEM analysis was carried out for kraft lignin, KL/TiO2-1.0 and SL/TiO2-1.0 and anatase TiO2 with Leo Supra 50 VP Field Emission Scanning Electron Microscope. The magnification was set as 10,000 for each sample. The EDX analysis was conducted for KL/TiO2-1.0 and SL/TiO2-1.0 using Oxford-Instruments INCA 400 with X-Max Detector.

Detection of hydroxyl radicals

Coumarin solution was used to detect the presence of hydroxyl radicals following the method reported by Ishibashi et al. [19] using Perkin Elmer LS 55 Fluorescence Spectrophotometer with the excitation wavelength of 332 nm. Coumarin powder (0.15 g) was dissolved in 1 L distilled water and sonicated at 40 kHz for 2 h to prepare 1 × 10−3 M coumarin solution. A total of five coumarin solutions were prepared by adding kraft lignin, soda lignin, KL/TiO2-1.0, SL/TiO2-1.0, and anatase TiO2, respectively. All the coumarin solutions were shaken at 500 rpm for 15 min before irradiated under sunlight. The sample was withdrawn from the coumarin solution and filtered with a 0.45 µm syringe filter every 15 min interval. The sample (0.5 mL) was diluted to 10 mL with distilled water. The diluted sample was used to determine the fluorescence intensity which indirectly corresponds to the amount of hydroxyl radicals produced. The procedures were repeated with KL/TiO2-0.5, KL/TiO2-1.0, KL/TiO2-1.5, and KL/TiO2-2.0.

Results and discussion

FTIR analysis

Figure 2 shows the FTIR spectra for kraft and soda lignins. The corresponding assignments and bands for both lignins are presented in Table 1. The assignments of the bands are reported according to previous literature finding [10]. It was revealed that kraft and soda lignins had similar functional groups. This finding is in agreement with the results reported by Ibrahim et al. [10]. A wide absorption band which appeared around 3400 cm−1 is assigned to aromatic and aliphatic OH groups. The absorption bands in the region between 3000 and 2840 cm−1 are attributed to C-H stretching in methyl, methylene and methoxyl groups. The absorption band between 1715 and 1705 cm−1 presented in the spectra of both lignins can be related to the unconjugated carbonyl stretching. Both kraft and soda lignins showed absorption bands around 1600 cm−1, 1515 cm−1, and 1425 cm−1 which are attributed to typical aromatic ring vibrations of the phenylpropane (C9) skeleton. The absorption band around 1460 cm−1 attributes to C–H deformation in methyl, methylene and methoxyl groups. The absorption band around 1270 cm−1 and 1117 cm−1 in the spectra can be attributed to C–O stretching vibration of a secondary alcohol and aromatic C–H in plane deformations of syringyl, respectively. The absorption band presented around 1220 cm−1 is assigned to C–O stretching in syringyl (S) and guaiacyl (G) which also indicates the presence of phenolic hydroxyl group and ether in syringyl and guaiacyl. The absorption band around 1030 cm−1 corresponds to the aromatic C–H in-plane deformation of guaiacyl. The aromatic C–H out of plane bending appears at 796 cm−1 and 814 cm−1 in the spectra for kraft lignin and soda lignin respectively.
Fig. 2

FTIR spectra of kraft lignin and soda lignin with wavenumber of 4000 cm−1 to 400 cm−1

Table 1

FTIR absorption bands and assignments for kraft and soda lignins


(cm−1) [10]







O–H stretching (phenolic OH and aliphatic OH)`




C–H stretching (CH3 and CH2 groups)




C–H stretching (OCH3)




C=O stretching (unconjugated ketone, carbonyl and ester groups)



~ 1600

C–C stretching (aromatic skeleton)




C–C stretching (aromatic skeleton)




C–H deformation (asymmetric in –CH3 and –CH2)




C–C stretching (aromatic skeleton) with C-H in-plane deformation




C–O stretching vibration of secondary alcohol



~ 1220

C–O(H) + C–O (Ar) (phenolic OH and ether in syringyl and guaiacyl)




Ar–CH in plane deformation (syringyl)



~ 1030

C–O(H) + C–O(C) (first order aliphatic Oh and ether




C–H out of plane (aromatic ring)



The absence of absorption band at 1166 cm−1 in the spectra which is normally assigned to p-hydroxyl phenylpropane indicates that OPEFB lignin is more similar to wood lignin instead of plant lignin which is normally HGS lignin. The FTIR spectra of lignin/TiO2 composites are shown in Figs. 3 and 4. Both composites, KL/TiO2-1.0, and SL/TiO2-1.0 have far more absorption bands between 4000 and 700 cm−1 compared to anatase TiO2 due to different functional groups and complex cross-linked phenolic structure in lignin. Besides, both composites showed typical sharp peaks around 663 cm−1 and 521 cm−1. These peaks are attributed to Ti–O-Ti stretching bonds [2]. The composites exhibited the absorption bands corresponding to both lignin and TiO2 indicating that lignin has successfully formed composite with TiO2.
Fig. 3

FTIR spectra of soda lignin, SL/TiO2-1.0 and anatase TiO2 with wavenumber of 4000 cm−1 to 400 cm−1

Fig. 4

FTIR spectra of kraft lignin, KL/TiO2-1.0 and anatase TiO2 with wavenumber of 4000 cm−1 to 400 cm−1

The surface of TiO2 and lignin molecules have abundant hydroxyl groups. Through condensation reaction, these hydroxyl groups can react with each other and form linkages as shown in Scheme 1. The bond formation is possible since the synthesis is carried in one pot route. Water is removed as the second product.
Scheme 1

The condensation reaction betwen hydroxyl groups of lignin and surface hydroxyl groups of TiO2

UV spectroscopy

The non-etherified phenolic group is the most important functional group in lignin. It is because the phenylpropane units are most likely to be attacked in the chemical reactions of lignin. In this study, the phenolic groups presented in both kraft and soda lignins was determined by UV spectroscopy and 13C NMR [10, 12]. Figure 5 shows the UV spectra of kraft lignin and soda lignin in neutral solution and alkaline solution which was a dioxane-water solution (9:1, v/v) and pH 12 NaOH solution respectively. The absorption around 280 nm can be attributed to non-conjugated phenolic units [19]. Both lignins showed first maximum absorption around 220 nm and second maximum absorption around 280 nm in dioxane-water solution. However, in pH 12 NaOH solution, the two lignins showed two maximum absorption around 220 and 290 nm. The maximum absorption of kraft lignin and soda lignin were shifted to 291 nm and 292 nm respectively in pH 12 NaOH solution as shown in Table 2.
Fig. 5

UV spectra of kraft lignin and soda lignin. 1—kraft lignin in pH 12 NaOH solution; 2—soda lignin in pH 12 NaOH solution; 3—kraft lignin in dioxane-water (9:1, v/v) solution; 4—soda lignin in dioxane-water (9:1, v/v) solution

Table 2

λmax around 280 nm for soda lignin and kraft lignin


λmax in dioxane-water solution (nm)

λmax in pH 12 NaOH solution (nm)







This is mainly due to the dissociation of phenolic group in alkaline solution increases the conjugation of the oxygen atom with the benzene ring and thus shifts the maximum absorption to a higher wavelength. The absorbance of kraft lignin was higher than that of soda lignin in both dioxane-water solution and pH 12 NaOH solution. This can be explained by the fact that kraft lignin contains higher phenolic hydroxyl content than soda lignin that increases the electron density in benzene ring and absorbance around 280 nm.

13C NMR spectroscopy

The results of UV analysis was supported by 13C NMR analysis. The estimation of lignin moieties was carried out by referring to Capanema et al. [20]. The 13C NMR spectra of acetylated kraft and soda lignins are shown in Figs. 6 and 7 respectively. The integral of the 155–102 ppm region was set as a reference and assumed that it includes six aromatic carbons and 0.12 vinylic carbons. The integral values were divided by 6.12 which is equivalent to one aromatic ring (Ar). It was observed that kraft lignin contained higher amount of secondary aliphatic –OH (0.35 Ar−1) than that of soda lignin (0.26 Ar−1) which was determined from the integration from 170 to 169 ppm region respectively. It was revealed that the amount of primary aliphatic –OH for kraft lignin (0.30 Ar−1) was higher than soda lignin (0.28 Ar−1) according to the integration from 173 to 170 ppm. On the other hand, kraft lignin consisted of a larger quantity of phenolic –OH (0.67 Ar−1) than soda lignin (0.46 Ar−1) based on the integration from 169 to 167 ppm. This can be contributed to the more intense cleavage of alkyl–aryl ether linkages during the kraft pulping process which lead to the formation of more phenolic end groups and thus increased the phenolic hydroxyl content in kraft lignin [16]. The higher phenolic –OH content enabled more hydroxyl radicals can be neutralized by the hydrogen atom abstraction from phenolic hydroxyl group.
Fig. 6

13C NMR spectrum of kraft lignin

Fig. 7

13C NMR spectrum of soda lignin

Both soda and kraft lignins showed signals at 104 ppm, 138.5 ppm and 152 ppm which can be attributed to C-2 or C6, C-4, and C-3 or C5 in S unit. Besides, both lignins also gave signals at 112 ppm and 119 ppm which can be assigned to C-2 and C-6 in G unit. The higher S unit signals in both lignins are owning to OPEFB lignin contained more S unit compared to G unit. The signals at 123.5 ppm and 131 ppm can be referred to pyridine which was used for acetylation of lignin [21].

XRD analysis

The crystal structure of KL/TiO2-1.0 and SL/TiO2-1.0 were investigated through XRD analysis. The XRD diffractograms in Fig. 8 reveal that both composites had similar XRD patterns to that of pure anatase TiO2 [22]. The diffraction peaks at 2θ = 25.4°, 37.9°, 48.1°, 53.9°, 55.1°, 62.7°, 68.8°, 70.4°, 75.1° and 82.7° can be indexed to (101), (004), (200), (105), (211), (204), (115), (220), (215) and (224) crystal planes of anatase TiO2, respectively. This indicates that the initial crystal cell structure of TiO2 is maintained and no other crystalline by-products are formed even after the formation of lignin/TiO2 composite. Since lignin is amorphous in nature and lack of ordered structure [10, 12], the XRD diffractograms of both composites did not show any diffraction peak that can be referred to lignin.
Fig. 8

XRD diffractograms of a SL/TiO2-1.0 and b KL/TiO2-1.0 composites

SEM and EDX analysis

The SEM analysis was carried out to study the surface morphologies of kraft lignin, KL/TiO2-1.0, SL/TiO2-1.0, and anatase TiO2. The micromorphology of TiO2 was presented as many small spherical particles tended to aggregate to form a large sphere as shown in Fig. 9. Figure 10 shows that kraft lignin possessed typical rough surface morphology of lignin [11]. Figures 11 and 12 depict the surface of KL/TiO2-1.0, and SL/TiO2-1.0 were rougher than and significantly different from the surface morphology of pure lignin and crystal morphology of naked TiO2. Based on Figs. 11 and 12, it was found that TiO2 particles were well dispersed in the lignin matrix indicating TiO2 is incorporated into lignin successfully. Besides, the tendency of TiO2 particles to aggregate was reduced in both composites compared to that in pure anatase TiO2. This is mainly because of the sonication used in the formation of composite prevents the aggregation of TiO2 particles.
Fig. 9

SEM image of anatase TiO2 at 10,000×  magnification

Fig. 10

SEM image of kraft lignin at 10,000× magnification

Fig. 11

SEM image of KL/TiO2-1.0 at 10,000×  magnification

Fig. 12

SEM image of SL/TiO2-1.0 at 10,000×  magnification

The element composition and distribution in the composites were investigated by EDX analysis. The EDX spectrum for KL/TiO2-1.0 and SL/TiO2-1.0 are shown in Figs. 13 and 14 respectively. Both composites were composed of the expected elements such as carbon, oxygen, and titanium. The carbon and oxygen can be assigned to lignin while titanium and oxygen can be ascribed to TiO2. It further indicates that TiO2 has been incorporated into lignin. The presence of sulfur in KL/TiO2-1.0 is owning to the hydrosulfide anions which are derived from the kraft pulping process [10].
Fig. 13

EDX analysis of KL/ TiO2-1.0 composite

Fig. 14

EDX analysis of SL/TiO2-1.0 composite

Relative production of hydroxyl radicals

The relative production of hydroxyl radicals by kraft lignin, soda lignin, KL/TiO2-1.0, SL/TiO2 and anatase TiO2 were investigated through the photo-oxidation of coumarin to 7-hydroxycoumarin as a test reaction under the sunlight exposure. Coumarin reacts directly with hydroxyl radical to produce a fluorescing compound 7-hydroxycoumarin which can be detected by spectrofluorometer as depicted in Fig. 15. The highly fluorescent 7-hydroxycoumarin can be detected at 460 nm in the fluorescence spectrum [23].
Fig. 15

The photo-oxidation of coumarin to 7-hydroxycoumarin [24]

Comparison between lignin/TiO2 composite and pure anatase TiO2

Fluorescence spectra of the coumarin solution irradiated under sunlight in the presence of kraft lignin, soda lignin, KL/TiO2-1.0, SL/TiO2-1.0, and anatase TiO2 are shown in Fig. 16. As shown in Figs. 16a–e and 17, coumarin solution in the presence of TiO2 exhibited the highest emission peak intensity throughout the experiment indicating the highest concentration of hydroxyl radicals being produced followed by SL/TiO2-1.0 and KL/TiO2-1.0. This can be attributed to the role of lignin as radical scavenger or antioxidant. Under the same sunlight irradiation, the peak intensity of coumarin solution in the presence of soda lignin and kraft lignin remained at the same level over irradiation time. This can be explained that both soda and kraft lignins possess no photocatalytic activity under sunlight irradiation. The result also indicated that the lignin does not completely quench the photocatalytic activity of TiO2 since hydroxyl radical generations still occur in the presence of both composites. The quenching process takes place when hydrogen atoms were abstracted from phenolic hydroxyl group by hydroxyl radical to form phenoxyl radical as proposed by Barclay et al. [24]. The presence of phenolic hydroxyl group in soda and kraft lignins has been proved by the UV and 13C NMR analyses. Moreover, according to the FTIR and 13C NMR spectra, both OPEFB lignins contained two main phenylpropanoid units which were guaiacyl (G) and syringyl (S). The methoxyl groups at the ortho position in G and S units aid in stabilizing phenoxyl radicals by resonance and hindering them from propagation. Besides, the interaction between the hydroxyl groups of phenolic compounds and the π-electrons of the benzene ring allows the phenolic compounds to produce radicals that can be stabilized by extended delocalization. Thus, the phenoxyl radical produced has much greater chemical stability than the initial radical.
Fig. 16

Fluorescence spectra of coumarin solution with kraft lignin, soda lignin, KL/TiO2-1.0, SL/TiO2-1.0 and TiO2 after being irradiated under sunlight for a 20 min, b 40 min, c 60 min, d 80 min, e 100 min

Fig. 17

Fluorescence intensity of coumarin solution with kraft lignin, soda lignin, KL/TiO2-1.0, SL/TiO2-1.0 and TiO2 at 460 nm against sunlight illumination time

Comparison between types of lignin

Figure 18 shows the fluorescence intensity of coumarin solution with KL/TiO2-1.0 and SL/TiO2-1.0 at 460 nm. The fluorescence intensity of both coumarin solutions increased with sunlight irradiation time. However, the fluorescence intensity of the solution with SL/TiO2-1.0 was higher than that of. KL/TiO2-1.0. The result indicates that kraft lignin has better hydroxyl radical quenching performance than soda lignin. This is highly possible due to higher phenolic hydroxyl group content of kraft lignin as mentioned in the UV and 13C NMR analysis. The higher phenolic hydroxyl content is caused by the severe process of kraft pulping which lead to extensive depolymerization of lignin such as cleavage of alkyl-aryl ether linkages. The hydroxide and hydrosulfide anions reacted with lignin causing the polymer to break down into smaller molecular weights fragments during the kraft pulping process and eventually the formation of new free phenolic hydroxyl group [10]. Hence, the low molecular weight fraction of kraft lignin possessed more non-etherified phenolic hydroxyl group than the high molecular weight fraction of soda lignin. It was suggested that the kraft lignin with higher content of non-etherified phenolic hydroxyl groups allows more hydroxyl radicals to be neutralized by the hydrogen atom abstraction from phenolic hydroxyl groups.
Fig. 18

Fluorescence intensity of coumarin solution with KL/TiO2-1.0 and SL/TiO2-1.0 at 460 nm against sunlight illumination time

Comparison between amounts of lignin

Since kraft lignin showed better performance in quenching hydroxyl radicals than soda lignin, it was used to prepare three other composites with different amount of lignin.

Figures 19a–e and 20 show that fluorescence intensity of coumarin solution in the presence of KL/TiO2-0.5 was the highest throughout the experiment compared to the solutions with other three composites. This may be due to the low amount of lignin used. The amount of lignin is not sufficient to form a neat coating layer around TiO2 particles and quench the hydroxyl radicals generated. According to Fig. 20, there was not much difference in the fluorescence intensities of the coumarin solutions with KL/TiO2-1.0, KL/TiO2-1.5 and KL/TiO2-2.0 under the same sunlight illumination. It was suggested that 1.0 of lignin is enough to cover TiO2 particles and quench hydroxyl radicals before they diffuse away from TiO2 which may cause damages to biomolecules or other sunscreen ingredients. Besides, the excess amount of lignin will also make the color of composite becomes darker which is unfavorable for the appearance of sunscreens. Although the fluorescent intensities of all the three coumarin solution increased slightly over the sunlight irradiation time, it does not mean that the lignin lost the capability to capture the free radicals. It could be attributed to the adsorption of coumarin molecules on vacant sites available on the surface of lignin. This will increase the competition between coumarin molecules and lignin in reacting with hydroxyl radicals. Thus, more coumarin adsorbed on the lignin surface over illumination time and produced more 7-hydroxycoumarin which lead to increasing of fluorescence intensity.
Fig. 19

Fluorescence spectra of coumarin solution with KL/TiO2-0.5, KL/TiO2-1.0, KL/TiO2-1.5 and KL/TiO2-2.0 after being irradiated under sunlight for a 20 min, b 40 min, c 60 min, d 80 min, e 100 min

Fig. 20

Fluorescence intensity of coumarin solution in the presence of KL/TiO2-0.5, KL/TiO2-1.0, KL/TiO2-1.5 and KL/TiO2-2.0 at 460 nm against sunlight illumination time


In this study, lignin/TiO2 composites were successfully synthesized by using kraft lignin and soda lignin. This was confirmed by the results of FTIR, XRD, SEM and EDX analysis. The kraft lignin/TiO2 composite exhibited lowest fluorescence intensity compared to pure anatase TiO2 and soda lignin/TiO2 composite which indirectly corresponds to the lowest hydroxyl radical production. This is mainly due to the higher phenolic hydroxyl content of kraft lignin which has been proven by UV and 13C NMR analysis. The higher phenolic hydroxyl content provides more hydrogen atoms to quench the activity of the hydroxyl radicals. The excess amount of lignin did not improve the radical scavenging activity but gave a darker color of the composite which is unfavorable for sunscreens and cosmetic products.


Authors’ contributions

All authors have equally contributed to the paper and have given approval to the final version of the paper. All authors read and approved the final manuscript.


This project was financially supported by Universiti Sains Malaysia (USM) through Short Term Research Grant (304/PKIMIA/6316174) and (304/PKIMIA/6313215), Research University Grant (RUI) (1001/PKIMIA/8011083) and Trans-disciplinary Research Grant Scheme (TRGS) (203/PKIMIA/6769001).

Competing interests

The authors declared that they have no competing interests.

Availability of data and materials

Not applicable.


Not applicable.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1.
    Sambandan DR, Ratner D (2011) Sunscreens: an overview and update. J Am Acad Dermatol 64(4):748–758CrossRefGoogle Scholar
  2. 2.
    Morsella M, d’Alessandro N, Lanterna AE, Scaiano JC (2016) Improving the sunscreen properties of TiO2 through an understanding of its catalytic properties. ACS Omega 1(3):464–469CrossRefGoogle Scholar
  3. 3.
    Ayed S, Belgacem RB, Zayani JO, Matoussi A (2016) Structural and optical properties of ZnO/TiO2 composites. Superlattices Microstruct 91:118–128CrossRefGoogle Scholar
  4. 4.
    Barnes RJ, Molina R, Xu J, Dobson PJ, Thompson IP (2013) Comparison of TiO2 and ZnO nanoparticles for photocatalytic degradation of methylene blue and the correlated inactivation of gram-positive and gram-negative bacteria. J Nanopart Res 15(2):1432CrossRefGoogle Scholar
  5. 5.
    Carlotti ME, Ugazio E, Sapino S, Fenoglio I, Greco G, Fubini B (2009) Role of particle coating in controlling skin damage photoinduced by titania nanoparticles. Free Radical Res 43(3):312–322CrossRefGoogle Scholar
  6. 6.
    Mao L, Meng C, Zeng C, Ji Y, Yang X, Gao S (2011) The effect of nitrate, bicarbonate and natural organic matter on the degradation of sunscreen agent p-aminobenzoic acid by simulated solar irradiation. Sci Total Environ 409(24):5376–5381CrossRefGoogle Scholar
  7. 7.
    Picatonotto T, Vione D, Eugenia Carlotti M (2002) Effect of some additives used in the cosmetic field on the photocatalytic activity of rutile. J Dispers Sci Technol 23(6):845–852CrossRefGoogle Scholar
  8. 8.
    Shen B, Scaiano JC, English AM (2006) Zeolite encapsulation decreases TiO2-photosensitized ROS generation in cultured human skin fibroblasts. Photochem Photobiol 82(1):5–12CrossRefGoogle Scholar
  9. 9.
    Chen X, Liu Y, Shi H, Wang X, Qi K, Zhou X, Xin JH (2010) Carboxymethyl chitosan coating to block photocatalytic activity of TiO2 nanoparticles. Text Res J 80(20):2214–2222CrossRefGoogle Scholar
  10. 10.
    Ibrahim MNM, Zakaria N, Sipaut CS, Sulaiman O, Hashim R (2011) Chemical and thermal properties of lignins from oil palm biomass as a substitute for phenol in a phenol formaldehyde resin production. Carbohyd Polym 86(1):112–119CrossRefGoogle Scholar
  11. 11.
    Ibrahim MNM, Ngah WW, Norliyana MS, Daud WW, Rafatullah M, Sulaiman O, Hashim R (2010) A novel agricultural waste adsorbent for the removal of lead (II) ions from aqueous solutions. J Hazard Mater 182(1–3):377–385CrossRefGoogle Scholar
  12. 12.
    Hussin MH, Zhang HH, Aziz NA, Samad NA, Faris AH, Ibrahim MNM, Iqbal A, Latip AFA, Haafiz MM (2017) Preparation of environmental friendly phenol-formaldehyde wood adhesive modified with kenaf lignin. Beni-Suef Univ J Basic Appl Sci 6(4):409–418CrossRefGoogle Scholar
  13. 13.
    Abdullah N, Sulaiman F (2013) The oil palm wastes in Malaysia. Biomass now-sustainable growth and use. InTech, pp 75–100Google Scholar
  14. 14.
    Ibrahim MNM, Salleh NM, Yusof NNM, Ghani AM (2010) Keistimewaan Lignin Daripada Kelapa Sawit. Penerbit Universiti Sains Malaysia, Pulau Pinang, pp 157–160Google Scholar
  15. 15.
    Salleh NM, Ismail S, Ibrahim MNM (2015) Radical scavenging activity of lignin extracted from oil palm empty fruit bunch and its effect on glutathione-S-transferase enzymes activity. Asian J Pharm Clin Res 8:81–87Google Scholar
  16. 16.
    Ugartondo V, Mitjans M, Vinardell MP (2008) Comparative antioxidant and cytotoxic effects of lignins from different sources. Biores Technol 99(14):6683–6687CrossRefGoogle Scholar
  17. 17.
    Morsella M, Giammatteo M, Arrizza L, Tonucci L, Bressan M, d’Alessandro N (2015) Lignin coating to quench photocatalytic activity of titanium dioxide nanoparticles for potential skin care applications. RSC Adv 5(71):57453–57461CrossRefGoogle Scholar
  18. 18.
    Ishibashi KI, Fujishima A, Watanabe T, Hashimoto K (2000) Detection of active oxidative species in TiO2 photocatalysis using the fluorescence technique. Electrochem Commun 2(3):207–210CrossRefGoogle Scholar
  19. 19.
    Zhao X, Dai L, Liu D (2009) Characterization and comparison of Acetosolv and Milox lignin isolated from crofton weed stem. J Appl Polym Sci 114(2):1295–1302CrossRefGoogle Scholar
  20. 20.
    Capanema EA, Balakshin MY, Kadla JF (2004) A comprehensive approach for quantitative lignin characterization by NMR spectroscopy. J Agric Food Chem 52(7):1850–1860CrossRefGoogle Scholar
  21. 21.
    Fulmer GR, Miller AJ, Sherden NH, Gottlieb HE, Nudelman A, Stoltz BM, Bercaw JE, Goldberg KI (2010) NMR chemical shifts of trace impurities: common laboratory solvents, organics, and gases in deuterated solvents relevant to the organometallic chemist. Organometallics 29(9):2176–2179CrossRefGoogle Scholar
  22. 22.
    Muniandy L, Adam F, Mohamed AR, Ng EP, Rahman NRA (2016) Carbon modified anatase TiO2 for the rapid photo degradation of methylene blue: a comparative study. Surf Interf 5:19–29CrossRefGoogle Scholar
  23. 23.
    Barclay LRC, Xi F, Norris JQ (1997) Antioxidant properties of phenolic lignin model compounds. J Wood Chem Technol 17(1–2):73–90CrossRefGoogle Scholar
  24. 24.
    Louit G, Foley S, Cabillic J, Coffigny H, Taran F, Valleix A, Renault JP, Pin S (2005) The reaction of coumarin with the OH radical revisited: hydroxylation product analysis determined by fluorescence and chromatography. Radiat Phys Chem 72(2–3):119–124CrossRefGoogle Scholar

Copyright information

© The Author(s) 2019

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (, which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver ( applies to the data made available in this article, unless otherwise stated.

Authors and Affiliations

  • Mohamad Nasir Mohamad Ibrahim
    • 1
    Email author
  • Anwar Iqbal
    • 1
  • Chai Chuan Shen
    • 1
  • Showkat Ahmad Bhawani
    • 2
  • Farook Adam
    • 1
  1. 1.School of Chemical SciencesUniversiti Sains MalaysiaGelugorMalaysia
  2. 2.Department of Chemistry, Faculty of Resource Science and TechnologyUniversiti Malaysia Sarawak (UNIMAS)Kota SamarahanMalaysia

Personalised recommendations