Abstract
A sol-gel method was adopted to obtain LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples. The effect of Ga doping on LiNi0.5Mn1.5O4 and its optimum content were investigated, and the electrochemical properties at room temperature and at a high temperature were discussed. The structural, morphological, and vibrational features of LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) compounds were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FT-IR). The XRD results demonstrate that all samples have a disordered spinel structure with a space group of Fd3m, and Ga doping restrains the formation of the LixNi1-xO secondary phase. FT-IR analysis reveals that Ga doping increases the degree of cation disorder. The SEM results reveal that all samples possess a fine spinel octahedron crystal. The electrochemical performance of the samples was investigated by galvanostatic charge/discharge tests, dQ/dV plots, and electrochemical impedance spectroscopy (EIS). The LiNi0.44Ga0.06Mn1.5O4 sample with the optimum content shows a superior rate performance and cycle stability after Ga doping, especially at a high discharge rate and high temperature. In addition, the LiNi0.44Ga0.06Mn1.5O4 sample retained 98.3% of its initial capacity of 115.7 mAhg−1 at the 3 C discharge rate after 100 cycles, whereas the pristine sample delivered a discharge capacity of 87.3 mAhg−1 at 3 C with a capacity retention of 80% at the 100th cycle. Compared with the pristine material, the LiNi0.44Ga0.06Mn1.5O4 sample showed a high capacity retention from 74 to 98.4% after 50 cycles at a 1 C discharge rate and 55 °C.
Avoid common mistakes on your manuscript.
Background
With the increasing application of lithium-ion batteries, their requirements are also increasing. Batteries with a long cycle life, high energy density, and low cost could meet the needs of consumers. Spinel LiNi0.5Mn1.5O4 (LNMO) has captured the attention of researchers in related fields [1] due to its high working potential [2], low cost [3], and high energy density [4]of 658 Wh kg−1. All of the advantages of LiNi0.5Mn1.5O4 are due to its three-dimensional lithium-ion diffusion path and high working voltage [5].
However, spinel LiNi0.5Mn1.5O4 materials also have several issues to be solved. Firstly, a LixNi1-xO secondary phase forms during the preparation process of spinel LiNi0.5Mn1.5O4 materials [6]. Secondly, the electrolyte is prone to decomposition at high working voltage (4.7 V) (vs Li/Li+) [1], which triggers a decrease in capacity and poor electrochemical performance.
Numerous attempts have been proposed to improve the electrochemical performance. Elemental doping and the application of coatings, such as Cr [7], Mg [8], Y [9], Ce [10], Al [11], Cu [12], and Ga [13] doping, as well as BiFeO3 [14] and Al2O3 [15] coatings, could enhance the cycle life or rate performance of LiNi0.5Mn1.5O4 samples to different degrees. For instance, Ce-doped LiNi0.5Mn1.5O4 can improve the cycling stability (94.51% capacity retention after 100 cycles) [10], Al2O3 coating layer reduces side reactions occurred. The first investigation of the substitution of Mn sites by Ga in the LiMn2O4 spinel structure was reported by Liu et al. They found that Ga doping can inhibit the Jahn-Teller cooperative distortion of the spinel structure [16]. In 2011, Shin et al. published a paper in which they determined that Ga-doped samples can form a more stable interface and stabilize the spinel structure due to the presence of Ga on the surface of the samples [13]. One year later, Shin [17] synthesized LiMn1.5Ni0.5 − xMxO4 (M = Cr, Fe, and Ga) by a hydroxide precursor method and found that the Ga-doped sample and the pristine sample exhibit a decline in the rate capability after annealing at 700 °C. Moreover, they also found that the poor rate capability was caused by the extensive segregation of Ga3+ after annealing. Wei Wu et al. published a paper in which they put forward that the characteristic of the solid-state method is that the particles were nonuniform in size and distribution [9]. Sol-gel method is in favor of the formation of well-crystallized octahedrons and a narrow particle distribution according to Wang [18]. However, little attention has been devoted to systematically investigating the rate capacity and electrical conductivity at different Ga-doping contents and the role of Ga at high temperatures. To understand how the Ga-doping concentrations influence the electrochemical properties in detail and to investigate suitable Ga-doped contents of LiNi0.5Mn1.5O4 materials, samples with various Ga-doping concentrations were prepared by a sol-gel method for the first time. The structure, morphology, and electrochemical performance of the samples were investigated systematically.
Results and discussion
Structural and morphological analysis
XRD patterns of the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) specimens are provided in Fig. 1, which clearly shows that the major diffraction peaks of the samples are consistent with the cards (JCPDS No. 80-2162) for the disordered spinel structure with space group Fd3m. Another paramount finding was that additional diffraction peaks appeared at 37.4°, 43.7°, and 63.8° (marked with an *) in the LiNi0.5Mn1.5O4 sample in addition to the major diffraction peaks, which should be assigned to the LixNi1-xO secondary phase. The finding agrees with results reported previously, in which the formation of the LixNi1-xO secondary phase should be ascribed to high-temperature sintering, and it was considered to decrease the amount of active material [19]. The existence of the LixNi1-xO secondary phase could inhibit the Li+ ion diffusion according to Wu [9]. However, no additional secondary phase was detected in the Ga-doped samples, suggesting that Ga doping could inhibit the formation of LixNi1-xO impure phases and provide a single phase.
According to a report that the intensity ratio of I311/I400 peaks could reflect the stability of the structure [20], whereby a positive correlation exists between the value of I311/I400 and the stability of the structure. The intensity ratios of the I311/I400 peaks for the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples are 0.8636, 0.9115, 0.9216, 0.9097, and 0.8966 (as listed Table 1), respectively. According to the value of I311/I400, we can infer that Ga doping can promote structural stability. In addition, Table 1 clearly shows the rise of the intensity ratio of I311/I400 peaks and then a decline as the Ga-doping content further increased; the ratio reached a maximum in the LiNi0.44Ga0.06Mn1.5O4 sample, suggesting that this sample has the most stable structure. The finding is consistent with the cyclic performance curve at a high rate and high temperature.
To further investigate the space group of the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples, FT-IR spectroscopy (shown in Fig. 2) was performed in the range of 400–700 cm−1. The key to determining the disordered Fd3m space group and the ordered P4332 space group is the disordering degree of the Ni2+ and Mn4+ in the spinel structure. The bands at 588 and 621 cm−1 correspond to the Ni-O bond and the Mn-O bond, respectively. A stronger peak intensity at 621 cm−1 rather than at 588 cm−1 is characteristic of the Fd3m structure [21]. Kunduraci et al. [22] published a paper in which they observed that the lower the value of I588/I621 was, the higher the disordering degree of the Mn4+ and Ni2+ ions in the spinel structure would be. The high degree of cation disorder leads to high conductivity. We calculated the intensity ratios of I588/I621 as 0.9524, 0.9187, 0.708, 0.8525, and 0.9263 (as listed in Table 2) for Ga-0, Ga-0.04, Ga-0.06, Ga-0.08, and Ga-0.1 samples, respectively. Interestingly, the value of I588/I621 first decreases and then increases with increasing Ga content, indicating the rise in the degree of cation disorder and then a decline following the increase of Ga-doping content. Ga-0.06 shows the lowest value of I588/I621, suggesting that it has the highest degree of cation disorder. The value of I588/I621 is less than 1, characteristic of the disordered Fd3m structure [21], which is consistent with the result of the above XRD analysis. Compared to the ordered P4332 structure, the disordered Fd3m structure showed better electrochemical properties than those of the ordered P4332 structure [23].
The particle morphologies of the samples are observed by SEM. The results, as shown in Fig. 3, imply that all samples have a spinel octahedron structure and possess a fine crystal. Some particles could be observed on the surface of the Ga-doped samples, but were absent in LiNi0.5Mn1.5O4. As shown in Fig. 4, EDS is a method of qualitative analysis which illustrates the presence of Ga in Ga-doped samples. Obviously, following the addition of x value, a significant increase in the concentration of Ga was recorded, indicating that Ga had been doped into the crystal lattice.
Electrochemical performance analysis
To examine the impacts of Ga doping on improving the rate capability of LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1), the capacities of the pristine and Ga-doped samples at 0.2, 0.5, 1, 2, and 3 C discharge rates were investigated. From Fig. 5a, rate capability was obviously promoted after Ga doping. It is notable that Ga-0.06 achieved an outstanding rate performance, 122.5, 120.9, 120.3, 117.5, 115.7 mAh/g at rates of 0.2, 0.5, 1, 2, and 3 C, respectively, compared to the 124.4, 114.2, 108, 99.8, 87.3 mAh/g of LiNi0.5Mn1.5O4 at the same rates. The discharge capacity of doped samples was lower than the pristine one at a 0.2 C discharge rate as a consequence of the electrochemically active Ni2+ that has been substituted with the Ga. For the discharge plateaus, the most obvious finding to emerge from Fig. 5a is that two discharge plateaus at ~ 4.0 V and ~ 4.7 V could be observed in accordance with Mn3+/Mn4+ and Ni2+/Ni4+ redox couples, which means that Ga doping does not modify the discharge mechanism. Figure 5b shows the rate capability curves of the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples. However, the discharge capacity of the pristine sample decreases rapidly with increasing C-rates. The excellent rate capability of Ga-0.06 can be ascribed to the reduced LixNi1-xO impurity phase, improved electronic conductivity, and the improved diffusion coefficient of Li+. The impurity phase would hinder the Li+ ions from taking off or embedding. The electrical conductivity was improved as a result of the increase of the Mn3+ content by Ga doping. This finding is in agreement with the dQ/dV plots. There are two sources of Mn3+; one source of Mn3+ is oxygen deficiency [24], resulting in Mn3+, while another is the substitution of Ga3+ for Ni2+ in which quite a few portions of Mn4+ should transform into Mn3+ to maintain charge neutrality. However, the disproportionation reaction of Mn3+ that occurs in the electrolyte is not conducive to structural stability. Simultaneously, the doped Ga formed a passivation layer and reduced the direct contact between the electrolyte and the electrode material. This inhibited the occurrence of disproportionation, leading to excellent rate properties. All of the above analysis is also in accordance with the SEM and EDS results.
The cycle performance of the cell is an essential parameter for electrochemical properties. From Fig. 6a, we calculated that the capacity retention at 1 C and 25 °C of the Ga-0, Ga-0.04, Ga-0.06, Ga-0.08, and Ga-0.1 samples are 90.8, 94.9, 98, 94.6, and 91.2%, respectively. The cycling performance clearly improved to different degrees after Ga doping, and Ga-0.06 samples showed the highest performance parameters. Figure 6b shows the cycle performance of the Ga-0, Ga-0.04, Ga-0.06, Ga-0.08, and Ga-0.1 samples at 1 C and 55 °C. The capacity retention of the Ga-0.06 samples was 98.4% of its initial capacity (121.5 mAh/g) at 1 C and 55 °C after 50 cycles, but the Ga-0 sample delivered a discharge capacity of 113 mAhg−1 and faded sharply, with a capacity retention of 74% at the 50th cycle. Consequently, the Ga-0.06 samples are better than that Ga-0 samples for improving the cycle stability at a high temperature, which should be ascribed to the reduced LixNi1-xO impurity phase and the stable structure provided by the passivation effect resulting from Ga doping. Figure 6c, d provides the discharge curves of the Ga-0 and Ga-0.06 composites at 3 C. The capacity retention of the Ga-0.06 sample reached 98.3% after 100 cycles at 3 C, which was higher than that of the pristine sample (80%). The discharge plateau at 3 C of the pristine sample was lower than that of Ga-0.06, which implied that the degree of polarization of the pristine sample was larger than that of Ga-0.06. It can be concluded that appropriate Ga-doping content is beneficial to the enhancement of the electrochemical properties, especially for the cycle stability at high temperatures and high discharge rates.
For more detailed analysis of the electrochemical behavior, the dQ/dV plots are represented in Fig. 7a–e. The peak at approximately 4.0 V is shown in Fig. 7f, which should be assigned to Mn3+/Mn4+ redox couple [25], indicating the characteristics of the disordered Fd3m spinel structure [9]. The two separating peaks are at approximately 4.7 V, corresponding to Ni2+/Ni3+ and Ni3+/ Ni4+ redox couples [26]. It is clear that the intensity of the peak at approximately 4.7 V tended to decrease with the content of Ga, which is caused by the substitution of electrically active Ni by Ga. The intensity of the peak at approximately 4.0 V increased, which is attributed to the concentration of Mn3+ ions increasing with the content of Ga. The smaller the potential difference between the redox peak and oxidation peak, the weaker the polarization. The degree of polarization is an indicator of the reversibility of Li+ ions in the electrode. From Fig. 7a–e, we determined that the smallest voltage difference between oxidation and reduction peaks of Ni3+/Ni4+ redox couples is 0.011 V for the Ga-0.06 sample, which is lower than that of the pristine sample (0.037 V), reflecting the best reversibility of Li+ ion insertion and de-insertion in the electrode. The analysis results of dQ/dV plots indicated that an appropriate Ga doping content has a positive effect on the reversibility of the samples. This finding is in good accordance with the results of rate capacity and DLi+ shown in Table 3.
To investigate the impact of Ga doping on the electrochemical reaction kinetics more deeply, Fig. 8a provides the EIS spectra of the obtained samples after 3 cycles at a rate of 0.1 C. The Nyquist plots and equivalent circuits (inset) of the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) composites are presented in Fig. 8a. CPE corresponds to the constant phase element of the double-layer, Re indicates the solution resistance, and Rct stands for charge transfer impedance, which is described by the diameter of a semicircle. W stands for the Warburg impedance, which reflects a speed of lithium-ion diffusion. We can determine that the Rct of the LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples are 168.4, 133, 86.73, 113.3, 143.66 Ω, respectively (as shown in Table 3). The Rct decreased along with the concentration of Ga doping, and the minimum Rct value occurred for the Ga doping content of 0.06, indicating an enhancement of electrochemical reaction kinetics. The lower Rct value of the Ga-0.06 samples reflects the lower electrochemical polarization, which is in line with the dQ/dV plots. The diffusion coefficient of Li+ (DLi+) is obtained from the following equation [27]:
In this equation, R represents the gas constant, (R = 8.314 JK mol−1), T stands for the temperature (298 K), A corresponds to the surface area of the electrode, n stands for the number of electrons per molecule attending the electronic transfer reaction, F stands for the Faraday constant (F = 96,500 C mol−1), CLi+ is the lithium ions content in samples, and σ is the Warburg factor. A relationship between σ and Z’ is listed in Eq. (2) and was determined from the slope of the line of the low frequency zone in Fig. 8b, (as listed in Table 3).
It is clear that there has been an increase and then decrease in the DLi+, which was the opposite of charge transfer impedance (Rct). The DLi+ values are 3.89 × 10−12, 6.99 × 10−12, 7.99 × 10−11, 4.88 × 10−11, 8.43 × 10−11 cm2 s−1 for Ga-0, Ga-0.04, Ga-0.06, Ga-0.08, Ga-0.1, respectively. The difference in the DLi+ between Ga-doped and pristine samples amount to 1 order of magnitude, indicating that Ga doping is a good way to enhance the ionic conductivity. The lowest charge transfer impedance and the highest diffusion coefficient of Li+ of Ga-0.06 gave it excellent cycling and rate properties compared to all the samples. The increase of DLi+ can be ascribed to the reduced LixNi1-xO impurity phase. These results indicate that an appropriate Ga-doping content can not only improve the conductivity of the LNMO but also enhance the diffusion coefficient of Li+.
Conclusions
A sol-gel method was utilized to synthesize LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples. All samples have a disordered Fd3m structure and possess a fine spinel octahedron crystal. Ga doping restrained the formation of the LixNi1-xO secondary phase and increased the degree of cation disorder. The outstanding performance should be attribute to the enhanced conductivity, reduced electrochemical polarization and the passivation layer by the Ga doping, which is more pronounced at high rates and high temperatures. Furthermore, the Ga-0.06 sample with an optimum content of Ga exhibits excellent electrochemical performance compared to the other samples; the capacity retention at 1 C and 55 °C of the Ga-0.06 sample was 98.4% of its initial capacity (121.5 mAh/g) after 50 cycles, but the Ga-0 sample delivered a discharge capacity of 113 mAhg−1 and faded sharply, with a capacity retention of 74% at the 50th cycle under the same test conditions. Our work provides a promising concept for improving the cycle stability of the cathode materials of Li-ion batteries at high temperatures.
Methods
Material syntheses
LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) was synthesized by a sol-gel method. The raw materials are listed as follows: CH3COOLi·2H2O (99.9%, Aladdin), Mn(CH3COO)2·4H2O (98%, Tianjin Damao), Ni(CH3COO)2·4H2O (99.9%, Aladdin), Ga(NO3)3·xH2O (99.9%, Aladdin), citric acid (99.5%, Aladdin), and ammonium hydroxide (25%, Tianjin Damao). The synthetic steps are shown below. Firstly, a certain stoichiometric ratio of CH3COOLi·2H2O, Mn(CH3COO)2·4H2O, Ni(CH3COO)2·4H2O, and Ga(NO3)3·xH2O was dissolved in a certain quality of distilled water under vigorous agitation at room temperature. Over 5% CH3COOLi·2H2O was added to make up for the loss of lithium salt. Secondly, a certain amount of citric acid was added to the above solution in a water bath with stirring at 80 °C. Thirdly, ammonium hydroxide was used to adjust the pH of the mixture to 7, and agitation was continued until a gel was obtained. Finally, the resulting gel was dried at 110 °C in a vacuum oven for 10 h. The dried precursors were pre-calcined at 650 °C for 5 h, grinding it into powder, and further calcined at 850 °C for 16 h in a muffle furnace. Samples with different Ga doping contents were obtained after cooling to room temperature, for the sake of convenience denoted as Ga-0, Ga-0.04, Ga-0.06, Ga-0.08, Ga-0.1, respectively.
Materials characterization
X-ray diffraction (XRD, Cu Kα, 36 kV, 20 mA) was employed on a Rigaku D/max-PC2200 system to assess the structure of the samples over a range from 10 to 80° at 4°/min. The Fourier transform infrared spectra (FT-IR) were measured by a Nicoletis 6700 instrument. Scanning electron microscopy (SEM, JEOL JMS-6700F) was used to record the morphology of the composites. Elemental composition was analyzed using energy dispersive spectrometry (EDS) along with SEM.
Electrochemical measurements
The electrochemical performance of the samples was evaluated by CR2032 coin cells. To prepare working electrodes, 90 wt% LiNi0.5-xGaxMn1.5O4 (x = 0, 0.04, 0.06, 0.08, 0.1) samples, 5 wt% super P conductive agent, and 5 wt% polypropylene fluoride (PVDF) binder were dissolved into N-methyl-2-pyrrolidone (NMP) to form a homogeneous slurry. The obtained slurry was cast onto an aluminum foil and dried under vacuum at 85 °C overnight. Then, the foil was pressed and cut into disks with a diameter of 14 mm. CR2032 coin cells with lithium foil as the counter and reference electrodes were used to assess the electrochemical performance of the materials, and it was assembled in an argon-filled glove box in which both the content of water and oxygen levels were kept below 0.1 ppm. Here, the electrolyte with high voltage resistance was 1 M LiPF6 in an ethylene carbonate (EC), propylene carbonate (PC), and ethylene methyl carbonate (EMC) mixture (EC:PC:EMC = 1:2:7, v:v:v). Galvanostatic charge-discharge measurements were carried out at 25 °C and 55 °C at a voltage of 3.5–4.95 V by the LAND battery testing system. Electrochemical impedance spectroscopy (EIS) tests were performed on a CHI600A electrochemical workstation. EIS spectroscopy in the frequency range of 0.01 Hz to 100 kHz with a perturbation of 5 mV was carried out.
Abbreviations
- A:
-
Surface area of the electrode
- CLi + :
-
Lithium ions content
- CPE:
-
Constant phase
- CV:
-
Cyclic voltammetry
- D Li + :
-
Diffusion coefficient of Li+
- EC/PC/EMC:
-
Ethylene carbonate/propylene carbonate/ethylene methyl carbonate
- EDS:
-
Energy dispersive spectrometry
- EIS:
-
Electrochemical impedence spectroscopy
- F:
-
Faraday constant
- FT-IR:
-
Fourier transform spectrophotometer
- Ga-0.04:
-
LiNi0.46Ga0.04Mn1.5O4
- Ga-0.06:
-
LiNi0.44Ga0.06Mn1.5O4
- Ga-0.08:
-
LiNi0.42Ga0.08Mn1.5O4
- Ga-0.1:
-
LiNi0.4Ga0.1Mn1.5O4
- I311 :
-
The intensity of (311) diffraction peak
- I400 :
-
The intensity of (400) diffraction peak
- I588 :
-
The intensity of 588 cm−1 band
- I621 :
-
The intensity of 621 cm−1 band
- LNMO/Ga-0:
-
LiNi0.5Mn1.5O4
- n :
-
The number of electrons per molecule
- NMP:
-
N-methyl-2-pyrrolidinone
- PVDF:
-
Polyvinylidene fluoride
- R:
-
Gas constant
- Rct :
-
Charge transfer resistance
- Re :
-
Solution resistance
- SEM:
-
Scanning electron microscope
- T:
-
Temperature
- W :
-
Warburg impedance
- XRD:
-
X-ray diffraction
- σ:
-
The Warburg factor
References
Kim Y-S, Kim T-H, Lee H, Song H-K (2011) Electronegativity-induced enhancement of thermal stability by succinonitrile as an additive for li ion batteries. Energy Environ Sci 4:4038–4045
Gao C, Liu H, Hao J, Chen Q, Bi S, Chen L (2018) Enhanced rate performance of nanosized RGO-LiNi0.5Mn1.5O4 composites as cathode material by a solid-state assembly method. Ionics 23:1–10
Tarascon JM (2010) Key challenges in future li-battery research. Philos Trans A Math Phys Eng Sci 368:3227–3241
Wang L, Hu Z, Zhao K, Luo Y, Wei Q, Tang C, Hu P, Ren W, Mai L (2016) Hollow spherical LiNi0.5Mn1.5O4 built from polyhedra with high-rate performance via carbon nanotube modification. Sci China Mater 59:95–103
Xu Y-H, Zhao S-X, Deng Y-F, Deng H, Nan C-W (2016) Improved electrochemical performance of 5 V spinel LiNi0.5Mn1.5O4 microspheres by F-doping and Li4SiO4 coating. J Mater 2:265–272
Muharrem Kunduraci JFA-S, Amatucci GG (2006) High-power nanostructured LiMn2-xNixO4 high-voltage lithium-ion battery electrode materials: electrochemical impact of electronic conductivity and morphology. Chem Mater 18:3585–3592
Li JLS, Xu S, Huang S, Zhu J (2017) Synthesis and electrochemical properties of LiNi0.5Mn1.5O4 cathode materials with Cr3+ and F− composite doping for Lithium-ion batteries. Nanoscale Res Lett 12:414–420
Liu M-H, Huang H-T, Lin C-M, Chen J-M, Liao S-C (2014) Mg gradient-doped LiNi0.5Mn1.5O4 as the cathode material for Li-ion batteries. Electrochim Acta 120:133–139
Wu W, Guo J, Qin X, Bi C, Wang J, Wang L, Liang G (2017) Enhanced electrochemical performances of LiNi0.5Mn1.5O4 spinel in half-cell and full-cell via yttrium doping. J Alloys Compd 721:721–730
Wu W, Qin X, Guo J, Wang J, Yang H, Wang L (2017) Influence of cerium doping on structure and electrochemical properties of LiNi0.5Mn1.5O4cathode materials. J Rare Earths 35:887–895
Luo Y, Lu T, Zhang Y, Yan L, Mao SS, Xie J (2017) Surface-segregated, high-voltage spinel lithium-ion battery cathode material LiNi0.5Mn1.5O4 cathodes by aluminium doping with improved high-rate cyclability. J Alloys Compd 703:289–297
Sun HY, Kong X, Wang BS, Luo TB, Liu GY (2018) Cu doped LiNi0.5Mn1.5−xCuxO4 (x = 0, 0.03, 0.05, 0.10, 0.15) with significant improved electrochemical performance prepared by a modified low temperature solution combustion synthesis method. Ceram Int 44:4603–4610
Shin DW, Manthiram A (2011) Surface-segregated, high-voltage spinel LiMn1.5Ni0.42Ga0.08O4 cathodes with superior high-temperature cyclability for lithium-ion batteries. Electrochem Commun 13:1213–1216
Mou J, Wu H, Deng Y, Zhou L, Zheng Q, Liao J, Lin D (2017) BiFeO3-coated spinel LiNi0.5Mn1.5O4 with improved electrochemical performance as cathode materials for lithium-ion batteries. J Solid State Electrochem 21:2849–2858
Song J, Han X, Gaskell KJ, Xu K, Lee SB, Hu L (2014) Enhanced electrochemical stability of high-voltage LiNi0.5Mn1.5O4 cathode by surface modification using atomic layer deposition. J Nanopart Res 16:2745–2752
Liu D-Q, He Z-Z, Liu X-Q (2007) Synthesis and characterization of LiGaxMn2−xO4 (0≤x≤0.05) by triethanolamine-assisted sol–gel method. J Alloys Compd 440:69–73
Shin DW, Bridges CA, Huq A, Paranthaman MP, Manthiram A (2012) Role of cation ordering and surface segregation in high-voltage spinel LiMn1.5Ni0.5–xMxO4 (M = Cr, Fe, and Ga) cathodes for lithium-ion batteries. Chem Mater 24:3720–3731
Wang S, Li P, Shao L, Wu K, Lin X, Shui M, Long N, Wang D, Shu J (2015) Preparation of spinel LiNi0.5Mn1.5O4 and Cr-doped LiNi0.5Mn1.5O4 cathode materials by tartaric acid assisted sol–gel method. Ceram Int 41:1347–1353
Alca’ntara MJ R, Lavela P, Tirado JL (2004) Changes in the local structure of LiMgyNi0.5-yMn1.5O4 electrode materials during lithium extraction. Chem Mater 16:1573–1579
Gao P, Wang L, Chen L, Jiang X, Pinto J, Yang G (2013) Microwave rapid preparation of LiNi0.5Mn1.5O4 and the improved high rate performance for lithium-ion batteries. Electrochim Acta 100:125–132
Kunduraci M, Amatucci GG (2006) Synthesis and characterization of nanostructured 4.7 V LixMn1.5Ni0.5O4 Spinels for high-power lithium-ion batteries. J Electrochem Soc 153:A1345–A1352
Kunduraci M, Amatucci GG (2008) The effect of particle size and morphology on the rate capability of 4.7V LiMn1.5+δNi0.5−δO4 spinel lithium-ion battery cathodes. Electrochim Acta 53:4193–4199
Wang L, Li H, Huang X, Baudrin E (2011) A comparative study of Fd-3m and P4332 “LiNi0.5Mn1.5O4”. Solid State Ionics 193:32–38
Chen Y, Sun Y, Huang X (2016) Origin of the Ni/Mn ordering in high-voltage spinel LiNi0.5Mn1.5O4: the role of oxygen vacancies and cation doping. Comput Mater Sci 115:109–116
Yang Z, Jiang Y, Kim J-H, Wu Y, Li G-L, Huang Y-H (2014) The LiZnxNi0.5-xMn1.5O4 spinel with improved high voltage stability for Li-ion batteries. Electrochim Acta 117:76–83
Mo M, Hui KS, Hong X, Guo J, Ye C, Li A, Hu N, Huang Z, Jiang J, Liang J, Chen H (2014) Improved cycling and rate performance of Sm-doped LiNi0.5Mn1.5O4 cathode materials for 5V lithium ion batteries. Appl Surf Sci 290:412–418
Liu GQ, Kuo HT, Liu RS, Shen CH, Shy DS, Xing XK, Chen JM (2010) Study of electrochemical properties of coating ZrO2 on LiCoO2. J Alloys Compd 496:512–516
Funding
This work is supported by Science and Technology Plan Foundation of Guangdong (2017B010119002), Science and Technology Plan Foundation of Guangzhou (201803030015), and Science and Technology Plan Foundation of Guangzhou (201704030031).
Availability of data and materials
The datasets supporting the conclusions of this article are included within the article and its additional files.
Author information
Authors and Affiliations
Contributions
The idea is from Dr. Li jun, the manuscript was mainly written by LL and SL, and the figures were mainly drawn by LL, YL, and SH, calibrated by SX and CP. FZ helped in the technical support for the characterizations. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
Not applicable.
Competing interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Lan, L., Li, S., Li, J. et al. Enhancement of the electrochemical performance of the spinel structure LiNi0.5-xGaxMn1.5O4 cathode material by Ga doping. Nanoscale Res Lett 13, 251 (2018). https://doi.org/10.1186/s11671-018-2666-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2666-3