Crystallization of Al-Co-Dy(Ho) amorphous alloys

  • V. Sidorov
  • S. Petrova
  • P. Svec Sr.
  • P. Svec
  • D. Janickovic
  • A. Palitsina
Regular Article
Part of the following topical collections:
  1. Phase Equilibria and Their Applications

Abstract

Amorphous ribbons of Al92−x Co8Dy(Ho) x (x = 6 and 10 at.%) composition were produced by a standard planar flow casting method. Their kinetics of crystallization was studied by X-rays, DSC and electric resistivity. The phase composition was determined at each stage of crystallization. In order to increase the stability of amorphous state, use of alloy with high REM content and holmium is preferred to dysprosium.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. Inoue, K. Ohtera, A.P. Tsai, T. Masumoto, Jpn. J. Appl. Phys. 27, L479 (1988)ADSCrossRefGoogle Scholar
  2. 2.
    T. Gloriant, A.L. Greer, Nanostruct. Mater. 10, 389 (1998)CrossRefGoogle Scholar
  3. 3.
    C. Triveño Rios, S. Suriñach, M.D. Bary, C. Bolfarini, W.J. Botta, C.S. Kiminami, J. Non-Cryst. Solids 354, 4874 (2008)ADSCrossRefGoogle Scholar
  4. 4.
    Y. Ouyang, J. Zhang, H. Chen, S. Liao, X. Zhong, J. Alloys Compd. 454, 359 (2008)CrossRefGoogle Scholar
  5. 5.
    W.J. Botta, C. Triveno Rios, R.D. Sa Lisboa, A.R. de Andrade, M.F. de Oliveira, C. Bolfarini, C.S. Kiminami, J. Alloys Compd. 483, 89 (2009)CrossRefGoogle Scholar
  6. 6.
    C.L. Li, J.W. Murray, K.T. Voisey, A.T. Clare, D.G. McCartney, Appl. Surf. Sci. 280, 431 (2013)ADSCrossRefGoogle Scholar
  7. 7.
    N.R. Tailleart, R. Huang, T. Aburada, D.J. Horton, J.R. Scully, Corr. Sci. 59, 238 (2012)CrossRefGoogle Scholar
  8. 8.
    S.H. Wang, X.F. Bian, H.R. Wang, Mater. Lett. 58, 539 (2004)CrossRefGoogle Scholar
  9. 9.
    Z. Huang, J. Li, Q. Rao, Y. Zhou, J. Non-Cryst. Sol. 354, 1671 (2008)ADSCrossRefGoogle Scholar
  10. 10.
    Z.H. Huang, J.F. Li, Q.L. Rao, Y.H. Zhou, Intermet. 16, 727 (2008)CrossRefGoogle Scholar
  11. 11.
    B. Sun, X. Bian, J. Guo, J. Zhang, T. Mao, Mater. Lett. 61, 111 (2007)CrossRefGoogle Scholar
  12. 12.
    V. Sidorov, P. Svec, D. Janickovic, V. Mikhailov, L. Son, J. Magn. Magn. Mater. 395, 324 (2015)ADSCrossRefGoogle Scholar
  13. 13.
    R.G. Zakharov, S.A. Petrova, A.E. Udilov, A.N. Petrov, A.I. Vilkov, V.L. Lisin, Patent No 72329, 2008, IB No 10 (in Russian)Google Scholar
  14. 14.
    DIFFRACPlus: Eva Bruker AXS GmbH, Ostliche. Rheinbruckenstraße 50, D-76187, Karlsruhe, Germany, 2008Google Scholar
  15. 15.
    DIFFRACPlus : TOPAS Bruker AXS GmbH, Ostliche. Rheinbruckenstraße 50, D-76187, Karlsruhe, Germany, 2008Google Scholar
  16. 16.
    Powder Diffraction File PDF4+ICDD Release, 2014Google Scholar
  17. 17.
    H.E. Kissinger, Anal. Chem. 29, 1702 (1957)CrossRefGoogle Scholar
  18. 18.
    A.K. Gangopadhyay, T.K. Croat, K.F. Kelton, Acta Mater. 48, 4035 (2000)CrossRefGoogle Scholar
  19. 19.
    B. Radiguet, D. Blavette, N. Wanderka, J. Banhart, K.L. Sahoo, Appl. Phys. Lett. 92, 103 (2008)CrossRefGoogle Scholar
  20. 20.
    G. Abrosimova, A. Aronin, A. Budchenko, Mater. Lett. 139, 194 (2015)CrossRefGoogle Scholar
  21. 21.
    V. Sidorov, P. Svec, P. SvecSr., D. Janickovic, V. Mikhailov, E. Sidorova, L. Son, J. Magn. Magn. Mater. 408, 35 (2016)ADSCrossRefGoogle Scholar

Copyright information

© EDP Sciences and Springer 2017

Authors and Affiliations

  • V. Sidorov
    • 1
    • 2
  • S. Petrova
    • 2
    • 3
  • P. Svec Sr.
    • 4
  • P. Svec
    • 4
  • D. Janickovic
    • 4
  • A. Palitsina
    • 1
  1. 1.Ural State Pedagogical UniversityEkaterinburgRussia
  2. 2.Ural Federal UniversityEkaterinburgRussia
  3. 3.Institute of Metallurgy UD RASEkaterinburgRussia
  4. 4.Institute of Physics SASBratislavaSlovakia

Personalised recommendations