Abstract
The static current density (J)-electric field (E) characteristics of SrCo x Ti x Fe(12−2x)O19 ferrite compositions (x = 0.0, 0.2, 0.3, 0.5, 0.6, 0.7, 1.0) have been investigated from 0.07 kV/m to 5.29 kV/m at room temperature. All compositions obey Ohms Law at low applied field and non-linearity conduction is observed at high field in compositions x = 0.0, 0.2, 0.3, 0.5, 0.6 and 1.0. The non-linear conduction mechanisms, Schottky, Poole-Frenkel, Ionic Hopping and Space Charge Limited Current mechanism, have been discussed. The current density is increased at higher substitution.
Similar content being viewed by others
References
L. Peng, L. Li, R. Wang, Y. Hu, X. Tu, J. Magn. Magn. Mater. 391, 136 (2015)
M.A. Gabal, Y.M. Al Angari, F.A. Al-Agel, J. Magn. Magn. Mater. 391, 108 (2015)
Y.J. Yang, X.S. Liu, D.L. Jin, J. Magn. Magn. Mater. 364, 11 (2014)
C. Singh, S. Bindra Narang, I.S. Hudiara, K. Sudheendran, K.C. James Raju, J. Magn. Magn. Mater. 320, 1657 (2008)
C. Singh, S. Bindra Narang, I.S. Hudiara, K. Sudheendran, K.C. James Raju, J. Electron. 27, 120 (2011)
C. Singh, S. Bindra Narang, I.S. Hudiara, K. Sudheendran, K.C. James Raju, K.N. Rozanov, Ceram. Silik. 54, 116 (2010)
C. Singh, S. Bindra Narang, I.S. Hudiara, Y. Bai, K. Marina, Mater. Lett. 63, 1991 (2009)
S. Yakovlev, J. Zekonyte, C.H. Solterbeck, M.E. Souni, Thin Solid Films 493, 24 (2005)
A. Zafar, Z. Imran, M.A. Rafiq, M.M. Hasan, Electronics, Communications and Photonics Conference (SIECPC), 2011 Saudi International (IEEE Explore, 2011), pp. 1–4
M. Belal Hassen, A.K.M. Akther Hossain, IEEE/OSA/I APR International Conference on Informatics, Electronics and Vision (IEEE Explore, 2012), pp. 903–907
I. Sadiq, I. Khan, F. Aen, M.U. Islam, M.U. Rana, Physica B 407, 1256 (2012)
S. Bindra Narang, I.S. Hudiara, J. Ceram. Process. Res. 7, 113 (2006)
F. Yan, S. Miao, I. Sterianou, I.M. Reaney, M.O. Lai, L. Lu, W.D. Song, Scr. Mater. 64, 458 (2011)
Y. Wang, J. Wang, J. Appl. Phys. 42, 162001 (2009)
Z.L. Wu, G.R. Govinda Raju, IEEE Trans. Dielectr. Electr. Insul. 2, 475 (1995)
T.Y. Kim, Exp. Polym. Lett. 1, 427 (2007)
R.S. Gulalkari, Y.G. Bakale, D.K. Burghate, V.S. Deogaonkar, Pramana J. Phys. 69, 485 (2007)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Bhikhan, V., Singh, C., Kaur, R. et al. Static conduction mechanisms in Co2+ and Ti4+ substituted M-type SrCox Tix Fe(12-2x) O19 ferrite. Eur. Phys. J. B 88, 324 (2015). https://doi.org/10.1140/epjb/e2015-60512-8
Received:
Revised:
Published:
DOI: https://doi.org/10.1140/epjb/e2015-60512-8