Abstract—
The impact of δ-ferrite in high-strength corrosion-resistant nitrogen-containing 04Kh20N6G11M2AFB steel on deformation resistance during hot deformation within the temperature range of 900–1200°С and strain rates of 0.1–10 s–1 was investigated. Analysis of diagrams shows that dynamic recrystallization of δ-ferrite steel starts at a lower threshold deformation rate compared with pure austenitic steel. The values of the deformation threshold necessary for the initiation and development of dynamic recrystallization depending on the phase composition of the nitrogen-containing steel were determined. The complex analysis of the structure proved that δ-ferrite contributes to the nucleation and development of dynamic recrystallization at 1200–1000°C (its initiation corresponds to the lowest deformation threshold) and formation of the recrystallized structure in a larger volume as compared with the purely austenitic structure.
Similar content being viewed by others
REFERENCES
Kalinin, G.Yu., Mushnikova, S.Yu., Nesterova, E.V., Fomina, O.V., and Khar’kov, A.A., The structure and properties of high-strength corrosion-resistant nitrogen steel 04Kh20N6G11M2AFB, Vopr. Materialoved., 2006, no. 1 (45), pp. 45–53.
Malyshevsky, V.A., Tsukanov, V.V., Kalinin, G.Yu., and Fomina, O.V., Modern low-magnetic steels for shipbuilding, Sudostroenie, 2009, no. 5, pp. 19–21.
Gorynin, I.V., Rybin, V.V., Malyshevsky, V.A., Kalinin, G.Yu., Mushnikova, S.Yu., Malakhov, N.V., and Yampol’skii, V.D., Creation of prospective fundamentally new corrosion-resistant cored steels doped with nitrogen, Vopr. Materialoved., 2005, no. 2 (42), pp. 40–54.
Gorynin, I.V., Malyshevsky, V.A., Kalinin, G.Yu., Mushnikova, S.Yu., Bannykh, O.A., Blinov, V.M., and Kostina, M.V., Corrosion-resistant high-strength nitro-genous steels, Vopr. Materialoved., 2009, no. 3 (59), pp. 7–16.
Kalinin, G.Yu., Malyshevsky, V.A., Teplenicheva, A.S., Fomina, O.V., Mushnikova, S.Yu., and Kharkov, A.A., High-strength austenitic welded steel for shipbuilding, Inorg. Mater.: Appl. Res., 2015, vol. 6, no. 6, pp. 559–565.
Kazakov, A.A., Oryshchenko, A.S., Fomina, O.V., Zhitenev, A.I., and Vikhareva, T.V., Controlling behavior of δ-ferrite in nitrogen-containing chromium–nickel–manganese steels, Inorg. Mater.: Appl. Res., 2017, vol. 8, no. 6, pp. 817–826.
Kane, R.H., The Hot Deformation of Austenite, Oxford: Pergamon, 1977.
Pickering, F.B., Physical Metallurgy and the Design of Steels, London: Appl. Sci., 1978.
Livshits, L.S., Metallovedenie dlya svarshchikov (Metal Science for Welders), Moscow: Mashinostroenie, 1979.
Demk, H., Deformation under Hot Working Conditions, London: Iron Steel Inst., 1968.
Sokol, I.Ya., Dvukhfaznye stali (Two-Phase Steels), Moscow: Metallurgiya, 1974.
Fomina, O.V., Vikhareva, T.V., Sagaradze, V.V., and Kataeva, N.V., Structure formation of the nitrogen-containing austenitic 04Kh20N6G11M2AFB steel at hot deformation: Part I. influence of deformation temperature and strain rate on the process of dynamic recrystallization, Inorg. Mater.: Appl. Res., 2018, vol. 9, no. 6, pp. 1060–1069.
ACKNOWLEDGMENTS
Experimental studies were performed by using the equipment of the Center for Collective Use Composition, Structure, and Properties of Structural and Functional Materials of the National Research Center Kurchatov Institute—CRISM Prometey under the financial support of the Ministry of Education within the framework of agreement 14.595.21.0004, unique identifier RFMEFI59517X0004.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated by E. Grishina
Rights and permissions
About this article
Cite this article
Fomina, O.V., Vikhareva, T.V. Structure Formation of the Nitrogen-Containing Austenitic 04Kh20N6G11M2AFB Steel at Hot Deformation: Part II. Influence of the Phase Composition and Conditions of Hot Deformation on the Process of Dynamic Recrystallization. Inorg. Mater. Appl. Res. 9, 1070–1075 (2018). https://doi.org/10.1134/S207511331806028X
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S207511331806028X