Abstract
Pulse electrodeposition technique was used to co-deposit Ni with NiCrAlY powder on Ni-based high temperature alloy substrate. Pure nickel anode was immersed in a standard Watt’s bath containing fine particles of NiCrAlY powder that were entrapped during electrodeposition to form a NiCrAlY electrodeposit on cathode specimen surface. Diffusion heat treatment was conducted in argon at ≈1150°C and the samples were oxidized at 1000°C in air. Scanning and transmission electron microscopy coupled with energy dispersive X-ray spectroscopy and X-ray diffraction were used to characterize the microstructure and identify the phases. Pulse electrodeposition resulted in dense and fine-grained deposit with the formation of Al2O3 oxide at the coating surface after exposure to high temperature.
Similar content being viewed by others
References
Padture, N., Gell, M., and Jordan, E., Science, 2002, vol. 296, p. 280.
Stott, F.H. and Wood, G.C., Mater. Sci. Eng., Ser. A., 1987, p. 267.
Kofstad, P., High Temperature Corrosion, N.Y.: Elsevier Appl. Sci., 1988.
Ul-Hamid, A., Oxidation Met., 2002, vol. 58, p. 23.
Saremi, M. and Bahraini, M., Trans. Inst. Met. Fin., 2003, vol. 81, p. 24.
US Patent 5 824 205, 1998.
US Patent 5 833 829, 1998.
US Patent 6 998 151, 2006.
Liu, Z., Gao, W., Dahm, K., and Wang, F., Acta Mater., 1998, vol. 46, p. 1691.
Liu, Z., Gao, W., and Li, M., Oxidation Met., 1998, vol. 51, p. 403.
Ul-Hamid, A., Dafalla, H., Quddus, A. et al., Appl. Surf. Sci., 2011, vol. 257, p. 9251.
Foster, J., Cameron, B.P., and Carew, J.A., Trans. Inst. Met. Finish, 1985, vol. 63, p. 115.
Zhou, Y., Peng, X., and Wang, F., Scripta Mater., 2004, vol. 50, p. 1429.
Puippe, J. and Leaman, F., Theory and Practice of Pulse Plating, Orlando: Am. Electroplaters and Surface Finishers Soc., 1986.
Gan, X.H., MS Thesis, Chin. Academy of Sci., 1992.
Susan, D.F., Marder, A.R., and Barmak, K., Thin Sol. Films, 1997, vol. 307, p. 133.
Susan D.F. and Marder, A.R., Oxidation Met., 2002, vol. 57, p. 159.
Zhang, Y., Peng, X., and Wang, F., Mater. Lett., 2004, vol. 58, p. 1134.
Partes, K., Giolli, C., Borgioli, F., et al., Surf. Coat. Tech., 2008, vol. 202, p. 2208.
Picas, J., Forna, A., Ajdelsztajnb, L., and Schoenung, J., Powder Tech., 2004, vol. 148, p. 20.
Ajdelsztajn, L., Picas, J., Kim, G., et al., Mater. Sci. Eng., Ser. A, 2002, vol. 338, p. 33.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Ul-Hamid, A., Dafalla, H., Al-Yousef, F. et al. Microstructural study of NiCrAlY electrodeposits. Prot Met Phys Chem Surf 50, 679–687 (2014). https://doi.org/10.1134/S2070205114050177
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2070205114050177