Abstract
The styrene-isoprene-butadiene terpolymers were prepared using n-butyl lithium as initiator, cyclohexane as solvent, tetrahydrofuran as structure modifier and tin tetrachloride as coupling agent by a method of the change addition time of structure modifier through the anionic polymerization technique. The polymerization rate of monomers, molecular weight, microstructure, tanδ and morphology of copolymers were investigated. The results showed that addition of THF had a great effect on the polymerization rate of three monomers, especially styrene, and could tune copolymer composition by using different addition time of THF; the copolymer composition could vary gradually along the chain from block copolymers (isoprene-butadiene) to gradient copolymers (isoprene-butadiene-styrene isoprene-butadiene). It resulted in broadening of glass transition region and damping range. The monomer ratio and molecular weight that affected the mechanical and dynamic mechanical properties of copolymers were also investigated. At the same time, the microstructure, morphology and mechanical properties were compared with random terpolymer and solution styrene-butadiene rubber/butadiene rubber/nature rubber blend.
Similar content being viewed by others
References
C. Zhang, K. Pal, J. U. Byeon, S. M. Han, and J. K. Kim, J. Appl. Polym. Sci. 119, 2737 (2011).
X. Lu, X. Li, and M. Tian, Polym. Adv. Technol. 25(1), 21 (2014).
R. Hu, V. L. Dimonie, M. S. Elasser, R. A. Pearson, A. Hiltner, S. G. Mylonakis, and L. H. Sperling, Polym. Phys. 35, 1501 (1997).
H. H. Chu, C. M. Lee, and W. G. Huang, J. Appl. Polym. Sci. 91, 1396 (2004).
N. Yamada, S. Shoji, H. Sasaki, A. Nagatani, K. Yamaguchi, S. Kohjiya, and A. S. Hashim, J. Appl. Polym. Sci. 71, 855 (1999).
D. C. Huang and R. M. C. Tsiang, J. Appl. Polym. Sci. 61, 333 (1996).
Q. Wang, Y. R. Wang, M. Y. Liao, and C. Q. Zhang, J. Appl. Polym. Sci. 103, 8 (2007).
T. Pakula and K. Matyjaszewski, Macromol. Theory Simul. 5, 987 (1996).
G Kraus, C. W. Childers, and J. T. Gruver, J. Appl. Polym. Sci. 11, 1581 (1967).
T. Hashimoto, Y. Tsukahara, K. Tachi, and H. Kawai, Macromolecules 16, 648 (1983).
W. Gronski, F. Annighofer, and R. Stadler, Makromol. Chem. 6, 141 (1984).
S. Jouenne, J. A. González-León, A.V. Ruzette, P. Lodefier, S. Tencé-Girault, and L. Leibler, Macromolecules 40, 2432 (2007).
R. Adhikar, R. Godehardt, W. Lebek, R. Weidisch, G. H. Michler, and K. J. Knoll, J. Macromol. Sci., Part B: Phys. 40, 833 (2001).
R. Adhikari, G. H. Michler, W. Lebek, S. Goerlitz, R. Weidisch, and K. Knoll, J. Appl. Polym. Sci. 85, 701 (2002).
R. N. Young, R. P. Quirk, and L. J. Fetters, Adv. Polym. Sci. 56, 1 (1984).
G.T. Jing and T. H. Li, J. Polym. Mater. 4, 41 (1987).
I. Tausendfreund, F. Bandermann, H.W. Siesler, and M. Kleimann, Polymer 43, 7085 (2002).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Liao, M., Wang, Q., Wang, N. et al. Preparation and dynamic mechanical properties of copolymers based on butadiene, isoprene, and styrene. Polym. Sci. Ser. B 56, 753–761 (2014). https://doi.org/10.1134/S1560090415010108
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1560090415010108