Abstract
The effect of melts from various groups of chemical compounds (NaCl, KCl, CaCl2, Li2CO3, H3BO3), their quantity, and charge calcination temperature on the yield of the target component (Zn2SiO4) was studied. The charge was calcined in the temperature range of 600–1100°С (step 100°С) with sampling, the phase composition of which was determined by X-ray phase analysis.
REFERENCES
Onufrieva, T.A., Buldakova, L.Y., Yanchenko, M.Y., Zaitseva, N.A., and Krasnenko, T.I., Russ. J. Phys. Chem. A, 2018, vol. 92, no. 7, pp. 1413–1416. https://doi.org/10.7868/S004445371807021X
Guretskaya, Z.I., Tekhnologiya materialov i izdelii elektronnoi tekhniki. Tekhnologiya lyuminoforov i lyuminestsentnykh ekranov (Technology of Materials and Electronic Products. Technology of Phosphors and Luminescent Screens), Zubkovskaya, V.N., Ed., Moscow: RKhTU im. D. I. Mendeleeva, 2005.
Petrovykh, K.A., Rempel, A.A., and Kortov, V.S., Inorg. Mater., 2015, vol. 51, no. 2, pp. 152–157. https://doi.org/10.7868/S0002337X15020153
Author information
Authors and Affiliations
Contributions
T.S. Volkova: selection of research objects, selection of conditions for the synthesis of samples; E.Yu. Tataurov: charge preparation for sample calcination, sample synthesis; V.V. Rudskikh: problem statement, choice of synthesis method and temperature range of charge calcination to study changes in the phase composition of samples; E.S. Shaburova: study of samples by X-ray phase analysis.
Corresponding author
Ethics declarations
The authors declare no conflict of interests requiring disclosure in this article.
Additional information
Translated from Zhurnal Prikladnoi Khimii, No. 8, pp. 1001–1005, August, 2022 https://doi.org/10.31857/S0044461822080060
Rights and permissions
About this article
Cite this article
Volkova, T.S., Tataurov, E.Y., Shaburova, E.S. et al. Effect of Melts on the Formation of a Zinc-Silicate Phosphor Matrix. Russ J Appl Chem 95, 1136–1140 (2022). https://doi.org/10.1134/S1070427222080079
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1070427222080079