Abstract
Structure of the crystalline component of a polyacrylonitrile fiber was studied in isothermal thermomechanical treatment by comparing X-ray diffraction data at various temperatures and mechanical loads of thermal stabilization.
Similar content being viewed by others
References
Rahaman, M.S.A., Ismail, A.F., and Mustafa, A., Polym. Degradation Stability, 2007, vol. 92, pp. 1421–1432.
Dalton, S., Heatley, F., and Budd, P., Polymer, 1999, vol. 40, pp. 5531–5543.
Wangxi, Z., Jie, L., and Gang, W., Carbon, 2003, vol. 41, pp. 2805–2812.
Mathur, R.B., Bahl, O.P., Mittal, J., and Nagpal, K.C., Carbon, 1991, vol. 29, pp. 1059–1061.
Ji, M., Wang, C., Bai, Y., et al., Polym. Bull., 2007, vol. 59, pp. 527–536.
He, D.X., Wang, C.G., Bai, Y.J., et al., J. Mater Sci., 2007, vol. 42, no. 17, pp. 7402–7407.
Gupta, A. and Harrison, I.R., Carbon, 1997, vol. 35, no. 6, pp. 809–818.
Lv, M.Y., Ge, H.Y., and Chen, J., J. Polym. Res., 2009, vol. 16, pp. 513–517.
Takaku, A. and Shimizu, J., J. Appl. Polym. Sci., 1984, vol. 29, pp. 1319–1326.
Yu, M., Wang, C., Bai, Y., et al., Polym. Bull., 2006, vol. 57, pp. 525–533.
Fitzer, E. and Mullier D.J., Carbon, 1975, vol. 13, pp. 63–69.
Yu, M., Wang, C., Bai, Y., et al., Polym. Bull. 2006, vol. 57, pp. 757–763.
Mathur, R.B., Bahl, O.P., and Mittal, J., Carbon, 1992, vol. 30, pp. 657–663.
Mittal, J., Bahl, O.P., Mathur, R.B., and Sandle, N.K., Carbon, 1994, vol. 32, pp. 1133–1136.
Bell, J.P. and Dumbleton, J.H., Tex. Res. J., 1971, vol. 41, pp. 196–203.
Jing, M., Wang, C.G., Bai, Y.J., et al., Polym. Bull., 2007, vol. 58, pp. 541–551.
Dongfeng, L., Haojing, W., and Xinkui, W., J. Mat. Sci., 2007, vol. 42, pp. 4642–4649.
Author information
Authors and Affiliations
Additional information
Original Russian Text © A.G. Fazlitdinova, V.A. Tyumentsev, E.P. Mayanov, S.A. Podkopaev, 2011, published in Zhurnal Prikladnoi Khimii, 2011, Vol. 84, No. 4, pp. 666–672.
Rights and permissions
About this article
Cite this article
Fazlitdinova, A.G., Tyumentsev, V.A., Mayanov, E.P. et al. Effect of thermomechanical treatment modes on nanostructure formation in thermally stabilized polyacrylonitrile fiber. Russ J Appl Chem 84, 701–707 (2011). https://doi.org/10.1134/S1070427211040252
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1070427211040252