Abstract
We present the results of experimental studies of the return of Ni–Fe–Ga–Co and Cu–Al–Ni single crystals to the initial form at the macro- and microlevels after their deformation by compression and subsequent restorative heating. It is found that the geometric dimensions of the sample are reproduced with high accuracy (up to 20 μm). The microrelief appearing on the initially polished surface during crystal compression (the arithmetic mean profile deviation Ra ≈ 0.25–0.75 μm, the average spacing of local protrusions of the profile S ≈ 0.027–0.11 mm) is not removed by subsequent heating and remains with further multiple repetition of deformation–restoration cycles.
Similar content being viewed by others
REFERENCES
Shape Memory Materials, Ed. by K. Otsuka and C. M. Wayman (Cambridge Univ. Press, Cambridge, 1998).
S. Barbarino, E. I. Saavedra Flores, R. M. Ajaj, I. Dayyani, and M. I. Friswell, Smart Mater. Struct. 23, 063001 (2014).
J. Mohd Jani, M. Leary, A. Subic, and M. A. Gibson, Mater. Des. 56, 1078 (2014).
D. Patil and G. Song, Smart Mater. Struct. 26, 093002 (2017).
H. Morito, A. Fujita, K. Oikawa, K. Ishida, K. Fukamichi, and R. Kainuma, Appl. Phys. Lett. 90, 062505 (2007).
V. I. Nikolaev, P. N. Yakushev, G. A. Malygin, A. I. Averkin, A. V. Chikiryaka, and S. A. Pulnev, Tech. Phys. Lett. 40, 123 (2014).
V. I. Nikolaev, P. N. Yakushev, G. A. Malygin, and S. A. Pul’nev, Tech. Phys. Lett. 36, 914 (2010).
V. I. Nikolaev, P. N. Yakushev, G. A. Malygin, A. I. Averkin, S. A. Pulnev, G. P. Zograf, S. B. Kustov, and Yu. I. Chumlyakov, Tech. Phys. Lett. 42, 399 (2016).
Ya. M. Golovchiner, in Problems of Metallurgy and Metal Physics, Collection of Articles (Metallurgizdat, Moscow, 1962), No. 7, p. 281 [in Russian].
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated by O. Zhukova
Rights and permissions
About this article
Cite this article
Nosov, Y.G., Soldatov, A.V., Krymov, V.M. et al. Deformation of the Shape Memory and Surface Microrelief of Ni–Fe–Ga–Co and Cu–Al–Ni Alloy Single Crystals. Tech. Phys. Lett. 45, 211–213 (2019). https://doi.org/10.1134/S1063785019030118
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063785019030118