Abstract
The influence of doping intermetallics based on rare-earth elements and ceramics with an extremely high low-temperature specific heat on the stability of combined NbTi superconductors against electromagnetic disturbances is studied experimentally and theoretically. The objects of investigation are standard NbTi conductors (0.85 mm in diameter) in a copper matrix that are soldered to copper wires containing high-specific-heat dopants. CeCu6, HoCu2, CeAl2, and PrB6 intermetallics (at 4.2 K, their specific heat is on average 150 times that of copper) or Cd2O2S ceramics (at 4.2 K, its specific heat is higher than that of copper by 600 times) are introduced into combined superconductor samples in the form of fine powder. The powder is placed into the copper wire either as one thick (0.6 mm in diameter) strand or as 19 thin (0.1 mm in diameter) strands. An undoped reference sample contains a solid conductor. Samples with a transport current placed in an external transverse magnetic field are subjected to longitudinal magnetic disturbances causing pulsed heating of the samples by eddy currents. The disturbance time is varied in a wide range: from 50 μs to 1.2 ms. To compare the critical energy densities of the disturbances in differently shaped samples, a mathematical technique is developed that is based on analytical solution of the equation of electromagnetic diffusion into the sample. It is found that the critical energy density of doped samples is much higher (by several times) than that of the reference sample. Upon direct cooling of the samples by liquid helium in a vertical channel (the most intense heat removal under steady-state conditions), the effect of stability improvement for the doped samples persists. Moreover, it is shown that the high-specific-heat dopants, raising the heat needed to warm the sample, restrict the heat flux into the liquid and thereby increase the energy removed by the coolant during unsteady heat transfer.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
P. A. Alekseev, V. E. Keilin, I. A. Kovalev, et al., Cryogenics 44, 763 (2004).
P. A. Alekseev, V. E. Keilin, I. A. Kovalev, et al., Cryogenics 46, 252 (2006).
I. I. Akimov, P. A. Alekseev, G. P. Vedernikov, et al., RF Patent No. 2 273 906.
Y. Iwasa, Case Studies in Superconducting Magnets Design and Operational Issues (Plenum, New York, 1994).
I. E. C. Williams, Proc. TM-11, Elsevier Applied Science (1989), pp. 1072–1077.
L. Trevisani, T. Kuriyama, F. Tegrini, et al., Cryogenics 42, 653 (2002).
B. J. Barbisch and K. Kwasnitza, J. Phys. (Paris) 45, 561 (1984).
T. Numazawa, T. Yanagitani, H. Nozava, et al., Cryoccolers (Kluwer, New York, 2003), Vol. 12, pp. 473–481.
V. E. Keilin, Dokl. Akad. Nauk SSSR 263, 90 (1982) [Sov. Phys. Dokl. 27, 253 (1982)].
D. E. Baynham, V. W. Edwards, and M. N. Wilson, IEEE Trans. Magn. 19, 676 (1987).
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © V.E. Keilin, P.A. Alekseev, I.A. Kovalev, S.L. Kruglov, V.N. Lazukov, M.I. Medvedev, D.I. Shutova, 2007, published in Zhurnal Tekhnicheskoĭ Fiziki, 2007, Vol. 77, No. 9, pp. 48–53.
Rights and permissions
About this article
Cite this article
Keilin, V.E., Alekseev, P.A., Kovalev, I.A. et al. Considerable rise in the stability of combined superconductors doped by intermetallic compounds with an extremely high low-temperature specific heat. Tech. Phys. 52, 1148–1154 (2007). https://doi.org/10.1134/S1063784207090071
Received:
Issue Date:
DOI: https://doi.org/10.1134/S1063784207090071