Abstract
We determined the spall strength of hafnium heated by a loading shock wave to thousands of degrees and subjected to transformations into denser polymorphic modifications. To achieve this goal, the following tasks were solved. The pressure profiles at the interface between the sample and soft buffer material in the spall experiments with flat, one-dimensional loading are measured. The equations of state of three polymorphic modifications of hafnium are constructed in the pressure range up to 100 GPa. The thermodynamic states of hafnium were calculated under the conditions of the performed experiments, which, together with the results of measurements of pressure profiles, made it possible to determine the spall strength of hafnium heated in a cycle of shock compression–unloading. The spall strength of hafnium was –4(1) GPa at a temperature of 1680(380) K. The spall experiments were mathematically simulated in the framework of a one-dimensional hydrocode.
Similar content being viewed by others
REFERENCES
A. M. Molodets, A. S. Savinykh, A. A. Golyshev, and G. V. Garkushin, Tech. Phys. Lett. 45, 27 (2019).
K. A. Gschneidner, Solid State Phys. 16, 275 (1964).
D. E. Grady and M. E. Kipp, in High-Pressure Shock Compression of Condensed Matter, Ed. by J. R. Asay and M. Shahinpoor (Springer, New York, 1992), p. 265.
A. A. Golyshev and A. M. Molodets, Combust. Explos., Shock Waves 49, 219 (2013).
Shock Hugoniot Data, Ed. by S. P. Marsh (Univ. California LASL, Berkeley, 1980).
S. A. Ostanin and V. Y. Trubitsin, Comput. Mater. Sci. 17, 174 (2000).
R. Hrubiak, PhD Thesis (Florida Int. Univ., Miami, 2012).
Cheng-Bin Zhang, Wei-Dong Li, Ping Zhang, and Bao-Tian Wang, Comput. Mater. Sci. 157, 121 (2019).
R. McQueen, S. Marsh, J. Taylor, J. Fritz, and W. Carter, in High Velocity Impact Phenomena, Ed. by R. Kinslow (Academic, New York, 1970), p. 293.
A. A. Bakanova, I. P. Dudoladov, and Yu. N. Sutulov, Sov. Phys. Solid State 11, 1515 (1969).
A. M. Molodets, J. Exp. Theor. Phys. 80, 467 (1995).
A. M. Molodets, High Press. Res. 30, 325 (2009).
L. V. Al’tshuler, S. B. Kormer, A. A. Bakanova, and R. F. Trunin, Sov. Phys. JETP 11, 573 (1960).
K. Pandey, J. Gyanchandani, M. Somayazulu, G. K. Dey, Surinder M. Sharma, and S. K. Sikka, J. Appl. Phys. 115, 233513 (2014).
V. V. Kim, A. A. Golyshev, D. V. Shakhrai, and A. M. Molodets, in Proceedings of the 11th International Conference Zababakhin’ Scientific Readings, Snezhinsk, 2012. http://www.vniitf.ru/images/zst/2012/s6/6-24.pdf.
A. M. Molodets, Phys. Solid State 57, 2045 (2015).
W. Carter and S. Marsh, Report No. LA-13006-MS (Los Alamos National Labor., NM, 1995).
A. M. Molodets, Phys. Solid State 56, 2233 (2014).
Funding
This work was supported by the State Atomic Energy Corporation Rosatom under the state contract no. H.4kh.241.9B.17.1013 dated February 20, 2017, and the state order no. 0089-2019-0001. The equipment of the unique scientific facility “Experimental Explosive Stand” was used.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they have no conflicts of interest.
Additional information
Translated by O. Zhukova
Rights and permissions
About this article
Cite this article
Molodets, A.M., Golyshev, A.A. Spall Strength of Shock-Heated Hafnium and the Equation of State of Its Polymorphic Modifications. Phys. Solid State 61, 1437–1443 (2019). https://doi.org/10.1134/S1063783419080201
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063783419080201