Abstract
It has been found that the phase with the fcc lattice of the NaCl structural type is formed due to the vacuum-arc deposition of the nanostructured multicomponent (TiZrHfVNbTa)N coating. Implantation of negative Au− ions with a dose of 1 × 1017 cm−2 leads to the formation of a disordered polycrystalline structure without a preferred orientation of the fcc phase and nanocrystallites from 5–7 to 1–3 nm is size, which are dispersed in a layer up to 35 nm in depth. Nanohardness increases to 33 GPa, and the Vickers hardness reaches 51 GPa. Gold nanoclusters are formed in the near-surface region, while the fcc lattice and the formation of local Au regions are observed in the coating itself. Fragments with the hcp lattice are formed at depths above 180 nm because of the low nitrogen concentration.
Similar content being viewed by others
References
Y. Zhang, T. T. Zuo, Z. Tang, M. C. Gao, K. A. Dahmen, P. K. Liaw, and Z. P. Lu, Prog. Mater. Sci. 61, 1 (2014).
A. D. Pogrebnjak, A. A. Bagdasaryan, I. V. Yakushchenko, and V. M. Beresnev, Russ. Chem. Rev. 83(11), 1027 (2014).
B. S. Murty, J. W. Yeh, and S. Ranganathan, High-Entropy Alloys (Butterworth-Heinemann, Oxford, 2014).
A. D. Pogrebnjak, I. V. Yakushchenko, G. Abadias, G. P. Chartier, O. V. Bondar, V. M. Beresnev, Y. Takeda, O. V. Sobol’, K. Oyoshi, A. A. Andreyev, and B. A. Mukushev, J. Superhard Mater. 35(6), 356 (2013).
A. D. Pogrebnjak, V. M. Beresnev, D. A. Kolesnikov, M. V. Kaverin, A. P. Shipilenko, K. Oyoshi, Y. Takeda, R. Krause-Rehberg, and A. G. Ponomarev, Tech. Phys. Lett. 39(3), 280 (2013).
A. D. Pogrebnjak, D. Eyidi, G. Abadias, O. V. Bondar, V. M. Beresnev, and O. V. Sobol, Int. J. Refract. Met. Hard Mater. 48, 222 (2015).
X. Feng, G. Tang, X. Ma, M. Sun, and L. Wang, Nucl. Instrum. Methods Phys. Res., Sect. B 301, 29 (2013).
A. D. Pogrebnjak, I. V. Yakushchenko, A. A. Bagdasaryan, O. V. Bondar, R. Krause-Rehberg, G. Abadias, P. Chartier, K. Oyoshi, Y. Takeda, V. M. Beresnev, and O. V. Sobol, Mater. Chem. Phys. 147(3), 1079 (2014).
F. F. Komarov, Ion Implantation into Metals (Metallurgiya, Moscow, 1990) [in Russian].
A. D. Pogrebnjak, S. N. Bratushka, V. M. Beresnev, and N. Levintant-Zayonts, Russ. Chem. Rev. 82(12), 1135 (2013).
N. Kishimoto, V. T. Gritsyna, Y. Takeda, C. G. Lee, and T. Saito, Nucl. Instrum. Methods Phys. Res., Sect. B 141, 299 (1988); N. Kishimoto, V. T. Gritsyna, Y. Takeda, C. G. Lee, and T. Saito, J. Surf. Sci. 4, 220 (1998).
V. Ivashchenko, S. Veprek, A. Pogrebnjak, and B. Postolnyi, Sci. Technol. Adv. Mater. 15(2), 025007 (2014).
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © A.D. Pogrebnjak, I.V. Yakushchenko, O.V. Bondar, O.V. Sobol’, V.M. Beresnev, K. Oyoshi, H. Amekura, Y. Takeda, 2015, published in Fizika Tverdogo Tela, 2015, Vol. 57, No. 8, pp. 1529–1534.
Rights and permissions
About this article
Cite this article
Pogrebnjak, A.D., Yakushchenko, I.V., Bondar, O.V. et al. Influence of implantation of Au− ions on the microstructure and mechanical properties of the nanostructured multielement (TiZrHf VNbTa)N coating. Phys. Solid State 57, 1559–1564 (2015). https://doi.org/10.1134/S1063783415080259
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063783415080259