Structure and Magnetic Properties of the FeCo–C Films Reduced by Carbohydrates


The structural and magnetic properties of FeCo–C films produced by electroless plating with different carbohydrates as reducing agents have been investigated. The surface morphology and coercivities of FeCo–C films are dependent on the iron content and type of reducing agent. The local magnetic anisotropy field value increases with a decrease in Fe content. For all systems, deposits with good soft magnetic properties were obtained, with coercivities less than 12 Oe and saturation magnetizations close to 240 emu/g for FeCo–C film with 30% cobalt. The best soft magnetic properties corresponded to the deposits with bcc structure and grain sizes less than 20 nm.

This is a preview of subscription content, access via your institution.

Fig. 1.
Fig. 2.
Fig. 3.


  1. M. Alper, H. Kockar, T. Sahin, and O. Karaagac, IEEE Trans. Magn. 46, 390 (2010).

    ADS  Article  Google Scholar 

  2. C. Rizal, J. Kolthammer, R. K. Pokharel, and B. C. Choi, J. Appl. Phys. 113, 113905 (2013).

    ADS  Article  Google Scholar 

  3. P. Wetzel, P. Bertoncini, D. Berling, A. Mehdaoui, B. Loegel, D. Bolmont, G. Gewinner, C. Ulhaq-Bouillet, and V. Pierron-Bohnes, Surf. Sci. 499, 210 (2002).

    ADS  Article  Google Scholar 

  4. S. Amsarajan and B. R. Jagirdar, J. Alloys Compd. 816, 152632 (2020).

    Article  Google Scholar 

  5. T. Yanai, K. Shiraishi, Y. Watanabe, T. Ohgai, M. Nakano, K. Suzuki, and H. Fukunaga, J. Appl. Phys. 117, 17A925 (2015).

  6. K. Sun, K. Wang, T. Yu, X. Liu, G. Wang, L. Jiang, Y. Bu, G. Xie, Int. J. Hydrogen Energy 44, 1328 (2019).

    Article  Google Scholar 

  7. S. Machado, S. L. Pinto, J. P. Grosso, H. P. A. Nouws, J. T. Albergaria, and C. Delerue-Matos, Sci. Total Environ. 445–446, 1 (2013).

    ADS  Article  Google Scholar 

  8. Magnetic Properties of Metals d-Elements, Alloys and Compounds, Data in Science and Technology, Ed. by H. P. J. Wijn (Springer, Berlin, Heidelberg, 1991)

    Google Scholar 

  9. R. S. Iskhakov and S. V. Komogortsev, Bull. Russ. Acad. Sci.: Phys. 71, 1620 (2007).

    Article  Google Scholar 

Download references


Measurements by electron microscopy were performed on equipment of the Krasnoyarsk Regional Center of Research Equipment of Federal Research Center “Krasnoyarsk Science Center SB RAS”.


This work was supported by the Russian Foundation for Basic Research, the Government of the Krasnoyarsk Territory, the Krasnoyarsk Regional Fund for the Support of Scientific and Technical Activities (project no. 18-42-240006 Nanomaterials with magnetic properties determined by the topological features of the nanostructure).

Author information

Authors and Affiliations


Corresponding authors

Correspondence to E. A. Denisova, L. A. Chekanova, S. V. Komogortsev, I. V. Nemtsev or R. S. Iskhakov.

Ethics declarations

The authors have no conflicts of interest to declare that are relevant to the content of this article.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Denisova, E.A., Chekanova, L.A., Komogortsev, S.V. et al. Structure and Magnetic Properties of the FeCo–C Films Reduced by Carbohydrates. Semiconductors 54, 1840–1842 (2020).

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:


  • FeCo–C alloy
  • electroless deposition
  • magnetic properties