Abstract
The results of studying the variation in the microhardness of SAV-1 and AMG-2 aluminum alloys after irradiation with neutrons with a fluence of 1016 to 1020 cm−2 are presented. Two ranges of variation in the microhardness dependent on the indenter load are revealed, which are retained in the entire fluence range. A strong dependence of the H μ value on P for loads less than 50 g (in the first range) is most likely caused by the physicochemical state of the surface layer.
Similar content being viewed by others
References
L. F. Mondolfo, Aluminum Alloys: Structure and Properties (Butterworths, London, 1976; Metallurgiya, Moscow, 1979).
V. G. Aden, E. F. Kartashev, V. A. Lukichee, et al., Vopr. At. Nauki Tekh., Fiz. Rad. Povrezhd. Rad. Materialoved., No. 5, 3 (2005).
V. V. Glazov, Microhardness of Metals and Semiconductors (Consultants Bureau, New York, 1971; Mir, Moscow, 1973).
V. A. Shabashov, A. V. Litvinov, A. G. Mukoseev, et al., Phys. Met. Metallogr. 98, 580 (2004).
S. N. Votinov, B. V. Sharov, S. V. Yarkovoi, et al., Acceleration of Structural Changes in Aluminium Alloy Acted by Reactor Irradiation (Melekess, Dmitrovgrad, 1970), p. 15 [in Russian].
U. S. Salikhbaev, S. A. Baitelesov, I. G. Khidirov, et al., At. Energy 104, 444 (2008).
Kh. B. Krast, M. E. Laivin’sh, A. V. Byalobzheskii, et al., At. Energ. 27(4), 286 (1969).
Author information
Authors and Affiliations
Additional information
Original Russian Text © S.A. Baitelesov, F.R. Kungurov, D.P. Tadzhibaev, E.T. Rakhimov, Sh.A. Alikulov, 2013, published in Poverkhnost’. Rentgenovskie, Sinkhrotronnye i Neitronnye Issledovaniya, 2013, No. 8, pp. 53–56.
Rights and permissions
About this article
Cite this article
Baitelesov, S.A., Kungurov, F.R., Tadzhibaev, D.P. et al. Effect of reactor irradiation on the microhardness of SAV-1 and AMG-2 structural materials. J. Surf. Investig. 7, 753–755 (2013). https://doi.org/10.1134/S1027451013040290
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1027451013040290