Abstract
A series of experiments were performed to investigate the effect of TiMn1.5 alloying on the structure, hydrogen storage properties and electrochemical properties of LaNi3.8Co1.1Mn0.1 hydrogen storage alloys at 303 K. For simple, A, B, and C are used to represent alloys (x = 0 wt %, x = 4 wt % and x = 8 wt %) respectively. The results of XRD and SEM show that LaNi3.8Co1.1Mn0.1−xTiMn1.5 hydrogen storage alloys have LaNi5 phase and (NiCo)3Ti phase. Based on the results of PCT curves, the hydrogen storage capacities of LaNi3.8Co1.1Mn0.1−xTiMn1.5 hydrogen storage alloys are about 1.28 wt % (A), 1.16 wt % (B) and 1.01 wt % (C) at 303 K. And the released pressure platform and the pressure hysteresis decrease with the increase of TiMn1.5 content. Meanwhile the activation curves show that LaNi3.8Co1.1Mn0.1−xTiMn1.5 hydrogen storage alloy electrodes can be activated in three times and the maximum discharge capacity is 343.74 mA h/g at 303 K. In addition, with the increase of TiMn1.5 content, the cyclic stability of the hydrogen storage alloy electrodes decreases obviously and the capacity retention decreases from 76.70% to 70.00% when TiMn1.5 content increases from A to C. It also can be seen that LaNi3.8Co1.1Mn0.1−xTiMn1.5 hydrogen storage alloy electrode C and B have the best self-discharge ability and the best high-rate discharge ability from self-discharge curves and high-rate discharge curves.
Similar content being viewed by others
References
Jain, I., Lal, C., and Jain, A., Int. J. Hydrogen. Energy., 2010, vol. 35, p. 5133.
Khaldi, C., Mathlouthi, H., and Lamloumi, J., J. Alloys. Compd., 2009, vol. 469, p. 464.
Wang, Y., Zhao, M., Li, S., and Wang, L., Electrochim. Acta, 2008, vol. 537, p. 831.
Pan, H.G., Ma, J.X., Wang, C.S., Chen, C.P., and Wang, Q.D., Electrochim. Acta, 1999, vol. 44, p. 3977.
Zhang, P., Wei, X., Liu, Y., Zhu, J., Zhang, Z., and Zhao, T., J. Alloys. Compd., 2005, vol. 399, p. 270.
Durairajan, A, Haran, B.S., White, R.E., and Popov, B.N., J. Power. Sources, 2000, vol. 87, p. 84.
Giza, K., Iwasieczko, W., and Pavlyuk, V.V., J. Alloys. Compod., 2007, vol. 429, p. 352.
Han, J.W., Feng, F., Geng, M.M., Buxbaum, R., and Northwood, D.O., J. Power. Sources, 1999, vol. 80, p. 39.
Zhang, X.B., Sun, D.Z., Yin, W.Y., Chai, Y.J., and Zhao, M.S., J. Solid. State. Chem., 2004, vol. 177, p. 2373.
Zhang, Y.H., Chen, M.Y., Wang, X.L., Wang, G.Q., Dong, X.P., and Qi, Y., Electrochim. Acta, 2004, vol. 49, p.1161.
Khaldi, C., Boussami, S., Rejeb, B.B., Mathlouthi, H., and Lamloumi, J., Mater. Sci. Eng. B, 2010, vol. 175, p. 22.
Lu, D.S., Li, W.S., Hu, S.J., Xiao, F.M., and Tang, R.H., Int. J. Hydrogen. Energy, 2006, vol. 31, p. 678.
Seo, C.Y., Choi, S.J., and Choi, J., Int. J. Hydrogen. Energy, 2003, vol. 28, p. 317.
Han, H.M., Zhao, M.S., and Qiao, Y.Q., J. Rare. Earth., 2002, vol. 26, p. 521.
Wang, Y.Z. and Zhao, M.S., J. Rare. Earth., 2010, vol. 28, p. 774.
Miao, H., Pan, H.G., Zhang, S.C., Chen, N., Li, R., and Gao, M.X., Int. J. Hydrogen. Energy, 2007, vol. 32, p. 3387.
Liu, X.D., Huang, L.H., Tian, X., Feng, H.W., and Chi, B., Int. J. Hydrogen. Energy., 2007, vol. 32, p. 4939.
Chu, H.L., Zhang, Y., Sun, L.X., Qiu, S.J., Xu, F., and Yuan, H.T., Int. J. Hydrogen. Energy, 2007, vol. 32, p.1898.
Ozu, Y., Kuji, T., and Uchida, H.H., J. Alloys. Compd., 2002, vol. 330, p. 632.
Gao, X.P., Sun, Y.M., Toyoda, E., Higuchi, E., Nakagima, T., and Suda, S., Electrochim. Acta, 2000, vol. 45, p. 3099.
Author information
Authors and Affiliations
Corresponding author
Additional information
Published in Russian in Elektrokhimiya, 2014, Vol. 50, No. 10, pp. 1060–1065.
The article is published in the original.
Rights and permissions
About this article
Cite this article
Lv, P., Wang, Zm., Shi, Nl. et al. Effect of TiMn1.5 alloying on the structure, hydrogen storage properties and electrochemical properties of LaNi3.8Co1.1Mn0.1 hydrogen storage alloys. Russ J Electrochem 50, 953–958 (2014). https://doi.org/10.1134/S102319351410005X
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S102319351410005X