Abstract
Damage to high-pressure deaerators’ metal and possible causes thereof are analyzed. The results of calculations and experimental studies of the stressed state of a deaerator vessel in the zones of maximum loading are presented. The results of studying the operating characteristics of carbon steels (Grades St3sp and St3kp) and welded seams made of these steels in different states are given as well. Examples are given of calculations of deaerator vessel longevity under conditions of low-cyclic fatigue at the stage of corrosion-fatigue crack development.
Similar content being viewed by others
References
On Provision of Operational Reliability of Elevated-Pressure Deaerators. Antifailure Guidelines No. Ts-02-82(T) (Glavtekhupravlenie Minenergo SSSR, Moscow, 1982).
J. H. Bulloch, “Some Field Observations Involving Deaerator Storage Vessel Cracking,” in Proceedings of Intern. Conf. “Prolongation of TPP’s Life Time” (VTI, Moscow, 1994).
Norms for Strength Calculations of the Equipment and Pipelines of Nuclear Power Plants PNAE G-7-002-86 (Energoatomizdat, Moscow, 1989).
P. Peterson, Coefficients of Stress concentration (Mir, Moscow, 1977).
B. N. Dranchenko, B. B. Portnov, A. V. Seleznev, and S. N. Komarova, “Systematization of experimental data on stress concentration in T-joints with internal pressure,” Teploenergetika No. 7, 27–29 (1988).
SO 153-34.17.439-2003. Guidelines for Prolongation of a Life Time of Vessels under Pressure (VTI, Moscow, 1995).
M. Isida, H. Noguchi, and T. Yoshida, “Tension and Bending of Finite Thickness Plates with Semi-Elliptical Surface Cracks,” Intern. J. Fract., 26(3), 157–188 (1984).
Author information
Authors and Affiliations
Additional information
Original Russian Text © E.A. Grin’, A.V. Zelenskii, 2009, published in Teploenergetika.
Rights and permissions
About this article
Cite this article
Grin’, E.A., Zelenskii, A.V. Studying the stressed state and operating characteristics of high-pressure deaerators’ metal and assessment of their longevity. Therm. Eng. 56, 103–112 (2009). https://doi.org/10.1134/S0040601509020037
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0040601509020037