Formation of the Structure of a V-1480 Alloy during Thermomechanical Treatment

Abstract

A comprehensive approach, which involves textural and metallographic studies, is used to study the structure of a V-1480 alloy of the Al–Cu–Li system (with zirconium, scandium, silver additives) after deformation under various temperature–rate conditions and subsequent annealing. Structural state diagrams are built.

This is a preview of subscription content, access via your institution.

Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.

REFERENCES

  1. E. N. Kablov, “Innovative developments of the FSUE VIAM SSC of RF for the realization of ‘Strategic Directions in Developing Materials and Their Processing Technologies up to 2030,’” Aviats. Mater. Tekhnol. 3 (1), 3–33 (2015).

    Google Scholar 

  2. V. V. Antipov, Yu. Yu. Klochkova, and V. A. Romanenko, “Modern aluminum and aluminum-lithium alloys,” Aviats. Mater. Tekhnol., No. S, 195–211 (2017).

  3. V. V. Antipov, “Outlook of aluminum, magnesium, and titanium alloys in the aerospace equipment,” Aviats. Mater. Tekhnol., No. S, 186–271 (2017).

  4. E. N. Kablov, E. A. Lukina, S. V. Sbitneva, L. B. Khokhlatova, and D. V. Zaitsev, “Formation of metastable phases during the decomposition of solid solution in the artificial aging of Al alloys,” Tekhnol. Legk. Splavov, No. 3, 7–17 (2016).

    Google Scholar 

  5. N. I. Kolobnev, L. B. Khokhlatova, and V. V. Antipov, “Advanced aluminum–lithium alloys for aircraft structures,” Tekhnol. Legk. Splavov, No. 2, 35–38 (2007).

    Google Scholar 

  6. A. Ya. Kochubei, P. N. Medvedev, G. G. Klochkov, and V. V. Avtaev, “Regularities of texture formation during planar precipitation of the Al–Cu–Li alloy system,” Tekhnol. Legk. Splavov, No. 1, 74–79 (2016).

    Google Scholar 

  7. Yu. M. Vainblat, “Critical parameters of hot deformation,” Material Science and Casting of Light Alloys (Metallurgiya, Moscow, 1977), pp. 287–300.

    Google Scholar 

  8. Yu. D. Koryagin and V. I. Krainov, “Structure and properties of aluminum 1421 alloy subjected to plastic deformation and heat treatment,” Vestn. Yuzh. Ural. Gos. Univ. Ser. Metallurgiya 17 (3), 64–72 (2017).

    Google Scholar 

  9. L. Cao, B. Liao, X. Wu, C. Li, G. Huang, and N. Cheng, “Hot deformation behavior and microstructure characterization of an Al–Cu–Li–Mg–Ag alloy,” Crystals 10 (5), 416 (2020).

    CAS  Article  Google Scholar 

  10. I. I. Novikov, Theory of Heat Treatment of Metals (Metallurgiya, Moscow, 1986).

    Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to E. A. Lukina.

Ethics declarations

The authors declare that they have no conflicts of interest.

Additional information

Translated by T. Gapontseva

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Lukina, E.A., Kochubei, A.Y., Filonova, E.V. et al. Formation of the Structure of a V-1480 Alloy during Thermomechanical Treatment. Russ. Metall. 2022, 363–367 (2022). https://doi.org/10.1134/S0036029522040164

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1134/S0036029522040164

Keywords:

  • aluminum–lithium alloy
  • rare-earth metals
  • heat treatment
  • recrystallization
  • polygonization
  • diagram of structural states
  • hot deformation