Abstract
A series of HM/MCM-48 samples with different SiO2/Al2O3 molar ratio were prepared by sol-gel method. The prepared catalysts were characterized by XRD, N2 adsorption-desorption, NH3-TPD, FT-IR, SEM, and TEM techniques, and their catalytic performance was investigated in alkylation of toluene with tert-butanol. The adsorption capacity and the acid sites amount of HM/MCM-48-4 sample prepared by growing MCM-48 on the surface of HM zeolite are much higher than that of their mechanical mixture (HM/MCM-48(4) sample) due to its biporous structure; it shows higher catalytic performance than other HM/MCM-48 samples. The influence of reaction conditions on the catalytic performance of HM/MCM-48-4 zeolite was discussed. Toluene conversion of 41.4% and p-tert-butyltoluene selectivity of 73.5% were obtained at the weight ratio of toluene to HM/MCM-48-4 of 5, reaction temperature of 453 K, reaction time of 5 h and the molar ratio of toluene to tert-butanol of 0.5.
Similar content being viewed by others
References
S. Kobayashi and K. Manabe, Pure Appl. Chem. 72, 1373 (2000).
C. P. Sebastian, S. Pai, N. Sharanappa, and C. V. V. Satyanarayana, J. Mol. Catal. A: Chem. 223, 305 (2004).
C. Perego and P. Ingallina, Catal. Today 76, 87 (2002).
M. Rueping and B. J. Nachtsheim, Beilstein J. Org. Chem. 6, 6 (2010).
D. Mravec, P. Zavadan, A. Kaszonyi, J. Joffre, and P. Moreau, Appl. Catal. A: Gen. 257, 49 (2004).
M. Selvaraj and T. G. Lee, Microporous Mesoporous Mater. 85, 59 (2005).
Z. W. Zhou, W. L. Wu, J. Luo, L. P. Yu, and J. Wang, Petrochem. Technol. 35, 79 (2006).
G. Kostrab, M. Lovic, A. Turan, P. Hudec, A. Kaszonyi, M. Bajus, J. Uhlar, P. Lehocky, and D. Mravec, Catal. Commun. 18, 176 (2012).
B. D. Prasher, G. A. Gabriel, and Y. H. Ma, Ind. Eng. Chem. Process Des. Dev. 17, 266 (1978).
R. C. Everson, E. T. Woodburn, and A. R. M. Kirk, J. Catal. 53, 186 (1978).
M. Selvaraj, S. H. Jeon, J. Han, P. K. Sinha, and T. G. Lee, Appl. Catal. A: Gen. 286, 44 (2005).
I. Fechete, B. Donnio, O. Ersen, T. Dintzer, A. Djeddi, and F. Garin, Appl. Surf. Sci. 257, 2791 (2011).
S. Namba, T. Yamagishi, and T. Yashima, Nippon Kagaku Kaishi, 595 (1989).
K. R. Kloetstra, H. W. Zandbergen, J. C. Jansen, and H. van Bekkum, Microporous Mesoporous Mater. 6, 287 (1996).
B. Xue, J. Xu, C. F. Xu, R. Z. Wu, Y. X. Li, and K. Zhang, Catal. Commun. 12, 95 (2010).
P. Prokesova, N. Zilkova, S. Mintova, T. Bein, and J. Cejka, Appl. Catal. A: Gen. 281, 85 (2005).
K. Schumacher, P. I. Ravikovitch, A. du Chesne, A. V. Neimark, and K. K. Unger, Langmuir 16, 4648 (2000).
P. Prokesova-Fojokova, S. Mintova, J. Cejka, N. Zilkova, and A. Zukal, Microporous Mesoporous Mater. 92, 154 (2006).
J. J. Zheng, G. S. Wang, M. Pan, D. L. Guo, Q. Q. Zhao, B. Li, and R. F. Li, Microporous Mesoporous Mater. 206, 114 (2015).
K. Zhang, E. H. Yuan, L. L. Xu, Q. S. Xue, C. Luo, B. Albela, and L. Bonneviot, Eur. J. Inorg. Chem., 4183 (2012).
W. Zhao, Q. Z. Li, L. N. Wang, J. L. Chu, J. K. Qu, S. H. Li, and T. Qi, Langmuir 26, 6982 (2010).
F. Liebau, Microporous Mesoporous Mater. 66, 363 (2003).
H. Shintaku, K. Nakajima, M. Kitano, N. Ichikuni, and M. Hara, ACS Catal. 4, 1198 (2014).
H. W. Lee, I. G. Lee, S. H. Park, J. K. Jeon, D. J. Suh, J. Jung, and Y. K. Park, J. Nanosci. Nanotechnol. 14, 2990 (2014).
Z. K. Xie, J. Q. Bao, Y. Q. Yang, Q. L. Chen, and C. F. Zhang, J. Catal. 205, 58 (2002).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Zhou, Z., Cheng, F., Qin, J. et al. Preparation of H-mordenite/MCM-48 composite and its catalytic performance in the alkylation of toluene with tert-butanol. Russ. J. Phys. Chem. 91, 1669–1675 (2017). https://doi.org/10.1134/S0036024417090345
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0036024417090345