123 Phases in CeLa₂Cu₂MgO₈ samples

Abstract

A tetragonal 123 phase with the composition close to CeLa₂ { Cu ²⁺₂ } [Mg²⁺]O₈ (the braces indicate the Cu(2) positions; the brackets indicate the Cu(1) positions) with the parameters a = b = 0.3909(3) nm, c = 1.6591(8) nm was prepared at 860°C under an oxygen atmosphere with an elevated oxygen pressure. When the lanthanum-for-barium substitution was incomplete, the resulting 123 phase had the composition close to CeLa_1.7Ba_0.3{ Cu ²⁺_1.7 } [Mg]O₈ with the unit cell parameters a = b = 0.3868(3) nm, c = 1.6578(8) nm that contains Cu³⁺ in the Cu(2) positions. The partial substitution of barium for lanthanum (the melting point of barium oxide is almost 500°C lower that of the lanthanum oxide) appreciably facilitated the synthesis: the 123 phase in this sample was more than 90%. The existence of Cu³⁺ in the Cu(2) positions enhanced the electrical conductivity of the sample.