Abstract
The swelling, microstructure, and composition of grain boundaries in neutron-irradiated V–Fe alloys has been studied. It has been established that the swelling of V–Fe alloys observed after irradiation at a temperature of 370°С to a damaging dose of 1.3 dpa continuously decreases with an increase in the iron concentration from 0.7 to 5 at %. It is shown that at the grain boundaries in the V–2Fe and V–5Fe alloys an increased iron content is observed.
Similar content being viewed by others
REFERENCES
T. Muroga, J. Chen, V. Chernov, R. Kurtz, and M. Le Flem, “Present status of vanadium alloys for fusion application,” J. Nucl. Mater. 455, 263−268 (2014).
M. Le Flem, J. Gentzbittel, and P. Wident, “Assessment of a european V–4Cr–4Ti alloys – CEA-J57,” J. Nucl. Mater. 442, 325–329 (2013).
H. Matsui, D. Gelles, and Y. Kohno, “Large swelling observed in a V–5 at. % Fe alloy after irradiation in FFTF,” Effect of Radiation on Materials: 15th International Symposium, ASTM STP 1125, Ed. by R.E. Stoller, A.S. Kumar, D.S. Gelles, (American Society for Testing and Materials, Philadelphia, 1992), pp. 928−941.
H. Matsui, H. Nakajima, and S. Yoshida, “Microstructural evolution in vanadium alloys by fast neutron irradiation,” J. Nucl. Mater. 205, 452−459 (1993).
H. Nakajima, S. Yoshida, Y. Kohno, and H. Matsui, “Effect of solute addition on swelling of vanadium after FFTF irradiation,” J. Nucl. Mater. 191–194, 952−955 (1992).
K. Fukumoto, A. Kimura, and Y. Matsui, “Swelling behavior of V–Fe binary and V–Fe–Ti ternary alloys,” J. Nucl. Mater. 258–263, 1431−1436 (1998).
N. Sekimura, T. Iwai, and F. Garner, “Influence of boron-generated helium on the swelling of neutron irradiated V, V–5Cr and V–5Fe,” J. Nucl. Mater. 233–237, 400−405 (1996).
K. Fukumoto, K. Fujita, H. Sakio, Y. Sekio, and M. Yamazaki, “Effect of temperature history on swelling behavior of V–Fe binary alloy irradiated in a fast reactor Joyo,” Nucl. Mater. Energy 24, 100760 (2020).
F. Garner, D. Gelles, H. Takahashi, S. Ohnuki, and H. Kinoshita, “High swelling rates observed in neutron-irradiated V–Cr and V–Si binary alloys,” J. Nucl. Mater. 191–194, 948−951 (1992).
H. Kamiyama, H. Rafii-Tabar, Y. Kawazoe, and H. Matsui, “An MD simulation of interaction between self-interstitial atoms and edge dislocation in bcc transition metals,” J. Nucl. Mater. 212–215, 231−235 (1994).
H. Kawanishi and S. Ishinj, “A TEM study of V and V–l at % 10B with fast neutron irradiations,” Reduced Activation Materials for Fusion Reactors, ASTM STP 1047, Ed. by R. L. Klueh, D. S. Gelles, M. Okada, and N. Packan (American Society for Testing and Materials, Philadelphia, 1990), pp. 179−189.
D. Braski, “Vanadium Alloys with Improved Resistance to Helium Embrittlement,” Effect of Radiation on Materials: 15th International Symposium, ASTM STP 1125 Ed. by R. E. Stoller, A. S. Kumar, and D. S. Gelles (American Society for Testing and Materials, Philadelphia, 1992), pp. 897−914.
S. I. Golubov, A. V. Barashev, and R. E. Stoller, “Radiation damage theory,” in Comprehensive Nuclear Materials, Ed. by R. J. M. Konings (Elsevier, Amsterdam, 2012), vol. 1, pp. 357−389.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they have no conflicts of interest.
Additional information
Translated by E. Chernokozhin
Rights and permissions
About this article
Cite this article
Porollo, S.I., Dvoryashin, A.M. & Konobeev, Y.V. Radiation Damage in Neutron-Irradiated V–Fe Alloys. Phys. Metals Metallogr. 123, 784–790 (2022). https://doi.org/10.1134/S0031918X22080075
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0031918X22080075