Abstract
The luminescence and recombination processes in crystals of lithium borates Li6Gd x Y1 − x (BO3)3:Eu have been investigated. The steady-state X-ray luminescence (XRL) spectra, the temperature dependences of the XRL intensity, and the thermally stimulated luminescence (TSL) spectra have been measured for the Li6Gd(BO3)3, Li6Eu(BO3)3, Li6Y0.5Gd0.5(BO3)3:Eu, and Li6Gd(BO3)3:Eu compounds in the temperature range of 90–500 K. It is established that the band at 312 nm, which is due to the 6 P J → 8 S 7/2 transitions in Gd3+ ions and the group of lines at 580–700 nm, which are due to the 5 D 0 → 7 F J (J = 0 … 4) transitions in Eu3+ ions dominate in the XRL spectra. The XRL intensity in these bands increases several times with a change in temperature from 100 to 400 K for undoped crystals. The likely mechanisms of the observed temperature dependence of the XRL intensity and their relationship with the features of electronic-excitation energy transfer in these crystals are discussed. The spectra of all crystals under study exhibit a dominant composite TSL peak with a maximum at 110–160 K and a series of weaker peaks, the composition and structure of which depend on the crystal type. The nature of the shallow traps, which are responsible for the TSL at temperatures below room, and their relationship with the defects of lithium cation sublattice are discussed.
Similar content being viewed by others
References
I. N. Ogorodnikov, V. A. Pustovarov, S. I. Omel’kov, A. V. Tolmachev, and R. P. Yavetskii, Opt. Spectrosc. 102(1), 60 (2007).
I. N. Ogorodnikov, V. A. Pustovarov, A. V. Tolmachev, and R. P. Yavetskii, Phys. Solid State 50, 1684 (2008).
J. B. Czirr, G. M. MacGillivray, R. R. MacGillivray, and P. J. Seddon, Nucl. Instrum. Methods Phys. Res., Sect. A 424, 15 (1999).
C. T. Garapon, B. Jacquier, J. P. Chaminade, and C. Fouassier, J. Lumin. 34, 211 (1985).
C. T. Garapon, B. Jacquier, Y. Salem, and R. Moncorge, J. Phys. Coll. C7 46, C7–141 (1985).
M. Buijs, J. I. Vree, and G. Blasse, Chem. Phys. Lett. 137, 381 (1987).
J. Sablayrolles, V. Jubera, J.-P. Chaminade, I. Manek-Hönninger, S. Murugan, T. Cardinal, R. Olazcuaga, A. Garcia, and F. Salin, Opt. Mater. 27, 1681 (2005).
R. P. Yavetskiy, M. F. Dubovik, A. V. Tolmachev, and V. Tarasov, Phys. Status Solidi (c) 2, 268 (2005).
R. P. Yavetskiy, E. F. Dolzhenkova, M. F. Dubovik, T. I. Korshikova, and A. V. Tolmachev, J. Cryst. Growth 276, 485 (2005).
R. P. Yavetskiy, A. V. Tolmachev, E. F. Dolzhenkova, and V. N. Baumer, J. Alloys Compd. 429, 77 (2007).
I. N. Ogorodnikov, N. E. Poryvai, V. A. Pustovarov, A. V. Tolmachev, R. P. Yavetskii, and V. Yu. Yakovlev, Phys. Solid State 51, 1160 (2009).
R. P. Yavetskii and A. V. Tolmachev, Pis’ma Zh. Tekh. Fiz. 30, 8 (2004).
R. T. Wegh, A. Meijerink, R.-J. Lamminmäki, and J. Hölsä, J. Lumin. 87–89, 1002 (2002).
R. Chen, J. Mater. Sci. 11, 1521 (1976).
G. Blasse, H. S. Kiliaan, and A. de Vries, J. Less-Common Met. 126, 139 (1986).
G. Blasse, C. van den Heuvel, and T. van Dijk, Chem. Phys. Lett. 62, 600 (1979).
I. N. Ogorodnikov, S. V. Kudyakov, A. Yu. Kuznetsov, V. Yu. Ivanov, A. V. Kruzhalov, V. A. Maslov, and L. A. Ol’khovaya, Tech. Phys. Lett. 19, 388 (1993).
M. P. Scripsick, X. H. Fang, G. J. Edwards, L. E. Halliburton, and J. K. Tyminski, J. Appl. Phys. 73, 1114 (1993).
I. N. Ogorodnikov, A. V. Porotnikov, S. V. Kudyakov, and A. V. Kruzhalov, Mater. Sci. Forum 239–241, 337 (1997).
A. V. Porotnikov, I. N. Ogorodnikov, S. V. Kudyakov, A. V. Kruzhalov, and S. L. Votyakov, Phys. Solid State 39, 1224 (1997).
W. Hong, M. M. Chirila, N. Y. Garces, L. E. Halliburton, D. Lupinski, and P. Villeval, Phys. Rev. B: Cond. Matter 68, 094111(9) (2003).
A. R. Lim, J. W. Ki, and C. S. Yoon, J. Appl. Phys. 94, 5095 (2003).
I. N. Ogorodnikov, L. I. Isaenko, A. V. Kruzhalov, and A. V. Porotnikov, Radiat. Meas. 33, 577 (2001).
A. Yu. Kuznetsov, A. B. Sobolev, I. N. Ogorodnikov, and A. V. Kruzhalov, Fiz. Tverd. Tela 36, 3530 (1994) Phys. Solid State 36, 1876 (1994).
I. N. Ogorodnikov, V. Yu. Ivanov, A. A. Maslakov, A. Yu. Kuznetsov, and V. A. Maslov, Tech. Phys. Lett. 19, 17 (1993).
I. N. Ogorodnikov, V. Yu. Ivanov, A. Yu. Kuznetsov, A. V. Kruzhalov, V. A. Maslov, and L. A. Ol’khovaya, Pis’ma Zh. Tekh. Fiz. 19, 14 (1993).
I. N. Ogorodnikov, A. Yu. Kuznetsov, and A. V. Porotnikov, Tech. Phys. Lett. 20, 417 (1994).
I. N. Ogorodnikov, V. Yu. Ivanov, A. Yu. Kuznetsov, A. V. Kruzhalov, and V. A. Maslov, Pis’ma Zh. Tekh. Fiz. 19, 1 (1993).
I. N. Ogorodnikov, E. A. Radzhabov, L. I. Isaenko, and A. V. Kruzhalov, Phys. Solid State 41, 197 (1999).
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © I.N. Ogorodnikov, N.E. Poryvai, I.N. Sedunova, A.V. Tolmachev, R.P. Yavetskii, 2011, published in Optika i Spektroskopiya, 2011, Vol. 111, No. 3, pp. 473–482.
Rights and permissions
About this article
Cite this article
Ogorodnikov, I.N., Poryvai, N.E., Sedunova, I.N. et al. Luminescence and recombination processes in bulky Li6Gd x Y1 − x (BO3)3:Eu crystals. Opt. Spectrosc. 111, 441–450 (2011). https://doi.org/10.1134/S0030400X11090190
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0030400X11090190