Residual stresses in rolled tungsten after pulsed irradiation with a plasma and an electron beam at the GOL-3 facility were measured. The mechanical stresses were derived from the strain, which was measured by the change in the interplanar distance in different directions. The interplanar distance was gaged from the shift of the peak of diffraction scattering of X-rays. The measured tension turned out to be a tensile stress along the surface. The tension along the direction of rolling and grinding was approximately three times larger than that in the perpendicular direction. The work was carried out at the VEPP-3/VEPP-4 complex.
Similar content being viewed by others
References
A. Huber, A. Arakcheev, G. Sergienko, et al., Phys. Scr., 159, 014005 (2014).
Th. Loewenhoff, J. Linke, G. Pintsuk, et al., J. Nucl. Mater., 463, 202 (2015).
A. V. Arzhannikov, V. T. Astrelin, A. V. Burdakov, et al., Fusion Technol., 35, No. 1T, 146 (1999).
A. V. Burdakov, V. V. Filippov, V. S. Koidan, et al., J. Nucl. Mater., 212-215, 1345 (1994).
A. S. Arakcheev, A. Huber, M. Wirtz, et al., J. Nucl. Mater., 463, 246 (2015).
R. A. Pitts, S. Carpentier, F. Escourbiac, et al., J. Nucl. Mater., 415, Suppl. 1, S957 (2011).
A. Burdakov, A. Arzhannikov, V. Astrelin, et al., Fusion Sci. Technol., 55, No. 2T, 63 (2009).
A. V. Arzhannikov, M. A. Makarov, S. L. Sinitsky, et al., Fusion Sci. Technol., 59, No. 1T, 304 (2011).
A. A. Shoshin, A. V. Arzhannikov, A. V. Burdakov, et al., Fusion Sci. Technol., 59, No. 1T, 57 (2011).
I. E. Garkusha, A. V. Burdakov, V. V. Chebotarev, et al., Probl. At. Sci. Technol., Ser.: Plasma Phys., 6, 58 (2008).
I. A. Ivanov, A. V. Burdakov, V. G. Ivanenko, et al., Fusion Sci. Technol., 59, No. 1T, 196 (2011).
A. A. Shoshin, A. V. Arzhannikov, A. V. Burdakov, et al., Fusion Sci. Technol., 59, No. 1T, 268 (2011).
S. V. Polosatkin, A. V. Arzhannikov, V. T. Astrelin, et al., Instrum. Exp. Tech., 51, No. 2, 251 (2008).
R. Yu. Akent'ev, A. V. Burdakov, I. A. Ivanov, et al., Instrum. Exp. Tech., 47, No. 2, 224 (2004).
A. V. Arzhannikov, V. A. Bataev, I. A. Bataev, et al., J. Nucl. Mater., 438, 438 (2013).
A. N. Shmakov, S. V. Mytnichenko, S. V. Tsybulya, et al., J. Struct. Chem., 35, No. 2, 224 (1994).
C. S. Barrett and T. B. Massalski, Structure of Metals, Pergamon Press, Oxford, UK (1980).
B. E. Warren, X-Ray Diffraction, Dover Publications, New York (1990).
L. D. Landau and E.M. Lifshitz, A Course of Theoretical Physics, vol. 7: Theory of Elasticity, Pergamon Press, Oxford, UK (1970).
H. E. Swanson and E. Tatge, Natl. Bur. Stand. Circ. (U.S.), 359, 1 (1953).
I. Smid, M. Akiba, G. Vieider, et al., J. Nucl. Mater., 258-263, 160 (1998).
NIST X-Ray Attenuation Databases, May (2003).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Zhurnal Strukturnoi Khimii, Vol. 57, No. 7, pp. 1389-1394, September-October, 2016.
Rights and permissions
About this article
Cite this article
Arakcheev, A.S., Shmakov, A.N., Sharafutdinov, M.R. et al. Modeling of plasma interaction with first wall in fusion reactor–measuring residual mechanical stresses in tungsten after irradiation at GOL-3 facility. J Struct Chem 57, 1314–1320 (2016). https://doi.org/10.1134/S0022476616070039
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0022476616070039