Defect structure of xSc2O3 · (1 − x)TiO2 (x = 0.4–0.5) solid solutions
- 61 Downloads
X-ray diffraction characterization with monochromatic synchrotron X-rays has demonstrated that xSc2O3 · (1 − x)TiO2 (x = 0.4–0.5) solid solutions consist of a fluorite-like (Fm3m) disordered phase and a nanoscale (≃ 10–50 nm) pyrochlore-like (Fd3m) ordered phase of the same composition, coherent with the disordered phase. We have determined their lattice parameters. The formation of nanodomains with different degrees of order is shown to be caused by the internal strain due to the high density of structural defects in their unit cells. The materials obtained in this study possess enhanced sorption capacity and can be used as catalysts, catalyst supports, gas sensors, etc.
KeywordsSolid Solution Superlattice Reflection National Research Centre Kurchatov Institute Monochromatic Synchrotron Super Lattice Reflection
Unable to display preview. Download preview PDF.
- 1.Lyashenko, L.P., Shcherbakova, L.G., and Glushkova, V.B., Interdiffusion in the TiO2-Sc2O3 system, Dokl. Akad. Nauk SSSR, 1977, vol. 233, no. 4, pp. 623–626.Google Scholar
- 2.Lyashenko, L.P., Shcherbakova, L.G., and Tatarintsev, V.M., High-temperature phase relations in the Sc2O3-TiO2 system, Dokl. Akad. Nauk SSSR, 1977, vol. 232, no. 1, pp. 73–74.Google Scholar
- 3.Manelis, G.B., Shcherbakova, L.G., Lyashenko, L.P., et al., Diffusion/kinetic control in solid-state reactions between Sc2O3 and TiO2, Dokl. Akad. Nauk SSSR, 1981, vol. 259, no. 5, pp. 1135–1139.Google Scholar
- 4.Kachapina, L.M., Lyashenko, L.P., Kichigina, G.A., et al., Raman scattering study of structural transitions in the TiO2-Sc2O3 system, Dokl. Akad. Nauk SSSR, 1979, vol. 244, no. 6, pp. 1402–1406.Google Scholar
- 5.Lyashenko, L.P., Nikonov, Yu.P., Raevskii, A.V., and Shcherbakova, L.G., Formation mechanisms of fluorite-like phases in the TiO2-R2O3 (R = Y, Er, Sc) systems, Materialovedenie, 1999, no. 1, pp. 29–33.Google Scholar
- 8.Bulatov, A.V., Izakovich, E.I., Khidekel’, M.L., et al., USSR Inventor’s Certificate no. 1 241 674, 1986.Google Scholar