Abstract
We have studied the phase composition of materials obtained by mechanochemical processing and subsequent heat treatment of mixtures of magnesium and boron powders in the atomic ratio 1: 2. Differential dissolution, differential scanning calorimetry, and X-ray diffraction data indicate that, during mechanical processing, some of the magnesium reacts with boron to form amorphous magnesium diboride. During annealing of the activated powder mixture, X-ray amorphous magnesium diboride forms at 340°C and crystallizes at 480°C. As shown by high-resolution transmission electron microscopy, the unreacted crystalline magnesium is covered with an amorphous layer consisting of magnesium diboride and boron. The amorphous material obtained by milling contains nuclei of MgB2 crystallites 3–5 nm in size. During subsequent heating of the activated mixture, magnesium and boron react further to form amorphous magnesium diboride and the amorphous phase crystallizes. Heating of mechanically activated mixtures to just below the crystallization temperature allow MgB2 nanoparticles to be produced. The formation of nanocrystalline magnesium diboride nuclei along with the amorphous phase during mechanochemical processing facilitates mechanochemical synthesis compared to thermal synthesis.
Similar content being viewed by others
References
Radev, D.D., Marinov, M., Tumbalev, V., et al., Mechanically Activated Self-Propagated High-Temperature Synthesis of Nanometer-Structured MgB2, Phys. C (Amsterdam, Neth.), 2005, vol. 418, pp. 53–58.
Varin, R.A. and Chiu, Ch., Synthesis of Nanocrystalline Magnesium Diboride (MgB2) Metallic Superconductor by Mechano-Chemical Reaction and PostAnnealing, J. Alloys Compd., 2006, vol. 407, pp. 268–273.
Gumbel, A., Eckert, J., Fuchs, G., et al., Improved Superconducting Properties in Nanocrystalline Bulk MgB2, Appl. Phys. Lett., 2002, vol. 80, no. 15, pp. 2725–2727.
Abe, H., Natio, M., et al., Low Temperature Formation of Superconducting MgB2 Phase from Elements by Mechanical Alloying, Phys. C (Amsterdam, Neth.), 2003, vol. 391, pp. 211–216.
Gao, Y.D., Ding, J., Rao, G.V.S., et al., Superconductivity of MgB2 after Mechanical Milling, Phys. Status Solidi, 2002, vol. 191, no. 2, pp. 548–554.
Gao, Y.D., Ding, J., Rao, G.V.S., and Chowdari, B.V.R., Structure, Superconductivity and Magnetic Properties of Mechanically Alloyed Mg1 − x FexB2 Powders with x = 0–0.4, Acta Mater., 2004, vol. 52, pp. 1543–1553.
Malakhov, V.V., Stoichiography As Applied to Studying Composition and Real Structure of Catalysts, J. Mol. Catal. A: Chem., 2000, vol. 158, no. 1, pp. 143–148.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © O.I. Lomovsky, G.V. Golubkova, L.S. Dovlitova, V.I. Zaikovskii, V.I. Maly, 2010, published in Neorganicheskie Materialy, 2010, Vol. 46, No. 1, pp. 28–33.
Rights and permissions
About this article
Cite this article
Lomovsky, O.I., Golubkova, G.V., Dovlitova, L.S. et al. Mechanochemical synthesis of amorphous and crystalline magnesium diboride. Inorg Mater 46, 22–27 (2010). https://doi.org/10.1134/S0020168510010061
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0020168510010061