Abstract
Nanocrystallization in amorphous Al83Ni10La7 and Al83.5Ni9.5La5.6Si1.4 alloys during heat treatment and flash lamp processing has been studied using X-ray diffraction, transmission electron microscopy, scanning calorimetry, and internal friction, modulus of elasticity, and microhardness measurements. The results demonstrate that thermal annealing and flash lamp processing have identical effects on the formation of a nanocrystalline structure in the amorphous alloys and their phase transformations.
Similar content being viewed by others
References
Sahoo, K.L., Wollgarten, M., Haug, J., and Banhart, J., Effect of La on the Crystallization Behavior of Amorphous Al94 − x Ni6Lax(x = 4–7) Alloys, Acta Mater., 2005, vol. 53, pp. 3861–3830.
Zhang, Z., Han, B.Q., Witkin, D., et al., Synthesis of Nanocrystalline Aluminum Matrix Composites Reinforced with In Situ Devitrified Al-Ni-La Amorphous Particles, Scr. Mater., 2006, vol. 54, no. 5, pp. 869–834.
Belousov, O.K., Vavilova, V.V., Ievlev, V.M., et al., Effects of Heat Treatment and Flash Lamp Processing on the Mechanical Properties of Amorphous Al83Ni10Nd3 with a Tendency to Nanocrystallization, Deform. Razrushenie Mater., 2007, no. 6, pp. 10–18.
Kovneristyi, Yu.K., Belousov, O.K., Popova, E.V., and Korshunova, A.S., Stability of Rare-Earth-Containing Aluminum-Base Alloys, Metally, 2003, no. 3, pp. 116–121.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © O.K. Belousov, V.V. Vavilova, V.M. Ievlev, Yu.E. Kalinin, S.B. Kushchev, N.A. Palii, S.A. Pokazan’eva, 2009, published in Neorganicheskie Materialy, 2009, Vol. 45, No. 8, pp. 941–948.
Rights and permissions
About this article
Cite this article
Belousov, O.K., Vavilova, V.V., Ievlev, V.M. et al. Nanocrystallization in amorphous Al83Ni10La7 and Al83.5Ni9.5La5.6 Si1.4 alloys during thermal annealing and flash lamp processing. Inorg Mater 45, 873–879 (2009). https://doi.org/10.1134/S0020168509080093
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0020168509080093