An Investigation of Surface Transformations of Nickel Highly Porous Cellular Material with an Applied Alumina Layer during Its Synthesis

  • A. Yu. Kirgizov
  • I. R. Il’yasov
  • A. I. Laskin
  • A. A. Lamberov
Nanoscale and Nanostructured Materials and Coatings
  • 13 Downloads

Abstract

For the development of a composite of nickel highly porous permeable cellular material with an applied secondary layer of alumina, transformation of the surface of the highly porous permeable cellular material is investigated at the stages of electrochemical synthesis and stages of alumina application on its surface. Etching of foamed-polyurethane bondings with 20% potassium hydroxide solution is accompanied by destruction of their surface and the formation of defective areas in the form of hillocks, hollows, and other imperfections acting as tin-hydroxide crystallization nuclei. Application of tin chloride with its subsequent hydrolysis leads to the formation of hemispherical tin-hydroxide grains with a mean size of about 80 nm uniformly distributed over the surface. The optimum values of temperature (50°C), solution pH (9–10), and electroless-nickel-plating duration (20–30 min), providing the formation of a conductive sublayer of chemically reduced nickel, are established. Nickel electroplating for 30 to 35 h at a current density of 0.1 A/dm2 yields high uniformity of a metal coating of foamed-polyurethane bondings across the thickness both in the bulk and at the outer periphery of a sample of 30 μm. A composite of nickel highly porous permeable cellular material with an applied alumina secondary layer is synthesized. The latter shows a high degree of uniformity and uniform thickness over the whole surface of bondings of the obtained composite.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Guliyants, S.T. and Liakumovich, A.G., Ochistka monomerov ot atsetilenovykh uglevodorodov selektivnym gidrirovaniem (Monomers Purification from Acetylenic Hydrocarbons with the Help of Selective Hydrogenation), Moscow: Central Research Institute of Information and Technical and Economic Research of the Oil Refining and Petrochemical Industry, 1988.Google Scholar
  2. 2.
    Khrenov, E.G., Perminova, E.A., and Fal’kov, I.G., Katalizatory i protsessy selektivnogo gidrirovaniya v neftekhimicheskoi i khimicheskoi promyshlennosti (Catalysators and Processes of Selective Hydrogenation for Petrochemical and Chemical Industry), Moscow: Central Research Institute of Information and Technical and Economic Research of the Oil Refining and Petrochemical Industry, 1993.Google Scholar
  3. 3.
    Schulze, G., Sliwka, A., and Wittmann, G., US Patent 3821323, 1972.Google Scholar
  4. 4.
    Jin, Y., Datye, A.K., Rightor, E., et al., J. Catal., 2001, vol. 203, p.292.CrossRefGoogle Scholar
  5. 5.
    Liying, X., Xian, G.J., Yee, L., et al., RF Patent 2259877, 2005.Google Scholar
  6. 6.
    Bal’zhinimaev, B.S., Zagoruiko, A.N., Paukshtis, E.A., and Simonova, L.G., RF Patent 2289565, 2006.Google Scholar
  7. 7.
    Furlong, B.K., PhD Thesis, Houston, TX: Rice Univ., 1996.Google Scholar
  8. 8.
    Khan, N.A., Shaikhutdinov, S., and Freund, H.J., Catal. Lett., 2006, vol. 108, p.159.CrossRefGoogle Scholar
  9. 9.
    Kang, J.H., Shin, E.W., Kim, W.J., et al., Catal. Today, 2000, vol. 63, p.183.CrossRefGoogle Scholar
  10. 10.
    Podyacheva, O.Yu., Ketov, A.A., Ismagilov, Z.R., et al., React. Kinet. Catal. Lett., 1997, vol. 60, p.243.CrossRefGoogle Scholar
  11. 11.
    Pestryakov, A.N., Yurchenko, E.N., and Feofilov, A.E., Catal. Today, 1996, vol. 29, p.67.CrossRefGoogle Scholar
  12. 12.
    Wang, Y. and Tonkovich, A.L.Y., US Patent 6652830, 2003.Google Scholar
  13. 13.
    Campbell, L.E., US Patent 5256387, 1993.Google Scholar
  14. 14.
    Pestryakov, A.N., Fyodorov, A.A., Gaisinovich, M.S., et al., React. Kinet. Catal. Lett., 1995, vol. 54, p.167.CrossRefGoogle Scholar
  15. 15.
    Pestryakov, A.N., Lunin, V.V., Devochkin, A.N., et al., Appl. Catal., A, 2002, vol. 227, p.125.CrossRefGoogle Scholar
  16. 16.
    Wang, Y., Vanderwiel, D.P., Tonkovich, A.L.Y., et al., US Patent 6660237, 2003.Google Scholar
  17. 17.
    Richardson, J.T., Garrait, M., and Hung, J.K., Appl. Catal., A, 2003, vol. 255, p. 69.CrossRefGoogle Scholar

Copyright information

© Pleiades Publishing, Ltd. 2018

Authors and Affiliations

  • A. Yu. Kirgizov
    • 1
  • I. R. Il’yasov
    • 1
  • A. I. Laskin
    • 1
  • A. A. Lamberov
    • 1
  1. 1.Alexander Butlerov Institute of ChemistryKazan (Volga Region) Federal UniversityKazan, TatarstanRussia

Personalised recommendations