Influence of Substrate Misorientation on the Composition and the Structural and Photoluminescence Properties of Epitaxial Layers Grown on GaAs(100)
- 24 Downloads
The influence of the degree of misorientation and treatment of a GaAs substrate on the structural and optical characteristics of homoepitaxial GaAs/GaAs(100) structures grown by metal–organic chemicalvapor deposition is studied. From the data obtained by a series of structural and spectroscopic techniques, it is shown that the degree of deviation of the substrate from the exact orientation towards the  direction by an angle of up to 4° brings about stepwise growth of the GaAs film in the initial stage and a further increase in the degree of misorienration towards the  direction to 10° results in an increase in the number of structural defects in the epitaxial film. At the same time, the samples of homoepitaxial structures grown by metal–organic chemical-vapor deposition on GaAs(100) substrates misoriented by 4° towards the  direction possess the highest photoluminescence efficiency; it is ~15% higher than the corresponding quantity for structures grown on precisely oriented GaAs(100) substrates. Preliminary polishing of the GaAs substrate (removal of an oxide layer) also yields the intensification of photoluminescence emission compared to emission in the case of an unpolished substrate of the same type. For samples grown on substrates misoriented by 4°, such an increase in the photoluminescence efficiency is ~30%.
Unable to display preview. Download preview PDF.
- 13.M. M. Lira, J. L. Alvarado, M. L. Lípez, and M. A. Vidal, Superficies Vacío, 32 (2000).Google Scholar
- 21.W. Hayes and R. Loudon, Scattering of Light by Crystals (Wiley, New York, 1978).Google Scholar
- 25.I. N. Arsent’ev, E. S. Kalevich, S. G. Konnikov, V. M. Lantratov, T. B. Popova, V. K. Tibilov, and V. P. Ulin, Avtometriya, 74 (1981).Google Scholar