Fatigue Wear Modeling of Elastomers

  • I. G. Goryacheva
  • F. I. Stepanov
  • E. V. TorskayaEmail author
Article
  • 4 Downloads

Abstract

This study presents modeling results on fatigue wear of elastomers. A contact problem solution has been derived for the sliding of a system of asperities over a viscoelastic half-space. The mechanical properties of the viscoelastic half-space are described by relations between stresses and strains given by the Volterra integral operator. The contact problem is solved by the boundary element method using an iterative procedure. Stresses in the subsurface layers of the viscoelastic material are analyzed. The damage function of the surface layer is calculated using a reduced stress criterion, the parameters of which are determined on the basis of available experimental data. The wear process is studied under the assumption that the accumulated damage can be summed up. Within the applied frictional interaction model, the wear process presents the delamination of material surface layers of finite thickness at discrete points in time and continuous surface wear by fatigue mechanism. A model calculation of contact fatigue damage accumulation has shown that the time to the first material delamination (incubation period) depends on the sliding velocity and the viscoelastic properties of the material. By analyzing the dependence of the wear rate on the input parameters of the problem, it was investigated how the sliding velocity affects the time of fatigue damage initiation and the run-in and steady-state wear rates in materials with different rheological properties. Model calculations revealed that the wear rate of material surface layers after the incubation period increases smoothly and then stabilizes. The presence of the steady-state wear rate agrees well with experimental data. The developed method for studying fatigue damage accumulation in the surface layers of viscoelastic materials in frictional interaction can also be applied on the macrolevel to determine possible crack initiation sites.

Keywords

contact fatigue damage accumulation wear viscoelasticity 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Ratner, S.B., Wear of Polymers as a Fatigue Fracture Process, in Theory of Friction and Wear, Ratner, S.B., Klitenik, G.S., and Lurie, E.G., Eds., Moscow: Nauka, 1965, pp.156–159.Google Scholar
  2. 2.
    Ratner, S.B. and Lurie, E.G., Abrasion of Polymers as a Thermally Activated Kinetic Process, Dokl. AN SSSR, 1966, vol. 166, no. 4, pp. 909–912.Google Scholar
  3. 3.
    Frictional Wear of Rubber: Coll. Papers, Evstratov, V.F., Ed., Moscow: Knimia, 1964.Google Scholar
  4. 4.
    Kragelsky, I.V. and Nepomnyashchy, E.F., Fatigue Mechanism in Elastic Contact, in Mechanics and Mechanical Engineering, Moscow: Izd–vo AN SSSR, 1963, pp. 49–56.Google Scholar
  5. 5.
    Kragelsky, I.V. and Nepomnyashchy, E.F., Theory of Wear of Highly Elastic Materials, in Plastics in Sliding Bearings, Moscow: Nauka, 1965, pp. 49–56.Google Scholar
  6. 6.
    Kragelsky, I.V., Reznikovsky, M.M., Brodsky, G.I., and Nepomnyashchy, E.F., Friction Contact Fatigue of Highly Elastic Materials, KauchukRezina, 1965, no. 9, pp. 30–34.Google Scholar
  7. 7.
    Clark, W.T. and Lancaster, J.K., Breakdown and Surface of Carbons during Repeated Sliding, Wear, 1963, vol. 6, no. 6, pp. 467–482.CrossRefGoogle Scholar
  8. 8.
    Kerridge, M. and Lancaster, J.K., The Stages in a Process of Severe Metallic Wear, Proc. Roy. Soc., 1956, vol. 236, pp.250–254.Google Scholar
  9. 9.
    Eiss, N.S., Jr., Fatigue Wear of Polymers, ACS Symposium Series, 1984, vol. 50, pp. 78–82.Google Scholar
  10. 10.
    Mars, W.V. and Fatemi, A., A Literature Survey of Fatigue Analysis Approaches for Rubber, Int. J. Fatigue, 2002, vol. 24, pp. 949–961.CrossRefzbMATHGoogle Scholar
  11. 11.
    Cadwell, S.M., Merrill, R.A., Sloman, C.M., and Yost, F.L., Dynamic Fatigue Life of Rubber, Ind. Eng. Chem., 1940, vol. 12, pp. 19–23.Google Scholar
  12. 12.
    Fielding, J.H., Flex Life and Crystallization of Synthetic Rubber, Ind. Eng. Chem., 1943, vol. 35, no. 12, pp. 1259–1261.CrossRefGoogle Scholar
  13. 13.
    Handbook of Molded and Extruded Rubber, Goodyear Tire and Rubber Company, 1969.Google Scholar
  14. 14.
    Ayoub, G., Naït–Abdelaziz, M., and Zaïri, F., Multiaxial Fatigue Life Predictors for Rubbers: Application of Recent Developments to a Carbon–Filled SBR, Int. J. Fatigue, 2014, vol. 66, pp. 168–176.CrossRefGoogle Scholar
  15. 15.
    Jardin, A., Leblond, J.–B., Berghezan, D., and Portigliatti, M., Theoretical Modelling and Experimental Study of the Fatigue of Elastomers under Cyclic Loadings of Variable Amplitude, Comp. Rend. Mécan., 2014, vol. 342, no. 8, pp. 450–458.CrossRefGoogle Scholar
  16. 16.
    Zhang, J., Xue, F., Wang, Y., Zhang, X., and Han, S., Strain Energy–Based Rubber Fatigue Life Prediction under the Influence of Temperature, R. Soc. Open Sci., 2018, vol. 5, p. 180951.CrossRefGoogle Scholar
  17. 17.
    Bezukhov, N.I., Fundamentals of the Theory of Elasticity, Plasticity, and Creep, Moscow: Vysshaya Shkola, 1961.Google Scholar
  18. 18.
    Kostetsky, B.I., Friction and Wear in Machine Parts, in Proc. 2nd All–Union Conf. on Friction and Wear in Machines, Vol. 4, Moscow: USSR Academy of Sciences, 1951, pp. 201–208.Google Scholar
  19. 19.
    Goryacheva, I.G., Mechanics of Frictional Interaction, Moscow: Nauka, 2001.Google Scholar
  20. 20.
    Goryacheva, I.G. and Chekina, O.G., Model of Fatigue Fracture of Surfaces, S v. J. Frict. Wear, 1990, vol. 11, no. 3, pp.389–400.Google Scholar
  21. 21.
    Goryacheva, I.G. and Chekina, O.G., Surface Wear: From Microfracture Modeling to Shape Change Analysis, Izv. RAN. MTT, 1999, no. 5, pp. 131–147.Google Scholar
  22. 22.
    Goryacheva, I.G. and Torskaya, E.V., Modeling of Fatigue Wear of a Two–Layered Elastic Half–Space in Contact with Periodic System of Indenters, Wear, 2010, vol. 268, no. 11–12, pp. 1417–1422.CrossRefGoogle Scholar
  23. 23.
    Chekina, O.G., Modeling of Fracture of Surface Layers in Contact of Rough Bodies, Prochn. Plastich., 1996, vol. 1, pp. 186–191.Google Scholar
  24. 24.
    Aleksandrov, V.M., Goryacheva, I.G., and Torskaya, E.V., Sliding Contact of a Smooth Indenter and a Viscoelastic Half–Space (3D Problem), Dokl. Phys., 2010, vol. 55, no. 2, pp. 77–80.ADSCrossRefzbMATHGoogle Scholar
  25. 25.
    Goryacheva, I.G., Stepanov, F.I., and Torskaya, E.V., Sliding of a Smooth Indentor over a Viscoelastic Half–Space When There is Friction, J. Appl. Math. Mech., 2015, vol. 79, no. 6, pp. 596–603.MathSciNetCrossRefGoogle Scholar
  26. 26.
    Stepanov, F.I., Sliding of Two Smooth Indenters on a Viscoelastic Foundation in the Presence of Friction, J. Appl. Mech. Tech. Phys., 2015, vol. 56, no. 6, pp. 1071–1077.ADSMathSciNetCrossRefzbMATHGoogle Scholar
  27. 27.
    Johnson, K.L., Contact Mechanics, Cambridge: Cambridge University Press, 1985.CrossRefzbMATHGoogle Scholar
  28. 28.
    Stepanov, F.I. and Torskaya, E.V., Study of Stress State of Viscoelastic Half–Space in Sliding Contact with Smooth Indenter, J. Frict. Wear, 2016, vol. 37, no. 2, pp 101–106.Google Scholar
  29. 29.
    Goryacheva, I.G., Makhovskaya, Yu.Yu., Morozov, A.V., and Stepanov, F.I., Friction of Elastomers: Modeling and Experiment, Moscow: Izhevsk Institute of Computer Science, 2017.Google Scholar
  30. 30.
    Barenblatt, G.I., Flow, Deformation and Fracture: Lectures on Fluid Mechanics and the Mechanics of Deformable Solids for Mathematicians and Physicists, Cambridge: Cambridge University Press, 2014.CrossRefzbMATHGoogle Scholar

Copyright information

© Pleiades Publishing, Ltd. 2019

Authors and Affiliations

  • I. G. Goryacheva
    • 1
  • F. I. Stepanov
    • 1
  • E. V. Torskaya
    • 1
    Email author
  1. 1.Ishlinsky Institute for Problems in MechanicsRussian Academy of SciencesMoscowRussia

Personalised recommendations