Low-Temperature Oxidation of Carbon Monoxide: The Synthesis and Properties of a Catalyst Based on Titanium Dioxide, Nanodiamond, and Palladium for CO Oxidation
- 7 Downloads
A catalyst based on TiO2 and nanodiamond with a 10 wt % palladium content of the catalyst was synthesized. The effect of the nanodiamond content on the catalytic properties in a reaction of CO oxidation at room temperature and low concentrations of CO (<100 mg/m3) was studied. It was established that, at a nanodiamond content of the catalyst from 7 to 9 wt % and a palladium content of 10 wt %, the rate of CO oxidation reached a maximum, and it was higher by a factor of 2.5 than the rate of CO oxidation on a catalyst based on pure TiO2, which included palladium clusters. With the use of transmission electron microscopy, XRD X-ray diffractometry, and X-ray photoelectron spectroscopy, it was found that the clusters of palladium covered with palladium oxide with an average cluster size of 4 nm were formed on the surface of the TiO2 carrier. It was assumed that the catalyst synthesized is promising for applications in catalytic and photocatalytic air-cleaning systems.
Keywordslow-temperature oxidation of CO catalyst based on titanium dioxide nanodiamond and palladium
Unable to display preview. Download preview PDF.
- 4.Vershinin, N.N., Goldshleger, N.F., Efimov, O.N., and Gusev, A.L., Al’tern. Energ. Ekol., 2008, vol. 8, p.99.Google Scholar
- 7.Vershinin, N.N., Efimov, O.N., Bakaev, V.A., Aleksenskii, A.E., Baidakova, M.V., Sitnikova, A.A., and Vul, A.Ya., Fullerenes, Nanotubes and Carbon Nanostruct., 2011, vol. 19, no. 1, p.63.Google Scholar
- 9.RF Patent 2348090, 2009.Google Scholar
- 11.Bennett, R.A., Pang, C.L., Perkins, N., Smith, R.D., Morrall, P., Kvon, R.I., and Bowker, M., J. Phys. Chem. B, vol. 106, no. 18, p. 4688.Google Scholar