Abstract
Reactivity and mass loss are considered mutually exclusive in conventional zero-valent metal (ZVM) technology to treat environmental contaminants. Here, we report the outstanding performance of Co-based metallic glass (MG) in degrading an aqueous solution of azo dye, thus eliminating this trade-off. Ball-milled Co-based MG powders completely degrade Acid Orange II at an ultrafast rate. The surface-area-normalized rate constant of Co-based MG powders was one order of magnitude higher than that of Co-based crystalline counterparts and three orders of magnitude higher than that of the widely studied Fe0 powders. The coordinatively unsaturated local structure in Co-based MG responds to the catalysis for degradation, resulting in very low mass loss. Wide applicability and good reusability were also present. Co-based MG is the most efficient material for azo dye degradation reported thus far and will promote the practical application of MGs as functional materials.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Dyes make the world more colorful but contribute significantly to the water pollution. Synthetic dyes, particularly azo dyes with aromatic structures, are refractory to degradation1,2 and the threat of dyes to the environment and ecosystem has attracted substantial public attention. Among the various physical and/or chemical processes to treat the wastewater with azo dyes, zero-valent metals (ZVMs)3,4,5,6,7, including Fe0, Mg0 and Zn0, are of high interest because they are inexpensive, easy to use and non-toxic and do not require further treatment of effluents. However, two key factors limit their wide practical application8,9,10,11. The first is the low reactivity of ZVMs, which results in a limited loading rate unsuitable for the industrial wastewater treatment. The second is the high mass loss of ZVMs due to corrosion in aqueous solution, which contributes to their low durability and induces secondary pollution, obviously increasing the processing cost. Several strategies have been proposed to enhance the reactivity of ZVMs, including making nanostructures by increasing the reactive surface area11,12,13,14,15, preparing bi-metals10,16,17,18,19 (Pd-Fe0, Ni-Fe0 and Pd-Mg0, etc.) by increasing the oxidation of ZVMs through the formation of infinite galvanic cells simultaneous with facilitating atomic hydrogen reduction by noble metal additives and coupling using other physical techniques20,21,22,23,24,25, e.g., ultrasound, UV-visible light and microwave. However, these methods enhance reactivity at the cost of intrinsic acceleration of the mass loss of ZVMs8,9,11 and may be more effective in groundwater remediation than industrial wastewater treatment because of the increase in cost and the secondary pollution. Thus, high-performance materials with high reactivity and without the expense of mass loss are urgently needed for industrial wastewater treatment.
Metallic glasses (MGs) show the good combination of some desirable chemical and physical properties such as corrosion resistance, soft magnetic property and high strength26,27. In addition to structural applications, various functional applications of MGs have also been investigated and exploited28,29,30, including as catalysts, biomaterials and nanotechnology. Fe-Si-B and Fe-Mo-Si-B MGs were recently reported to decolorize azo dyes at an enhanced surface area normalized degradation rate with compared to crystalline Fe0 and nano-Fe0 31,32. These findings develop a tremendous application potential of MGs in remediation of wastewater contaminated with azo dyes. More MGs, e.g., Fe-, Mg-, MgZn- and Al-based ones, were subsequently applied to azo dye degradation33,34,35,36,37,38,39,40,41. The reacting rate was effectively enhanced and the problem of mass loss was alleviated to a certain extent. Here, we report the application of Co-based MG to degrade azo dyes in an aqueous solution for the first time. Co-based MG exhibits better resistance to corrosion in wastewater due to its relatively higher standard reduction potential in aqueous solutions than Fe- and Mg-based MGs42. The ball-milled Co-based MG exhibited superior catalytic activity and durability as well as little mass loss when degrading the azo dye compared to reported Fe- and Mg-based MGs and their crystalline counterparts.
Results
Preparation and characterization of Co-based MG powders
Degradation of azo dyes by ZVMs is a surface-mediated process43. Ball milling can increase the surface area of powders, thus accelerating the degradation process34,35,39. Prior to ball milling, the MG ribbons were annealed at approximately the onset glass transition temperature (Tg). Sufficient thermal relaxation cannot alter the amorphous structure (Fig. S1a) but embrittles the ribbons, thus facilitating the pulverization of the ribbons in the ball-milling process. Four powders were prepared: Powder Gbm, Powder Cbm, Powder Can and Powder p-Co (details are provided in the Methods). Figure 1a presents the X-ray diffraction (XRD) patterns of Powder Gbm, which exhibits broad diffusive diffraction peaks characteristic of an amorphous structure. Due to the metastable nature of the amorphous phase, high-energy input (i.e., an increase in the rotation speed or milling time) reduced its stability, inducing nanocrystallization of β-Co, Co3B and Co4B40, as indicated by the XRD patterns of Powder Cbm in Fig. 1a. The amorphous nature of Powder Gbm was further verified by differential scanning calorimetry (DSC, Fig. S1b) and transmission electron microscopy (TEM). Figure 1c shows a high-resolution TEM (HRTEM) image inset with selected area electron diffraction (SAED) patterns, which clearly demonstrate that the particles are fully amorphous either on the surface or inside. By contrast, in Powder Cbm (Fig. 1d), the surface layer, with a thickness of several nanometers, is amorphous, whereas the inside is composed of nanocrystals. Powder Can and Powder p-Co, which correspond to Co-based nanocrystallized powders prepared by annealing Powder Gbm at 900 K for 120 min and pure Co nanocrystalline powders prepared by ball-milling the gas-atomized pure Co powders, respectively, are shown in Fig. 1a.
The morphology of the particles was characterized by scanning electron microscopy (SEM), which revealed that the particles had similar morphology for all powders (Fig. S2). Figure 1b shows the corresponding SEM images of Powder Gbm. The particles have good separability. The surface exhibits high roughness and corrugation, which would significantly expand the active surface area and provide more active sites for the reaction to improve the degradation rate. The size distribution of the particles was 8 ~ 12 μm in median diameter (D50), as measured by a laser particle analyzer (Fig. S3). The specific surface area for Powder Gbm was approximately 0.24 m2 g−1 as determined by the Brunauer-Emmett-Teller (BET) method.
Reactivity in the Acid Orange II aqueous solution
Acid Orange II (AO II), a model compound of azo dye, was used to examine the degradation capabilities of the Co-based MG powders. UV-vis absorption spectra of AO II usually exhibit a strong absorption at λmax = 484 nm originating from the conjugated structure formed by the azo bond (-N = N-); the intensity of this bond is proportional to the concentration of AO II in solution3. Figure 2a shows the change in the UV-vis absorption spectra of the AO II solution (the initial concentration of AO II was 0.2 g/L) treated with Powder Gbm as a function of reaction time. As the reaction progressed, the intensity of the absorption peak decreased due to degradation of the azo bond. In this study, the AO II solution treated by Powder Gbm changed from orange to colorless and transparent in less than 2 minutes, as shown in the inset of Fig. 2a. Complete degradation of the azo bond was also indicated by the intensity of the absorption peak (λmax = 484 nm), which approached zero in the 2-minute spectra in Fig. 2a. These results demonstrate that Powder Gbm completely degraded AO II ultrafast in aqueous solution, approximately 30 times faster than the ball-milled Fe-based MG34 and several thousand times faster than the widely investigated Fe0 4.
(a) UV-vis spectra of the AO II solution treated with Powder Gbm at room temperature as a function of reaction time, inset with a photograph of the AO II solution at different treating times. (b) The dependence of Ct normalized by C0 on reaction time for all four powders at room temperature. The solid lines are nonlinear fitting to the experimental data points. (c) Comparison of the AO II degradation efficiency and degradation rate for the four studied powders. (d) Comparison of the degradation capability of the present Co-based MG and other investigated ZVMs, confirming the ultrahigh reactivity of the Co-based MG in degrading the AO II solution.
To illustrate the structural effect, the degradation behaviors (Fig. S4) of Powder Cbm, Powder Can and Powder p-Co were compared with that of Powder Gbm. The dependence of Ct normalized by C0 on the reaction time for all four powders is presented in Fig. 2b, where Ct and C0 are the real-time and initial concentrations of AO II in solution, respectively. When the structure was nanocrystalline rather than amorphous, the degradation capacity decreased and the time required for complete degradation increased, for example, to 14 minutes for Powder Cbm. These results suggest that an amorphous structure is more effective for AO II degradation. The decay behavior of Ct/C0 with reaction time was fit well nonlinearly (Fig. 2b) by
![](http://media.springernature.com/lw336/springer-static/image/art%3A10.1038%2Fsrep18226/MediaObjects/41598_2015_Article_BFsrep18226_Equ1_HTML.gif)
where Cult is the ultimate residual dye concentration, t is the reaction time and k denotes the empirical rate constant15. Thus, the degradation of AO II obeys a pseudo-first-order kinetic model. The parameters k representing the degradation rate and η = 1 − Cult/C0 defining the degradation efficiency14 can be derived by nonlinear fitting, as shown in Fig. 2c. Powder Gbm not only exhibits the highest empirical degradation rate constant of k = 2.687, more than an order of magnitude higher than the other three powders, but also achieves the highest degradation efficiency of η = 99.72%. Thus, the Co-based MG powder exhibits superior performance in degrading the AO II solution.
Figure 2d compares the degradation capabilities of Powder Gbm and other investigated ZVMs. To take the reported differences in the surface areas of the ZVMs and initial concentrations of dyes into account, the parameter kSAC0 was calculated to compare the degradation capability4, where kSA is the surface-area-normalized rate constant. Although the empirical rate constant of the amorphous alloys is not always higher than that of the crystalline ZVMs, kSAC0 is larger for MGs than for crystalline alloys, indicating MGs can support more active sites. The rate constant of the Co-based MG powder is higher than those of all investigated amorphous alloys: two times higher than that of MgZn-based MG35 and tens of times higher than those of Fe-based amorphous alloys31,32,33. The parameter kSAC0 is also highest for the present Co-based MG and is thousands of time higher than that of commercial Fe0 3,4. As shown in Fig. 2d, the parameter kSAC0 was not determined for MgZn-based MG because the specific surface area was not reported35. Although the experimental parameters, such as the mass concentration of the particles and the initial concentration of dyes, were the same for both MgZn- and Co-based MGs, the density of MgZn-based MG was significantly lower than that of Co-based MG. Consequently, kSAC0 should be slightly smaller for MgZn-based MG. In short, Co-based MG may be the most efficient material for degrading azo dyes thus far.
In addition to high reactivity in the degradation process, the Co-based MG powder exhibits relatively low mass loss. We used inductively coupled plasma-atomic emission spectrometry (ICP-AES) to measure the total concentration of Co cations in the solution at different times when Co-based MG powder was exposed to the azo-dye aqueous solution (Fig. S5). The total concentration of Co cations remained constant at 2.8~4.5 mg L−1, thus indicating much lower mass loss than Fe- and MgZn-based MGs31,32,33,34,35. The mechanism of Co-based MG may differ from that of reported Fe- and MgZn-based MGs and Fe0, breaking the trade-off between reactivity and mass loss in popular ZVM techniques and making the application of Co-based MG of high commercial interest.
Applicability of Co-based MG
To explore the applicability of Co-based MG, we examined the influence of working conditions, such as the initial concentration of azo dye, pH and environmental temperature, on the degradation behaviors. As shown in Fig. 3a, when the concentration increased from 0.2 g L−1 to 2.0 g L−1, the degradation of AO II remained very fast and was nearly complete in 10 minutes. The parameters of k and η were obtained by nonlinear fitting, revealing a high degradation efficiency above 98% for all concentrations, as illustrated in the inset of Fig. 3a. Changes in AO II concentration in the experimental range slightly affected the degradation capability of Co-based MG powders. The influence of pH variation differed (Fig. 3b). In the examined pH range of 3~10, the degradation process was complete in a very short period of time, consistent with the fast degradation rate of this MG. However, high degradation efficiency of ~98% was maintained for pH values lower than 7, whereas the degradation efficiency decreased to ~78% for pH values larger than 7. The difference in the degradation efficiency induced by the increase in pH is probably attributable to a different degradation mechanism, which could be inferred from the different UV-vis absorption spectra of the products (Fig. S6) in solution with pH of 3~10.
Influence of (a) the initial concentration of azo dye, (b) pH and (c) environmental temperature on the degradation behaviors of AO II solutions, inset with the corresponding degradation rate and degradation efficiency, respectively. (d) The dependence of Ct normalized by C0 as a function of time for the different recycles of Powder Gbm, inset with the corresponding degradation efficiencies and degradation rates for the different recycles.
To illustrate the influence of environmental temperature, we selected the AO II solution with a concentration of 2.0 g L−1 because the degradation reaction in the 0.2 g L−1 solution of AO II is too rapid. Figure 3c shows the decay behaviors of Ct/C0 with reaction time at environmental temperatures of 293 K to 323 K. Increasing the environmental temperature enhanced the degradation capability of the Co-based MG powder, as indicated by the increase in k from 0.526 min−1 to 1.815 min−1 and η higher than 99%.
We further tested the durability of the present Co-based MG powders (Fig. 3d). As recycling increased, more time was needed to accomplish the degradation process. However, all degradation processes continued to obey the pseudo-first-order exponential decay kinetic model, as indicated by the good nonlinear fitting of the dependence of Ct/C0 on reaction time with Equation (1). The obtained k and η are shown in the inset of Fig. 3d. A dramatic decrease in k from 2.687 min−1 to 0.993 min−1 occurred on the second use. After the first use, we examined the morphology of the Co-based MG powders by SEM. Products partially covered the surface of the powders, directly reducing the reaction sites for the second use and correspondingly lowering k. By the sixth use, k declined to 0.152 min−1, i.e., two orders of magnitude. However, η remained above 94%. On the eighth use, the degradation capability further deteriorated, as indicated by k = 0.094 min−1 and η = ~80%. These results demonstrate that the present Co-based MG is very durable. XRD measurements (Fig. S7) revealed that the Co-based MG powders still retained the amorphous structure after the eighth use.
Discussion
The prevailing degradation mechanism of azo dyes in the ZVM-H2O system can be summarized as follows6,8,43: (i) reductive degradation of azo dyes with direct electron transfer from ZVM at the surface of ZVM; (ii) degradation of azo dyes by reaction with dissolved M(II) or H/H2, which are products of ZVM corrosion; and (iii) catalytic hydrogenation. All pathways are presumably coupled with the electrochemical corrosion of metals6,8. Take Fe0 as an example. The corrosion of Fe0 governs the rate of contaminant removal by Fe0 8,9. Consequently, methods that accelerate Fe0 corrosion can be used to enhance contaminant sequestration by Fe0 8,9. This strategy was not applicable in this study because Co-based MG powders exhibited the highest reaction rate of all investigated powders, as shown in Fig. 2 and amorphous alloys usually possess higher corrosion resistance than their crystalline counterparts26,27, as evidenced by the low mass loss in the present study. The ultrafast degradation of azo dyes by Co-based MG powders is attributable to their amorphous structure. Figure 4 illustrates the possible degradation reactions and mechanisms occurring in the present system.
At the atomic level, Co-Si-B MG can be described as a space-filling network of short-range ordering polyhedra with a scale of several angstroms to several nanometers44. The atoms are in the highly coordinatively unsaturated state. More atoms with unsaturated coordination are present on the surface of the amorphous structure than the crystalline one. The role of these atoms is similar to that of Pd atoms in bimetallic Pd-Fe0 and Pd-Mg0 particles, in which they function as catalysts and the absorbed atomic hydrogen species are responsible for hydrogenation degradation of azo dyes10,16,17,18,19. Thus, these atoms obviously contribute to the increase in the reaction rate. This mechanism predominates the degradation process of azo dyes and is also supported by the following results in the present study. First, if this pathway predominates the reductive cleavage of the -N = N- bond, the cobalt content should be at least 67.290 mg L−1 as quantitatively calculated by mass balance. In fact, the cobalt content in the solution was merely 2.8~4.5 mg L−1 as determined by ICP-AES after the reaction (Fig. S5), which is far below that calculated for degrading the azo dye by direct transfer of electrons from MG to the dye molecules. Second, the activation energy for the degradation reaction of AO II was evaluated by the Arrhenius-type relationship lnkT = lnA − Ea/RT, where kT is the empirical rate constant at the thermodynamic temperature T, A is the pre-exponential factor, Ea is the activation energy and R is the molar gas constant. Ea was approximately 33 kJ mol−1 over the temperature range of 293 K to 323 K (Fig. S8), much lower than that for Fe0 34 and Fe- and MgZn-based MGs34,35. These results support the catalytic effect and the transfer of active hydrogen to the azo dye molecules to facilitate the cleavage of the -N = N- bond.
Moreover, the Co-based MG contains metalloid elements of Si and B as high as 22 at.%, which not only enhances glass-forming ability, thus facilitating the preparation of the Co-based MG powder, but may also promote the degradation process through the formation of local galvanic couples between Si, B and Co42. The role of local galvanic couples is controversial and it is generally accepted that they could benefit the oxidizing degradation of azo dyes8,9,10. Hydroxyl radicals produced by the reaction of water and dissolved oxygen electro-catalyzed on the surface of Co-based MG would have a high oxidation potential of ~2.8 V and oxidatively decompose the azo dye18.
The amorphous structure is not the equilibrium state and is energetically higher than the corresponding crystalline state; consequently, MGs are always more active than their crystalline counterparts. The degradation reaction can occur on more sites of the MG surface, thus improving the reaction rate. We observed the morphologies of particles exposed in aqueous solution for 5 min for all investigated materials (Fig. S2). Although no obvious difference was observed among the four types of particles before reaction, a significant difference was observed after 5 min exposure. The surface of MG particles was quickly coated with the reaction products uniformly and fluffily, whereas sparse reaction products were observed on the surface of the other types of particles32,34. This result implies that the amorphous structure supports more reactive sites than the crystalline structure, which undoubtedly favors an increase in the reaction rate for a surface-mediated degradation process43. The precipitated reaction products will also enhance the absorption of the dye molecules because of the porous structure8. Consequently, the concentration of azo dye increased in the vicinity of the surface of the particles, likewise accelerating the degradation reaction.
In summary, Co-based MG was applied to degrade azo dyes for the first time. The Co-based MG exhibits superior properties, such as high reactivity and efficiency, wide applicability, good reusability and low corrosion loss. The degradation process can be described by a pseudo-first-order kinetic model. Surface catalysis plays a significant role in the degradation process, which contributes to the ultrafast degradation rate. The effects of Co-based MG should remain similar to those of Fe0 technology when treating other environmental contaminants. From this perspective, Co-based MG particles may be an ideal ZVM technology to sequestrate environmental contaminants9. These findings will promote the practical application of MGs as functional materials.
Methods
Preparation of Co-based MG powders
Metallic glass ribbons with a nominal composition of Co78Si8B14 in atomic percentage were prepared by vacuum melt-spinning. Then, the ribbons were annealed (673 K, 5 h) below the crystallization temperature according to the DSC pattern shown in Fig. 1a under an argon atmosphere. After annealing embrittlement, the ribbons were cut into pieces and subjected to high-energy ball milling. The mill pots containing ribbon pieces and steel ball bearings were pumped to a high vacuum and then filled with high-purity argon gas for protection. Powder Gbm and Powder Cbm were manufactured by ball milling the glassy ribbon pieces for 40 h at a speed of 250 r min−1 and for 34 h at 400 r min−1, respectively. Powder Can was obtained by vacuum annealing Powder Gbm at 900 K for 120 min. Powder p-Co was prepared by ball milling the gas-atomized pure Co powders for 40 h at 250 r min−1.
Physical characterization
The structure of the powders was verified by DSC, XRD and TEM. The diameter and the morphology of the particles were characterized using a laser particle analyzer and by SEM, respectively. The BET surface area was determined by N2 absorption/desorption analysis conducted at 77 K.
AO II degradation characterization
The AO II aqueous solution (0.2 g L−1) was prepared by dissolving Acid Orange II at the desired concentration in distilled water to prepare 1 L of solution. Degradation experiments were conducted in a reactor (100 mL) fastened in a reciprocating shaker. The shaker was timed starting at 360 r min−1 when the powders (0.12 g) and Acid Orange II aqueous solution (20 mL) were injected into the reactor. Periodically, 3 mL of solution was withdrawn and used to measure the concentration of AO II after centrifugation. The concentration of the AO II solution was analyzed by UV-vis spectroscopy (Model V-550JAS.CO., America) at a maximum wavelength of 484 nm, corresponding to the azo bond (-N = N-). After the reaction, the collected powders washed of reagents were again studied by SEM to examine the change in surface morphology. In addition, the cobalt content in the AO II aqueous solution after reaction was determined by ICP-AES. The powders after reaction were collected and washed of reagents, then cleaned of products coated on the surface using HCl (0.1 M); finally, the powders were washed with ethyl alcohol at least three times. After drying, the powders were applied in the degradation process a second time and the same procedure was repeated until the degradation efficiency decreased radically. The effects of temperature, solution acidity, solution concentration and particle dosage on the degradation process were also examined. All experiments were conducted at room temperature (~25 °C) except those studying the effect of temperature. For experiments studying the effect of temperature, the solution temperature remained at 20, 30, 40 and 50 °C, respectively. Thus, the influence of temperature on the degradation rate was investigated. We also adjusted the solution acidity with pH values of 3, 4, 5, 8, 9 and 10 by adding HCl (0.1 M) or NaOH (0.1 M) to observe the influence of the pH value on the degradation rate. AO II solutions with concentrations of 0.2 g L−1 ~ 2.0 g L−1 were used in the degradation process.
Additional Information
How to cite this article: Qin, X. D. et al. Ultrafast degradation of azo dyes catalyzed by cobalt-based metallic glass. Sci. Rep. 5, 18226; doi: 10.1038/srep18226 (2015).
References
Robinson, T., McMullan, G., Marchant, R. & Nigam, P. Remediation of dyes in textile effluent: a critical review on current treatment technologies with a proposed alternative. Bioresour. Technol. 77, 247–255 (2001).
Stolz, A. Basic and applied aspects in the microbial degradation of azo dyes. Appl. Microbiol. Biotechnol. 56, 69–80 (2001).
Cao, J., Wei, L., Huang, Q., Wang, L. & Han, S. Reducing degradation of azo dye by zero-valent iron in aqueous solution. Chemosphere 38, 565–571 (1999).
Nam, S. & Tratnyek, P. G. Reduction of azo dyes with zero-valent iron. Water Res. 34, 1837–1845 (2000).
Gillham, R. W. & O’Hannesin, S. F. Enhanced degradation of halogenated aliphatics by zero-valent iron. Groundwater 32, 958–967 (1994).
Matheson, L. J. & Tratnyek, P. G. Reductive dehalogenation of chlorinated methanes by iron metal. Environ. Sci. Technol. 28, 2045–2053 (1994).
Roberts, A. L., Totten, L. A., Arnold, W. A., Burris, D. R. & Campbell, T. J. Reductive elimination of chlorinated ethylenes by zero-valent metals. Environ. Sci. Technol. 30, 2654–2659 (1996).
Noubactep, C. Metallic iron for environmental remediation: the long walk to evidence. Corros. Rev. 31, 51–59 (2013).
Guan, X. et al. The limitations of applying zero-valent iron technology in contaminants sequestration and the corresponding countermeasures: The development in zero-valent iron technology in the last two decades (1994–2014). Water Res. 75, 224–248 (2015).
O’Carroll, D., Sleep, B., Krol, M., Boparai, H. & Kocur, C. Nanoscale zero valent iron and bimetallic particles for contaminated site remediation. Adv. Water Resour. 51, 104–122 (2013).
Zhang, W. X. Nanoscale iron particles for environmental remediation: an overview. J. Nanopart. Res. 5, 323–332 (2003).
Wang, C. B. & Zhang, W. X. Synthesizing nanoscale iron particles for rapid and complete dechlorination of TCE and PCBs. Environ. Sci. Technol. 31, 2154–2156 (1997).
Liu, Y., Choi, H., Dionysiou, D. & Lowry, G. V. Trichloroethene hydrodechlorination in water by highly disordered monometallic nanoiron. Chem. Mater. 17, 5315–5322 (2005).
Fan, J., Guo, Y., Wang, J. & Fan, M. Rapid decolorization of azo dye methyl orange in aqueous solution by nanoscale zerovalent iron particles. J. Hazard. Mater. 166, 904–910 (2009).
Shu, H. Y., Chang, M. C., Yu, H. H. & Chen, W. H. Reduction of an azo dye Acid Black 24 solution using synthesized nanoscale zerovalent iron particles. J. Colloid. Interface Sci. 314, 89–97 (2007).
Grittini, C., Malcomson, M., Fernando, Q. & Korte, N. Rapid dechlorination of polychlorinated biphenyls on the surface of a Pd/Fe bimetallic system. Environ. Sci. Technol. 29, 2898–2900 (1995).
Zhang, W. X., Wang, C. B. & Lien, H. L. Treatment of chlorinated organic contaminants with nanoscale bimetallic particles. Catal. Today 40, 387–395 (1998).
Bokare, A. D., Chikate, R. C., Rode, C. V. & Paknikar, K. M. Effect of Surface Chemistry of Fe−Ni Nanoparticles on Mechanistic Pathways of Azo Dye Degradation. Environ. Sci. Technol. 41, 7437–7443 (2007).
Liu, W. J., Qian, T. T. & Jiang, H. Bimetallic Fe nanoparticles: Recent advances in synthesis and application in catalytic elimination of environmental pollutants. Chem. Eng. J. 236, 448–463 (2014).
Hung, H.-M. & Hoffmann, M. R. Kinetics and Mechanism of the Enhanced Reductive Degradation of CCl4 by Elemental Iron in the Presence of Ultrasound. Environ. Sci. Technol. 32, 3011–3016 (1998).
Geiger, C. L., Ruiz, N. E., Clausen, C. A., Reinhart, D. R. & Quinn, J. W. Ultrasound pretreatment of elemental iron: kinetic studies of dehalogenation reaction enhancement and surface effects. Water Res. 36, 1342–1350 (2002).
Chang, M. C., Shu, H. Y. & Yu, H. H. An integrated technique using zero-valent iron and UV/H2O2 sequential process for complete decolorization and mineralization of C.I. Acid Black 24 wastewater. J. Hazard. Mater. 138, 574–581 (2006).
Im, J. K., Son, H. S. & Zoh, K. D. Perchlorate removal in Fe0/H2O systems: Impact of oxygen availability and UV radiation. J. Hazard. Mater. 192, 457–464 (2011).
Shu, H. Y., Chang, M. C. & Chang, C. C. Integration of nanosized zero-valent iron particles addition with UV/H2O2 process for purification of azo dye Acid Black 24 solution. J. Hazard. Mater. 167, 1178–1184 (2009).
Lee, Y. C., Lo, S. L., Chiueh, P. T., Liou, Y. H. & Chen, M. L. Microwave-hydrothermal decomposition of perfluorooctanoic acid in water by iron-activated persulfate oxidation. Water Res. 44, 886–892 (2010).
Schroers, J. Bulk Metallic Glasses. Phys. Today 66, 32–37 (2013).
Wang, W. H. Bulk metallic glasses with functional physical properties. Adv. Mater. 21, 4524–4544 (2009).
Brower, W. E., Matyjaszczyk, M. S., Pettit, T. L. & Smith, G. V. Metallic glasses as novel catalysts. Nature 301, 497–499 (1983).
Schroers, J., Kumar, G., Hodges, T., Chan, S. & Kyriakides, T. Bulk metallic glasses for biomedical applications. JOM 61, 21–29 (2009).
Kumar, G., Tang, H. X. & Schroers, J. Nanomoulding with amorphous metals. Nature 457, 868–872 (2009).
Zhang, C., Zhang, H., Lv, M. & Hu, Z. Decolorization of azo dye solution by Fe–Mo–Si–B amorphous alloy. J. Non-cryst. Solids 356, 1703–1706 (2010).
Zhang, C. Q., Zhu, Z. W., Zhang, H. F. & Hu, Z. Q. Rapid reductive degradation of azo dyes by a unique structure of amorphous alloys. Chin. Sci. Bull. 56, 3988–3992 (2011).
Zhang, C. Q., Zhu, Z. W., Zhang, H. F. & Hu, Z. Q. Rapid decolorization of Acid Orange II aqueous solution by amorphous zero-valent iron. J. Environ. Sci. 24, 1021–1026 (2012).
Wang, J. Q. et al. Rapid Degradation of Azo Dye by Fe-Based Metallic Glass Powder. Adv. Fun. Mater. 22, 2567–2570 (2012).
Wang, J. Q. et al. Excellent capability in degrading azo dyes by MgZn-based metallic glass powders. Sci. Rep. 2, 418; 10.1038/srep00418 (2012).
Liu, P., Zhang, J. L., Zha, M. Q. & Shek, C. H. Synthesis of an Fe rich amorphous structure with a catalytic effect to rapidly decolorize Azo dye at room temperature. ACS Appl. Mater. Interfaces 6, 5500–5505 (2014).
Luo, X. et al. Enhanced degradation of azo dye by nanoporous-copper-decorated Mg–Cu–Y metallic glass powder through dealloying pretreatment. Appl. Surf. Sci. 305, 314–320 (2014).
Tang, Y., Shao, Y., Chen, N. & Yao, K. F. Rapid decomposition of Direct Blue 6 in neutral solution by Fe-B amorphous alloys. RSC Adv. 5, 6215–6221 (2015).
Das, S. et al. Synergistic catalytic effect of iron metallic glass particles in direct blue dye degradation. J. Mater. Res. 30, 1121–1127 (2015).
Das, S., Garrison, S. & Mukherjee, S. Bi-Functional Mechanism in Degradation of Toxic Water Pollutants by Catalytic Amorphous Metals. Adv. Eng. Mater., 10.1002/adem.201500239 (2015).
Zhao, Y. F., Si, J. J., Song, J. G., Yang, Q. & Hui, X. D. Synthesis of Mg–Zn–Ca metallic glasses by gas-atomization and their excellent capability in degrading azo dyes. Mater. Sci. Eng. B 181, 46–55 (2014).
Bard, A. J., Parsons, R. & Jordan, J. Standard potentials in aqueous solution, vol. 6. CRC press, 1985.
Weber, E. J. Iron-Mediated Reductive Transformations Investigation mechanism of reaction. Environ. Sci. Technol. 30, 716–719 (1996).
Sheng, H. W., Luo, W. K., Alamgir, F. M., Bai, J. M. & Ma, E. Atomic packing and short-to-medium-range order in metallic glasses. Nature 439, 419–425 (2006).
Acknowledgements
The authors gratefully acknowledge the financial support of the National Natural Science Foundation of China (No. 51101156), the “One Hundred Talented People” program of the Chinese Academy of Sciences and Youth Innovation Promotion Association CAS.
Author information
Authors and Affiliations
Contributions
Z.W.Z. and H.F.Z. proposed the idea and designed the study. X.D.Q. conducted the experiments and collected the data. X.D.Q., Z.W.Z., G.L., H.M.F., H.W.Z., A.M.W., H.L. and H.F.Z. analyzed the data together. X.D.Q., Z.W.Z. and H.F.Z. wrote the manuscript. Z.K.L. is acknowledged for experimental assistance.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Qin, X., Zhu, Z., Liu, G. et al. Ultrafast degradation of azo dyes catalyzed by cobalt-based metallic glass. Sci Rep 5, 18226 (2016). https://doi.org/10.1038/srep18226
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep18226
- Springer Nature Limited
This article is cited by
-
Highly efficient cobalt-based amorphous catalyst for peroxymonosulfate activation toward wastewater remediation
Rare Metals (2023)
-
Photocatalytic Activity of Soft Magnetic Fe80−xCoxZr10Si10 (x = 0, 40, and 80) Nanocrystalline Melt-Spun Ribbons
Topics in Catalysis (2022)
-
Enhanced degradation performance of Fe75B12.5Si12.5 amorphous alloys on azo dye
Environmental Science and Pollution Research (2022)
-
Nanomaterials for remediation of contaminants: a review
Environmental Chemistry Letters (2021)
-
The catalytic performance of Cu46Zr47-xAl7Yx amorphous ribbons in the degradation of AO II dye wastewater
Environmental Science and Pollution Research (2021)