A partial sequential galvanic exchange method is reported for synthesizing heterostructured interfaces between ordered intermetallic phases on a preformed metal template. Four distinct phases with engineered interfaces between them could be combined in one particle.
References
Xia, X., Wang, Y., Ruditskiy, A. & Xia, Y. Adv. Mater. 25, 6313–6333 (2013).
De Trizio, L. & Manna, L. Chem. Rev. 116, 10852–10887 (2016).
Fenton, J. L., Steimle, B. C. & Schaak, R. E. Science 360, 513–517 (2018).
Yu, J., Yin, Y. & Huang, W. Nat. Synth. https://doi.org/10.1038/s44160-023-00289-4 (2023).
Zhou, M., Li, C. & Fang, J. Chem. Rev. 121, 736–795 (2021).
Yu, J. et al. ACS Appl. Mater. Interfaces 13, 52073–52081 (2021).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interests
The author declares no competing interest.
Rights and permissions
About this article
Cite this article
Fenton, J.L. Interfaced intermetallics on the nanoscale. Nat. Synth 2, 703–704 (2023). https://doi.org/10.1038/s44160-023-00308-4
Published:
Issue Date:
DOI: https://doi.org/10.1038/s44160-023-00308-4
- Springer Nature Limited