Abstract
Micro-light-emitting diode displays are generating considerable interest as a promising technology for augmented-reality glasses. However, the fabrication of highly efficient and ultra-small ( <3 μm) micro-light-emitting diodes, which are required for augmented-reality applications, remains a major technical challenge due to the presence of strong sidewall nonradiative recombination. In this study, we demonstrate a 3.5 × 3.5 μm2 blue GaN micro-light-emitting diode with negligible sidewall nonradiative recombination compared with bulk nonradiative recombination. We achieve this by using an ultralow-damage dry etching technique, known as neutral beam etching, to create the micro-light-emitting diode mesa. Our 3.5 × 3.5 μm2 micro-light-emitting diode exhibits a low decrease in external quantum efficiency of only 26% at a current density of 0.01 A/cm2, compared with the maximum external quantum efficiency that is reached at the current density of ∼3 A/cm2. Our findings represent a significant step towards realizing micro-light-emitting diode displays for augmented-reality glasses.
Similar content being viewed by others
Introduction
Microdisplays using semiconductor micro-light-emitting diodes (micro-LEDs) as light emitters are considered to be ideal candidates for next-generation virtual reality (VR) and augmented reality (AR) smart glasses that require high-resolution, high-luminance, and energy-efficient displays1. However, the near-eye operating environment of VR/AR microdisplays imposes strict limitations on the size and power consumption of the micro-LEDs. For AR displays, a resolution of at least 4000 pixels per inch (ppi) is required to achieve a high-quality display, which corresponds to a pixel pitch of approximately 6 μm2,3,4. To achieve this resolution, the maximum size of the micro-LEDs for each primary color should be reduced to below 3 μm. Heat generation during the operation of AR microdisplays is not allowed because the display is located very close to the human eye. Unfortunately, approximately only 50% of the injected electrical power is converted into light, even in state-of-the-art red, green, and blue semiconductor LEDs5. The remaining 50% of electrical power is converted into heat, which increases the temperature of the LED package without an efficient thermal management design6. However, it would be impractical to implement an active thermal dissipation design in AR glasses owing to the light-weight requirement. The most effective way to suppress heat generation is to reduce the operation current density of micro-LEDs. A simple estimation of a 4000-ppi microdisplay using GaN micro-LEDs suggests that the temperature increase can be suppressed to approximately 20 °C by reducing the operating current density to the order of 1 A/cm2 (Supplementary Fig. 2).
The fabrication of highly efficient sub-3-μm micro-LEDs in the <1 A/cm2 current density region is a significant challenge because of the presence of strong Shockley-Read-Hall nonradiative recombination arising from mesa sidewall defects. Typically, GaN micro-LEDs are produced by inductively coupled plasma (ICP) etching of a planar LED wafer, which introduces high-density defects acting as nonradiative recombination centers to the sidewall surfaces of the micro-LED mesa owing to ion bombardment and deep ultraviolet photon irradiation7,8. As a result, strong sidewall surface nonradiative recombination occurs, reducing the emission efficiency of micro-LEDs by decreasing the chip size9,10, especially in sub-3-μm micro-LEDs where the micro-LED dimension becomes comparable to the diffusion length of minority carriers in GaN11,12. This efficiency reduction was particularly significant in the current density region below 1 A/cm2, since the external quantum efficiency (EQE) of a high-quality InGaN/GaN LED typically shows a maximum at a current density of a few to tens of A/cm2 and decreases with decreasing current density owing to enhanced Shockley-Read-Hall nonradiative recombination13.
Intrinsic surface defects such as dangling bonds in the outermost surface layer also play an important role in sidewall surface nonradiative recombination of GaN micro-LEDs. These defects act as nonradiative recombination centers and cause pinning of the Fermi level at the sidewall surface14,15, leading to the bending of the surface band energy near the surface area and the accumulation of carriers at the sidewall surface. This accumulation provides an additional channel for nonradiative surface recombination. Jiang et al. conducted a theoretical investigation into the impact of intrinsic surface states on GaN blue micro-LEDs grown on a c-plane sapphire substrate16. They found that the presence of intrinsic surface states reduced the maximum internal quantum efficiency (IQE) from 58% to 24% when the chip size was decreased from 300 to 3 μm, even without plasma-etching-induced surface damage.
Despite the considerable efforts to reduce sidewall surface nonradiative recombination in GaN micro-LEDs smaller than 10 μm, this problem persists. To address this issue, Wang et al. used neutral beam etching (NBE), an ultralow-damage dry etching technique for semiconductor materials17, to fabricate GaN blue micro-LEDs18,19. Their 6 × 6 μm2 GaN micro-LED displayed EQE vs. current density characteristics similar to those of a 40 × 40 μm2 device in the current density region higher than 1 A/cm2, indicating a significant reduction in dry-etching-induced nonradiative recombination. Ley et al. reported the first 2 μm InGaN/GaN blue micro-LED fabricated by ICP etching, where potassium hydroxide (KOH) treatment of mesa sidewalls was employed to remove plasma-induced defects, and the sidewall surface was further passivated by a thin Al2O3 layer deposited by atomic layer deposition20. However, the EQE of the fabricated micro-LED decreased to approximately 17% of its peak EQE at a current density of 15 A/cm2 when the current density was decreased to 0.1 A/cm2.
In this work, we successfully fabricate a 3.5 × 3.5 μm2 GaN blue micro-LED with negligible mesa sidewall nonradiative recombination compared with bulk nonradiative recombination of the epitaxial wafer, using the NBE process. Our devices exhibit a low decrease in EQE (approximately 26%) at a current density of 0.01 A/cm2 compared to the peak EQE observed around 3 A/cm2. Analysis of the EQE characteristics and measurement of the surface potential of the NBE-etched sidewall surface using Kelvin force microscopy (KFM) reveals that our devices effectively suppress nonradiative recombination related to not only sidewall defects generated during mesa etching but also intrinsic surface states.
Results
Fabrication of the 3.5 × 3.5 μm2 micro-LED
The NBE system employs a unique carbon electrode featuring a high-aspect-ratio aperture positioned between the ICP discharge chamber and the etching chamber. As accelerated ions pass through the aperture, charge exchange with the carbon electrode efficiently neutralizes them, resulting in a neutral beam with controlled kinetic energy directed towards the sample surface for etching17,19. Moreover, the carbon aperture blocks deep ultraviolet photons, allowing for ultralow damage etching of semiconductor materials. Overall, the NBE process is an effective means of providing semiconductor material etching with minimal damage.
Commercial InGaN/GaN blue LED wafers grown on patterned (0001) c-plane sapphire substrates using metal-organic vapor phase epitaxy (MOVPE) were utilized as epitaxial materials. The active region comprised 16 pairs of InGaN/GaN multiple quantum wells (MQWs), emitting light at approximately 458 nm. Figure 1a illustrates the schematic of the micro-LEDs fabricated in this study. Square-shaped micro-LED mesas with sizes ranging from 3 to 20 μm were etched by NBE, using SiO2 deposited by plasma-enhanced chemical vapor deposition (PECVD) as a mask. In addition, a series of reference samples were fabricated using the conventional ICP process, followed by a KOH solution treatment to remove the plasma-induced damage layer. Subsequently, a 150-nm-thick SiO2 film was deposited on the sample surface by PECVD as an electrical isolation and surface passivation layer. Next, a self-aligned Ni/Au p-type Ohmic contact was prepared on the mesa top (Supplementary Fig. 3), and a Cr/Au n-type contact was formed on the n-GaN surface (Supplementary Fig. 3). The thickness of the entire layer was adjusted such that the surface of the n-contact was at the same height as the p-contact. The device process was completed by the deposition of an Au/Sn multilayer on both the p-type and n-type Ohmic contacts, which acted as a eutectic bonding layer. Figure 1b, c depict 45° tilted scanning electron microscopy (SEM) images of a 3-μm micro-LED fabricated by the NBE process and the same device where the SiO2 passivation layer was removed by wet etching using buffered hydrofluoric acid (BHF) to expose the details of the micro-LED mesa, respectively. The micro-LED mesa comprised four vertical sidewall surfaces with a very smooth surface morphology. These surfaces are close to the nonpolar m- and a-planes of the GaN crystal based on the crystalline orientation of the epitaxial wafer, but they may not represent the exact m- and a-planes of GaN because of the limited precision of device processes. To avoid misleading, we refer to these surfaces as “m-plane-like surface” or “a-plane-like surface” hereafter. The depth of the mesa is approximately 700 nm. The presence of vertical nonpolar-like sidewall surfaces indicates that the chemical reaction is the dominant mechanism in the NBE etching of GaN. The mesa size was approximately 3.5 × 3.5 μm2, slightly larger than the designed size of 3 × 3 μm2. The size of the Au/Sn multilayer and Ni/Au p-contact (not clearly revealed in Fig. 2c) was 2 × 2 μm2. Hereafter, we refer to the device size by the actual size measured by SEM observation, e.g., a 3.5 × 3.5 μm2 micro-LED.
a Cross-sectional schematic illustration of the micro-LEDs fabricated in this work. The sapphire substrate was thinned from the backside to 200 μm and polished to a mirror surface. b A 45° tilted SEM image of a 3.5 × 3.5 μm2 micro-LED fabricated by the NBE process is shown. Scale bar, 3 μm. c A 45° tilted SEM image of the same micro-LED after the SiO2 passivation layer was etched off by BHF solution. Scale bar, 3 μm.
EQE of micro-LEDs fabricated by the NBE process with different sizes ranging from 3.5 × 3.5 μm2 to 20.5 × 20.5 μm2 as a function of current density is shown. Here, a uniform current density over the whole mesa area was assumed since the spacing between the edge of the metal contact and the edge of the chip (approximately 0.75 μm, see Fig. 1c) is small enough than the current spreading length (see Fig. 3c), and the chip size measured from SEM observation was used to calculate the current density. A 3 × 3 μm2 device fabricated by the ICP process and treated with a KOH solution was also given for comparison. The solid up-pointing triangle (open up-pointing triangle), solid circle (open circle), solid right-pointing triangle (open right-pointing triangle), and solid diamond (open diamond) represent the EQEs calculated from the light emission power measured using a photodiode (an integrating sphere) for the 3.5 × 3.5 μm2, 6.5 × 6.5 μm2, 10.5 × 10.5 μm2, and 20.5 × 20.5 μm2 micro-LEDs fabricated by the NBE process, respectively. The solid and open down-pointing triangles represent the EQEs calculated from the light emission power measured using a photodiode and integrating sphere, respectively, for the 3 × 3 μm2 micro-LED fabricated by the ICP process.
After completing the device fabrication process, the micro-LED chip was diced into a 1 × 1 mm2 size and bonded to an Si submount with an electrical injection circuit using the flip-chip eutectic bonding technique (Supplementary Fig. 4). The light emission was extracted from the sapphire substrate side and measured using a Si photodiode calibrated to detect emission with a limit of 0.5 nW (Thorlabs, S130VC). The Si photodiode was placed approximately 4 mm from the micro-LED chip, which corresponds to a collection half angle of approximately 52°. The light emission under high current densities was also measured using a 2-inch integrating sphere (Thorlabs, S142C) with a detection limit of 1 μW to evaluate the absolute emission efficiency value.
EQE analysis as a function of current density
Figure 2 depicts the EQE measured as a function of current density for four micro-LEDs with sizes ranging from 3.5 × 3.5 μm2 to 20.5 × 20.5 μm2, which were fabricated using the NBE process. For comparison, a 3 × 3 μm2 sample etched using ICP and treated with a KOH solution is also shown. The EQE was calculated using the following equation:
where P is the measured light output power, λ is the peak light emission wavelength, I is the injected current, c is the speed of light in a vacuum, h is the Planck constant, and e is the elementary charge. All four EQE curves of the NBE samples exhibited a maximum at a current density of approximately 3 A/cm2. The current density at which EQE peaks is indicative of the nonradiative recombination velocity and can be used as a figure of merit to evaluate LED efficiency20,21. A lower current density at the peak EQE implies a lower nonradiative recombination rate and thus, a higher EQE for devices with similar radiative and Auger recombination rates. Therefore, the observation of a similar current density at the peak EQE for all the four micro-LEDs fabricated by the NBE process suggests that all the four devices have a similar nonradiative recombination rate. Here, we assumed that all the devices have a similar Auger recombination rate. This is a reasonable assumption because Auger recombination rates of GaN blue LEDs have been shown to be nearly size-independent for LEDs smaller than 100 µm22. Moreover, the peak EQE was found to increase as the chip size decreased. The peak EQE of the 3.5 × 3.5 μm2 chip was calculated to be as high as 37.5% from the total emission power measured using the integrating sphere. Although the differences in light-extraction efficiency need to be considered, the aforementioned EQE value is substantially higher than those reported for GaN blue micro-LEDs with comparable dimensions20. However, the most notable finding revealed in Fig. 2 is that all NBE-etched devices exhibited very slow decreases in EQEs with decreasing current density from the current density at peak EQEs. We defined an efficiency droop as \(({{{\mbox{EQE}}}}_{{{\mbox{peak}}}}-{{{\mbox{EQE}}}}_{0.01{{\mbox{A/}}}{{{\mbox{cm}}}}^{2}})/{{{\mbox{EQE}}}}_{{{\mbox{peak}}}}\) to quantitatively evaluate the efficiency decrease in the low current density region, where EQEpeak and \({{{{\rm{EQE}}}}}_{0.01{{{\rm{A}}}}/{{{{\rm{cm}}}}}^{2}}\) are the peak EQE and the EQE at a current density of 0.01 A/cm2, respectively. The efficiency droop for the 3.5 × 3.5 μm2, 6.5 × 6.5 μm2, 10.5 × 10.5 μm2, and 20.5 × 20.5 μm2 micro-LEDs fabricated by the NBE process were calculated from Fig. 2 to be approximately 26%, 34.7%, 36.7%, and 37.2%, respectively. The findings of this study reveal a surprising result that the efficiency droop decreases with decreasing chip size. The 3.5 × 3.5 μm2 micro-LED exhibited the lowest efficiency droop of approximately 26%. This observation contrasts with the behavior of conventional ICP-etched GaN micro-LEDs, where the efficiency droop typically increases rapidly with chip size reduction below 10 μm because of the enhanced sidewall nonradiative recombination, even with KOH treatment9,10,23. These results indicate that sidewall nonradiative recombination, which typically increases when the chip size decreases, was effectively suppressed in the micro-LEDs fabricated using the NBE process to a level that can be neglected relative to the bulk nonradiative recombination of the epitaxial wafer. In other words, the emission efficiency is only limited by the bulk nonradiative recombination which should be size-independent. Considering a size-independent nonradiative recombination rate (a similar IQE) in NBE-etched micro-LEDs, the increase in peak EQEs when the chip size decreases, can be explained by an increase in light-extraction efficiencies in smaller micro-LEDs, which resulted from enhanced sidewall light extraction20,23. On the other hand, the 3 × 3 μm2 micro-LED fabricated by the ICP process (Supplementary Fig. 5) exhibited a lower peak EQE of approximately 28.5%, a higher current density at peak EQE of approximately 9 A/cm2, and a much larger efficiency droop of approximately 60% at a current density of 0.01 A/cm2 compared to the NBE-etched devices. These differences clearly indicate the existence of strong sidewall nonradiative recombination in the ICP-etched device, and that KOH treatment cannot entirely remove sidewall nonradiative recombination, consistent with previous reports12,20,23,24,25.
To further confirm the influence of sidewall nonradiative recombination, we examined the intrinsic EQE of the epitaxial wafer by fabricating a 200 × 200 μm2 LED with a small (3 μm in diameter) p-contact at the center, using the same processes as those employed for the micro-LEDs in Fig. 2 (Supplementary Fig. 6). The microscopic photograph of the 200 × 200 μm2 LED and the 30° tilted high-magnification SEM image of the 3-μm diameter p-contact are shown in Fig. 3a, b, respectively. In this case, the current is injected into the device through the p-contact and spreads out from the p-contact with a diffusion length Ls, which is defined by the following equation:
where t represents the thickness of the p-type layer, ρ denotes the resistivity of the p-type layer, rc denotes the radius of the p-contact metal, J0 represents the current density at the edge of the p-contact, which can be calculated from the injection current I by \(I/\pi {({r}_{{{\mbox{c}}}}+{L}_{{{\mbox{s}}}})}^{2}\) (see inset of Fig. 3c), nideality is the ideality factor of the LED, e is the elementary charge, k is the Boltzmann constant, and T is the temperature26. Additionally, ρ was measured by Hall measurement to be approximately 18 Ωcm. nideality was determined to be approximately 2.18 from the I–V curve (Supplementary Figs. 7 and 8). The radius of the Ni/Au p-contact was 1.5 μm (rc). We assumed that sidewall nonradiative recombination was completely avoided if the current spreading length was much shorter than the distance between the p-contact and the mesa edge (approximately 100 μm). Consequently, the measured EQE solely reflected the intrinsic emission efficiency of the epitaxial wafer.
a A microscopic photograph of the 200 × 200 μm2 LED with a small Ni/Au p-contact (3 μm in diameter) to investigate the intrinsic EQE of the epitaxial wafer is shown. A stripe-shaped n-contact surrounding the 200 μm mesa was employed. Scale bar, 100 μm. b A high-magnification 30° tilted SEM image showing the details of the p-contact. Scale bar, 1 μm. c Measured EQE (the black curve) and calculated current spreading length Ls (the red curve) as a function of current density. The inset illustrates schematically the variation of current density along the radial direction, where J0, rc, and Ls represent the current density at the edge of the p-contact, the radius of the p-contact, and the current spreading length, respectively.
Figure 3c shows the current density dependence of the calculated current spreading length and measured EQE. The EQE reached a maximum at a current density of approximately 40 A/cm², which was one order of magnitude larger than that observed in Fig. 2. This was due to the fact that the current density decreases outside the p-contact with increasing distance from the p-contact edge, as depicted in the inset of Fig. 3c. When the current density under the p-contact is increased to the value at peak EQE in Fig. 2, the local EQE underneath the p-contact will reach a maximum. However, further current injection was needed for the position-averaged EQE to reach a maximum, as the EQE outside the p-contact decreased with distance from the p-contact edge. As a rough approximation, we assumed that the EQE vs. current density curve shifted by one order of magnitude towards a higher current density with respect to those given in Fig. 2, where the current density was spatially uniform. Therefore, the efficiency droop at the current density of 0.1 A/cm2 in Fig. 3c which was estimated to be approximately 55% are considered corresponding to that at the current density of 0.01 A/cm2 in Fig. 2. The current spreading length at the current density of 0.1 A/cm2 (approximately 6.3 μm) was much shorter than the distance between the p-contact and the mesa edge (100 μm), so we assumed that the influence of sidewall nonradiative recombination could be neglected, and that the above efficiency droop represented the intrinsic EQE characteristics of the epitaxial wafer.
Considering the uncertainties related to the non-uniform current density distribution in the 200 × 200 μm2 device, the above efficiency droop is in reasonable agreement with that of the 20.5 × 20.5 μm2 micro-LED in Fig. 2. This suggests that the efficiency droops of the NBE-etched micro-LEDs shown in Fig. 2 were solely determined by nonradiative recombination in the InGaN/GaN bulk layers, and that sidewall-related nonradiative recombination did not give rise to any further reduction in the emission efficiency. This was a surprising conclusion, as nonradiative recombination related to intrinsic sidewall surface states is generally believed to inevitably exist. Nonetheless, our results suggest that both nonradiative recombination induced by sidewall damage generated during mesa etching and that induced by intrinsic sidewall surface states resulting from surface dangling bonds in micro-LEDs fabricated by the NBE process were suppressed to a level that made the influence of sidewall nonradiative recombination on micro-LED efficiencies negligible compared to bulk nonradiative recombination.
Surface potential measurement of NBE-etched sidewall surfaces
Intrinsic surface states induced by dangling bonds can cause surface band bending, which can be characterized using KFM27,28. In this study, we investigated the surface band bending of the NBE-etched surface by KFM, using the sample shown in Fig. 4a. The wafer was grown on a (0001) c-plane n-type freestanding GaN substrate with a resistivity of approximately 0.025 Ω cm, using MOVPE. The substrate was misoriented 0.4° towards the [1-100] direction. The layer structure consisted of 0.5-μm-thick Si-doped GaN layer (electron concentration of approximately 3 × 1018 cm−3), 0.5-μm-thick unintentionally doped GaN layer (n-type conductivity), a 5-period InGaN/GaN blue-emitting MQW layer (total thickness of approximately 80 nm), and 0.5-μm-thick unintentionally doped GaN layer. The sample was subsequently processed into a 1-μm-pitched grating with equal line and space widths, using photolithography and NBE etching (Fig. 4a). The etching depth is approximately 0.9 μm. The sample was then cleaved along the line-stripe direction, and KFM observations were performed on the exposed m-plane-like surface etched by NBE. An as-cleaved sample without a grating pattern was measured as a reference. Figure 4b shows the measured surface potentials of the NBE-etched samples. Distorted images appearing just beneath the etching bottom position are attributed to dimples observed around the corner between the vertical m-plane-like surface and the bottom c-plane in the SEM image shown in Fig. 4a.
a A tilted SEM image of the 1-μm-pitched grating for KFM observation is shown. The dashed line indicates the cleave direction. Scale bar, 1 μm. b A typical measured surface potential image is shown. The scan area was 1.5 μm × 1.5 μm. The MQW and Si-doped GaN positions were marked based on growth thickness. The etching bottom position was marked using the NBE etching depth obtained from SEM observation. Scale bar, 200 nm. c Surface potential as a function of distance from the edge of the NBE-etched (the red curve) and as-cleaved (the blue curve) reference samples. The small fluctuations marked by dashed circles are due to measurement artifacts.
Although a uniform potential image was observed along the grating stripe direction, the surface potential tended to increase from the MQW position toward the sample edge. In Fig. 4c, we present the surface potentials of the NBE-etched sample and the as-cleaved reference sample as a function of the distance from the sample edge. KFM measures the difference in contact potential between the atomic force microscopy (AFM) probe tip and the GaN surface. This difference can be expressed by (χtip - χGaN) − SBB − (EC - EF), where χtip is the electron affinity (or Fermi level) of the AFM tip, χGaN is the electron affinity of GaN, SBB is the surface band bending of GaN, EC is the conduction band bottom of GaN, and EF is the Fermi level of GaN27. Since χtip, χGaN, EC, and EF are the same for the NBE-etched and reference samples, the measured potential difference in Fig. 4c reflects only the difference in the surface band bending between the two samples. The m-plane GaN surface is typically reported to show upward band bending (towards the vacuum level) of the order of a few hundred meV14,28. In this study, we observed that the NBE-etched sample had a slightly higher (0.3–0.4 V) surface potential and upward surface band bending compared to the reference sample in the region between the etching bottom and MQW, while the two samples exhibited similar surface potentials around the MQW position. This suggests that the NBE-etched sample has a similar or slightly larger number of surface states compared to the reference sample. However, as the measurement position moved towards the sample edge from the MQW position, the surface potential started to increase, and we speculate that this could be due to the adsorption of Cl on the etched surface, because this area was exposed to the Cl neutral beam for a longer time29. The KFM results, together with the EQE data presented in Fig. 2, indicate that the surface states on the NBE-etched sidewall surface are not efficient nonradiative recombination centers. Further investigation is necessary to comprehend the unusual behavior of surface states in NBE-etched GaN and InGaN. Nonetheless, we have demonstrated that it is possible to fabricate InGaN/GaN micro-LEDs with negligible sidewall surface nonradiative recombination.
Mechanism for the low efficiency droop in the 3.5 × 3.5 μm2 micro-LED
Finally, we would like to briefly discuss the mechanism behind the observed decrease in efficiency droop with decreasing chip size in micro-LEDs fabricated by the NBE process, as shown in Fig. 2. It is well established that patterning InGaN/GaN MQWs into sub-micrometer-sized nanostructures can lead to strong strain relaxation, which in turn weakens the quantum-confined Stark effect and enhances emission efficiency30,31,32. Strain relaxation is also present in InGaN/GaN mesa structures with diameters of a few to tens of micrometers, with relaxation mainly occurring near the mesa surface over a width of a few hundred nanometers33,34. Therefore, we presumably attributed the low-efficiency droop observed in the 3.5 × 3.5 μm2 micro-LED to the strain relaxation effect occurring near the mesa surface. To confirm the existence of strain relaxation, we performed cathode luminescence (CL) mapping of the emission wavelength of the 3.5 × 3.5 μm2 mesa fabricated by the NBE process. As shown in Fig. 5, a blue shift of 1–2 nm in the emission wavelength can be clearly observed near the m-plane-like sidewall surface over a width of a few hundred nanometers. This experiment provides direct evidence for the existence of strain relaxation near the mesa sidewall surface of micro-LEDs studied in this work. However, observation of efficiency increase induced by strain relaxation in the low current density region is challenging in micro-LEDs with strong sidewall nonradiative recombination because the decrease in efficiency caused by sidewall nonradiative recombination can easily offset the efficiency increase induced by strain relaxation. The above discussion indicates again that the sidewall surface nonradiative recombination in micro-LEDs fabricated by the NBE process is negligible compared with the bulk nonradiative recombination.
Discussion
In summary, we successfully demonstrated a 3.5 × 3.5 μm2 InGaN/GaN blue micro-LED with negligible sidewall surface nonradiative recombination. This was achieved through an ultralow-damage NBE etching process. The micro-LED exhibited an EQE droop as low as 26% at a current density of 0.01 A/cm2, compared with the peak EQE observed around 3 A/cm2. This efficiency droop is approximately 11% lower than that of a 20.5 × 20.5 μm2 device. With these results, we anticipate that it will be possible to reduce the chip size even further to meet the requirements of AR smart glasses, because the mesa sidewall does not give rise to any reduction in micro-LED efficiencies.
Methods
NBE experiments
For the Cl2-based etching process, the ICP source power was set to 800 W and modulated at a frequency of 10 kHz with a 50% duty ratio. A Cl2 gas flow rate of 40 sccm was used as the etching gas, and the pressure in the etching chamber was 0.1 Pa. To enhance the evaporation of the In-containing etching products, the sample stage temperature was set to 130 °C. Additionally, a bias power of 6 W was applied to the carbon aperture in order to control the kinetic energy of the neutral beam. The etching rate achieved under these conditions for the LED wafer used in this study was approximately 5 nm/min, though it is worth noting that the InGaN well layer may exhibit slower etching rates due to the low volatility of In-containing etching products.
ICP experiments and KOH etching
In the ICP experiments, an ICP machine (RIE-400iPS, Samco Inc.) was utilized. A mixture of Cl2 and BCl3 gases was used as the etching gas with flow rates of 50 sccm and 6 sccm, respectively. The ICP and RF bias powers were set to 150 W and 5 W, respectively. The etching pressure and stage temperature were 1 Pa and 20 °C, respectively, resulting in an etching rate of approximately 20 nm/min for the LED wafer used in this study. After ICP etching of the micro-LED mesa, the sample was treated with a 48% KOH solution at approximately 25 °C for 35 min to remove ICP-induced surface damage.
KFM measurements
KFM measurements were conducted using a Bruker NanoscopeV/Dimension Icon Glovebox AFM in a high-purity argon gas atmosphere at room temperature, where the residual concentrations of both water and oxygen were approximately 0.1 ppm. An Si cantilever covered with Pt/Ir was used as the probe. After cleaving the NBE-etched sample along the grating stripe direction, SEM observation was performed to find a surface area with minimal height differences around the etching bottom. A bias was applied to adjust the surface potential in the starting area (approximately 1.5 μm from the sample edge) to zero, enabling a comparison between the two samples. As the a-plane GaN surface is more difficult to cleave, KFM measurements were performed only on the m-plane.
CL mapping
A CL mapping experiment was conducted using a Schottky-type field-emission SEM machine (JEOL, JSM-7100F). An acceleration voltage of 8 kV, giving rise to a penetration depth of approximately 450 nm in GaN, was used. The beam current was set at 0.5 nA. An epitaxial wafer with the same layer structure as that used for micro-LED fabrication grown on a planar sapphire substrate was used because the patterned substrate will cause scattering of light and lower the spatial resolution of the mapping. The emission wavelength was measured to be approximately 451 nm by photoluminescence excited by a 375-nm laser (excitation power density: 7.5 W/cm2). An SiO2 passivation layer was not deposited on the sample surface to avoid the charge-up effect.
Data availability
The source data underlying all figures presented in the main manuscript and Supplementary Information are provided in the Figshare repository at https://doi.org/10.6084/m9.figshare.23961723.
References
Lin, J. Y. & Jiang, H. X. Development of microLED. Appl. Phys. Lett. 116, 100502 (2020).
Wierer, J. J. & Tansu, N. III-nitride micro-LEDs for efficient emissive displays. Laser Photonics Rev. 13, 1900141 (2019).
Huang, Y., Hsiang, E.-L., Deng, M.-Y. & Wu, S.-T. Mini-LED, micro-LED and OLED displays: present status and future perspectives. Light Sci. Appl. 9, 105 (2020).
Park, J. et al. Electrically driven mid-submicrometre pixelation of InGaN micro-light-emitting diode displays for augmented-reality glasses. Nat. Photon. 15, 449 (2021).
Karpov, S. Y. Light-emitting diodes for solid-state lighting: searching room for improvements. Proc. SPIE 9768, 97680C (2016).
U.S. Department of Energy. Thermal Management of White LEDs. https://www1.eere.energy.gov/buildings/publications/pdfs/ssl/thermal_led_feb07_2.pdf (2007).
Shul, R. J. et al. Inductively coupled plasma induced etch damage of GaN p-n junctions. J. Vac. Sci. Tech. A 18, 1139–1143 (2000).
Minami, M. et al. Analysis of GaN damage induced by Cl2/SiCl4/Ar plasma. Jpn. J. Appl. Phys. 50, 08JE03 (2011).
Smith, J. M. et al. Comparison of size-dependent characteristics of blue and green InGaN microLEDs down to 1 μm in diameter. Appl. Phys. Lett. 116, 071102 (2020).
Olivier, F. et al. Influence of size-reduction on the performances of GaN-based micro-LEDs for display application. J. Lumin. 191, 112–116 (2017).
Karpov, S. Y. & Makarov, Y. N. Dislocation effect on light emission efficiency in gallium nitride. Appl. Phys. Lett. 81, 4721–4723 (2002).
Finot, S. et al. Surface recombination in III-nitride micro-LEDs probed by photon-correlation cathodoluminescence. ACS Photon 9, 173–178 (2022).
David, A., Young, N. G., Lund, C. & Craven, M. D. Review – The physics of recombination in III-nitride emitters. ECS J. Solid State Sci. Technol. 9, 016021 (2020).
Himmerlich, M. et al. Confirmation of intrinsic electron gap states at nonpolar GaN(1-100) surfaces combining photoelectron and surface optical spectroscopy. Appl. Phys. Lett. 104, 171602 (2014).
Kim, P. et al. Impact of Ga and N vacancies at the GaN m-plane on the carrier dynamics of micro-light-emitting diodes. Phys. Rev. Appl. 19, 014018 (2023).
Jiang, F., Hyun, B.-R., Zhang, Y. & Liu, Z. Role of intrinsic surface states in efficiency attenuation of GaN-based micro-light-emitting-diodes. Phys. Status Solidi RRL 15, 200487 (2021).
Samukawa, S. A neutral beam process for controlling surface defect generation and chemical reaction at the atomic layer. ECS J. Solid Sci. Tech. 4, N5089 (2015).
Zhu, J. et al. Near-complete elimination of size-dependent efficiency decrease in GaN micro-light-emitting-diodes. Phys. Status Solidi A 216, 1900380 (2019).
Wang, X. L. & Samukawa, S. Damage-free neutral beam etching for GaN micro-LEDs processing. in Semiconductors and Semimetals (eds. Jiang H. & Lin J.) 106, 203–221 (Academic Press, Cambridge, 2021).
Ley, R. T. et al. Revealing the importance of light extraction efficiency in InGaN/GaN microLEDs via chemical treatment and dielectric passivation. Appl. Phys. Lett. 116, 251104 (2020).
Konoplev, S. S., Bulashevich, K. A. & Karpov, S. Y. From large-size to micro-LEDs: scaling trends revealed by modeling. Phys. Status Solidi A 215, 1700508 (2018).
Olivier, F., Daami, A., Licitra, C. & Templier, F. Shockley-Read-Hall and Auger non-radiative recombination in GaN based LEDs: A size effect study. Appl. Phys. Lett. 111, 022104 (2017).
Wolter, S. et al. Size-dependent electroluminescence and current-voltage measurements of blue InGaN/GaN μLEDs down to the submicron scale. Nanomaterials 11, 836 (2021).
Lee, T.-Y. et al. Increase in the efficiency of III-nitride micro LEDs by atomic layer deposition. Opt. Exp. 30, 18552 (2022).
Park, J.-H. et al. Impact of sidewall conditions on internal quantum efficiency and light extraction efficiency of micro-LEDs. Adv. Optical Mater. 11, 2203128 (2023).
Schubert, E. F. Light-Emitting Diodes Ch. 8 (Cambridge Univ. Press, Cambridge, 2007).
Baret, S. et al. Surface potential of n- and p-type GaN measured by Kelvin force microscopy. Appl. Phys. Lett. 93, 212107 (2008).
Henning, A. et al. Measurement of the electrostatic edge effect in wurtzite GaN nanowires. Appl. Phys. Lett. 105, 213107 (2014).
Ohori, D. et al. Etching characteristics for InGaN/GaN hydrogen iodide (HI) neutral beam etching for micro-LED fabrication. Nanotechnology 34, 365302 (2023).
Wang, S.-W. et al. Wavelength tunable InGaN/GaN nano-ring LEDs via nano-sphere lithography. Sci. Rep. 7, 42962 (2017).
Ley, R. et al. Strain relaxation of InGaN/GaN multi-quantum well light emitters via nanopatterning. Opt. Exp. 27, 30081 (2019).
Zhang, K. X. et al. High-efficiency nanodisk of InGaN/GaN MQWs fabricated by neutral-beam etching and GaN regrowth: towards directional micro-LED in top down structure. Semicond. Sci. Technol. 35, 075001 (2020).
Xie, E. Y. et al. Strain relaxation in InGaN/GaN micro-pillars evidenced by high resolution cathodoluminescence hyperspectral imaging. J. Appl. Phys. 112, 013107 (2012).
Zhan, J. L. et al. Investigation on strain relaxation distribution in GaN-based μLEDs by Kelvin probe force microscopy and micro-photoluminescence. Opt. Exp. 26, 5265 (2018).
Acknowledgements
We would like to express our gratitude to Dr. Naoto Kumagai for his valuable discussions on KFM measurements, Dr. Hisashi Yamada for his advice on MOVPE growth on free-standing GaN substrates, and Dr. Reiko Azumi for her continuous support of this work. Dr. Toshikazu Yamada and Ms. Akiko Murai also provided significant help in wire bonding the micro-LED chips.
Author information
Authors and Affiliations
Contributions
S.S. invented the neutral beam technique. X.W. and S.S. jointly proposed applications of the neutral beam technique to micro-LED processing. X.W. performed most of the device fabrication and characterization experiments and prepared the manuscript. X.Z. conducted the majority of the SEM observations, while T.T. performed the MOVPE growth for the KFM measurements. D.O. carried out part of the NBE etching experiments. X.W., S.S. and D.O. participated in extensive discussions on the experimental results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Byung-Ryool Hyun, and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, X., Zhao, X., Takahashi, T. et al. 3.5 × 3.5 μm2 GaN blue micro-light-emitting diodes with negligible sidewall surface nonradiative recombination. Nat Commun 14, 7569 (2023). https://doi.org/10.1038/s41467-023-43472-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-43472-z
- Springer Nature Limited