Abstract
The high dielectric optical contrast between the amorphous and crystalline structural phases of non-volatile phase-change materials (PCMs) provides a promising route towards tuneable nanophotonic devices. Here, we employ the next-generation PCM In3SbTe2 (IST) whose optical properties change from dielectric to metallic upon crystallization in the whole infrared spectral range. This distinguishes IST as a switchable infrared plasmonic PCM and enables a programmable nanophotonics material platform. We show how resonant metallic nanostructures can be directly written, modified and erased on and below the meta-atom level in an IST thin film by a pulsed switching laser, facilitating direct laser writing lithography without need for cumbersome multi-step nanofabrication. With this technology, we demonstrate large resonance shifts of nanoantennas of more than 4 µm, a tuneable mid-infrared absorber with nearly 90% absorptance as well as screening and nanoscale “soldering” of metallic nanoantennas. Our concepts can empower improved designs of programmable nanophotonic devices for telecommunications, (bio)sensing and infrared optics, e.g. programmable infrared detectors, emitters and reconfigurable holograms.
Similar content being viewed by others
Introduction
Many recent technological advances in key areas like telecommunication, lighting, health care, and solar energy harvesting have benefited from increasing control over light. Confining light waves to ever-smaller length scales and thus overcoming Abbe’s diffraction limit enables ultracompact optical components1. Plasmonics achieves this goal by employing evanescent electromagnetic modes supported by metallic nanostructures to concentrate light fields to deeply subwavelength regions2,3. Arranging plasmonic nanoantennas (“meta-atoms”) in subwavelength assemblies in so-called metasurfaces allows for realizing ultrathin optical devices with exciting functionalities like beam steering4, lensing5,6, and holography7,8. While these functionalities are originally fixed upon fabrication, they can be rendered active by multiple means including antenna geometry change by mechanical deformation9,10,11, charge carrier tuning by electric biasing12,13, and inducing an insulator-metal transition in VO2 by heating14,15,16,17. All of these tuning mechanisms are volatile, i.e., they only persist as long as an external stimulus is provided. In contrast, phase-change materials (PCMs) offer non-volatile tuning. Because of the huge property contrast between their amorphous and crystalline phases resulting from a unique bonding mechanism18,19,20,21, they enable exciting tuneable functionalities like waveguiding22,23,24, chemical sensing25, light detection26, and emission27, as well as lensing28. This makes them prime candidates for non-volatile nanophotonic applications such as integrated optical memories, color displays, or active metasurfaces1,29. The resonance wavelength of antennas in metasurfaces is approximately proportional to the effective refractive index of the antennas’ dielectric environment and size. So far, PCMs have been used in active metasurfaces29,30 to change the effective refractive index of the dielectric environment, leading to significant resonance shifts31,32. While PCMs have been successfully used previously to directly optically write dielectric antennas in thin PCM films33,34,35, the plasmonic properties of typical PCMs have only recently been reported36,37. However, they are limited to the near-infrared spectral range by the materials’ band gap, leaving the full infrared spectral range unexplored, up to now. By employing the next-generation non-volatile plasmonic PCM In3SbTe2 (IST)38,39, we tap here into this unfulfilled potential for PCMs for infrared plasmonics. IST is a semiconductor in the amorphous phase (aIST) but becomes metallic with negative permittivity in the whole-infrared range in the crystalline phase (cIST)40. Compared with other alternative plasmonic materials41,42, IST’s optical properties can be optically and locally switched. Thus, we propose a programmable nanophotonics material platform in the infrared based on it.
After comparing IST with common PCMs, we show how to write and erase plasmonic antenna arrays by optical switching on the single meta-atom level. Additionally, we demonstrate flexible antenna reconfiguration on the sub-meta-atom level by elongating, shortening and cutting individual rod antennas in half, causing significant resonance shifts. Next, we demonstrate optically tuneable, frequency-selective perfect absorbers based on cIST. Finally, we demonstrate how IST can be used together with conventional, prepatterned plasmonic metasurfaces to either screen individual antennas from incident light or to “solder” them together. Our concepts could lead towards fast and simple fabrication of plasmonic metasurfaces. Moreover, they can empower programmable functionalities of plasmonic devices for infrared optics, sensing and telecommunications. One could devise, for example, real-time (bio)sensing, in-situ pixel reprogramming of infrared detectors and displays, tuneable localized optical heating, and delicate post-fabrication metasurface adjustments to correct fabrication errors or minutely adapt the functionality (e.g., realizing ultracompact adaptive optics43).
Results
The phase-change material IST
PCMs are characterized by a significant change of their optical properties upon crystallization, which has been attributed to a change in bonding mechanism. Amorphous phase-change materials show the characteristic features of covalently bonded materials (moderate optical dielectric constant ε∞, low electrical conductivity and an atomic arrangement compatible with the 8-N rule20) like Phosphor and GaAs. Covalently bonded materials share about two electrons between adjacent atoms and are therefore located in the red shaded region of the bonding map44 in Fig. 1a (for a more detailed map see Supplementary Fig. 1 and its description). Crystalline phase-change materials such as GeTe, Sb2Te3 and Ge2Sb2Te5 (also called “incipient metals”20) on the contrary are characterized by an unconventional bonding mechanism coined metavalent bonding18,21,45 where about one electron is shared between adjacent atoms. Hence, ordinary phase-change materials like GeSbTe (GST) compounds are all located in the green shaded region of the map (see e.g., the denoted area between GeTe and Sb2Te3).
Remarkably now, crystalline IST has even less electrons shared between adjacent atoms40 and the electrons are significantly delocalized, more akin to a metal (blue shaded region in the map). The conductivity of IST at about 104 S/cm46 is correspondingly also about 10–1000 times larger than that of crystalline GST47. This metal-like conductivity in the crystalline state leads to a very different change of optical properties upon crystallization and the potential to exploit extraordinary functionalities, as will be shown below. While GST compounds can be classified as “incipient metals”, IST belongs to the material class of non-volatile “bad metals”48, which form a bridge between the common PCMs and metals. Here, we reveal the opportunities offered by this interesting material class and IST especially for programmable infrared nanophotonics. To emphasize this potential, we denote IST as a plasmonic PCM.
The delocalization of electrons in the metavalent bond results in an increased polarizability and thus larger permittivity of common PCMs in their crystalline phase than in their covalently bound amorphous phase. This significant difference in permittivity can also be observed in Fig. 1b, where the real part of the permittivity ε‘ at 2.5 µm is plotted for several PCMs49 (see Supplementary Fig. 3 for more detailed permittivity plots). PCMs like GST compounds have a real permittivity ε‘ ≈ 10–20 in the infrared spectral range in their amorphous structural phase, with a negligible imaginary part. Upon crystallization, ε‘ increases by a factor of about two because of the change in bonding. These PCMs are semiconductors in both phases50 and the real part of their permittivity stays positive, ε‘ > 0, in this spectral region.
However, for crystalline IST the case is different: Because the electrons are delocalized similar to free electrons in a metal, IST changes from a semiconductor to a (bad) metal51 upon crystallization, exhibiting a change of the sign of the real part of the permittivity ε‘ from positive to negative (blue point in Fig. 1b). In Fig. 1c, the Drude-like permittivity of crystalline IST (blue) is evident (zero-transition at about 900 nm, see Supplementary Fig. 2) when compared to the permittivity of Ge3Sb2Te6 (GST-326).
The marked difference of optical properties in the crystalline phase between IST and other PCMs gives access to different antenna resonance tuning mechanisms. Instead of changing the refractive index Δn of an antenna’s dielectric surrounding, IST can be used to directly change the antenna size by Δl or even totally change the antenna shape itself. While the large refractive index change has been shown to be a powerful tool, it is limited by the naturally occurring refractive indices of PCMs (as mentioned, they are usually about twice as large in the crystalline phase than in the amorphous phase). In addition, the antenna is often not completely surrounded with PCM but, e.g., lies on a substrate, effectively lowering the influence of the PCM’s refractive index change. In contrast, there is almost no limit to the antenna reconfigurations that can be facilitated by IST: Even subdiffraction switching becomes possible when combining crystallizing and amorphizing pulses. Thus, the accessible degrees of freedom for designing infrared properties of antennas significantly exceeds that available with other PCMs.
As exploited by previous studies36,37, other PCMs, like GeSbTe compounds, usually also have a small spectral window (mostly in the VIS-NIR) where ε‘ < 0 due to interband transitions at energies larger than the band gap energy. Because the charge carriers are not sufficiently delocalized, however, their permittivity does not follow the typical form of the Drude model and stays close to zero there. As a measure for a material’s plasmonic performance in nanoresonators52, in Fig. 1d we calculated the Q factors of rod antennas in free space made from different materials (see Supplementary Fig. 4 for the optical properties). The Q factor is defined as Q = ν/FWHM, where ν is the resonance frequency. Common metals like Al and Ag have Q factors of about 6. It is noteworthy that Al has a slightly larger Q factor compared to Ag due to its smaller skin depth in the infrared (7.7 nm for Al and 11 nm for Ag at a wavelength of 2.5 µm). The Q factor for IST is about 4, which is significantly larger than that of VO2 and still slightly larger than that of TiN and AZO (alternative metals41). Not only for localized but also for propagating surface plasmon polaritons, IST has a superior figure of merit compared to GST in the interband transition region and VO2 (see Supplementary Fig. 5).
Active infrared metasurfaces based on PCMs can be switched between multiple operation states via heating26,28, or short electrical53 and optical pulses33,34,54,55,56,57. The electrical and optical switching of IST has been studied previously in the contexts of nanowires58 and data storage39, respectively. In the latter study, it was demonstrated that IST can be optically switched without phase separation on short time scales (about 50 ns). Optical addressing has recently been used with GeSbTe alloys to fabricate thin-film dielectric metasurfaces33,34 and to program individual meta-atoms in prepatterned PCM-incorporating metallic55 and dielectric metasurfaces56. Going one step further, it is now possible to directly write and erase metallic elements on and below the meta-atom level in a metasurface containing a thin IST film by nanosecond laser pulses. Compared to conventional lithography, no cumbersome additional steps like lift-off or etching are required and the whole metasurface can be erased and rewritten fast and easily at any time. This vastly expands the possibilities of how PCMs can be employed in active metasurfaces.
Optical writing and erasing of plasmonic nanoantennas
As a platform for the following applications, we investigated how to write and erase plasmonic nanostructures on the meta-atom level in a thin film of 50-nm thick aIST on a CaF2 substrate (see Fig. 2). To prevent oxidization and ablation, the IST layer is capped with a 70-nm thick layer of (ZnS)80:(SiO2)20 (see Fig. 2a). A light micrograph of an optically written cIST nanoantenna array is shown in Fig. 2b. A pulsed laser with a wavelength of 660 nm was used for switching (see Methods). The bottom half of the array is replaced with the image of the erased array, where the cIST of each antenna was reamorphized. As shown, only a faint shadow of the antennas is left after erasing. The measured transmittance spectra of the written and erased arrays are shown in Fig. 2c. A clear resonance dip at λ = 4.66 µm is visible in the written state (red), whereas the resonance is completely gone in the erased state and almost unity transmittance is obtained (blue). To demonstrate the performance over several switching cycles, the transmittance at λ = 4.66 µm is plotted for the first 20 switching steps in Fig. 2d. It consistently switches between about 0.65 in the written state (bottom axis) and about 1 in the erased state (top axis). Finally, the written, erased and rewritten cIST nanoantennas are characterized by several microscopy methods (see Fig. 2e): light microscopy (LM), atomic force microscopy (AFM), and scattering-type near-field optical microscopy (s-SNOM, see Methods). The top row contains a sketch of the three switching states. Below that in the LM image, the written and rewritten cIST antennas are distinguishable as bright areas, whereas the erased antenna is not visible and appears as dark as the rest of the aIST film. The cIST areas appear bright because the real part of its permittivity ε‘ < 0 in the visible spectral range (because of interband transitions), which results in high reflectance in the light microscope. In contrast, aIST has ε‘ > 0 in the visible spectral range and thus reflects much less light. In the AFM topography image, however, all three cases can be discerned. The written and rewritten cIST antennas are visible as depressions in the aIST film (decreased density of crystalline PCMs59), while the erased antenna shows a slight elevation in topography (microbump formation60). With s-SNOM, it is possible to measure the local infrared optical properties of the submicrometer crystalline areas with a resolution that is well below the diffraction limit61. The measured near-field optical amplitude signal s3 at a wavelength of λ = 10.57 µm, referenced to the amplitude signal s3(aIST) of the aIST, is shown in the bottom row of Fig. 2e. Again, only the written and rewritten antennas, i.e., the cIST areas, are visible as bright features. The erased antenna shows the same optical contrast as the surrounding aIST film, confirming the successful reamorphization.
Optical antenna resonance control
After establishing the viable writing and erasing of metallic nanostructures in an IST thin film on the meta-atom level, we performed first proof-of-principle experiments (see Fig. 3) to demonstrate the optical modification of infrared plasmonic antennas on the sub-meta-atom level. This effectively lays the foundation for sub-pixel reconfiguration and pixel-by-pixel programming in plasmonic metasurfaces (1 pixel = 1 meta-atom).
We employed the same layer stack as in Fig. 2a. Rod antennas were arranged in a 20 × 20 µm2 antenna array. After the initial writing, the antenna lengths were subsequently changed by switching the IST at the antenna tips. Figure 3a depicts the measured infrared transmittance spectra of the corresponding antenna arrays (see light microscope images on the right). In each spectrum, a minimum at the resonance wavelength (electric dipole resonance) can be observed as well as smaller features at shorter wavelengths originating from the antenna grating orders. The first antenna resonance lies at 5.7 µm (red). By crystallizing the IST at the antenna tips (see dark gray, dotted ellipse in the top sketch in Fig. 3a), the antennas are elongated and the resonance then gradually redshifts up to a wavelength of 7.9 µm. Next, the antennas were shortened by reamorphizing the IST at the antenna tips (see white, dotted ellipse in the bottom sketch in Fig. 3a). This led to a gradual blueshift from 7.9 µm down to 4.4 µm, totalling a complete tuning range of Δλ = 3.5 µm.
Remarkably, the antennas can be made even shorter via reamorphization than the initial cIST antennas. This results in a significantly shorter resonance wavelength: 4.4 µm instead of 5.7 µm. By overlapping slightly shifted (diffraction-limited) crystallizing and reamorphizing laser pulses, it becomes possible to achieve optically switched structures on a scale below the diffraction limit of the VIS switching laser.
The longest antennas in Fig. 3a (green framed light micrograph) are already almost touching and cannot be elongated further. Longer antennas require a larger array period. Moreover, the amplitude for the shortest antennas is dramatically reduced due to their reduced area-density and cross-section. With our proposed material platform based on IST, it is now possible to completely rearrange the antennas in the array in addition to changing the antenna lengths (see Supplementary Movie 1). Figure 3b displays measured transmittance spectra and light micrographs of corresponding IST antenna arrays (see Methods), demonstrating a tuning range of Δλ = 4.3 µm, which is more than 20% larger than the tuning range achieved for the static array periods in Fig. 3a. The experimental data are in good agreement with numerical simulations of infinite cIST antenna arrays of the same dimensions (see Supplementary Fig. 6).
The large total shift yields a large tuning figure of merit TFOM = Δλ/FWHM ≈ 1.9. Here, the FWHM = 2.3 µm of the smallest antennas was considered in accordance with literature31,62. This is an exceptionally large TFOM value when compared with common GeSbTe compounds, which facilitate resonance shifts of Δλ ≈ 1 µm and TFOM ≲ 1.232. The resonance tuning with IST of Δλ = 4.3 µm also surpasses other tuning concepts based on charge carrier density tuning (graphene63, doped semiconductors64) or on phase-transition materials like VO216, where Δλ ≈ 1–2 µm.
The resonance wavelength (electric dipole) of classic metallic nanorod antennas follows the relation λres = neff2l + δ, where neff is the effective refractive index of the antenna’s dielectric surrounding and δ is a constant offset parameter65. This linear relation is confirmed in Fig. 3c, where the antenna length is plotted against the resonance wavelength. The fit (red line) to the blue data points reveals the relation λres = 1.7·2l + 2.1 µm. Thus, the cIST antennas can be indeed described as plasmonic nanorod antennas. For substrates with a larger refractive index (e.g., about 3.4 for Si instead of 1.4 for CaF2), the effective refractive index neff of the antennas’ dielectric surrounding, and thus their resonance wavelength, is increased. Accordingly, by adjusting the substrate material, one can change the antenna lengths required for a certain spectral resonance position66 and optimize the resonance quality in that wavelength range (see Supplementary Fig. 7). As can be seen from the orange data points in Fig. 3c, the resonance wavelengths of cIST antennas on Silicon are about 2–3 µm larger than on CaF2 for the same antenna lengths and still follow a linear trend over the antenna length. The lower slope of the linear fit is due to Silicon’s larger refractive index. Moreover, the dipole antenna characteristics of the cIST antennas could be confirmed with numerical field simulations of the electric, magnetic and current density fields. Compared to gold antennas of the same dimensions, the field distributions are strikingly similar (see Supplementary Fig. 8).
Modifying cIST nanoantennas is not limited to adding or removing cIST at the antenna ends. In Fig. 3d, it is demonstrated that one can also directly access and modify the interior of individual antennas (meta-atoms). As depicted in the sketch (white dotted ellipse), the long nanorod antennas (red frame) were “cut through” in the middle by a reamorphizing pulse, resulting in two smaller rod antennas for each previous long antenna (blue frame). The measured transmittance spectra also reflect this with a blueshift of the resonance by 2.7 µm from 8.2 µm to 5.5 µm. This is only exemplary for the freedom given for design and modification of nanostructures in our introduced platform. One can switch the IST differently in each individual meta-atom and for instance write a metasurface where the antenna lengths increase along the array (see Supplementary Fig. 9a). Going beyond the modification of simple rod antennas, one can also write freeform shapes (see Supplementary Fig. 9b), as well as more complex resonator structures like split ring resonators by combining writing and erasing laser pulses (see Supplementary Fig. 10).
The creation of more complex structures also allows to access different resonance modes and to change between them: As shown, one can switch from a single electrical dipole to either two coupled electrical dipoles (cut nanorod) or to a magnetic dipole (split ring resonator). Higher-order modes like quadrupole resonances could also become attainable by reshaping or coupling of individual resonators.
Optical writing of frequency-selective infrared absorbers
In another proof-of-principle experiment for optically written plasmonic IST metasurfaces, we fabricated a frequency-selective IR absorber (see Fig. 4). First, a 100-nm thick Au mirror is evaporated onto a Si substrate. On top of that, 230 nm (ZnS)80:(SiO2)20, 115 nm aIST, and 70 nm (ZnS)80:(SiO2)20 are deposited (Fig. 4a). According to the previously discussed concepts of optical writing, metallic cIST grating bars of variable width w and period p can be directly written into the unstructured layer stack (cf. Fig. 4b). The metallic bars and the Au bottom mirror form a resonant infrared absorber system. Because of the Au mirror, there is 0 transmittance and the difference of the reflectance R to unity equals the absorptance A = 1 − R. Moreover, absorption and emission are linked by Kirchhoff’s law of thermal radiation. Thus, good infrared absorbers are also good thermal emitters67. In our experiment, we set the period to p = 2 µm and varied w between 470 and 900 nm by adjusting the switching laser pulse duration. The incident infrared light was polarized perpendicularly to the bars. In the measured reflectance spectra (Fig. 4c), there is a reflectance minimum at wavelengths larger than 5 µm (magnetic resonance) and 2 significant minima at wavelengths smaller than 5 µm (thin-film resonances). The magnetic resonance is created by the oscillating charges in the cIST at the top and their mirror image in the Au at the bottom. When increasing the bar width w from 470 to 900 nm, one can now continuously spectrally tune the reflectance minimum associated with the magnetic resonance between about 5 and 8 µm. The minimum reflectance is always smaller than 15% and for w = 0.8 µm (green), it almost reaches down to 10%. This corresponds to a maximum absorptance of A ≈ 90 % and the tuning enables an absorptance modulation of up to 65%.
In Fig. 4c, the crystallization depth d is plotted against the bar width w. It is determined by a comparison of minimum reflectance between simulations and measurements. The simulated spectra (Fig. 4d) only fit well to the measured spectra if a vertical extent of the cIST bars is assumed that is smaller than the total aIST film thickness (inset in Fig. 4a). The existence and importance of this crystallization depth d for resonance tuning of GST-covered nanoantennas by optical switching has been demonstrated just recently55,68. Due to different thermal properties of the layers above and below the aIST layer, a temperature gradient arises from top to bottom. Because the temperature is highest at the top (air is a bad thermal conductor), crystallization starts there and then proceeds downwards. Experimentally, the different crystallization depths are realized by using increasing laser pulse durations for increasing cIST bar widths w (cf. Methods). The optical heating for longer times then allows for crystallization deeper into the aIST layer, resulting in larger crystallization depths. For the given absorber structure, the crystallization depth is an important parameter because it not only defines the total crystallized volume but also the distance between the plasmonic structures and the metallic back-mirror, which is directly related to their electromagnetic coupling and the resulting magnetic dipole moment. Only by optimizing the crystallization depth, the absorptance can be maximized to close to 100% for a given layer stack (see Supplementary Fig. 11).
Our frequency-selective IR absorber design has great potential for thermal imaging applications (see Supplementary Fig. 12) and leads the way towards optical programming of light absorbers26 for infrared color, both for detection and emission. This might for example be employed for programmable simultaneous thermal infrared invisibility and holographic illusion69.
Nanoscale screening and soldering
So far, we have used unpatterend IST thin-films to directly optically write tuneable plasmonic antennas and active metasurfaces. In a different approach, one can also use IST to adjust prepatterned metallic antennas. Then, IST can either work like a nanoscale screen on the meta-atom level or like a “solder” for metallic nanostructures on the sub-meta-atom level. A similar concept, though designed for large-area tuning, has very recently also been demonstrated with the volatile phase-transition material VO270.
Generally, each individual nanoantenna in an IST-coated metasurface can be permanently switched off (antennas not excited) and on (antennas excited) by optically switching the IST above the antennas. In the crystalline state, the cIST area acts like a mirror, which screens the antenna from the incident light and thus prevents antenna excitation. This is demonstrated here for the case of an IST-coated Al slit antenna array on a Si substrate (see Fig. 5a). In Fig. 5b, measured reflectance spectra are plotted for three different switching states: the default on-state (red), the off-state with cIST above the slits (blue) and the restored on-state with reamorphized IST above the slits (green). In the two on-states, there is a distinct reflectance minimum (slit resonance), whereas it is gone in the off-state. In Fig. 5c, the corresponding light micrographs are displayed. Please note that the resolution of these images is limited by diffraction and that the shape of the slits does not change because of the switching.
Until now, the switching of IST was performed optically and was therefore limited by diffraction of the red light of the switching laser. In case the IST needs to be switched at even smaller scales, it can be prepatterned with nanofabrication methods like electron beam lithography. In this way, ultrasmall IST switches can be strategically arranged on a metasurface and selectively toggled between dielectric and metallic optical properties at the sub-meta-atom level. As an application, we show how the two rods in a gold dimer antenna can be conductively connected by a small patch of IST positioned in the dimer gap (Fig. 5d). Thus, two neighbouring, separated nanoantennas can be turned into a single long nanoantenna. The results of such switching for a dimer antenna array with IST-bridged 100 nm dimer gaps are shown in the transmittance measurements in Fig. 5e. There, 50-nm thick IST and 10-nm thick ZnS:SiO2-capping are deposited exclusively at the 100 nm dimer gap of 150-nm wide, 30-nm thick Au antennas of different lengths l and period p = 2.4 l. The aIST was then crystallized by heating on a hotplate (see Methods). In the plotted transmittance spectra, the spectral redshift of the transmittance minimum (resonance) from aIST (solid lines) to cIST (dashed lines) patches is observable for each length l. This resonance shift resulting from the conductive connection between the dimer antennas becomes larger with increasing l. For l = 600 nm, it is about 600 nm large, which corresponds to a tuning figure of merit of about 0.7. Here, the resonance shift would originally be even larger, but the Au antenna lengths decreased after annealing in the oven (see Supplementary Fig. 13a). The kink in the spectra at smaller wavelengths results from grating resonances and thus stays at the same wavelength after switching the IST because the array periodicity is conserved even though the antenna lengths slightly decrease. The resonance shift will generally increase even more for longer antennas and larger gaps (cf. Supplementary Fig. 13b). The topography and near-field optical contrast (measured with s-SNOM at a wavelength of λ = 10.57 µm) of a dimer with 600 nm long antennas and a cIST patch are depicted in Fig. 5f. In both images, it is visible that the cIST patch in the dimer gap overlaps with both antennas. Notably, the near-field contrast of the cIST patch and the Au antennas is the same in the bottom image, which signifies similar optical properties. This underlines again the metallic infrared optical properties of crystalline IST.
Multiple potential nanoantenna geometries can now be encoded on a single metasurface with strategically positioned IST patches and then switched between by nanoscale soldering. On the one hand, this allows for minor adjustments, which is, e.g., important for compensating tight fabrication tolerances and for adaptive optics43. On the other hand, one can also realize major reconfigurations like a total change of functionality, e.g., between beam focusing and beam steering. Please note that the switching of prepatterned IST structures is not limited to optical laser pulses but can also be achieved via electrical voltage pulses58.
Discussion
We introduced the next-generation, switchable, infrared plasmonic phase-change material In3SbTe2 (IST) as a material platform for programmable plasmonics and nanophotonics in the infrared. On the meta-atom level, we demonstrated direct writing and erasing of metallic crystalline IST (cIST) nanoantennas into a dielectric amorphous IST (aIST) thin film for 20 switching steps and characterized them by diffraction-limited far-field as well as super-resolution near-field measurement techniques. On the sub-meta-atom level, we demonstrate flexible antenna reconfiguration by elongating, shortening and cutting individual rod antennas in half, tuning the infrared plasmonic antenna resonances by more than 4 µm. Subsequently, a tuneable broad-band infrared absorber with absorptance of nearly 90%, a mid-infrared spectral tuning range of about 3 µm and an absorption amplitude tuning range of about 65% was shown. Nanoscale screening of prepatterned antennas with a thin IST film results in an on/off functionality, while strategically positioned IST patches allow for nanoscale “soldering” of individual meta-atoms.
These concepts are fundamentally impossible to achieve with common dielectric PCMs (e.g., GeSbTe alloys). In addition to a large resonance tuning, IST enables the creation of complex plasmonic structures with different resonance modes. The optical switching can be easily scaled up and parallelized (e.g., by laser interference lithography) towards large-area fabrication with high throughput. Our work thus lays the foundation for a programmable nanophotonics material platform for the infrared. It also holds great potential for application in integrated photonics, where, reconfigurable plasmonic components for, e.g., routing, waveguiding and filtering are now made possible by optically or electrically switched IST elements. The extension of our frequency-selective near-perfect IR absorber could lead towards real-time biosensing or the in-situ reprogramming of infrared detectors and displays working in absorption or emission mode.
A thin IST layer on top of negative permittivity materials that host surface waves such as polar crystals (phonon polariton) or doped semiconductors (plasmon polariton) could enable the writing of nanophotonic elements for polaritons like deeply subwavelength resonators or waveguides17,34,71,72. Composing dielectric metasurfaces56,57,73,74,75 out of amorphous IST could enable the switching from narrow Mie resonances to broad plasmonic resonances. Finally, the non-volatile switching of IST could be combined with the dynamic, volatile tuning methods offered by materials like VO2, leading to interesting functionalities like multilevel, intelligent switches76,77.
Methods
Sample fabrication
In3SbTe2 (IST) was deposited on the substrates by direct current magnetron sputtering, while (ZnS)80:(SiO2)20 was deposited with radio frequency magnetron sputtering. A LS 320 von Ardenne systems (base pressure 2 ∙ 10−6 mbar, 20 s.c.c.m. Ar flow, deposition rates 1 Å/s for IST and 0.3 Å/s for ZnS:SiO2) was operated in constant power mode (24 W for IST and 59 W for ZnS:SiO2) using stoichiometric targets of 99.99% purity. The Al slit antennas were fabricated by first thermally evaporating Aluminum (2 Å/s, 2 × 10−5 mbar base pressure) onto a Si substrate and then patterning the Al thin film with focused ion beam milling with a Helios NanoLab DualBeam 650 by FEI company (30 kV acceleration voltage, 83 pA beam current, 3 µs dwell time). The gold dimer antennas with IST in their gaps were fabricated by two-step electron beam lithography with PMMA as resist and Electra92 as conductive polymer. In the first step, gold was evaporated onto the patterned resist. After a lift-off process, the gold dimer antennas are left on the glass substrate. In the second step, the resist was only patterned in the gaps of the dimers. Onto this patterned resist, 50 nm IST and 10 nm (ZnS)80:(SiO2)20 were sputtered (see above). After another lift-off process, the finished gold dimers with IST in their gaps are left on the glass substrate.
Switching of IST
The localized phase change of the IST thin-films was realized with an in-house-built laser setup55. A pulsed laser beam (wavelength λ = 660 nm) is focused through a 10-fold objective with a numerical aperture of 0.5 on the sample surface. The sample is placed on a Thorlabs NanoMax-TS (Max311/M) stage, which is movable in x-, y-, and z-direction and connected to a Thorlabs closed-loop piezo controller (BPC303). A custom program allows for the automated positioning of pulsed laser shots on the sample surface within 5 nm accuracy. By using long (~500 ns) and low-powered (~10 mW) laser pulses, an IST thin film can be locally crystallized by heating it above the glass transition temperature. The crystallized area has an elliptical shape, whose size can be tuned by changing the laser parameters (pulse power, pulse duration and number of pulses)55, see e.g., Supplementary Fig. 7b. By using short (~20 ns) and high-powered pulses (~300 mW), the crystalline PCM can be melted locally by heating it above the melting temperature, after which a rapid cooling (>109 K/s) yields amorphization. The laser pulse parameters [power, duration, number of pulses] for Fig. 2 are [7.2 mW, 500 ns, 1000] for crystallization and [281 mW, 10 ns, 1] for reamorphization. For Fig. 3a, the laser pulse parameters are [8.2 mW, 500 ns, 1000] for crystallization and [205 mW, 10 ns, 1] and the array periods are [px, py] = [2.2 µm, 3.5 µm]. For Fig. 3b, the laser pulse parameters are [7.2 mW, 500 ns, 1000] and the antenna array dimensions [l, px, py] in µm are measured by light microscopy and given as [0.9, 2.1, 1.8], [1.4, 2.9, 2.2], [1.7, 3.8, 2.6] and [2.1, 4.7, 3.0]. For Fig. 3c, the laser pulse parameters are [8.2 mW, 500 ns, 1000] for crystallization and [182.3 mW, 10 ns, 1] for reamorphization the array periods are [px, py] = [2.2 µm, 3.5 µm]. In Fig. 4, the employed laser pulse power is 0.4 mW, the number of pulses is 500 and the pulse durations for the respective bar widths are: 250 ns for w = 0.47 µm, 310 ns for w = 0.65 µm, 340 ns for w = 0.8 µm, and 370 ns for w = 0.9 µm. The switching parameters for screening the slits in Fig. 5a, b are [53.5 mW, 1000 ns, 150] for crystallization and [394.5 mW, 10 ns, 1] for reamorphization. For crystallizing the IST patches in the dimer gaps in Fig. 5c–e, the sample was heated uniformly on in an oven at 250 °C for 30 min.
FTIR spectroscopy
The Fourier transform infrared (FTIR) spectroscopy data were collected using a Bruker Vertex 70 interferometer coupled to a Bruker Hyperion 2000 microscope. The FTIR measurement parameters for the data from the Figures is as follows: 1000 scans with 16 cm−1 spectral resolution for Figs. 2, 3, and 5; 2000 scans with 32 cm−1 spectral resolution for Fig. 4. For the measurements from Figs. 3 and 4, ×15 Cassegrain objectives were used, for all the other measurements ×36 objectives. The area around the antenna arrays was excluded from the measurement with knife edge apertures and the polarization was along the long antenna axes in Figs. 2, 3, and 5e, and perpendicular to the grating bars and slits in Figs. 4 and 5b, respectively. For all measurements the free area on the sample next to the antenna arrays was used as a reference, except for those in Fig. 4, for which reflectance at an Au mirror was taken as reference.
Scattering-type scanning near-field optical microscope (s-SNOM) measurements
Our s-SNOM system (Neaspec GmbH) is based on a tapping-mode AFM. The metallized AFM tip (radius ∼25 nm) vibrates with an amplitude of ~40 nm at a tapping frequency Ω ≈ 235–250 kHz. This oscillating tip is illuminated by light from a CO2 gas laser at 10.57 µm and the backscattered light from the tip is collected. To suppress background scattering, the detector signals are demodulated at a higher harmonic nΩ(n ≥ 2). By means of pseudo-heterodyne interferometric detection78, the near-field optical amplitude sn and phase φn are obtained. For measurements in Fig. 2, the signals were referenced to the aIST film next to the crystalline spots and demodulated at 3Ω. For measurements in Fig. 5, the signals were referenced to the gold of the dimer antennas and demodulated at 2Ω.
Simulations
Full-wave 3D simulations have been performed using a commercial solver, CST Studio Suite. Excitation by Floquet Mode Ports has been used to model the experiment setup and to calculate the spectra. Periodic boundary conditions have been used in the lateral directions. Spectra for angles of incidence between 8° and 24° were calculated and averaged according to the intensity distribution of the ×15 Cassegrain objective. The permittivity of IST is shown in Supplementary Fig. 2. For ZnS:SiO2, a constant refractive index of about 2.1 and for CaF2 a constant refractive index of 1.4 were assumed.
Data availability
All data needed to evaluate the conclusions in the paper are present in the paper or the supplementary materials. The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Wuttig, M., Bhaskaran, H. & Taubner, T. Phase-change materials for non-volatile photonic applications. Nat. Photon. 11, 465–476 (2017).
Gramotnev, D. K. & Bozhevolnyi, S. I. Plasmonics beyond the diffraction limit. Nat. Photon. 4, 83–91 (2010).
Meinzer, N., Barnes, W. L. & Hooper, I. R. Plasmonic meta-atoms and metasurfaces. Nat. Photon. 8, 889–898 (2014).
Kildishev, A. V., Boltasseva, A. & Shalaev, V. M. Planar photonics with metasurfaces. Science 339, 1232009 (2013).
Yu, N. & Capasso, F. Flat optics with designer metasurfaces. Nat. Mater. 13, 139–150 (2014).
Prämassing, M. et al. Freestanding metasurfaces for optical frequencies. Opt. Lett. 44, 2105 (2019).
Zheng, G. et al. Metasurface holograms reaching 80% efficiency. Nat. Nanotechnol. 10, 308–312 (2015).
Ni, X., Kildishev, A. V. & Shalaev, V. M. Metasurface holograms for visible light. Nat. Commun. 4, 2807 (2013).
Ou, J. Y., Plum, E., Jiang, L. & Zheludev, N. I. Reconfigurable photonic metamaterials. Nano Lett. 11, 2142–2144 (2011).
Lapine, M., Shadrivov, I. V., Powell, D. A. & Kivshar, Y. S. Magnetoelastic metamaterials. Nat. Mater. 11, 30–33 (2012).
Ee, H.-S. & Agarwal, R. Tunable metasurface and flat optical zoom lens on a stretchable substrate. Nano Lett. 16, 2818–2823 (2016).
Huang, Y.-W. et al. Gate-tunable conducting oxide metasurfaces. Nano Lett. 16, 5319–5325 (2016).
Sherrott, M. C. et al. Experimental demonstration of >230° phase modulation in gate-tunable graphene–gold reconfigurable mid-infrared metasurfaces. Nano Lett. 17, 3027–3034 (2017).
Dicken, M. J. et al. Frequency tunable near-infrared metamaterials based on VO2 phase transition. Opt. Express 17, 18330–18339 (2009).
Driscoll, T. et al. Memory metamaterials. Science 325, 1518–1521 (2009).
Kats, M. A. et al. Thermal tuning of mid-infrared plasmonic antenna arrays using a phase change material. Opt. Express 38, 368 (2013).
Folland, T. G. et al. Reconfigurable infrared hyperbolic metasurfaces using phase change materials. Nat. Commun. 9, 4371 (2018).
Wuttig, M. & Yamada, N. Phase-change materials for rewriteable data storage. Nat. Mater. 6, 824–832 (2007).
Raty, J.-Y. et al. A quantum-mechanical map for bonding and properties in solids. Adv. Mater. 31, 1806280 (2018).
Wuttig, M., Deringer, V. L., Gonze, X., Bichara, C. & Raty, J.-Y. Incipient metals: functional materials with a unique bonding mechanism. Adv. Mater. 30, 1803777 (2018).
Zhu, M. et al. Unique bond breaking in crystalline phase change materials and the quest for metavalent bonding. Adv. Mater. 30, 1706735 (2018).
Rudé, M., Simpson, R. E., Quidant, R., Pruneri, V. & Renger, J. Active control of surface plasmon waveguides with a phase change material. ACS Photonics 2, 669–674 (2015).
Passler, N. C., Heßler, A., Wuttig, M., Taubner, T. & Paarmann, A. Surface polariton-like s-polarized waveguide modes in switchable dielectric thin films on polar crystals. Adv. Opt. Mater. 8, 1901056 (2019).
Rios, C., Hosseini, P., Wright, C. D., Bhaskaran, H. & Pernice, W. H. P. On-chip photonic memory elements employing phase-change materials. Adv. Mater. 26, 1372–1377 (2014).
Bakan, G., Ayas, S., Ozgur, E., Celebi, K. & Dana, A. Thermally tunable ultrasensitive infrared absorption spectroscopy platforms based on thin phase-change films. ACS Sens. 1, 1403–1407 (2016).
Tittl, A. et al. A switchable mid-infrared plasmonic perfect absorber with multispectral thermal imaging capability. Adv. Mater. 27, 4597–4603 (2015).
Qu, Y. et al. Dynamic thermal emission control based on ultrathin plasmonic metamaterials including phase-changing material GST. Laser Photon. Rev. 11, 1700091 (2017).
Yin, X. et al. Beam switching and bifocal zoom lensing using active plasmonic metasurfaces. Light Sci. Appl. 6, e17016 (2017).
Ding, F., Yang, Y. & Bozhevolnyi, S. I. Dynamic metasurfaces using phase-change chalcogenides. Adv. Opt. Mater. 7, 1801709 (2019).
Gholipour, B., Zhang, J., MacDonald, K. F., Hewak, D. W. & Zheludev, N. I. An all-optical, non-volatile, bidirectional, phase-change meta-switch. Adv. Mater. 25, 3050–3054 (2013).
Michel, A.-K. U. et al. Using low-loss phase-change materials for mid-infrared antenna resonance tuning. Nano Lett. 13, 3470–3475 (2013).
Michel, A.-K. U., Wuttig, M. & Taubner, T. Design parameters for phase-change materials for nanostructure resonance tuning. Adv. Opt. Mater. 5, 1700261 (2017).
Wang, Q. et al. Optically reconfigurable metasurfaces and photonic devices based on phase change materials. Nat. Photon. 10, 60–65 (2016).
Li, P. et al. Reversible optical switching of highly confined phonon-polaritons with an ultrathin phase-change material. Nat. Mater. 15, 870–875 (2016).
Dong, K. et al. A lithography-free and field-programmable photonic metacanvas. Adv. Mater. 30, 1703878 (2018).
Ahmadivand, A., Gerislioglu, B., Sinha, R., Karabiyik, M. & Pala, N. Optical switching using transition from dipolar to charge transfer plasmon modes in Ge2Sb2Te5 bridged metallodielectric dimers. Sci. Rep. 7, 42807 (2017).
Gholipour, B. et al. Phase-change-driven dielectric-plasmonic transitions in chalcogenide metasurfaces. NPG Asia Mater. 10, 533–539 (2018).
Kim, E. T., Lee, J. Y. & Kim, Y. T. Investigation of electrical characteristics of the In3Sb1 Te2 ternary alloy for application in phase-change memory. phys. Stat. Sol. (RRL) 3, 103–105 (2009).
Maeda, Y., Andoh, H., Ikuta, I. & Minemura, H. Reversible phase‐change optical data storage in InSbTe alloy films. J. Appl. Phys. 64, 1715–1719 (1988).
Deringer, V. L. et al. A chemical link between Ge–Sb–Te and In–Sb–Te phase-change materials. J. Mater. Chem. C. 3, 9519–9523 (2015).
Naik, G. V., Shalaev, V. M. & Boltasseva, A. Alternative plasmonic materials: beyond gold and silver. Adv. Mater. 25, 3264–3294 (2013).
Zhong, Y., Malagari, S. D., Hamilton, T. & Wasserman, D. M. Review of mid-infrared plasmonic materials. J. Nanophoton. 9, 093791 (2015).
Tyson, R. Principles of Adaptive Optics (CRC Press, 2010).
Kooi, B. J. & Wuttig, M. Chalcogenides by design: functionality through metavalent bonding and confinement. Adv. Mater. 32, 1908302 (2020).
Pries, J., Cojocaru-Mirédin, O. & Wuttig, M. Phase-change materials: empowered by an unconventional bonding mechanism. MRS Bull. 44, 699–704 (2019).
Rausch, Pascal. Investigations of binary and ternary phase change alloys for future memory applications. Dissertation, RWTH Aachen University. (2012).
Siegrist, T. et al. Disorder-induced localization in crystalline phase-change materials. Nat. Mater. 10, 202–208 (2011).
Hartnoll, S. A. Theory of universal incoherent metallic transport. Nat. Phys. 11, 54–61 (2015).
Shportko, K. et al. Resonant bonding in crystalline phase-change materials. Nat. Mater. 7, 653–658 (2008).
Yáñez-Limón, J. M., González-Hernández, J., Alvarado-Gil, J. J., Delgadillo, I. & Vargas, H. Thermal and electrical properties of the Ge:Sb:Te system by photoacoustic and Hall measurements. Phys. Rev. B. 52, 16321–16324 (1995).
Schröder, T. et al. Disorder and transport properties of In3SbTe2—an X-ray, -neutron and electron diffraction study: disorder and transport properties of In3SbTe2. Z. Anorg. Allg. Chem. 639, 2536–2541 (2013).
Piccinotti, D. et al. Stoichiometric engineering of chalcogenide semiconductor alloys for nanophotonic applications. Adv. Mater. 31, 1807083 (2019).
Hosseini, P., Wright, C. D. & Bhaskaran, H. An optoelectronic framework enabled by low-dimensional phase-change films. Nature 511, 206–211 (2014).
Michel, A.-K. U. et al. Reversible optical switching of infrared antenna resonances with ultrathin phase-change layers using femtosecond laser pulses. ACS Photon. 1, 833–839 (2014).
Michel, A.-K. U. et al. Advanced optical programming of individual meta-atoms beyond the effective medium approach. Adv. Mater. 31, 1901033 (2019).
Leitis, A. et al. All-dielectric programmable Huygens’ metasurfaces. Adv. Funct. Mater. 30, 1910259 (2020).
Galarreta, C. R. et al. Reconfigurable multilevel control of hybrid all-dielectric phase-change metasurfaces. Optica 7, 476–484 (2020).
Selmo, S. et al. Low power phase change memory switching of ultra-thin In3Sb1Te2 nanowires. Appl. Phys. Lett. 109, 213103 (2016).
Njoroge, W. K., Wöltgens, H.-W. & Wuttig, M. Density changes upon crystallization of Ge2Sb2.04Te4.74 films. J. Vac. Sci. Technol. 20, 230–233 (2002).
Wang, R., Wei, J. & Fan, Y. Chalcogenide phase-change thin films used as grayscale photolithography materials. Opt. Express 22, 4973–4984 (2014).
Lewin, M. et al. Imaging of phase change materials below a capping layer using correlative infrared near-field microscopy and electron microscopy. Appl. Phys. Lett. 107, 151902 (2015).
Pryce, I. M., Aydin, K., Kelaita, Y. A., Briggs, R. M. & Atwater, H. A. Highly strained compliant optical metamaterials with large frequency tunability. Nano Lett. 10, 4222–4227 (2010).
Yao, Y. et al. Electrically tunable metasurface perfect absorbers for ultrathin mid-infrared optical modulators. Nano Lett. 14, 6526–6532 (2014).
Miao, X. et al. Doping tunable resonance: toward electrically tunable mid-infrared metamaterials. Appl. Phys. Lett. 96, 101111 (2010).
Cubukcu, E. & Capasso, F. Optical nanorod antennas as dispersive one-dimensional Fabry–Pérot resonators for surface plasmons. Appl. Phys. Lett. 95, 201101 (2009).
Hoffmann, J. M. et al. Low-cost infrared resonant structures for surface-enhanced infrared absorption spectroscopy in the fingerprint region from 3 to 13 μm. J. Phys. Chem. C. 117, 11311–11316 (2013).
Watts, C. M., Liu, X. & Padilla, W. J. Metamaterial electromagnetic wave absorbers. Adv. Mater. 24, OP98–OP120 (2012).
Meyer, S., Tan, Z. Y. & Chigrin, D. N. Multiphysics simulations of adaptive metasurfaces at the meta-atom length scale. Nanophotonics 9, 675–681 (2020).
Xie, X. et al. Plasmonic metasurfaces for simultaneous thermal infrared invisibility and holographic illusion. Adv. Funct. Mater. 28, 1706673 (2018).
Audhkhasi, R. & Povinelli, M. L. Design of far-field thermal rectifiers using gold–vanadium dioxide micro-gratings. J. Appl. Phys. 126, 063106 (2019).
Chaudhary, K. et al. Polariton nanophotonics using phase-change materials. Nat. Commun. 10, 4487 (2019).
Fali, A. et al. Refractive index-based control of hyperbolic phonon-polariton propagation. Nano Lett. 19, 7725–7734 (2019).
Karvounis, A., Gholipour, B., MacDonald, K. F. & Zheludev, N. I. All-dielectric phase-change reconfigurable metasurface. Appl. Phys. Lett. 109, 051103 (2016).
Staude, I. et al. Tailoring directional scattering through magnetic and electric resonances in subwavelength silicon nanodisks. ACS Nano 7, 7824–7832 (2013).
Chu, C. H. et al. Active dielectric metasurface based on phase-change medium. Laser Photon. Rev. 10, 986–994 (2016).
Meng, Y. et al. Design of a 4-level active photonics phase change switch using VO2 and Ge2Sb2Te5. Appl. Phys. Lett. 113, 071901 (2018).
Lyu, X. et al. Combining phase-change materials and phase-transition materials for thermally regulated smart mid-infrared modulators. Manuscript in preparation.
Ocelic, N., Huber, A. & Hillenbrand, R. Pseudoheterodyne detection for background-free near-field spectroscopy. Appl. Phys. Lett. 89, 101124 (2006).
Acknowledgements
A.H., S.W., A.A., C.S., and T.T. acknowledge funding from the German Federal Ministry of Education and Research within the funding program Photonics Research Germany (contract number 13N14151). T.L., L.N., and S.L. acknowledge funding from the German Federal Ministry of Education and Research within the funding program Photonics Research Germany (contract number 13N14150). N.E., M.L., T.T., and M.W. also acknowledge funding from the DFG (German Science Foundation) within the collaborative research center SFB 917 “Nanoswitches”. We acknowledge J. Gao and D. Köhn for the sputter deposition of the thin-film layer stacks, and L. Naumann for helping with the electron beam lithography.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
A.H., M.L., T.W.W.M., and T.T. conceived the research idea; A.H., S.L., and T.T. designed the research; A.H., T.L., and L.N. fabricated the samples; A.H., A.A., C.S., and S.W. carried out the optical switching, measurements, and analysed the data; N.E. and M.L. performed the SNOM experiments; A.H. carried out the numerical simulations; C.-F.S. performed the bonding map calculations; M.W. provided the sputtering equipment and phase-change material expertise; and all authors contributed to writing the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Heßler, A., Wahl, S., Leuteritz, T. et al. In3SbTe2 as a programmable nanophotonics material platform for the infrared. Nat Commun 12, 924 (2021). https://doi.org/10.1038/s41467-021-21175-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-21175-7
- Springer Nature Limited
This article is cited by
-
Direct programming of confined surface phonon polariton resonators with the plasmonic phase-change material In3SbTe2
Nature Communications (2024)
-
Programmable nanophotonic planar resonator filter-absorber based on phase-change InSbTe
Scientific Reports (2023)
-
Reconfigurable phase-change metasurfaces from efficient wavefront manipulation to perfect absorption
Journal of Materials Science (2022)
-
Design of hybrid narrow-band plasmonic absorber based on chalcogenide phase change material in the infrared spectrum
Scientific Reports (2021)