Abstract
Synthesis and properties of fusion-cast high-alumina refractories in the Al2O3 – B2O3 system are reported. Adding B2O3 is shown to improve density and fabricability of the fusion-cast products. As shown by x-ray diffractometry and petrographic analysis, the phase composition of synthetic products is represented by corundum and 9Al2O3 ċ 2B2O3 boroaluminate. Corrosion tests in molten industrial glasses have shown the potential use of these materials in the melting technology of VS-92-grade optical lead silicate glass.
Similar content being viewed by others
REFERENCES
V. A. Sokolov, M. D. Gasparyan, S. V. Rudenko, et al., in: 5th All-Union Seminar “Refractory materials for optical glass melting,” Abstracts [in Russian], TsNII Informatsii i TekhnikoÉkonomicheskikh Issledovanii, Moscow (1989), pp. 50–51.
K. H. Kim and F. A. Hummel, “Studies in lithium oxide systems: XII, Li2O3-B2O3-Al2O3,” Am. Ceram. Soc., 45(10), 487–489 (1962).
P. J. Gielisse and W. R. Foster, “The system Al2O3-B2O3,” Nature, 195(7), 69–70 (1962).
H. N. Baumann and C. H. Moore, “Electric furnace boroaluminate,” Am. Ceram. Soc., 25(14), 391–394 (1942).
T. Raymon-Lipinski, H. W. Hennicke, and W. Lingenberg, “Die Reaction von Al2O3 mit B2O3 bei hohen Temperaturen,” Keramische Zeitschrift, 36(11), 601–606 (1984).
V. A. Sokolov, “Effect of modifying additives on the properties of electrofused corundum refractories,” in: 8 Internationale Baustoff-und Silikattagung, Weimar (1982), pp. 142–147.
V. K. Pavlovskii, E. K. Romanova, and A. D. Semenov, “Structure and phase composition of fusion-cast materials in the Al2O3-B2O3 system,” Steklo Keram., No. 11-12, 22–24 (1994).
Inorganic Index to the Powder Diffraction File, ASTM (1967).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sokolov, V.A., Gasparyan, M.D. Synthesis and Properties of Fusion-Cast Refractories in the Al2O3 – B2O3 System. Refractories and Industrial Ceramics 45, 177–180 (2004). https://doi.org/10.1023/B:REFR.0000036725.55824.07
Issue Date:
DOI: https://doi.org/10.1023/B:REFR.0000036725.55824.07