Abstract
The crystallization behavior of Co75-xFexGe15B10 (x=3.0, 4.6 and 6.0) amorphous alloys was monitored by differential thermal analysis and thermo-mechanical analysis. The crystallization process of the melt spun ribbons was interrupted at 450, 525, 650, 800 and 900°C and their microstructures were investigated by X-ray diffractometry. It was observed that the crystallization occurs in a sequential mode attributed to the formation of different types of precipitates. It was shown that the crystallization products change as a function of Fe content. After full crystallization, GeFe, Co3B, FeGe2 and Co2Ge compounds were found as well as a Co rich solid solution.
Similar content being viewed by others
References
J. M. Dubois and G. Le Caer, Acta Metall., (1984) 2101.
K. Chrissafis, J. Therm. Anal. Cal., 73 (2003) 745.
N. Imamura and T. Kobayashi, IEEE Trans. Magn., 12 (1976) 779.
M. N. Baibich, J. M. Broto, A. Fert, F. N. Van Dau and F. Petroff, Phys. Rev. Letter, 61 (1988) 2472.
F. L. Barquín, J. R. Fernández and J. C. Gómez-Sal, J. Magn. Magn. Mater., 83 (1990) 357.
A. D. Santos, A. S. Medici and F. P. Missell, J. Magn. Magn. Mater., 60 (1986) 153.
S. Al Bijat, R. Iraldi, C. Cunat, G. Le Caer, J. M. Dubois and C. Tete, Proc. of the 4th Int. Conf. on Rapidly Quenched Metals, Sendai-Japan 1981.
J. R. Bedell, U. S. Patent No 3 862 658, Jan. 28, 1975.
C. K. N. Oliveira, MS Dissertation, CPGEM/CT/UFPB, João Pessoa, PB, Brasil 1996.
J. J. Suñol, M. T. Clavaguera-Mora and N. Clavaguera, J. Therm. Anal. Cal., 72 (2003) 347.
V. Pearson's and L. D. Calvert, Pearson's Handbook of Crystallographic Data for Intermetallic Phases, ASM, 2 (1985) 1750.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Barroso, M.D.B., Melo, T.A.A., Prasad, S. et al. Crystallization of Co75-xFexGe15B10 amorphous alloys. Journal of Thermal Analysis and Calorimetry 75, 655–660 (2004). https://doi.org/10.1023/B:JTAN.0000027159.35556.57
Issue Date:
DOI: https://doi.org/10.1023/B:JTAN.0000027159.35556.57