Abstract
Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) under constant stirring at 3°C, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470°C, temperature lower than the tetragonal-cubic transition.
Similar content being viewed by others
References
G. Pfaff, J. Mater. Chem., 2 (1992) 591.
K. W. Kirby, Mater. Res. Bull., 23 (1998) 881.
W. S. Cho and E. Hamada, J. All. Comp., 266 (1998) 118.
X. H. Wang, C. Zhao, Z. C. Wang, F. Q. Wu and M. Y. Zhao, J. All. Comp., 204 (1994) 33.
D. Hennings, G. Rosenstein and H. Schreinemacher, J. Eur. Ceram. Soc., 8 (1991) 107.
H. S. Potdar, P. Singh, S. B. Deshpande, P. D. Godbole and S. K. Date, Mater. Lett., 10 (1990) 112.
Y. S. N. Murthy, R. Gopalan, S. Raoot, T. Rajasekharan, S. Ravi and V. S. Bai, Mater. Lett., 9 (1990) 154.
M. Kakihana, J. Sol-Gel Sci. Technol., 6 (1996) 7.
H. W. Wang, D. A. Hall and F. R. Sale, J. Thermal Anal., 42 (1994) 823.
M. S. G. Baythoun and F. R. Sale, J. Mater. Sci., 17 (1982) 2757.
H. W. Wang, D. A. Hall and F. R. Sale, J. Am. Ceram. Soc., 75 (1992) 124.
F. H. Chen, H. S. Koo and T. Y. Tseng, J. Am. Ceram. Soc., 75 (1992) 96.
G. R. Fox, J. H. Adair and R. E. Newnham, J. Mater. Sci., 26 (1991) 1187.
J. A. Davies and S. Utremez, J. Am. Ceram. Soc., 73 (1990) 942.
H. E. Zorel Jr., C. A. Ribeiro and M. S. Crespi, J. Mater. Sci. Lett., 20 (2001) 621.
W. W. Wendlandt, Thermal Analysis, Wiley Interscience, New York 1986.
V. Savostina, F. Lobanov and V. Peshkova, Zh. Neorg. Khim., 12 (1967) 2162.
H. Steger and A. Corsini, J. Inorg. Nucl. Chem., 35 (1973) 1621.
L. S. Guinesi, H. E. Zorel Jr., C. A. Ribeiro and M. S. Crespi, An. Assoc. Bras. Quím., 48 (1999) 221.
M. S. Crespi, H. E. Zorel Jr., C. A. Ribeiro and A. G. C. Costalonga, J. Therm. Anal. Cal., 64 (2001) 783.
M. S. Crespi, H. E. Zorel Jr. and C. A. Ribeiro, J. Therm. Anal. Cal. 72 (2003) 507.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zorel, H.E., Crespi 2, M.S. & Ribeiro, C.A. Attainment of lead titanate. Journal of Thermal Analysis and Calorimetry 75, 545–550 (2004). https://doi.org/10.1023/B:JTAN.0000027144.59771.53
Issue Date:
DOI: https://doi.org/10.1023/B:JTAN.0000027144.59771.53