Abstract
A modified polymeric precursor method based on the Pechini process was used to synthesize β-BaB2O4 (β-BBO) crystalline phase. D-sorbitol (C6H14O6) was used as a polymerizing agent to avoid the loss of boron during the samples' calcination and crystallization. The β-BBO stoichiometric crystalline phase was only obtained when sorbitol was added to the solution. The results of Raman spectroscopy show that the amorphous phase is only completely eliminated when the samples are heat-treated at 750°C for 20 h. Thin films of β-BBO phase displaying a preferred orientation were obtained when crystallized at 750°C for 2 h and deposited on sapphire substrate.
Similar content being viewed by others
References
C.T. Chen, B.C. Wu, A.D. Jiang, and G.M. You, Sci. Sin. Ser. B (Eng. Ed.) 28, 235 (1985).
I. Shoji, H. Nakamura, K. Ohdaira, T. Kondo, R. Ito, T. Okamoto, K. Tatsuki, and S. Kubota, J. Opt. Soc. Am. 16, 620 (1999).
D.B. Studebaker, G.T. Stauf, T.H. Baum, T.J. Marks, H. Zhou, and G.K. Wong, Appl. Phys. Lett. 70, 565 (1997).
H.B. Liao, R.F. Xiao, P. Yu, and G.K.L. Wong, J. Crystal Growth 174, 434 (1997).
S.I. Hirano, T. Yogo, K.I. Kikuta, and K. Yamagiwa, J. Am. Ceramic. Soc. 75, 2590 (1992).
T. Yogo, K. Kikuta, K. Niwa, M. Ichida, A. Nakamura, and S.I. Hirano, J. Sol-gel Sci. Tech. 9, 201 (1997).
T. Kobayashi, R. Ogawa, and M. Kuwabara, Materials Letters 57, 1056 (2003).
R.F. Xiao, L.C. Ng, P. Yu, and G.K.L. Wong, Appl. Phys. Lett. 67(3), 305 (1995).
T. Kobayashi, R. Ogawa, K.I. Miyazawa, and M. Kuwabara, J. Mater. Res. 17(4), 844 (2002).
E.M. Levin and H.F. McMurdie, J. Res. Nat. Bur. Stand. 42(2), 131 (1949).
E.M. Levin and H.F. McMurdie, J. Am. Ceram. Soc. 32(3), 99 (1949).
D. Eimerl, L. Davis, S. Velsko, E.K. Graham, and A. Zalkin, J. Appl. Phys. 62(5), 1968 (1987).
R. Frohlich, Z. Kristallogr, 168, 109 (1984).
Y.Y. Ivanova, E.P. Kashchieva, and Y.B. Dimitriev, Phys. Chem. Glasses 41, 349 (2000).
M.P. Pechini, U.S. Patent No. 3.330.697 (1967).
Joint Commitee for Powder Diffraction Standards, JCPDS Powder Diffraction File, File Card No. [24-0084] (1998).
A. Tapparo, P. Pastore, and G.G. Bombi, Analyst 123, 1771 (1998).
K. Nose and M. Zenki, Analyst 116, 711 (1991).
H.P. Klug and L.E. Alexander, X-Ray Diffraction Procedures (John Wiley & Sons, USA, 1954), p. 491.
P. Ney, M.D. Fontana, A. Maillard, and K. Polgár, J. Phys.: Condens. Matter 10, 673 (1998).
Joint Commitee for Powder Diffraction Standards, JCPDS Powder Diffraction File, File Card No. [24-0087] (1998).
M. Ohyama, H. Kozuka, and T. Yoko, J. Am. Ceram. Soc. 81, 1622 (1998).
H. Gu, D. Bao, S. Wang, D. Gao, A. Kuang, and X. Li, Thin Solid Films 283, 81 (1996).
Y. Li, W.V. Youdelis, B.S. Chao, and H. Yamauchi, J. Am. Ceram. Soc. 76, 2985 (1995).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Neves, P.P., Maia, L.J., Bernardi, M.I. et al. Synthesis and Characterization of the β-BaB2O4 Phase Obtained by the Polymeric Precursor Method. Journal of Sol-Gel Science and Technology 29, 89–96 (2004). https://doi.org/10.1023/B:JSST.0000023010.79540.6f
Issue Date:
DOI: https://doi.org/10.1023/B:JSST.0000023010.79540.6f