Abstract
A range of high resolution techniques have been used to characterise the grain boundary segregation behaviour of rare earth (RE) doped (La, Gd, Eu and Yb) alumina and spinel. TEM based techniques (HR-TEM, HAADF STEM and EDS) have been used to study the structure and chemistry of grain boundaries. The use of a HAADF detector in STEM provides atomic number contrast and easy identification of heavy (RE) segregants. This has been used to produce high resolution RE elemental maps, showing the width of the segregated region to be less than the size of the electron probe (1 nm) for all boundaries studied. EDS showed that within a 1 nm thick boundary region (an upper limit) the RE cations would account for 10 (±2)% and 15 (±2)% of the cation total in alumina and spinel respectively. Preliminary results from ultra-high resolution STEM (probe size ∼0.1 nm) suggest that, in spinel, the segregated region is actually composed of a much thinner continuous monolayer of RE atoms at the grain boundary. This is consistent with HR-TEM, which showed spinel grain boundaries possessed minimal grain boundary structural disorder.
AFM has been used to study the effect of RE grain boundary segregation on thermal grooving behaviour. The improvement in resolution that is achieved by operating in Tapping™ mode is shown to translate into an improved profile of the groove root. This has been used in conjunction with Electron Backscattered Diffraction (EBSD) to examine the relationship between grain boundary geometry and misorientation. The addition of RE dopants to alumina was found to significantly increase the size of grain boundary grooves. This can be attributed to the out-diffusion of RE segregants, an effect which compromises grain boundary energy calculations for materials with grain boundary segregation. AFM and EBSD are also used to relate anisotropic tribo-chemical polishing-wear with grain orientation.
Similar content being viewed by others
References
K. HAYASHI, O. KOBAYASHI, S. TOYODA and K. MORINAGA, Mater. Trans. JIM 32(1991) 1024.
R. APTEZ and M. P. B. VAN BRUGGEN, J. Amer. Ceram. Soc. 86(2003) 480.
A. KRELL, Mater. Sci. Eng. A 245(1998) 277.
S. LARTIGUE, L. PRIESTER, F. DUPAU, P. GRUFFEL and C. CARRY, ibid. A 164(1993) 211.
J. CHO, C. M. WANG, J. M. RICKMAN and M. P. HARMER, Acta Mater. 47(1999) 4197.
Y. M. CHIANG and W. D. KINGERY, J. Amer. Ceram. Soc. 72(2) (1989) 271.
S. WILKES, Mater. World 11(3) (2003) 23.
J. K. FARRER, J. R. MICHAEL and C. B. CARTER,in "Electron Backscatter Diffraction in Materials Science," edited by A. J. Schwartz, M. Kumar and B. L. Adams (Kluwer Academic, 2000) p. 299.
G. D. WEST, J. M. PERKINS and M. H. LEWIS, Key Eng. Mater. 264–268(2004) 801.
A. M. THOMPSON, K. K. SONI, H. M. CHAN, M. P. HARMER, D. B. WILLIAMS, J. M. CHABALA and R. LEVI-SETTI, J. Amer. Ceram. Soc. 80(2) (1997) 373.
R. F. COOK and A. G. SCHROTT, ibid. 71(1988) 50.
M. A. GÜLGÜN, R. VOYTOVYCH, I. MACLAREN, M. RÜHLE and R. M. CANNON, Interf. Sci. 10(2002) 99.
C. M. WANG, G. S. CARGILL III, H. M. CHAN and M. P. HARMER, Acta Mater. 48(2000) 2579.
H. YOSHIDA, Y. IKUHARA and T. SAKUMA, ibid. 50(2002) 2955.
J. BRULEY, J. CHO, H. M. CHAN, M. P. HARMER and J. M. RICKMAN, J. Amer. Ceram. Soc. 82(10) (1999) 2865.
D. B. WILLIAMS and C. B. CARTER,"Transmission Elec-tron Microscopy" (Plenum, New York, 1996)(a)p600, (b) p40.
S. J. PENNYCOOK, Annu. Rev. Mater. Sci. 22(1992) 22.
O. L. KRIVANEK, N. DELBY and A. R. LUPINI, Ultra-microscopy 78(1999) 1.
T. GEMMING, S. NUFER, W. KURTZ and M. RÜHLE, J. Amer. Ceram. Soc. 86(4) (2003) 590.
J. CHO, C. M. WANG, H. M. CHAN, J. M. RICKMAN and M. P. HARMER, J. Mater. Sci. 37(2002) 59.
A. RAVIKIRAN, J. Mater. Sci. Lett. 19(2000) 1041.
Idem., Tribol. Trans. 43(2000) 287.
D. M. SAYLOR and G. S. ROHRER, J. Amer. Ceram. Soc. 82(6) (1999) 1529.
W. SHIN, W. S. SEO and K. KOUMOTO, J. Eur. Ceram. Soc. 18(1998) 595.
U. D. SCHWARZ, H. HAEFKE, P. REIMANN and H. GUNTERODT, J. Microscopy 173(3) (1994) 183.
E. SAIZ, R. M. CANNON and A. P. TOMSIA, Acta Mater. 47(15) (1999) 4209.
J. M. DYNYS, R. L. COBLE, W. S. COBLENZ and R. W. CANNON,in"Sintering Processes," edited by G. C. Kuczynski (Plenum Press, New York, 1980) p. 391.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
West, G.D., Perkins, J.M. & Lewis, M.H. Characterisation of fine-grained oxide ceramics. Journal of Materials Science 39, 6687–6704 (2004). https://doi.org/10.1023/B:JMSC.0000045600.77776.08
Issue Date:
DOI: https://doi.org/10.1023/B:JMSC.0000045600.77776.08