Abstract
Spinel/zirconia-glass dental composites were prepared by melt infiltration to investigate the effect of zirconia addition on mechanical, optical properties and infiltration rate of the composites. The glass infiltration rate decreased with raising the zirconia content having a parabolic dependence of infiltration distance on time described by the Washburn equation due to the reduction in pore size. Although the optimum strength (308 MPa) of the spinel/zirconia-glass dental composite was observed when 20 wt% of zirconia was added, transmittance decreased with further increase in the zirconia content.
Similar content being viewed by others
References
H. Hornberger, Ph.D. Dissertation, University of Birmingham, 1995.
D.-J. Kim, M.-H. Lee and C.-E. Kim, J. Amer. Ceram. Soc. 82 (1999) 3167.
W. D. Wolf, L. F. Francis, C. P. Lin and W. H. Douglas, ibid. 76 (1993) 2691.
D.-J. Kim, M.-H. Lee, D. Y. Lee and J.-S. Han, J. Biomed. Mater. Res. 53 (2000) 314.
D. Y. Lee, J.-W. Jang, D.-J. Kim, I.-S. Park, J.-K. Lee, M.-H. Lee and B.-Y. Kim, J. Kor. Ceram. Soc. 38 (2001) 799.
D. Y. Lee, J.-W. Jang, M.-H. Lee, J.-K. Lee, D.-J. Kim and I.-S. Park, ibid. 39) (2002) 145.
J. Gauckler, F. Filser, P. Kocher, H. Luthy, P. Scharer and A. Feher, Intl. Symp. Advanced Materials with Biomedical Applications, Gaithersburg, MD, USA, 1999.
D. Y. Lee, D.-J. Kim and B.-Y. Kim, Intl. Conf. on Modern Materials & Technologies, Florence, Itlay, 2002.
D.Y. Lee, D.-J. Kim and D.-H. Cho, J. Mater. Sci. Lett. 17 (1998) 185.
D.-J. Kim, M.-H. Lee, D. Y. Lee and J.-S. Han, J. Biomed. Mater. Res. 53 (2000) 438.
D. Y. Lee, D.-J. Kim and Y.-S. Song, J. Mater. Sci. Lett. 21 (2002) 1223.
Standard Test-Method for Biaxial Flexure Strength (Modulus of rupture) of Ceramic Substrates. Annual Book of ASTM Standards, Vol 15.02, Sect. 15, Philadelphia, Am. Soc. Test. Mater., 1996. p. 446.
P. Chantikul, G. R. Anstis, B. R. Lawn and D. B. Marshall, J. Amer. Ceram. Soc. 64 (1981) 539.
D. B. Marshall, N. Noma and A. G. Evans, ibid. 65 (1982) C175.
S. Taruta, K. Kawashima, K. Kitajima, N. Takusagawa, K. Okada and N. Otsuka, J. Ceram. Soc. Jpn. 102 (1994) 139.
M. Guazzato, M. Albakry, M. V. Swain and S. P. Ringer, Key Eng. Mater. 240–242 (2003) 879.
D. Y. Lee, J.-W. Jang and B.-Y. Kim, J. Mater. Sci. Lett. 22 (2003) 1451.
W. B. Hillig, Comm. Amer. Ceram. Soc. 71 (1988) C96.
Idem., Ceram. Eng. Sci. Proc. 6 (1985) 674.
D. Y. Lee, D.-J. Kim, Y.-S. Song and B.-Y. Kim, Mater. Sci. Eng. A341 (2003) 98.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, D.Y. Optical, mechanical properties and infiltration rate of spinel/zirconia-glass dental composites prepared by melt infiltration. Journal of Materials Science 39, 3141–3145 (2004). https://doi.org/10.1023/B:JMSC.0000025844.84500.c3
Issue Date:
DOI: https://doi.org/10.1023/B:JMSC.0000025844.84500.c3