Abstract
The conditions to fabricate the bulk porous specimens have been studied on account of sodium borosilicate (NBS) glasses. Glass composition, heat treatment at phase separation and TiO2 addition have been considered in this study. Original glass samples of composition in mol%: sample A: 9.19 Na2O - 23.58 B2O3 - 67.23 SiO2, sample B: 9.29 Na2O - 3.17 TiO2 - 23.82 B2O3 - 63.72 SiO2 were prepared by melting reagent grade chemicals (Na2CO3, HBO3, SiO2 and AgNO3) in platinum crucibles at 1480°C for 1 h in air. The melts were poured onto stainless steel plates and were annealed at 500°C for 0.5 h after cooling. Thus, obtained samples were phase separated at 700°C for 2, 15, 25 and 50 h to study their microstructure by scanning electron microscope (SEM). Besides the direct study of the microstructure by SEM, information on glass structural changes of samples are provided by measuring in situ changes by the optical transmittance thermal analysis. The isothermal measurements were carried out at 700, 720 and 740°C. The temperature of phase separation, the leaching and nucleator addition (TiO2), significantly influence the microstructure of the resulting leached product. TiO2 additive seems to suppress crystallization of cristobalite: especially at the extended above heat treatment phase separation runs. The phase-separated domains of glasses containing above 80 moles of SiO2 are so small that it is very hard to observe them by SEM. The glass composition in our case was selected in a way to have relatively large phase separated areas easily observed by SEM at magnification 20 000·. The influence of TiO2 is not too pronounced. It seems to suppress the cristobalite crystallization, especially of longer heating runs. The image analysis of leached glasses shows the prevailing content of the skeletal phase in a comparison to pores. The TiO2 content diminishes the content of the skeletal phase.
Similar content being viewed by others
References
L. Šašek, Speciální technologie skla, SNTL–Nakladatelství technické literatury, Praha 1985, p. 107.
J. Voldán, Odmísení skel, Státní výzkumní Ústav sklá řsky v Hradci Králové, Informativní přehled, 1974, 1, 11.
K. Nakashima, K. Noda and K. Mori, J. Am. Ceram. Soc., 80 (1997) 1102.
H. Wang and G. R. Gavalas, J. Membr. Sci., 176 (2000) 75.
N. Koga, Z. Strnad, J. Šesták and J. Strnad, J. Therm. Anal. Cal., 71 (2003) 927.
J. Majling, J. Therm. Anal. Cal., 67 (2002) 201.
G. E. Romanos, V. Kasselouri, K. Beltsios and N. K. Kanellopoulos, J. Therm. Anal. Cal., 73 (2003) 183.
C. Moisescu, C. Jana, S. Habelitz, G. Carl and C. Rüssel, J. Non-Cryst. Solids, 248 (1999) 176.
Y. Yue, C. Moisescu, G. Carl and C. Rüssel, Phys. Chem. Glasses, 40 (1999) 243.
I. Fanderlik, Vlastnosti skel, Informatorium, Praha 1996, p. 285.
J. Majling, V. Kremničan, L. Pach and J. Chocholoušek, High Temperatures-High Pressures, 33 (2001) 43.
L. Pach, L'. Bača and J. Majling, Chem. Papers, 54 (2000) 265.
J. Majling, P. Šimon and V. Khunova, J. Therm. Anal. Cal., 67 (2002) 201.
M. B. Volf, Technická skla a jejich vlastnosti, SNTL, Praha 1987, p. 214.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mojumdar, S.C., Kozánková, J., Chocholoušek, J. et al. The microstructure and optical transmittance thermal analysis of sodium borosilicate bio-glasses. Journal of Thermal Analysis and Calorimetry 78, 145–152 (2004). https://doi.org/10.1023/B:JTAN.0000042162.20289.ab
Issue Date:
DOI: https://doi.org/10.1023/B:JTAN.0000042162.20289.ab