Abstract
Lithium metazirconate Li2ZrO3 with a monoclinic lattice is synthesized; the lattice parameters are: a = 0.5432 nm, b = 0.5427 nm, c = 0.903 nm, γ = 112.72°, and Z = 4. The conductivity of both the stoichiometric compound and samples rich or deficient in Li2O near this composition is determined. The conductivity of the synthesized compound reaches 0.029 S cm–1 at 600°C. The activation energy for the high-temperature segment is 13.8 kJ mol–1. An abnormal behavior (abrupt jump) of the temperature dependence of the conductivity at 430°C is discovered and attributed to a phase transition. The change in the structure in this temperature domain (400 to 500°C) is corroborated by the high-temperature X-ray analysis.
Similar content being viewed by others
REFERENCES
Gaur, H.C. and Sethi, R.S., Indian J. Chem., 1967, vol. 5, p. 485.
Hoppe, D., Z. Anorg. Chem., 1969, vol. 371, p. 306.
Helstrom, E.E. and Vangool, W., Solid State Ionics, 1981, vol. 2, p. 59.
Enriquez, L.J., Quintana, P., and West, A.R., Trans. Br. Ceram. Soc., 1982, vol. 81, p. 17.
Suiter, D.J., Lithium Based Oxide Ceramics for Tritium Breeding Application, Report MDC-E2677-UC 20, McDonnell Douglas Corp., 1983.
Wyers, G.P. and Condfunke, E.H.P., J. Nucl. Mater., 1989, vol. 168, p. 24.
Zelyutin, G.V., Cand. Sci. (Chem.) Dissertation, Yekaterinburg, 1994.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Andreev, O.L., Pantyukhina, M.I., Antonov, B.D. et al. Synthesis and Electrical Properties of Lithium Metazirconate. Russian Journal of Electrochemistry 36, 1335–1337 (2000). https://doi.org/10.1023/A:1026672202194
Issue Date:
DOI: https://doi.org/10.1023/A:1026672202194