Abstract
Polyvinylalcohol (PVA) polymer gel is a temperature sensitive polymeric gel, with a critical transition temperature (with H2O) of 310 K. At higher than 310 K, this temperature sensitive polymer gel shrinks because of discharging water, whereas at lower temperatures, the gel swelled because of absorbing water. The reversibility of the gel's volume change was confirmed by temperature swing. The adsorption behavior of an organic compound onto the PVA polymer gel in water was tested at various temperatures. The amount of adsorbed organic compound increased remarkably at temperatures higher than about 310 K. Then, it was confirmed that the organic compound in PVA polymer gel could be reversibly adsorbed and desorbed by a temperature change between 293 and 323 K. The mechanism of adsorption of the organic compound onto the PVA polymer gel could be explained by hydration and dehydration of polymer gel.
Similar content being viewed by others
Reference
S. Juodkazis, N. Mukai, R. Wakaki, A. Yamaguchi, S. Matsuo, and H. Misawa, Nature 408:178(2000).
Y. Seida and Y. Nakano, Kagaku Kogaku Ronbunshu 20:213(1994).
X. Hung, H. Unno, T. Akehata, and O. Hirasa, J. Chem. Eng. Jpn. 20:123(1987).
S. Hirotsu, Y. Hirokawa, and T. Tanaka, J. Chem. Phys. 87:1392(1987).
Y Seida and Y. Nakano, Kagaku Kogaku Ronbunshu 18:346(1992).
K. Yamagiwa, T. Sasaki, A. Ohkawa, and O. Hirasa, J. Chem. Eng. Jpn. 26:747(1993).
S. Hayashi, S. Onoue, T. Hatamachi, M. Nakamura, and J. Motoyoshiya, Koubunshi Ronbunshu 54:94(1997).
H. Suong, C. H. Won, and Y. Ikeda, Koubunshi Ronbunshu 46:673(1987).
H. Yamamoto, N. Heyamoto, Y. Takami, and J. Shibata, Kagaku Kogaku Ronbunsyu 27:786(2001).
H. Yamamoto and J. Shibata, Removal of Toxic Organic Compounds in Waste Water Using Temperature Sensitive Polymetric Gel, The Resources Processing Society of Japan, Vol. 159 (2001), p. 23.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yamamoto, H., Heyamoto, N., Matsui, T. et al. Volumetric Change and Surface Properties of Temperature-Sensitive Polyvinylalcohol (PVA) Hydrogel. International Journal of Thermophysics 24, 1385–1394 (2003). https://doi.org/10.1023/A:1026163404394
Issue Date:
DOI: https://doi.org/10.1023/A:1026163404394