Silicification and Biosilicification Part 7: Poly-L-Arginine Mediated Bioinspired Synthesis of Silica

  • Published:
Journal of Inorganic and Organometallic Polymers Aims and scope Submit manuscript

Abstract

Precipitated silica is synthesized commercially by neutralizing sodium silicate solution under harsh conditions of pH and temperature. In contrast, the formation of ornate silica structures in biological systems (biosilicification) occurs at (or close to) pH 7 under ambient conditions and is thought to be mediated by proteins. Determination of the primary sequences of these proteins has led to the identification of various amino acids that have been proposed to be important in biosilicification. The corresponding synthetic polyamino acids are now being successfully used in bioinspired materials chemistry for developing new materials and processes. Here we report the formation of well-defined silica in vitro as facilitated by poly-L-arginine (PLAr) under ambient conditions and at neutral pH. Two different silica precursors were used in this investigation; tetramethoxysilane (TMOS) and water glass. Scanning Electron Microscopy (SEM) was used for studying the silica morphology and it was revealed that the silica spheres had typical diameters in the range 300–500nm. The PLAr is a cationically charged macromolecule at neutral pH and is believed to act as a catalyst/template/scaffold for the formation of silica in vitro in analogous fashion to certain biomacromolecules that are able to facilitate silicification/biosilicification. These results are discussed here in the context of the role(s) of (bio)macromolecules that facilitate (bio)mineralization.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Subscribe and save

Springer+ Basic
EUR 32.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or Ebook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. R. K. Iler, The chemistry of silica (Wiley, New York, 1979), (a) pp. 172.

    Google Scholar 

  2. T. L. Simpson and B. E. Volcani, eds., Silicon and Siliceous Structures in Biological Systems (Springer-Verlag, New York, 1981).

    Google Scholar 

  3. N. Kroger, R. Deutzmann, and M. Sumper, Science 286, 1129(1999). The amino acid structure and sequence of the silaffin proteins isolated from the diatom C. fusiformis has been revised in subsequent publications. The findings suggest that arginine residues may be proteolytically removed after translation of the silaffins.

    Google Scholar 

  4. L. L. Brott, D. J. Pikas, R. R. Naik, S. M. Kirkpatrick, D. W. Tomlin, P. W. Whitlock, S. J. Clarson, and M. O. Stone, Nature 413, 291(2001).

    Google Scholar 

  5. K. Shimizu, J. N. Cha, G. D. Stucky, and D. E. Morse, PNAS 95, 6234(1998).

    Google Scholar 

  6. C. C. Harrison (formerly Perry), Phytochemistry 41(1), 37(1996).

    Google Scholar 

  7. S. V. Patwardhan, N. Mukherjee, M. Steinitz-Kannan, and S. J. Clarson, Chem. Commun. 10, 1122(2003).

    Google Scholar 

  8. S. V. Patwardhan, N. Mukherjee, and S. J. Clarson, J. Inorg. Organomet. Polym. 11(3), 193(2001).

    Google Scholar 

  9. S. V. Patwardhan and S. J. Clarson, Silicon Chemistry 1(3), 207(2002).

    Google Scholar 

  10. S. V. Patwardhan and S. J. Clarson, manuscript in preparation.

  11. S. J. Clarson, P. W. Whitlock, S. V. Patwardhan, L. L. Brott, R. R. Naik, and M. O. Stone, Polymeric Materials: Science & Engineering 86, 81(2002).

    Google Scholar 

  12. S. V. Patwardhan and S. J. Clarson, J. Inorg. Organomet. Polym. 13(1), 49(2003).

    Google Scholar 

  13. S. V. Patwardhan and S. J. Clarson, J. Inorg. Organomet. Polym. 12(3-4), 109(2002).

    Google Scholar 

  14. T. Coradin and J. Livage, Colloids and Surfaces B: Biointerfaces 21, 329(2001).

    Google Scholar 

  15. T. Coradin, O. Durupthy, and J. Livage, Langmuir 18(6), 2331(2002).

    Google Scholar 

  16. T. Coradin, C. Roux, and J. Livage, J. Mater. Chem. 12, 1242(2002).

    Google Scholar 

  17. L. Sudheendra and A. R. Raju, Mater. Res. Bull. 37, 151(2002).

    Google Scholar 

  18. J. N. Cha, G. D. Stucky, D. E. Morse, and T. J. Deming, Nature 403, 289(2000).

    Google Scholar 

  19. S. V. Patwardhan, N. Mukherjee, and S. J. Clarson, Silicon Chemistry 1(1), 47(2002).

    Google Scholar 

  20. S. V. Patwardhan, N. Mukherjee, and S. J. Clarson, Polym. Bull. 48(4-5), 367(2002).

    Google Scholar 

  21. S. V. Patwardhan, N. Mukherjee, and S. J. Clarson, J. Inorg. Organomet. Polym. 11(2), 117(2001).

    Google Scholar 

  22. T. Mizutani, H. Nagase, N. Fujuwara, and H. Ogoshi, Chem. Lett. 2, 133(1998).

    Google Scholar 

  23. C. C. Perry and T. Keeling-Tucker, J. Biol. Inorg. Chem. 5, 537(2000).

    Google Scholar 

  24. R. Tacke, Angew. Chem. Int. Ed. 38(20), 3015(1999).

    Google Scholar 

  25. W. Heller, Pure Appl. Chem. 12, 249(1966).

    Google Scholar 

  26. V. K. La Mer and T. W. Healy, Rev. Pure Appl. Chem. 13, 112(1963).

    Google Scholar 

  27. R. Borsali, in Handbook of Polyelectrolytes and Their Applications v. 2, S. K. Tripathy, K. Kumar, and H. S. Nalwa, eds. (American Scientific Publishers, California, 2002), Chap. 9.

    Google Scholar 

  28. S. V. Patwardhan, Ph.D. Dissertation, Department of Materials Science and Engineering (University of Cincinnati, 2003).

  29. R. E. Hecky, K. Mopper, P. Kilham, and E. T. Degens, Mar. Biol. 19 323(1973).

    Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Stephen J. Clarson.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Patwardhan, S.V., Clarson, S.J. Silicification and Biosilicification Part 7: Poly-L-Arginine Mediated Bioinspired Synthesis of Silica. Journal of Inorganic and Organometallic Polymers 13, 193–203 (2003). https://doi.org/10.1023/A:1026120309903

Download citation

  • Issue Date:

  • DOI: https://doi.org/10.1023/A:1026120309903

Navigation