Controlled temperature and relative humidity dynamic mechanical analysis of paint films

Abstract

A description is given of modifications to a dynamic mechanical analyser (DMA) to allow controlled relative humidity (RH) experiments to be performed under isothermal or thermal scanning conditions. Free film samples of polyester melamine paints (under-cured, normal-cured and over-cured) were supplied and the viscoelastic properties measured in the tensile mode of the DMA. A reduction in the glass transition temperature (T g) of up to 10°C was found as the controlled RH was increased.

This is a preview of subscription content, access via your institution.

References

  1. 1

    M. F. Macklenburg and C. S. Tumosa, ASHRAE J., 41 (1999) 77.

    Google Scholar 

  2. 2

    M. Odlyha, G. M. Foster and N. S. Cohen, et al., J. Environ. Monitor, 2 (2000) 127.

    CAS  Article  Google Scholar 

  3. 3

    M. Odlyha, N. S. Cohen and R. Campana, et al. J., Therm. Anal. Cal., 56 (1999) 1219.

    CAS  Article  Google Scholar 

  4. 4

    M. Odlyha, G. M. Foster and N. S. Cohen, et al. J., Therm. Anal. Cal., 59 (2000) 587.

    CAS  Article  Google Scholar 

  5. 5

    M. E. Nichols and C. A. Darr, J. Coating Technol., 70 (1998) 141.

    CAS  Google Scholar 

  6. 6

    D. M. Price, J. Therm. Anal., 49 (1997) 953.

    CAS  Article  Google Scholar 

  7. 7

    D. M. Price, Thermochim. Acta, 294 (1997) 127.

    CAS  Article  Google Scholar 

  8. 8

    L. Barral, J. Caro and J. Lopez, et al. J. Therm. Anal. Cal., 52 (1998) 823.

    CAS  Article  Google Scholar 

  9. 9

    K. I. Ivanova, R. A. Pethrick and S. Affrossman, J. Appl. Polym. Sci., 82 (2001) 3477.

    CAS  Article  Google Scholar 

  10. 10

    G. Kumar and K. Ramani, J. Compos. Mater., 34 (2000) 1582.

    CAS  Article  Google Scholar 

  11. 11

    P. R. Ebrahimzadeh, Wood Sci. Technol., 32 (1998) 101.

    CAS  Google Scholar 

  12. 12

    G. M. Foster, M. Odlyha and S. Hackney, Thermochim. Acta, 294 (1997) 81.

    CAS  Article  Google Scholar 

  13. 13

    T. Y. A. Chan and M. Odlyha, Thermochim. Acta, 269 (1995) 755.

    Article  Google Scholar 

  14. 14

    M. Odlyha and T. Y. A. Chan, Thermochim. Acta, 263 (1995) 127.

    Article  Google Scholar 

  15. 15

    M. Odlyha, G. M. Foster and S. Hackney, et al. J. Therm. Anal., 50 (1997) 191.

    CAS  Article  Google Scholar 

  16. 16

    J. Foreman, American Laboratory, 29 (1997) 21.

    CAS  Google Scholar 

  17. 17

    It All Starts with the Finish, NCCA Chicago, Illinois, 1997.

  18. 18

    Coil Coating Today, January 1995.

  19. 19

    W. Wicks, F. N. Jones and S. P. Pappas, Org. Coat. Sci. & Technol., 1 (1992).

  20. 20

    T. P. Golden, Personal Communication, 1999.

  21. 21

    L. Hill, J. Coating Technol., 62 (1992).

  22. 22

    G. Wisanrakkit and J. K. Gillham, J. Coating Technol., 35 (1990) 783.

    Google Scholar 

Download references

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Foster, G.M., Ritchie, S. & Lowe, C. Controlled temperature and relative humidity dynamic mechanical analysis of paint films. Journal of Thermal Analysis and Calorimetry 73, 119–126 (2003). https://doi.org/10.1023/A:1025133508109

Download citation

  • dynamic mechanical analyser
  • relative humidity
  • films
  • paint